Abstract
Oxygen is vital for the existence of all multicellular organisms, acting as a signalling molecule regulating cellular activities. Specifically, hypoxia, which occurs when the partial pressure of oxygen falls below 5%, plays a pivotal role during development, regeneration and cancer. Here we report a novel hypoxia-inducible (HI) hydrogel composed of gelatin and ferulic acid that can form hydrogel networks via oxygen consumption in a laccase-mediated reaction. Oxygen levels and gradients within the hydrogels can be accurately controlled and precisely predicted. We demonstrate that HI hydrogels guide vascular morphogenesis in vitro via hypoxia-inducible factors activation of matrix metalloproteinases and promote rapid neovascularization from the host tissue during subcutaneous wound healing. The HI hydrogel is a new class of biomaterials that may prove useful in many applications, ranging from fundamental studies of developmental, regenerative and disease processes through the engineering of healthy and diseased tissue models towards the treatment of hypoxia-regulated disorders.
Similar content being viewed by others
Introduction
An emerging paradigm in the mimicry of three-dimensional (3D) microenvironments involves using a variety of bioinspired materials to reconstruct critical aspects of the native extracellular niche1,2. Synthetic hydrogels have attracted substantial attention as 3D microenvironments owing to their structural similarity to the natural extracellular matrix (ECM) and their tunable properties3,4. Researchers have endeavoured to develop synthetic hydrogels to recapitulate temporal and spatial complexity in the native ECM, which varies not only in composition but also in physico-chemical parameters, including cell adhesion ligands5, growth factors/cytokines6, mechanical properties7, proteolytic degradability8 and topography9. Thus, these studies have established how such parameters individually or synergistically regulate cell behaviour.
Oxygen (dioxygen, O2) is vital for the existence of all multicellular organisms, acting as a signalling molecule for cells and regulating their metabolism, survival, cell-to-cell interactions, migration and differentiation10,11. Cellular responses to O2 deprivation (hypoxia) are primarily regulated by hypoxia-inducible factors (HIFs) that accumulate under hypoxic conditions and activate the expression of numerous genes that regulate myriad cellular activities12. HIFs act as key regulators, promoting angiogenesis during embryonic development, tumour progression and tissue regeneration13,14,15. HIFs regulate the expression of many angiogenic genes that promote vascular differentiation and morphogenesis, such as vascular endothelial growth factor (VEGF), VEGF receptor 2 (VEGFR2)16,17,18, angiopoietin 1 (ANG1)19 and matrix metalloproteinases (MMPs)20,21,22,23,24. Although hypoxia plays a pivotal role in vascular development, nobody has simulated controlled hypoxia in a 3D microenvironment.
This study reports a new class of O2-controlling biomaterials, hypoxia-inducible (HI) hydrogels, that can serve as 3D hypoxic microenvironments. We demonstrate control over and precise prediction of dissolved O2 (DO) levels and gradients in the HI hydrogel. The HI hydrogel matrix stimulates tubulogenesis of endothelial-colony-forming cells (ECFCs) by activating HIFs and promotes rapid neovascularization from the host during subcutaneous wound healing. To our knowledge, this is the first hydrogel material with precisely controlled intramural DO levels, a new class of biomaterials for a wide range of possible applications.
Results
Design of HI hydrogels
We began by hypothesizing that conjugating ferulic acid (FA) to a polymer backbone would let us fabricate a HI hydrogel by consuming O2 in laccase-mediated reactions. Though many fields (for example, food chemistry and biosensors25) have explored such reactions, derived from phytochemistry, they have not yet been used to fabricate O2 controllable biomaterials.
We selected gelatin (Gtn) as the polymer backbone for its cell-response properties, including cell adhesion sites and proteolytic degradability, which are critical in vascular morphogenesis26,27. Gtn would enable a relatively simple functionalization with FA for the formation of intramural hypoxia for both in vitro and in vivo vascular inductions. This approach could also generate HI hydrogels using other natural/synthetic polymers, like polyethylene glycol, hyaluronic acid and dextran. These might require incorporation of adhesion sites, such as Arg-Gly-Asp, and additional degradability features, such as MMP-sensitive peptides, depending on the application.28,29,30
We synthesized HI hydrogels by coupling carboxyl groups of FA to amine groups of Gtn (GtnFA) via a carbodiimide-mediated reaction (Supplementary Fig. 1; Supplementary Table 1) and characterized the chemical structure of the functionalized polymer using 1H NMR, indicating the specific peaks of anomeric carbon and alkyl protons of Gtn, as well as the aromatic protons of FA (Supplementary Fig. 2a). UV/VIS spectroscopy determined the degree of substitution (DS) of the FA molecule (Supplementary Fig. 2b). We fabricated the HI hydrogel by crosslinking FA molecules via a laccase-mediated chemical reaction (Fig. 1a) to form diferulic acid (DiFA)31, which yields polymer networks (Fig. 1b)32.
To test hydrogel formation and viscoelastic modulus, we performed rheological analysis, including dynamic time sweep of hydrogels with varying laccase concentration (Fig. 2a–c). The crosslink point of elastic (G′) and viscous (G″) modulus, which provides an estimate of the gelation time, occurs within 2–30 min, suggesting that laccase concentration affects the network formation kinetics. These data agree with the gelation kinetics observed by phase transition (Fig. 2d,e), suggesting that higher concentrations of laccase or polymer induce faster hydrogel formation. These results could have occurred because the rate of radical generation, which can induce DiFA formation, increased with higher laccase and polymer concentrations. Moreover, viscoelastic measurements showed tunable mechanical properties of the HI hydrogels (35–370 Pa), suggesting that they could maintain their 3D shapes, providing structural frameworks as extracellular microenvironments to support cell function. Another parameter to consider in designing cellular microenvironments, proteolytic degradability allows cell migration and niche remodelling4,8. Thus, we examined protease-sensitive degradation of HI hydrogels. We observed that hydrogels incubated with collagenase degraded completely within 3 h, the rate varying with the concentrations of collagenase (0.001–0.05%) and polymer (3–5%) solutions (Fig. 2f,g). These data demonstrate that the proteolytic degradability of the Gtn-based HI hydrogel is retained following functionalization with FA molecules.
We evaluated the cytocompatibility of hydrogels using human fibroblasts. We first examined the toxicity of the GtnFA conjugate and laccase because precursor and free enzyme molecules have the potential to induce toxicity in a hydrogel matrix. We observed no significant cytotoxicity in the GtnFA polymer and laccase (80–98% of control) (Supplementary Fig. 3a,b). We also encapsulated fibroblasts within the HI hydrogels to determine cell viability and morphological changes within the matrix. The results show a predominantly viable fibroblast population, as well as cell spreading and elongation within HI hydrogel matrices (Supplementary Fig. 3c,d). Similar viability was observed when encapsulating ECFCs (Supplementary Fig. 3e). We demonstrate the successful preparation of cytocompatible HI hydrogels with tunable parameters essential for their use as a 3D cellular microenvironment2,4,33.
