Abstract
Modern optoelectronics needs development of new materials characterized not only by high optical transparency and electrical conductivity, but also by mechanical strength, and flexibility. Recent advances employ grids of metallic micro- and nanowires, but the overall performance of the resulting material composites remains unsatisfactory. In this work, we propose a new strategy: application of natural scaffoldings perfected by evolution. In this context, we study two bio-inspired networks for two specific optoelectronic applications. The first network, intended for solar cells, light sources and similar devices, has a quasi-fractal structure and is derived directly from a chemically extracted leaf venation system. The second network is intended for touch screens and flexible displays, and is obtained by metalizing a spider’s silk web. We demonstrate that each of these networks attain an exceptional optoelectonic and mechanical performance for its intended purpose, providing a promising direction in the development of more efficient optoelectronic devices.
Similar content being viewed by others
Introduction
The advent of optoelectronics in the 1950s has depended on the development of transparent conductors1. Such electrically conducting and optically transparent materials play a critical role in numerous important optoelectronic devices such as photovoltaic sensors, solar cells, photo diodes and lasers, all of which harvest or emit light. However, high optical transmission and good electrical conductivity are mutually limiting requirements since electrical carriers invariably scatter photons, and require a compromise. One successful approach had been to exploit the fundamental property of any carrier plasma, electromagnetic transparency above its plasma frequency. This idea led to the development of an entire class of materials (metal-oxides), which dominate the field today, such as the ubiquitous indium tin oxide (ITO), a metal with the plasma frequency in the infrared range, and thus transparent in the visible range2. However, while metal-oxides often have desirable electro-optical properties, they are also brittle, and this deficiency limits their usefulness in many practical applications. To address these challenges, new approaches have been recently devised, based on metallic micro- and nanoscaffoldings (such as wire and nanowire grids3,4,5,6,7,8,9,10, nanoparticles11,12 and so on) and even using atomic-scale scaffolds such as graphene13,14. Structures of this kind do in fact improve mechanical flexibility, but their electro-optical performance has not yet been sufficiently high.
In this work, we propose a new strategy, based on adopting ingenuous network designs readily found in nature. Indeed, micro- and nanoscaffolds of exceptional properties occur naturally in many biological systems, generated by a genetic code of a given organism, and self-assembled during the organism development15,16,17. These structures perform various functions, such as a support for mechanical cellular integrity (for example, nanoscopic cellular cytoskeletons)18, nutrients distribution via microfluidic channels (for example, leaf or insect wing venations)19,20, light management (for example, the Moth eye)21, improved mobility (for example, shark skin microtextures)22,23,24, super-hydrophobic behaviour (Lotus leaf)23, antibacterial protection (cicada wings)25 and so on. Some of the most ingenious man-made material designs, such as velcro23, have effectively ‘copied’ existing solutions in nature. Moreover, most of these solutions have been undergoing a natural process of an evolutionary optimization for millions of years.
In this work, inspired by such biostructures, we develop two distinct highly conducting and transparent microscaffold networks, each satisfying different requirements dictated by a specific application. We demonstrate that these networks show exceptional performance, outperforming most other recently proposed micro- and nanoscaffold schemes.
Results
The first network, to be employed as a window electrode for solar cells, light sources (for example, light-emitting diode), transparent heaters and so on, is obtained by metallization of a leaf venation (LV), a natural microfluidic network structure present in all leafs. This structure has been modified by evolution (at each generation) towards the optimized function of efficient delivery of nutrients to every cell of a leaf from a central vein, with very low light shading. The result of this natural optimization process is a quasi-fractal (or hierarchical) structure of LV26. Even though the process of this evolutionary optimization still continues, as evidenced by the variety of the existing LV structures today, the natural quasi-fractal structures are expected to be close to the optimum. Indeed, striking similarities have been observed for natural and optimal networks (obtained by computationally minimizing the total rate of energy expenditure), in their fractal aggregation structure27. This implies, that a whole class of natural hierarchical (quasi-fractal) structures exist, which are close to optimum, that is, each can be considered an approximately optimal network. Note that the question whether strictly fractal structures are indeed optimal, continues to be debated28,29,30. The key justification for employing the metalized near-optimal LV network as an efficient electrode, is the assumption that the electrical current flow properties of this structure are analogous to those of fluid. Indeed, the electric current flow is described by the Laplace equation, and so is the inviscid, incompressible and irrotational fluid flow31. Thus, even though not strictly optimal, the metallized, quasi-fractal LV networks are expected to outperform the uniform networks, as well as the primitive hierarchical bar-finger structures (often used) in solar cells, light sources and other similar applications. The second network, to be employed in various display applications (including touch screens and flexible displays), is obtained by metallizing a common silk spider web (SSW), a natural insect trap, made of nearly invisible, nanoscopically thin threads of exceptional mechanical strength and elasticity32.