Controllable O2 levels and model predictions
We next hypothesized that GtnFA induces polymer network formation by O2 consumption during hydrogel formation. To determine O2 levels within the matrix, we monitored DO levels at the bottom of hydrogels using a noninvasive sensor patch34. We found that several factors—including hydrogel thickness, laccase concentrations, and DS values of polymer—affected DO levels and O2 consumption rates. It should be noted that we used the same concentration of FA molecule, maintaining the same crosslinking density and thus diffusivity in all samples examined. Increasing laccase concentrations decreased both the DO levels and the time to reach the minimum DO level (DOmin), demonstrating that high laccase concentrations induce rapid O2 consumption reactions and low O2 levels (Fig. 3a). These data agree with the results of hydrogel formation studies, indicating that laccase concentrations significantly affect both hydrogel network formation kinetics and O2 consumption rates. Similarly, the higher DS value of FA molecules resulted in the lowest DO levels (Fig. 3b). Decreasing the FA content increased the DOmin. This is expected, since the FA molecule acts as a crosslinker, consuming O2 molecules during hydrogel network formation.
Finally, we determined the influence of hydrogel thickness on DO levels. We varied gel thickness in a volume-dependent manner. Figure 3c shows that controllable DO levels depend on the HI hydrogel thickness (3 wt%, DS 45, and 25 U ml−1 laccase). The DOmin decreased as thickness increased, demonstrating that intramural DO levels vary with matrix thickness. Notably, we observed DO levels within thick hydrogels (>2.5 mm) reaching hypoxic levels (<5%).
To enable accurate prediction of DO levels and gradients within HI hydrogels, we employed a mathematical model developed in our previous report.34 We assumed that O2 consumption kinetics during hydrogel formation follows Michaelis–Menten kinetics, as shown in equation (2). To accurately estimate DO gradients in HI hydrogels, we first determined the Vmax and Km parameters. We measured DO levels in hydrogels (3 wt%, DS45, and 25 U ml−1 laccase) until they reached steady state. We plotted the O2 consumption rate of the laccase-mediated reaction (experimental data) and the theoretical Michaelis–Menten equation (numerical model) using the initial Vmax and Km values. We then calibrated the graphs while varying the Vmax and Km parameters to obtain the best fit to the experimental values according to the residual sum of squares method (Supplementary Fig. 4). We determined that the Vmax and Km values of our HI hydrogels were 0.43 μM/second and 70 μM, respectively. We then compared the experimental DO values at the different hydrogel thicknesses to numerical DO values determined by the mathematical modelling to confirm the reliability of the given parameters. As can be seen, the experimental values are similar to the numerical model simulated by using the obtained Vmax and Km values (Fig. 3d). These results showed that the O2 consumption rate (for example, hydrogel formation kinetics) follows the theoretical Michaelis–Menten equation.
Using the Michaelis–Menten parameters determined for the given conditions, we estimated the DO gradients throughout the gel depth in a two-layer (air-hydrogel) model. We found that, 30 min after hydrogel formation, the 5 DO levels at the bottom of hydrogels decreased as gel thickness increased, due to insufficient O2 diffusion (Fig. 3e), and a broad range of O2 tensions occurred within the gel matrices (Fig. 3f). For instance, the O2 gradient of the thin hydrogel (1.25 mm) ranged from 15 to 17%, while a thicker one (3.13 mm) exhibited a 1.8–21% range. Measurements of DO at different hydrogel depths confirmed the accuracy of the simulation, demonstrating DO gradient throughout the hydrogel matrix (Fig. 3g,h) and the robust effect of hydrogel thickness on O2 levels and gradients.
Overall, O2 measurements and computer simulations showed that our HI hydrogels consume O2 during their formation, yielding an O2 gradient within the matrix. Various factors could affect O2 consumption rate and thus regulating not only the level of O2 tensions but also the range of O2 gradients. This is a very important advantage of the HI hydrogels as O2 gradients are generated in many tissues during embryonic development, tissue regeneration and cancer growth13,35,36,37,38. Overall, the HI hydrogels may provide an innovative approach to generate hypoxic environments towards the delineation of the mechanism by which hypoxia regulates cellular responses and may facilitate the discovery of pathways involved in O2 gradient environments.
Hypoxic microenvironment for vascular tube formation
We next speculated that HI hydrogel could provide controllable hypoxic environments to generate tissue models in vitro. Towards this, we selected an optimized hydrogel sample (3 wt% of polymer concentration, DS 45 of FA, and 25 U ml−1 laccase) and controlled the DO levels by altering thickness.
We first performed computer simulation for media effects on O2 gradients using a three-layer (air-media-hydrogel) model. As Fig. 3i,j shows, hydrogels placed in media for 30 min exhibited lower intramural DO levels. In fact, at thicknesses between 2.5 and 3.13 mm, DO levels were hypoxic (<5%) through the hydrogels’ depth, suggesting their potential suitability for providing artificial hypoxic microenvironments. Towards using the HI hydrogel to study vascular morphogenesis, we chose to encapsulate ECFCs, which are capable of undergoing morphogenesis in synthetic matrices26,39. We first determined how DO levels of hydrogels encapsulated with ECFCs depend on gel thickness. To test this, we encapsulated ECFCs within HI hydrogel matrices of different thickness (hypoxic gel, 2.50 mm; nonhypoxic gel (control), 1.25 mm) and cultured the constructs in ECFC media. Interestingly, the DO levels of the hypoxic gels decreased markedly for the first 30 min and retained prolonged low O2 levels for up to 50 h (Fig. 3k), demonstrating that the HI hydrogel allowed the exposure of ECFCs to hypoxia and that the ECFCs also affected O2 levels within the matrix. In fact, the DO levels of hypoxic gels without cells reached DOmin within 30 min, followed by a gradual increase after the inflection point, while the DO levels within the hypoxic gels encapsulating ECFCs remained hypoxic after DOmin for up to 50 h (Fig. 3k) due to O2 consumption by the cells. In contrast, nonhypoxic gels exhibited higher O2 levels (>8%) than hypoxic gels but with a similar pattern, due to the encapsulated ECFCs.
We show that hypoxic environments can be generated and controlled in cultured HI hydrogels independently of cell encapsulation. Importantly, as O2 consumption rates vary among different cell types, the HI hydrogel system provides opportunity to study hypoxia in diverse tissue models in vitro. We also show that the hypoxic environment in HI hydrogels is affected by the encapsulated ECFCs, which support continuous hypoxic environments.
To study the importance of the 3D hypoxic niche in cellular response, we next hypothesized that HI hydrogels would stimulate vascular morphogenesis through HIF pathway activation. To test this, we encapsulated ECFCs within HI hydrogel matrices of different thicknesses (hypoxic gel, 2.50 mm; nonhypoxic gel (control), 1.25 mm) and cultured them for up to 3 days. We observed different cell morphologies in hypoxic versus nonhypoxic gels. Unlike the limited sprout and tube formation of ECFCs within the nonhypoxic hydrogels, ECFCs within hypoxic gels underwent tubulogenesis, forming complex network structures after 3 days in culture (Fig. 4a). We also found significant increases in tube coverage, length and thickness (Fig. 4b–d), demonstrating that our HI hydrogels stimulate vascular morphogenesis. We observed more evolved vascular structures in hypoxic gels than in nonhypoxic gels, as demonstrated by 3D z−stack confocal analysis (Fig. 4e). We further noticed the formation of lumens in the vascular structures formed in hypoxic hydrogels, indicating mature vascular tube formation (Fig. 4e and Supplementary Fig. 5).
To better understand the molecular mechanisms underlying tube formation in HI hydrogels, we analysed relevant gene expression soon after ECFC encapsulation. We found that ECFCs cultured in hypoxic gels expressed significantly higher levels of two isoforms of HIFα (HIF-1α and HIF-2α) after 12 h than ECFCs within nonhypoxic hydrogels (Fig. 5a). Interestingly, we found that HIF-1α gene expression gradually became upregulated in ECFCs in nonhypoxic gel for up to 24 h during the culture period, probably due to the presence of FA molecules. A recent study demonstrated that free FA molecules could induce upregulation of HIF-1α expression in endothelial cells (ECs) in a concentration-dependent manner40. We also examined the expression of three MMP genes in ECFCs—membrane type 1 (MT1)-MMP, MMP-1 and MMP-2—as these play a critical role in vascular morphogenesis26,41,42. We found that all MMP gene expressions in ECFCs from the hypoxic gel were upregulated over 48 h of culture compared with ECFCs encapsulated in non-hypoxic gel (Fig. 5b). We also confirmed protein levels and activities, finding higher levels of MT1-MMP and activated forms of MMP-1 and MMP-2 in hypoxic hydrogels (Supplementary Fig. 6). Finally, we examined the gene expression of proangiogenic factors within the hypoxic microenvironment. We noticed upregulation of VEGF and VEGFR2 in ECFCs encapsulated in hypoxic gels compared with nonhypoxic gels (Fig. 5c). ANG1, which contributes to blood vessel maturation and stabilization, was upregulated, while ANG2, an antagonist of ANG1, was downregulated in hypoxic hydrogels compared with nonhypoxic hydrogels. (Fig. 5c). Collectively, these results demonstrate that hypoxic hydrogels stimulate upregulation of proangiogenic and MMP genes affecting vascular morphogenesis.
To further understand the pathway activation that stimulates vascular morphogenesis within the HI hydrogels, we first performed a reoxygenation study. Reoxygenation, the phenomenon in which hypoxic regions become more exposed to O2 by changing partial pressure of O2, induces production of reactive O2 specimens, which involves an angiogenic response43. Our previous study demonstrated that reoxygenation affected the tube formation kinetics of ECs encapsulated in collagen gels in atmospheric conditions through a HIFα-independent pathway34. In our HI hydrogel system, we observed slight O2 fluctuations (from 0.1 to 1.3% O2) and a gradual increase after media changes (see Fig. 3k). Thus, we wondered whether this slight reoxygenation due to media change affects vascular morphogenesis in the HI hydrogels. We encapsulated ECFCs within HI hydrogels and cultured them for up to 3 days with or without media changes. We found that ECFCs cultured without media changes underwent vascular morphogenesis similar to those cultured with media changes (Supplementary Fig. 7), demonstrating that reoxygenation does not affect the vascular morphogenesis of ECFCs in HI hydrogel systems. These results demonstrate that in contrast to existing hydrogel systems, which may provide uncontrolled and transient hypoxic environments, the HI hydrogel supports controllable and stable environments to activate hypoxia-regulated pathways.
We next aimed to determine whether vascular morphogenesis within HI hydrogels occurs through the activation of HIFs. Small interfering RNA (siRNA) studies examined the involvement of HIF-1α and HIF-2α during ECFC tubulogenesis in HI hydrogels. We encapsulated ECFCs treated with either or both HIF siRNAs in HI hydrogels after confirming the suppression (Supplementary Fig. 8). Knocking down each or both HIFs reduced tube formation compared with untreated and luciferase-treated ECFCs (Fig. 5d and Supplementary Fig. 9). Notably, when both HIFs were knocked down, most of the encapsulated ECFCs exhibited round shapes, even after 3 days in culture (Supplementary Fig. 9). To delineate whether vascular network formation in the HI hydrogel is regulated through HIF-secreted angiogenic growth factors, we examined the exogenous addition of Ang1 to the culture media (that already contains VEGF). We found that addition of Ang1 did not promote vascular network formation in the nonhypoxic hydrogels (Supplementary Fig. 10). Examining MT1-MMP, we detected significant downregulation of MT1-MMP expression after 24 h of culture in the ECFCs treated with both HIFs siRNA compared with non-treated, luciferase-treated and each HIF-treated-alone groups (Fig. 5e). When MT1-MMP was suppressed, encapsulated ECFCs did not generate vascular networks in HI hydrogels (Fig. 5f; Supplementary Fig. 11). Collectively, these results demonstrate that accumulation of HIF-1α and HIF-2α activates MT1-MMP, which enables vascular morphogenesis of ECFCs within HI hydrogels. Indeed, MT1-MMP was previously established as a critical component for the progression of 3D tubulogenesis within hydrogel materials26,41,42. In sum, our HI hydrogels, which can induce hypoxic microenvironments, promote complex and mature vascular tube structures by activating HIFs through the upregulated expression of proangiogenic factors and MMPs.