LV networks
For the LV network, we have chosen the plant Magnolia alba (common name White Jade Orchid Tree). This abundant plant has leaves about 20 cm in length, of lanceolate shape and prominent secondary veins paired oppositely (pinnate venation), see Fig. 1a. From these secondary veins emanate smaller veins forming an angular network (reticulate veins). Insets in this figure show subsequent magnifications of the dotted area, with the finest, chemically extracted microstructure of the network shown in the scanning electron microscope (SEM) image (Fig. 1b). The smallest veins have diameter of about 50–110 μm, and are split into two shorter branches at each node. Networks of this kind, called ‘umbrella trees’, are non-uniform fractals, whose fractal properties pertain to the ‘canopy,’ that is, to the structure formed by the tips of the branches rather than the whole pattern33. The difficulty in characterizing the structure shown in Fig. 1b, and determining its approximate fractal dimension using the standard method based on branch ordering taxonomy34,35 is the irregular nature of the venation network, which leads to large uncertainty in the measurements. An alternative approach, proposed here, is to consider angles between subveins at each bifurcation level, which are relatively easy to measure. Umbrella canopies usually display a particular branching angle for a given magnification ratio, namely the smallest angle compatible with self-avoidance (in two dimension), as discussed in ref. 33. Since the fractal dimension is a nearly linear function of the branching angle ϑB, based on data taken from plate 155 in ref. 33, it is easy to convert ϑB into the fractal dimension DS. Using five prominent nodes in Fig. 1a yields ϑB=110±10o, and, accordingly, Ds=1.4±0.2. This value is consistent with the typical range 1.4–1.8 as reported in ref. 36, and thus confirms that the network is an approximate non-uniform fractal. Note that the maximal distance between veins is much less than 1,000 μm, much smaller (better for current extraction) than in the conventional, commercial c-Si solar cells. The fabrication process for the LV metallic network skeleton is shown in Fig. 1c. It involves three steps: removing mesophyll while leaving the vein structure of the leaf intact by alkali solution etching37, metal coating (by silver sputtering) and transferring the network onto a chosen substrate, which could be glass, polymer or semiconductor. With a proper care, good adhesion could be assured.
Spider web networks
For the SSW network, we have chosen a common spider Agelena labyrinthica, since its web has a distinct two-dimensional character, ideal for planar electrodes. Figure 2a shows schematically the processes of the SSW-based silver network fabrication, which includes three steps: collecting SSW onto a sample holder, metal coating (Ag sputtering) and finally transferring the SSW network onto a substrate.
The micro- and nanomorphology of this network is demonstrated with SEM images in Fig. 2b–f. This is a nanostructure, with diameters of individual threads of the order of 100 nm, and the inter-thread spacing of the order of a few microns. Figure 2c shows an incomplete core-shell structure: silk core (~80 nm diameter), coated with an ~40-nm thin layer of silver. AFM image of the silver SSW network, and the corresponding AFM profile are shown in Supplementary Fig. 1.