In vivo angiogenic effect of HI hydrogels
Although numerous studies have suggested that hypoxia stimulates blood vessel formation both in vitro and in vivo11,23,44, nobody has yet reported inducing acute hypoxia by manipulating a material-tissue interface to affect blood vessel invasion. To investigate the potential in vivo application of HI hydrogels, we hypothesized that our hypoxic hydrogel would induce acute hypoxia in surrounding tissues through in situ gel formation with O2 consumption, which in turn would stimulate blood vessel invasion. We first performed a simulation to estimate DO levels after in vivo injection of hypoxic hydrogels using the given parameters. For this purpose, we assumed a partial pressure of O2 in rat subcutaneous tissue of 40 mm Hg, following previous reports45,46, although the exact pressure was not defined. We found that the DO gradient from the center of the hydrogel to the hydrogel’s edge (that is, the interface of the hydrogel and the surrounding tissue) is independent of the shape of the hydrogel (Fig. 6a–c). Notably, we found that DO levels at the edge of the hydrogel are lower than the physiological or pathological O2 levels of the in vivo environments (from 10 mm Hg to 40 mm Hg; Fig. 6d–f), suggesting that HI hydrogels can induce an acutely hypoxic environment and may stimulate the surrounding tissues.
To confirm the effect of HI hydrogels on blood vessel recruitment in vivo, we generated two types of HI hydrogels (hypoxic and nonhypoxic). To control O2 levels in vivo, we mixed calcium peroxide (CaO2) as an O2-releasing compound to generate nonhypoxic gels (>8% O2). To generate a hypoxic gel, we encapsulated calcium hydroxide—Ca(OH)2—a side product of CaO2 decomposition that does not influence the change of O2 tension within the gel matrix (Supplementary Fig. 12). We injected the hydrogels subcutaneously to mice and examined them for up to 5 days. While microvasculature was observed surrounding both hydrogels, higher density and larger size of microvasculature were observed surrounding the hypoxic hydrogel than surrounding nonhypoxic gels after 1 day. After 3 and 5 days, the density of blood vessels surrounding and penetrating the hypoxic matrices increased to a greater extent than in nonhypoxic hydrogels (Fig. 7a–d). Similar trends were observed in subcutaneous injections into rats (Supplementary Fig. 13). Evaluating whether the recruited blood vessels are anastomosed with the host vessels and are functional, we found that within 3 days hypoxic hydrogels were invested with perfused microvasculature networks, while isolated occasions of perfused microvasculature were detected in the nonhypoxic matrices (Fig. 8a) These perfused networks extended throughout the entire hypoxic hydrogels after 5 days while were limited in the nonhypoxic hydrogels (Fig. 8b).
Taken together, our results demonstrate that acute hypoxic conditions induced in vivo by the HI hydrogel promote blood vessel recruitment and neovascularization from the host during the wound-healing process. Thus, HI hydrogels can be further explored as an acellular matrix for the study of hypoxia-regulated cellular processes. In addition, HI hydrogels can be delivered through injection into the site of interest, thus requiring the use of minimally invasive techniques.
Discussion
The current study presents a new class of synthetic biomaterials that can mimic hypoxic conditions in native niches. Our novel approach demonstrated that HI hydrogels form via an enzyme-mediated reaction with O2 consumption. We can accurately predict and control O2 levels and gradients within our HI hydrogels, thus offering controllable and stable hypoxic environments. ECFCs encapsulated within HI hydrogel undergo morphogenesis and generate extensive vascular network structures via HIF-mediated activation of MT1-MMP. Hypoxic hydrogels promote blood vessel recruitment and infiltration via the material-tissue interface. To our knowledge, this is the first example of HI hydrogel materials. Moreover, this approach can be adapted for many other natural/synthetic polymers and may encourage innovation in a broad range of applications, including the study and treatment of hypoxia-regulated disorders, generation of artificial tissue constructs using progenitor or stem cells in regenerative medicine and development of engineered de novo disease models such as in vitro cancer models.
Methods
Materials
Gelatin (Gtn, type A from porcine skin, less than 300 bloom), laccase (lyophilized powder from mushroom, ⩾4.0 units/mg), 3-methoxy-4-hydroxycinnamic acid (ferulic acid, FA), N-(3-dimethylaminopropyl)-N′-ethylcarbodiimide hydrochloride (EDC), N-hydroxysuccinimide (NHS), dimethyl sulfoxide (DMSO), deuterium oxide (D2O) and collagenase type IV were purchased from Sigma-Aldrich (Saint Louis, MO) and used as obtained without purification. Dulbecco’s Phosphate-Buffered Saline (DPBS), Dulbecco’s Modified Eagle Medium (DMEM), and fetal bovine serum (FBS) were all purchased from Gibco, Invitrogen (Life Technologies, CA). Dialysis membrane (molecular cutoff=3,500 Da) was purchased from Spectrum Laboratories (Rancho Dominguez, CA).
Synthesis of gelatin-g-ferulic acid
Gelatin-g-ferulic acid (GtnFA) conjugate was synthesized using EDC and NHS as coupling reagents. For the synthesis, a mixture of DMSO and distilled water (DIW) with a 1:1 volume ratio was prepared as a solvent. Gtn (1.0 g) was dissolved in 50 ml of the solvent at 40 °C. FA (0.78 g, 4.0 mmol) was dissolved in 20 ml of the solvent and reacted with EDC (0.92 g, 4.8 mmol, 1.2 equation of carboxyl unit of FA) and NHS (0.64 g, 5.6 mmol, 1.4 equation of carboxyl unit of FA) at room temperature for 15 min to activate the terminal carboxyl groups of FA. The activated solution was then applied to the Gtn solution, and a conjugative reaction was conducted at 40 °C for 24 h. After reaction, the solution was dialysed against water for 5 days (molecular weight cutoff=3,500 Da). After dialysis, we obtained GtnFA by freeze-drying and kept the product in a refrigerator before use. The degree of substitution (DS) of FA was measured using a UV/Vis spectrometer (SpectraMax; Molecular Devices, Sunnyvale, CA). GtnFA polymer (10 mg) was dissolved in 1 ml of a mixture of DMSO and DIW with a volume ratio of 1:1, and the absorbance was measured at the 320 nm wavelength. The concentration of the conjugated FA molecules was calculated from a calibration curve given by monitoring the absorbance of a known concentration of FA; it was standardized with the baseline measured using Gtn solution (10 mg ml−1). The chemical structure of GtnFA was characterized using a 1H NMR spectrometer (Bruker AMX-300 NMR spectrometer, Billerica, MA). The GtnFA polymer solution (10 mg ml−1 of D2O) was prepared for the measurement. Supplementary Table 1 lists the synthesized polymer series depending on the feed amount of FA molecules.
Preparation of hypoxia-inducible hydrogels
Hypoxia-inducible (HI) hydrogels were prepared by mixing aqueous GtnFA polymer and laccase solution. Hydrogels (100 μl) were prepared in 1 ml vials at 37 °C. Seventyfive microliters of the GtnFA polymer solution (4.0–6.7 wt%) and 25 μl of laccase solution (25–100 U ml−1 of stock solution) were simply mixed and gently shaken. To generate gel matrices of different thicknesses, we fabricated HI hydrogels in a 96-well plate (BD Bioscience or DO sensor patched plate-please see below for details) in a volume-dependent manner. For example, to generate hydrogel that was 2.5 mm thick, we pipetted 80 μl of the mixture of polymer and laccase solutions in each well and allowed them to react at 37 °C. All solutions used were dissolved in DPBS (pH 7.4), and the final concentration of the hydrogels was 3–5 wt%.