Electro-optical performance
The electro-optical properties of LV and SSW networks are summarized in Fig. 3a, which presents the transmittance (T) versus sheet resistance (Rs) measurements, compared with those of other networks reported in the literature4,5,6,7,8,9,10, as well as the conventional transparent conducting electrode material ITO. Transmittance represents percentage of the light flux transmitted across the sample at a given frequency (or vacuum wavelength, here chosen to be λ=550 nm). The sheet resistance is the resistance (at zero frequency) of a square of a thin film of thickness d, measured from side-to-side, also given by RS=ρ/d, where ρ is the material resistivity. The data displayed are also quantified by using the so-called figure of merit, defined as4,13 F=σdc/σopt, where σdc=1/ρ is the electrical conductance at zero frequency and σopt is the electrical conductance measured in the optical frequency range (typically at the vacuum wavelength λ=550 nm). It has been shown13 that F is simply related to T and RS via
Thus, F can be simply determined by fitting equation (1) to the data points for a given network, with F as the fitting parameter. These fits are shown in Fig. 3a as lines, and the corresponding extracted F’s are indicated in the legend. Clearly, larger figure of merit F corresponds to more efficient networks. Our SSW networks are represented in Fig. 3a as solid squares (single layer), blue triangles (two layers) and solid circles (four layers) and our LV networks by orange right-pointing triangles (colour online).
All our networks show superior performance, with the record high figures of merit, in the range F=1,000 to 1,700, and the four-layer SSW network reaching approximately F=1,700. Note that all the other reported uniform networks (based on nanowires, nanotroughs, nanocracks and so on) have much smaller figure of merit in the range F<400. In particular, our networks are superior to the industry standard ITO. This is further illustrated in Fig. 3b, which shows transmittances versus wavelength for our SSW-based networks and for the standard, 150-nm thick ITO film. Clearly, a single layer of our SSW network is ~10% more transparent, and by a factor of ~2 more conducting than the ITO film. Two layers of this network are equally transparent, but six times less resistive than ITO.
Our LV network has also a very high figure of merit, F=1,000, even though its quasi-fractal structure is not far from optimal for current delivery but not necessarily for minimizing the total sheet resistance. To account for the LV network quasi-fractal structure, we have also measured resistances of the LV, as well as the uniform (non-hierarchical) SSW and the ‘crack’4 networks, adjusted to have all identical transmittances (of about 85%), and with the sample contacts configuration chosen so that the main vein of the LV network and its local, highly bifurcated region were contacted. The same contact configuration was also used for the SSW and ‘crack’ networks. The resulting resistance of the LV network has been found to be reduced by the factors of 0.81 and 0.61 compared with the SSW and the ‘crack’ networks, respectively, clearly demonstrating the advantage of the quasi-fractal structure for a directed current transport.
Figure 3c–f shows optical images of the LV network, as well as one, two and four layers of the SSW network, respectively. Photographs were taken with the networks placed against a printed logo to visualize transparency. Even though the LV network is very transparent, the large-scale veins clearly visible in the inset of Fig. 3c make this network not suitable for display applications. However, in addition to solar cell and light source applications, LV network also can be used as a transparent film heater. Such a heater is demonstrated in the Supplementary Fig. 2.
Elastic properties
We now address elastic properties of the networks. Figure 4a is a plot of the SSW network resistance (after tension release) versus strain. Three ranges can be identified. In the elastic range (strains smaller ~25%), the original network resistance is repeatedly and fully recovered after each strain. In the reversible range (for larger strains, but smaller than ~100%), for multiple stretching the sample returns repeatedly the same value of the total resistance. For strains larger than ~100% (irreversible range), repeated stretching leads to the overall increase of the total resistance. The inset in Fig. 4a shows time evolution of the network resistance subject to a sequence of eight stretching pulses, each located at the beginning of the corresponding peak. The first six correspond to 50% and the last two to 100% strain pulses. The microscopic investigation of the samples clarifies this behaviour. In the elastic range, stretching of the SSW network breaks no fibres, since they are quite loose (see Fig. 2d), with very few fibres fully stretched. The stretching therefore simply straightens the fibres, which causes only minimal damage of the metal coating. In the reversible range, stretching breaks some fraction of the fibres, which causes an increase of the total resistance. However, if the strain is limited to the same level at each subsequent stretching, no further breaking of fibres occurs, and resistance repeatedly returns to the same value. Finally, in the irreversible range, a large number of fibres, as well as the coating, become broken, while the remaining are near the breaking point, irreversibly affecting resistance of the metallic coating. The network conduction becomes unstable, very sensitive to stretching and fluctuates with every stretch. SSW network is therefore shown to have excellent stability only in the elastic range. Figure 4b further confirms this by demonstrating network’s resilience to repeated elastic bending; its resistance changes reversibly from 2.2 to 2.7 Ω (180°, 1 mm bending radius), even after 1,500 bending events. Due to these remarkable properties, SSW-based networks could be used in touch screen displays and stretch sensors. A touch-screen device based on a SSW network is demonstrated in the Supplementary Fig. 3.