Gelation time
The gelation time of the HI hydrogels was determined by the vial-tilting method47. We prepared 100 μl of hydrogel in a 1-ml vial and mixed gently to initiate the crosslinking reaction at 37 °C. Gelation time was measured as the time point after inverting the solution when more than 3 min passed without flow. The experiments were performed with different concentrations of laccase and polymer, as detailed in the article.
Measurement of viscoelastic properties
We performed rheological analysis of the HI hydrogels using a rheometric fluid spectrometer (RFS3, TA Instruments, New Castle, DE) with a 25 mm plate geometry. In the rheological experiments, hydrogel samples were prepared on the plate in the instrument. We performed dynamic time sweeps on hydrogel samples in various conditions. We monitored the elastic modulus (G′) and viscous modulus (G′′) at 10 percent of strain and a frequency of 0.1 Hz at 37 °C. A solvent trap wetted with deionized water was used to prevent sample evaporation.
In vitro proteolytic degradation study
In vitro degradation of HI hydrogels was gravimetrically determined. Hydrogels (100 μl) were prepared in microtubes and subsequently incubated in 500 μl of PBS with or without collagenase at 37 °C. We removed the media from the microtubes at a pre-determined time and measured the weight of degraded hydrogels (Wd). Fresh media were added into the tube after weighing. The weight of the remaining hydrogels was then calculated according to the following equation (1):
where Wd is the weight of the degraded hydrogels and Wi is the weight of the initial hydrogels.
Cytocompatibility of HI hydrogels
All solutions for the in vitro cytotoxicity and viability studies were prepared using DPBS and filtered for sterilization using a syringe filter with a pore size of 0.2 μm. We investigated the cytotoxicity of the synthesized polymer and the enzyme using XTT (Sigma-Aldrich), according to the manufacturer’s instructions and our previous report48. In brief, newborn human foreskin fibroblasts (NUFF; Global Stem, Rockville, MD) were expanded. To test cytocompatability, 2.8 × 104 cells cm−2 were cultured in 100 μl media and in the presence of polymer solution (0.63–10.0 mg ml−1) or laccase solution (1.6–25 U ml−1) for 24 h, following by their incubation in medium containing 20 percent (v/v) XTT solution for 4 h. For the quantitative analysis, we removed 100 μl of the medium, placed it in a 96-well plate and read it in a microplate reader at the 450 nm wavelength. Cell viability was determined as a percentage of control cells (nontreated cells that were defined as 100% viable). Cell viability of HI hydrogels was evaluated using a live/dead kit (Invitrogen). In brief, 5 × 105 NUFF cells ml−1 were encapsulated within HI hydrogels and cultured under standard cell culture conditions (37 °C and 5% CO2) in high-glucose DMEM with 10% FBS. After incubation for 2 and 24 h, we treated each well with 100 μl of 2 μM of the acetomethoxy derivate of calcein (calcein AM) and 4 μM of ethidium homodimer-1 (EthD-1) mixture and incubated at 37 °C for 30 min. The stained samples were washed three times using PBS and then counted with fluorescence microscopy (BX60, Olympus, Tokyo, Japan).
DO measurement and mathematical model prediction
We measured DO levels non-invasively throughout hydrogels using commercially available sensor patches (Presens, Regensburg, Germany), as previously described34,49,50. To measure O2 levels at the bottom of hydrogels, the polymer solutions were added on top of the sensors, which were immobilized in each well of a 96-well plate (BD Bioscience), and then mixed with laccase solutions. To measure O2 levels within different regions of the hydrogel (top, 3 mm; middle, 1.5 mm), we measured O2 levels using a simple device we designed (Supplementary Fig. 14). All experiments were conducted in a controlled environment at 37 °C and 5% CO2 in incubators with and without culture media (DMEM plus 10% FBS). We controlled hydrogel thicknesses by varying the solution volume. DO gradients within the hydrogels were estimated using a mathematical model based on Michaelis–Menten kinetics, as described in our previous report34. In brief, we assumed that the O2 consumption rate (R) of laccase-mediated crosslinking reactions follow Michaelis–Menten kinetics (equation 2) and determined the Michaelis–Menten parameters of the O2-consuming hydrogel formation.
where Vmax represents the maximum O2 consumption rate and Km is the O2 concentration at which the reaction rate is half of Vmax. To determine these parameters, we measured the steady-state DO level of 3 wt% hydrogel (DS 45) formed with 25.0 U ml−1 laccase and plotted the experimental data using the Michaelis–Menten equation. We also calibrated the plots according to the residual sum of squares method to give the best-fit graphs between the theoretical equation and experimental values. We simulated the two-layer (air-hydrogel) and three-layer (air-media-hydrogel) models of the DO gradients with commercial software, Comsol Multiphysics (Comsol, LA, CA), as previously described51.
ECFC encapsulation and viability
All solutions for the in vitro viability were prepared using DPBS and filtered for sterilization using a syringe filter with a pore size of 0.2 μm. ECFCs (Lonza, Walkersville, MD) were cultured, as previously described52, in endothelial growth media-2 (EGM2; Lonza) containing VEGF and 10% FBS on the plate coated with type I collagen (BD Biosciences, Franklin Lakes, NJ). GtnFA polymer solution (4 wt%) was dissolved in PBS (pH 7.4) and mixed with ECFC pellets to provide cell suspension, and then laccase solution (100 U ml−1) was added at a volume ratio of 3:1 (polymer solution:laccase solution) and gently mixed for 2 min at 37 °C. The final concentration of the polymer, laccase and cells were 3 wt%, 25 U ml−1 and 2 × 106 cells ml−1, respectively. The mixture was placed in the 96-well plate and allowed to react at 37 °C for 15 min. The ECFCs encapsulated within the hydrogels were cultured with 200 μl in growth media (Lonza) under standard cell culture conditions (37 °C and 5% CO2) for up to 72 h. The culture medium was replaced every 24 h. For viability, after incubation for 24 and 72 h, we treated each well with 100 μl of 2 μM of calcein AM and 1 μM of EthD-1 mixture, incubate and analysed as detailed above for NUFF cells. We observed the ECFCs at different region of hydrogels by controlling the coaxial coarse/fine-focusing knob of microscope. ECFC morphologies were observed using optical microscopy (in phase-contrast mode) and confocal microscopy (LSM 510 Meta, Carl Zeiss). For confocal observations, ECFCs within hydrogels were fixed using 3.7% paraformaldehyde for 40 min at room temperature and washed three times using PBS. The fixed cells were permeabilized with 0.1% Triton X-100 for 20 min and incubated with 1% BSA blocking solution at room temperature for 1 h. The hydrogel samples were incubated with phalloidin (1:40; Molecular Probes, Eugene, OR) and Hoechst 33258 (1:10,000; Molecular Probes) to visualize the cytoplasm and nuclei, respectively.
Real-time RT-PCR
Quantitative real time RT-PCR was performed as described previously26,52. In brief, total RNA was isolated from ECFCs encapsulated in hydrogels using TRIzol (Invitrogen) according to the manufacturer’s instructions. Total RNA was quantified using an ultraviolet spectrophotometer and validated for having no DNA contamination. RNA (1 μg per sample) was transcribed using reverse transcriptase M-MLV and oligo(dT) primers (both from Promega, Madison, WI) according to the manufacturer’s instructions. We used TaqMan Universal PCR MasterMix and Gene Expression Assay (Applied Biosystems, Foster City, CA) according to the manufacturer’s instructions for HIF-1α, HIF-2α, VEGF, VEGFR, ANG1, ANG2, MT1-MMP, MMP-1, MMP-2- and β-actin, as described previously.
Live staining and angiogenesis assay
We performed live staining using Calcein-AM (Invitrogen) to quantify the mean tube coverage, length and thickness, as described previously34. In brief, ECFCs were encapsulated and cultured for 3 days using the above-described method. One hundred microlitres of 2 μM calcein solution was added to each well, and the ECFCs embedded in the hydrogel were incubated at room temperature for 60 min. The stained cells were washed three times using PBS and then observed with fluorescence microscopy (BX60, Olympus, Tokyo, Japan). For the angiogenesis analysis, we use 5–20 images at × 20 magnifications of different fields within the hydrogels, and the vascular tube structure was analysed using MetaMorph software (Universal Imaging, Downingtown, PA) with the angiogenesis tools.
Effect of ANG-1 on ECFC vascular morphogenesis in HI hydrogels
We encapsulated ECFCs within HI hydrogels (hypoxic versus nonhypoxic gel) as described above and cultured them in EGM2 (Lonza) containing 10% FBS with additional 50 ng ml−1 of ANG-1. ECFC morphologies were observed using optical microscopy (in phase-contrast mode) along the 3-day culture period.
Zymography
We collected the conditioned media from each condition at pre-determined time points and analszed for MMP-1 and MMP-2 as previously described39. In brief, collected media were loaded on 10% gelatin (for MMP-2) and 12% casein (for MMP-1) zymography gels (Bio-Rad, Hercules, CA). We performed electrophoresis for 90 min at room temperature. After washing the gels in water, SDS was extracted from the gels with renaturation buffer (Invitrogen). MMP activities were developed in a developing buffer (Invitrogen) at 37 °C for 24 h and visualized by staining with Coomassie Blue R-250.
Western blot
We performed western blot analysis as described previously52. Cell lysates were prepared in a Tris-Triton-X buffer (1% Trion-X, 150 mM NaCl, and 50 mM Tris, pH 7.5) with 1 × protease inhibitor cocktail (Thermo Scientific, Waltham, MA). Protein isolated from cell lysates was quantified with the DC assay (Bio-Rad) and boiled at 95 °C for 5 min in Laemmli buffer (Bio-Rad) with β-mercaptoethanol. Protein (25 μg per well) was loaded into a 4–20 percent SDS-PAGE gel (Bio-Rad). Proteins were transferred to nitrocellulose membranes, blocked in three percent nonfat milk for 1 h, and incubated overnight at 4 °C (under constant shaking) with primary antibody: rabbit anti-MMP14 (MT1-MMP, 1:1,000) and GAPDH (1:3,000; both from Abcam, Cambridge, MA). We washed the membranes three times in Tris-buffered saline containing 0.1% Tween 20 (TBST) for 15 min each and incubated with anti-rabbit horseradish peroxidase (HRP) (1:1,000; Cell Signaling Technology, Danvers, MA). Membranes were washed three times in TBST, developed with enhanced chemiluminescence (Pierce) and visualized using the ChemiDoc XRS+ System (Bio-Rad).
Small interfering RNA transfection
ECFCs were transfected with siGENOME SMARTpool human HIF-1α, HIF-2α and MT1-MMP (Dharmacon, Lafayette, CO) following the manufacturer’s protocol, as previously described26,51,52. Cells were seeded on a six-well plate and treated with 100 nM siRNA. We performed mRNA analysis after 24 h and used confirmed transfected cells for experiments after 48 h.
In vivo subcutaneous injection
We performed subcutaneous injection in rats (n=6, 6–10 week-old Sprague–dawley female) or mice (n=4, 6–10 week-old C57/6 female) to investigate the in vivo angiogenic effects of HI hydrogels. To control O2 levels in vivo, we mixed a small amount of calcium peroxide (CaO2; Sigma-Aldrich) and calcium hydroxide—Ca(OH)2 (Sigma-Aldrich)—with the polymer solution. The solid calcium peroxide begins to decompose and release O2 molecules when in contact with water53. Thus, we encapsulated CaO2 as an O2-releasing compound to generate nonhypoxic hydrogel as a control group. To minimize the difference between the sample groups, we also encapsulated Ca(OH)2, a by-product of CaO2 decomposition, within hypoxic hydrogels. Ca(OH)2 does not influence the change of O2 tension within the gel matrix. In our initial study, we optimized concentrations of calcium derivatives to control O2 levels for in vivo studies. We injected 200 μl of hydrogels formed with 0.02% Ca(OH)2 (hypoxic hydrogel), and the same volume of hydrogels formed with 0.02% CaO2 (nonhypoxic hydrogel) into the backs of animals. For this study, polymer solutions were sterilized by filtering using syringe filter (pore size, 0.2 μm) and injected using 26-gauge needles. At each pre-determined time point (1, 3 and 5 days), we killed the animals, removed the hydrogels with the surrounding tissue, fixed the explants in formalin-free Accustain fixative and proceeded to histological analysis. To confirm the vascular functionality of blood vessels infiltrated into hydrogel matrix, we injected Alexa Fluor 568-conjugated isolectin GS-IB4 from Griffonia simplicifolia (Invitrogen) through the tail veins of the mice, as we previously described54. After 30 min, we killed the mice, removed the hydrogels, stained with Hoechst and then proceeded for visualization using confocal microscopy (LSM 510 Meta, Carl Zeiss). The animal study was performed using a protocol (RA11A196 and MO12A210) approved by The Johns Hopkins University Institutional Animal Care and Use Committee.