Scale and scalability
Even though both LV and SSW networks are clearly good candidates for applications, the scalability and associated with that costs must be assessed. The structure of the LV network could be simply and massively replicated by printing. A schematic of a possible method is shown in Fig. 4c, where an LV network pattern is engraved on a drum, allowing large-scale roll-to-roll printing of the pattern on flat substrates. Figure 4d provides a schematic of the LV network replication by using a contact photolithography; this method could be used to engrave the drum shown in Fig. 4c. Figure 4e is an image of an LV network printed directly from the LV in silver ink on paper. This was achieved by attaching LV directly to a metallic block, and then using it as a stamp. The resolution of the stamped image is very good, with most features reproduced. Because of the relatively large size of the features in the LV network, photolithography can be employed as a part of the engraving procedure. Figure 4f shows an image of the photolitographically obtained LV network print (details in Supplementary Fig. 4). While such LV networks would be relatively easy and inexpensive to replicate on a large scale, a method to do the same for the SSW networks must yet be invented. A possible practical way could be to base the SSW-like network on inexpensive polymers (for example, Kevlar nanofiber, nanocellulose and so on).
Discussion
In conclusion, we have developed two different metallic networks for specific applications, inspired by, and employing natural network structures. The first network, designed for solar cells, light sources and surface heaters, exploits the fractal properties of LV systems. This network achieves superior current delivery to, and extraction from, a substrate, with minimal optical shading. The second network, envisioned for display applications and based on a spider web, was demonstrated to have outstanding electro-optical and mechanical properties, strength and flexibility. In particular, these two nature-inspired structures outperform all electrode systems and optoelectronic networks devised here-to-fore.
Methods
Leaf etching by alkali solution
The 0.1 g ml−1 NaOH solution (lab prepared) was used for etching. Magnolia alba leaves were immersed in the solution at 50–70 °C for 3 h. By continually tapping the softened leaf, the mesophyll was removed leaving the vein structure of the leaf intact. This procedure was followed by washing and drying.
Ag and ITO film depositions
Sputtering (AJA International. ATC Orion 8, USA) was used to deposit Ag and ITO films. The SSW and LV structures were placed in vacuum chambers, and the sputtering was performed at ~50 °C to avoid damaging the samples.
Performance measurements
Morphologies of samples were characterized in a SEM system (JEOL JCM-5700, Tokyo, Japan), and by employing an optical microscope (MA 2002, Chongqing Optical & Electrical Instrument Co.). The sheet resistance of samples was measured by employing the standard van der Pauw method. Four contacts were deposited at the corners of a square sample (2 × 2 cm), numbered clockwise 1–4, and I–V data were recorded with the Keithley 2400 Source meter. Sheet resistance was calculated from the usual formula: Rab,cd=4.5(R12,34+R34,12+R14,23+R23,14)/4, with Rab,cd=Uab/Icd and where Uab is the voltage drop between ‘a’ and ‘b’ contacts, produced by current Icd flowing from contact ‘c’ to contact ‘d’. The second method, employed when the van der Pauw could not be used (for example, while the sample was stretched) was the two-probe method. In this method, two parallel electrodes (sputtered narrow silver lines of length L) were placed on the surface of the sample. Sheet resistance was calculated from Rs=R*L/W, where R is the measured resistance and the sample width is W. A modified two-probe method was also used for the directed current transport in the LV network, in which one electrode was a narrow line, and the other was a circular silver contact. In this case, a simple resistance between the electrodes was measured. To test the flexibility of SSW and LV networks, the structures were transferred to elastic substrates, for example, PDMS (Polydimethylsiloxane) and PET (polyethylene terephthalate). A lab-made stretching and bending system was used, with an automatic control and a data acquisition system. Optical transmittance was measured in an integrating sphere system (Ocean Optics, USA). These measurements were normalized to the absolute transmittance of the substrate (glass, PET or PDMS).