Histological analysis
After we fixed the explants as described above, the samples were then dehydrated in graded ethanol (80–100%), embedded in paraffin, serially sectioned using a microtome (5 μm) and stained with either haematoxylin and eosin (H&E) or underwent immunohistochemistry for α-SMA and CD31.
Statistical analysis
We performed all measurements of hydrogel characterizations, including gelation time, proteolytic degradation and mechanical strength, using triplicate samples for each data point. We performed RT-PCR analysis for HIFs, MMPs and proangiogenic factors in triplicate with duplicate readings. We performed statistical analysis using GraphPad Prism 4.02 (GraphPad Software Inc., La Jolla, CA). We also used this software to perform t-tests to determine significance. Significant levels, determined using post-tests, were set at: *P<0.05, **P<0.01 and ***P<0.001. All graphical data were reported.
Additional information
How to cite this article: Park, K. M. and Gerecht, S. Hypoxia-inducible hydrogels. Nat. Commun. 5:4075 doi: 10.1038/ncomms5075 (2014).
References
Huebsch, N. & Mooney, D. J. Inspiration and application in the evolution of biomaterials. Nature 462, 426–432 (2009).
Place, E. S., Evans, N. D. & Stevens, M. M. Complexity in biomaterials for tissue engineering. Nat. Mater. 8, 457–470 (2009).
Cushing, M. C. & Anseth, K. S. Hydrogel cell cultures. Science 316, 1133–1134 (2007).
Lutolf, M. P. & Hubbell, J. A. Synthetic biomaterials as instructive extracellular microenvironments for morphogenesis in tissue engineering. Nat. Biotechnol. 23, 47–55 (2005).
Luo, Y. & Shoichet, M. S. A photolabile hydrogel for guided three-dimensional cell growth and migration. Nat. Mater. 3, 249–253 (2004).
Martino, M. M. et al. Engineering the growth factor microenvironment with fibronectin domains to promote wound and bone tissue healing. Sci. Transl. Med. 3, 100ra189 (2011).
Engler, A. J., Sen, S., Sweeney, H. L. & Discher, D. E. Matrix elasticity directs stem cell lineage specification. Cell 126, 677–689 (2006).
Lutolf, M. P. et al. Synthetic matrix metalloproteinase-sensitive hydrogels for the conduction of tissue regeneration: engineering cell-invasion characteristics. Proc. Natl Acad. Sci. USA 100, 5413–5418 (2003).
Kilian, K. A., Bugarija, B., Lahn, B. T. & Mrksich, M. Geometric cues for directing the differentiation of mesenchymal stem cells. Proc. Natl Acad. Sci. USA 107, 4872–4877 (2010).
Semenza, G. L. Life with oxygen. Science 318, 62–64 (2007).
Covello, K. L. & Simon, M. C. HIFs, hypoxia, and vascular development. Curr. Top. Dev. Biol. 62, 37–54 (2004).
Keith, B. & Simon, M. C. Hypoxia-inducible factors, stem cells, and cancer. Cell 129, 465–472 (2007).
Simon, M. C. & Keith, B. The role of oxygen availability in embryonic development and stem cell function. Nat. Rev. Mol. Cell Biol. 9, 285–296 (2008).
Heddleston, J. M. et al. Hypoxia inducible factors in cancer stem cells. Br. J. Cancer 102, 789–795 (2010).
Jopling, C., Sune, G., Faucherre, A., Fabregat, C. & Izpisua Belmonte, J. C. Hypoxia induces myocardial regeneration in zebrafish. Circulation 126, 3017–3027 (2012).
Ferrara, N., Gerber, H. P. & LeCouter, J. The biology of VEGF and its receptors. Nat. Med. 9, 669–676 (2003).
Lee, Y. M. et al. Determination of hypoxic region by hypoxia marker in developing mouse embryos in vivo: a possible signal for vessel development. Dev. Dyn. 220, 175–186 (2001).
Gassmann, M. et al. Oxygen supply and oxygen-dependent gene expression in differentiating embryonic stem cells. Proc. Natl Acad. Sci. USA 93, 2867–2872 (1996).
Augustin, H. G., Koh, G. Y., Thurston, G. & Alitalo, K. Control of vascular morphogenesis and homeostasis through the angiopoietin-Tie system. Nat. Rev. Mol. Cell Biol. 10, 165–177 (2009).
Fong, G. H. Regulation of angiogenesis by oxygen sensing mechanisms. J. Mol. Med. 87, 549–560 (2009).
Manalo, D. J. et al. Transcriptional regulation of vascular endothelial cell responses to hypoxia by HIF-1. Blood 105, 659–669 (2005).
Ottino, P. et al. Hypoxia activates matrix metalloproteinase expression and the VEGF system in monkey choroid-retinal endothelial cells: Involvement of cytosolic phospholipase A2 activity. Mol. Vision 10, 341–350 (2004).
Pugh, C. W. & Ratcliffe, P. J. Regulation of angiogenesis by hypoxia: role of the HIF system. Nat. Med. 9, 677–684 (2003).
Ben-Yosef, Y., Lahat, N., Shapiro, S., Bitterman, H. & Miller, A. Regulation of endothelial matrix metalloproteinase-2 by hypoxia/reoxygenation. Circ. Res. 90, 784–791 (2002).
Rosana, C. M., Glasucia, M. P. & Nelson, D. Potential applications of laccase in the food industry. Trends Food Sci. Technol. 13, 205–216 (2002).
Hanjaya-Putra, D. et al. Controlled activation of morphogenesis to generate a functional human microvasculature in a synthetic matrix. Blood 118, 804–815 (2011).
Davis, G. E. & Senger, D. R. Endothelial extracellular matrix: biosynthesis, remodeling, and functions during vascular morphogenesis and neovessel stabilization. Circ. Res. 97, 1093–1107 (2005).
Cuchiara, M. P., Gould, D. J., McHale, M. K., Dickinson, M. E. & West, J. L. Integration of Self-Assembled Microvascular Networks with Microfabricated PEG-Based Hydrogels. Adv. Funct. Mater. 22, 4511–4518 (2012).
Khetan, S. et al. Degradation-mediated cellular traction directs stem cell fate in covalently crosslinked three-dimensional hydrogels. Nat. Mater. 12, 458–465 (2013).
DeForest, C. A., Polizzotti, B. D. & Anseth, K. S. Sequential click reactions for synthesizing and patterning three-dimensional cell microenvironments. Nat. Mater. 8, 659–664 (2009).
Grabber, J. H., Hatfield, R. D., Ralph, J., Zon, J. & Amrhein, N. Ferulate cross-linking in cell-walls isolated from maize cell-suspensions. Phytochemistry 40, 1077–1082 (1995).
Riva, S. Laccases: blue enzymes for green chemistry. Trends Biotechnol. 24, 219–226 (2006).
Tibbitt, M. W. & Anseth, K. S. Hydrogels as extracellular matrix mimics for 3D cell culture. Biotechnol. Bioeng. 103, 655–663 (2009).
Abaci, H. E., Truitt, R., Tan, S. & Gerecht, S. Unforeseen decreases in dissolved oxygen levels affect tube formation kinetics in collagen gels. Am. J. Physiol.: Cell Physiol. 301, C431–C440 (2011).
Griffith, L. G. & Swartz, M. A. Capturing complex 3D tissue physiology in vitro. Nat. Rev. Mol. Cell Biol. 7, 211–224 (2006).
Helmlinger, G., Yuan, F., Dellian, M. & Jain, R. K. Interstitial pH and pO2 gradients in solid tumors in vivo: high-resolution measurements reveal a lack of correlation. Nat. Med. 3, 177–182 (1997).
Hunt, T. K., Zederfeldt, B. & Goldstick, T. K. Oxygen and healing. Am. J. Surg. 118, 521–525 (1969).
Remensnyder, J. P. & Majno, G. Oxygen gradients in healing wounds. Am. J. Pathol. 52, 301–323 (1968).
Hanjaya-Putra, D. et al. Spatial control of cell-mediated degradation to regulate vasculogenesis and angiogenesis in hyaluronan hydrogels. Biomaterials 33, 6123–6131 (2012).
Lin, C. M. et al. Ferulic acid augments angiogenesis via VEGF, PDGF and HIF-1 alpha. J. Nutr. Biochem. 21, 627–633 (2010).
Chun, T. H. et al. MT1-MMP-dependent neovessel formation within the confines of the three-dimensional extracellular matrix. J. Cell Biol. 167, 757–767 (2004).
Stratman, A. N. et al. Endothelial cell lumen and vascular guidance tunnel formation requires MT1-MMP-dependent proteolysis in 3-dimensional collagen matrices. Blood 114, 237–247 (2009).
Pan, Y. et al. Multiple factors affecting cellular redox status and energy metabolism modulate hypoxia-inducible factor prolyl hydroxylase activity in vivo and in vitro. Mol. Cell Biol. 27, 912–925 (2007).
Marti, H. J. et al. Hypoxia-induced vascular endothelial growth factor expression precedes neovascularization after cerebral ischemia. Am. J. Pathol. 156, 965–976 (2000).
Fischer, B. & Bavister, B. D. Oxygen tension in the oviduct and uterus of rhesus monkeys, hamsters and rabbits. J. Reprod. Fertil. 99, 673–679 (1993).
Zhang, Y. & Wilson, G. S. In vitro and in vivo evaluation of oxygen effects on a glucose oxidase based implantable glucose sensor. Anal. Chim. Acta 281, 513–520 (1993).
Park, K. M., Ko, K. S., Joung, Y. K., Shin, H. & Park, K. D. In situ cross-linkable gelatin-poly(ethylene glycol)-tyramine hydrogel via enzyme-mediated reaction for tissue regenerative medicine. J. Mater. Chem. 21, 13180–13187 (2011).
Sun, G., Shen, Y. I., Ho, C. C., Kusuma, S. & Gerecht, S. Functional groups affect physical and biological properties of dextran-based hydrogels. J. Biomed. Mater. Res., Part A 93, 1080–1090 (2010).
Abaci, H. E., Truitt, R., Luong, E., Drazer, G. & Gerecht, S. Adaptation to oxygen deprivation in cultures of human pluripotent stem cells, endothelial progenitor cells, and umbilical vein endothelial cells. Am. J. Physiol.: Cell Physiol. 298, C1527–C1537 (2010).
Abaci, H. E., Devendra, R., Smith, Q., Gerecht, S. & Drazer, G. Design and development of microbioreactors for long-term cell culture in controlled oxygen microenvironments. Biomed. Microdevices 14, 145–152 (2012).
Abaci, H. E., Truitt, R., Tan, S. & Gerecht, S. Unforeseen decreases in dissolved oxygen levels affect tube formation kinetics in collagen gels. Am. J. Physiol.: Cell Physiol. 301, C431–C440 (2011).
Kusuma, S., Zhao, S. & Gerecht, S. The extracellular matrix is a novel attribute of endothelial progenitors and of hypoxic mature endothelial cells. FASEB J. 26, 4925–4936 (2012).
Oh, S. H., Ward, C. L., Atala, A., Yoo, J. J. & Harrison, B. S. Oxygen generating scaffolds for enhancing engineered tissue survival. Biomaterials 30, 757–762 (2009).
Kusuma, S. et al. Self-organized vascular networks from human pluripotent stem cells in a synthetic matrix. Proc. Natl Acad. Sci. USA 110, 12601–12606 (2013).
Acknowledgements
We thank S. Kusuma for critically reviewing this paper; A. Hielscher for assistance with zymography and western blot; H. E. Abaci for technical assistance with oxygen measurement, RT-PCR, and reoxygenation studies; Y. I. Shen for assistance with in vivo animal injection and immunohistochemistry; S. F. Barreto for assistance with ECFCs culture. This work was supported by NIH grants R01HL107938 and U54CA143868 and National Science Foundation grant 1054415 (to S.G).
Author information
Authors and Affiliations
Contributions
K.M.P. designed and performed research, analysed data and wrote the paper; S.G. designed research, analysed data and wrote the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-14 and Supplementary Table 1 (PDF 9069 kb)
Rights and permissions
About this article
Cite this article
Park, K., Gerecht, S. Hypoxia-inducible hydrogels. Nat Commun 5, 4075 (2014). https://doi.org/10.1038/ncomms5075
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms5075
This article is cited by
-
Hydrogels with tunable mechanical plasticity regulate endothelial cell outgrowth in vasculogenesis and angiogenesis
Nature Communications (2023)
-
Sustained delivery of MMP-9 siRNA via thermosensitive hydrogel accelerates diabetic wound healing
Journal of Nanobiotechnology (2021)
-
Current hydrogel advances in physicochemical and biological response-driven biomedical application diversity
Signal Transduction and Targeted Therapy (2021)
-
Interpenetrating Polymer Network Hydrogels of Gelatin and Poly(ethylene glycol) as an Engineered 3D Tumor Microenvironment
Macromolecular Research (2019)
-
Stabilization of enzyme-immobilized hydrogels for extended hypoxic cell culture
Emergent Materials (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.