Additional information
How to cite this article: Han, B. et al. Bio-inspired networks for optoelectronic applications. Nat. Commun. 5:5674 doi: 10.1038/ncomms6674 (2014).
References
Ginley, D. S., Hosono, H. & Paine, D. C. Handbook of transparent conductors Springer (2010).
Wang, Y., Plummer, E. & Kempa, K. Foundations of plasmonics. Adv. Phys. 60, 799–898 (2011).
Ye, S., Rathmell, A. R., Chen, Z., Stewart, I. E. & Wiley, B. J. Metal nanowire networks: the next generation of transparent conductors. Adv. Mater. 26, 6670–6687 (2014).
Han, B. et al. Uniform self‐forming metallic network as a high‐performance transparent conductive electrode. Adv. Mater. 26, 873–877 (2013).
De, S. et al. Silver nanowire networks as flexible, transparent, conducting films: extremely high DC to optical conductivity ratios. ACS Nano 3, 1767–1774 (2009).
Leem, D. S. et al. Efficient organic solar cells with solution‐processed silver nanowire electrodes. Adv. Mater. 23, 4371–4375 (2011).
Tokuno, T., Nogi, M., Jiu, J., Sugahara, T. & Suganuma, K. Transparent electrodes fabricated via the self-assembly of silver nanowires using a bubble template. Langmuir 28, 9298–9302 (2012).
van de Groep, J., Spinelli, P. & Polman, A. Transparent conducting silver nanowire networks. Nano Lett. 12, 3138–3144 (2012).
Wu, H. et al. A transparent electrode based on a metal nanotrough network. Nat. Nanotechnol. 8, 421–425 (2013).
Guo, C. F., Sun, T., Liu, Q., Suo, Z. & Ren, Z. Highly stretchable and transparent nanomesh electrodes made by grain boundary lithography. Nat. Commun. 5, (2014).
Layani, M. & Magdassi, S. Flexible transparent conductive coatings by combining self-assembly with sintering of silver nanoparticles performed at room temperature. J. Mater. Chem. 21, 15378–15382 (2011).
Gao, J. et al. Transparent nanowire network electrode for textured semiconductors. Small 9, 733–737 (2013).
Hecht, D. S., Hu, L. & Irvin, G. Emerging transparent electrodes based on thin films of carbon nanotubes, graphene, and metallic nanostructures. Adv. Mater. 23, 1482–1513 (2011).
Du, J., Pei, S., Ma, L. & Cheng, H. M. 25th anniversary article: carbon nanotube‐and graphene‐based transparent conductive films for optoelectronic devices. Adv. Mater. 26, 1958–1991 (2014).
Camazine, S. Self-Organization in Biological Systems Princeton Univ. Press (2003).
Tan, J. & Saltzman, W. M. Biomaterials with hierarchically defined micro-and nanoscale structure. Biomaterials 25, 3593–3601 (2004).
Zhou, H., Fan, T. & Zhang, D. Biotemplated materials for sustainable energy and environment: current status and challenges. ChemSusChem 4, 1344–1387 (2011).
Michie, K. A. & Löwe, J. Dynamic filaments of the bacterial cytoskeleton. Annu. Rev. Biochem. 75, 467–492 (2006).
Arber, A. The Natural Philosophy of Plant Form Cambridge Univ. Press (2012).
Chapman, R. F. The Insects: Structure and Function Cambridge Univ. Press (1998).
Xia, F. & Jiang, L. Bio‐inspired, smart, multiscale interfacial materials. Adv. Mater. 20, 2842–2858 (2008).
Ball, P. Engineering shark skin and other solutions. Nature 400, 507–509 (1999).
Singh, R. A., Yoon, E.-S. & Jackson, R. L. Biomimetics: the science of imitating nature. Tribol. Lubri. Technol. 65, 40–47 (2009).
Dean, B. & Bhushan, B. Shark-skin surfaces for fluid-drag reduction in turbulent flow: a review. Philos. Trans. R. Soc. A 368, 4775–4806 (2010).
Ivanova, E. P. et al. Natural bactericidal surfaces: mechanical rupture of Pseudomonas aeruginosa cells by cicada wings. Small 8, 2489–2494 (2012).
Coppens, M.-O. Scaling-up and-down in a nature-inspired way. Ind. Eng. Chem. Res. 44, 5011–5019 (2005).
Rinaldo, A., Rodriguez-Iturbe, I., Rigon, R., Ijjasz-Vasquez, E. & Bras, R. Self-organized fractal river networks. Phy. Rev. Lett. 70, 822–825 (1993).
Banavar, J. R., Maritan, A. & Rinaldo, A. Size and form in efficient transportation networks. Nature 399, 130–132 (1999).
Banavar, J. R. et al. Sculpting of a fractal river basin. Phys. Rev. Lett. 78, 4522–4525 (1997).
Maritan, A., Colaiori, F., Flammini, A., Cieplak, M. & Banavar, J. R. Universality classes of optimal channel networks. Science 272, 984–986 (1996).
Moon, P. Field theory for engineers. Am. J. Phys. 29, 717–717 (1961).
Cranford, S. W., Tarakanova, A., Pugno, N. M. & Buehler, M. J. Nonlinear material behaviour of spider silk yields robust webs. Nature 482, 72–76 (2012).
Mandelbrot, B. B. The Fractal Geometry of Nature Freeman (1983).
Horton, R. E. Erosional development of streams and their drainage basins; hydrophysical approach to quantitative morphology. Geol. Soc. Am. Bull 56, 275–370 (1945).
Strahler, A. N. Hypsometric (area-altitude) analysis of erosional topography. Geol. Soc. Am. Bull 63, 1117–1142 (1952).
de Araujo Mariath, J. E., dos Santos, R. P. & dos Santos, R. P. Fractal dimension of the leaf vascular system of three Relbunium species (Rubiaceae). Rev. Bras. Biociênc. 8, 30–33 (2010).
Melcher, U., Gardner, C. O. Jr & Essenberg, R. C. Clones of cauliflower mosaic virus identified by molecular hybridization in turnip leaves. Plant Mol. Biol. 1, 63–73 (1981).
Acknowledgements
This work has been supported by the following projects: ‘The Leading Talents of Guangdong Province Program (2011)’, ‘Special Construction Funds of Guangdong Province Foundation’, No. 2013KJCX0056, ‘China National Undergraduate Innovation Experiment Program (2013)’ and partial support from PCSIRT and Green Optoelectronic Technologies Interdisciplinary Innovation Platform in China.
Author information
Authors and Affiliations
Contributions
B.H. and J.G. conceived the idea. B.H., Y.H., R.L., Q.P., J.L. and K.P. conducted material fabrication and tests. J.G., K.K., A.H. and Z.R. co-wrote the paper. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-4 and Supplementary References (PDF 548 kb)
Rights and permissions
About this article
Cite this article
Han, B., Huang, Y., Li, R. et al. Bio-inspired networks for optoelectronic applications. Nat Commun 5, 5674 (2014). https://doi.org/10.1038/ncomms6674
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms6674
This article is cited by
-
A multimaterial 3D printing-assisted micropatterning for heat dissipation applications
Advanced Composites and Hybrid Materials (2023)
-
Flexible biodegradable transparent heaters based on fractal-like leaf skeletons
npj Flexible Electronics (2020)
-
Biomimic Vein-Like Transparent Conducting Electrodes with Low Sheet Resistance and Metal Consumption
Nano-Micro Letters (2020)
-
Recyclable and Flexible Starch-Ag Networks and Its Application in Joint Sensor
Nanoscale Research Letters (2019)
-
Bioinspired networks consisting of spongy carbon wrapped by graphene sheath for flexible transparent supercapacitors
Communications Chemistry (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.