Abstract
The interplay between antagonistic superconductivity and ferromagnetism has been a interesting playground to explore the interaction between competing ground states. Although this effect in systems of conventional superconductors is better understood, the framework of the proximity effect at complex-oxide-based superconductor/ferromagnet interfaces is not so clear. The main difficulty originates from the lack of experimental tools capable of probing the interfaces directly with high spatial resolution. Here we harness cross-sectional scanning tunnelling microscopy and spectroscopy together with atomic-resolution electron microscopy to understand the buried interfaces between cuprate and manganite layers. The results show that the fundamental length scale of the electronic evolution between YBa2Cu3O7−δ (YBCO) and La2/3Ca1/3MnO3 (LCMO) is confined to the subnanometre range. Our findings provide a complete and direct microscopic picture of the electronic transition across the YBCO/LCMO interfaces, which is an important step towards understanding the competition between ferromagnetism and superconductivity in complex-oxide heterostructures.
Similar content being viewed by others
Introduction
The interplay between superconductors (SC) and ferromagnetic (FM) metals (the so-called ‘proximity effect’) has been intensively studied for decades due to the interest in understanding the antagonistic interactions between singlet Cooper pairs with singlet alignments of spins of paired electrons, and ferromagnetism (FM) that favours parallel alignment of spins1. In complex-oxide-based systems composed of high-temperature superconducting YBa2Cu3O7−δ (YBCO) and ferromagnetic La2/3Ca1/3MnO3 (LCMO), however, these interfacial effects are still not well understood2,3. Experiments have been closely focused on the antagonism between FM- and SC-order parameters in strongly correlated systems; however, based on macroscopic physical properties, such as superconducting transition temperature and overall magnetic moment, the length scale of interactions at the boundary between the two phases is still unclear4,5,6,7,8,9,10,11,12,13,14. This results from a lack of a microscopic understanding of how the FM and SC phases evolve across the YBCO/LCMO interface. Although many phenomena participate at the interface (superconducting coherence, strain, magnetism, charge transfer, and so on), it becomes necessary to isolate them in order to build a proper framework of understanding. Of specific interest here is the question of interfacial charge transfer.
Spatially averaged X-ray spectroscopy has demonstrated that a charge of ~0.2e− per Cu ion is transferred from Mn to Cu ions, causing an orbital reconstruction at the YBCO/LCMO interface15. At the same time, the length scale of the valence change measured by electron energy loss spectroscopy (EELS) between YBCO and LCMO was reported to be on the order of 4 nm, but with surprisingly opposite sign—that is, an increase in the 3d electron count on the Mn sites, opposite to that expected from the alignment of the chemical potentials, and, more puzzling, beyond 4 nm from the interface, a reduction in the Mn 3d electron count throughout the interior of the LCMO layer was also claimed16. Understanding the link between SC and charge transfer, however, requires a nanoscale-resolution probe that can spatially resolve states at the Fermi level as well as those deep in the occupied states.
In this article, by utilizing the combination of cross-sectional scanning tunnelling microscopy and spectroscopy (XSTM/S) and scanning transmission electron microscopy (STEM) to study the YBCO/LCMO interface, we gain a complete picture of how the electronic and chemical structures evolve across the interface. The results demonstrate directly that the length scale of the spatial electronic evolution at the interfaces between YBCO and LCMO is <0.4 nm. The results also reveal an unexpected asymmetry of the interfacial electronic structure closely correlated with an asymmetric interface crystal structure. In short, contrary to the previously conjectured charge transfer length scales, we demonstrate that the YBCO and LCMO electronic structures are only altered within a few atomic planes from the interface, thus ruling out the long-range charge transfer scenarios.
Results
Imaging interfaces with scanning tunnelling microscopy
Scanning tunneling microscopy/spectroscopy (STM/S) has excellent spatial resolution combined with the capability of simultaneously revealing the electronic local density of states (LDOS). These features of STM/S are essential for studying short-range (subnanometre) charge transfer at oxide interfaces. STM works by maintaining a constant tunnelling current at a fixed DC tip-sample bias and monitoring the tip-sample separation to measure the surface topography. At the same time, if one applies a small AC modulation to the tip bias, a lock-in technique can be utilized to measure the dI/dV signal, which is related to the electronic LDOS at the particular bias determined by the DC voltage. Furthermore, by parking the tip at a particular location on the surface, sweeping the DC voltage and recording the dI/dV signal, the LDOS near the Fermi energy can be measured. The spatial evolution of the dI/dV spectra across interfaces of dissimilar materials in cross-sectional geometry can provide valuable information about the band bending/alignment. This method has been applied to study interfaces in semiconductor heterojunctions17, and we have recently demonstrated how this technique can be adapted to study oxide interfaces and to monitor the band bending due to the charge transfer at these oxide interfaces18.
In order to measure the charge transfer between LCMO and YBCO, a superlattice (SL) of (LCMO(10 nm)/YBCO(10 nm))10 was grown on Nb-doped SrTiO3 (001) using pulsed laser deposition19. (See Methods for details of sample growth.) A Tc ~70 K is determined by transport measurement (see Fig. 1a). As seen in other published studies20,21,22, there is a suppression of Tc in the SLs (compared with the bulk value of ~91 K). A cross-sectional view of the interfaces was created by fracturing the samples in situ in the ultrahigh vacuum (UHV) chamber prior to the XSTM/S measurements18,23,24,25,26,27,28,29. Figure 1b shows a schematic of the geometry of the XSTM measurements in this study. Figure 1c,d shows the resulting XSTM and XSTS images recorded in the SL region at 56 K, which is below the superconducting transition temperature. The topography (Fig. 1c) and the STS image (Fig. 1d) show clear SL features. In the STS image, the YBCO exhibits bright electronic contrast compared with both the LCMO and Nb:STO regions. Note that we have previously demonstrated that the dI/dV contrast between LCMO and Nb:STO is very similar at +3.0 V (ref. 18). The topography of the fractured YBCO/LCMO SLs is not atomically flat. Instead, as shown in Fig. 2, the height variations in the averaged topography line profile are found to be on the scale of ~2 nm. As the dI/dV contrast can be readily used to identify the different layers, by comparing the averaged topography and dI/dV line profiles, the right and left sides of the hill in topography can thus be directly attributed to YBCO layers and LCMO layers, respectively. The main reason for the presence of the hill-valley type of topography in the cross-sectional view of the SL is still unclear, but is most probably due to the fracturing dynamics of two layers with different fracturing toughness and strain, as was discussed in Chien et al.18 By comparing the forward and backward topography dI/dV matching (Fig. 2a,b), we confirmed that the dI/dV is free from topography-induced artefacts.
Interfacial band mapping
Next we turn our attention to the discussion of the electronic properties across the interfaces. We examine the spatial evolution of the LDOS by measuring a local bias-dependent dI/dV spectrum across the YBCO/LCMO interfaces with a spatial resolution of 0.4 nm per pixel, as shown in Fig. 3a. Figure 3b shows the spectra measured at the centres of an LCMO and of a YBCO layer, indicated as red and black dots in Fig. 3a. In the bulk, YBCO is a non-Fermi-liquid metallic phase above the superconducting Tc30. On the other hand, bulk LCMO is insulating at room temperature with an energy gap of ~1.1 eV that collapses below the transition to a metallic state accompanied by FM31, which occurs in the SL at ~200 K. Our XSTS measurements were performed at 56 K, well below the superconducting and magnetic transition temperatures. The spectrum of LCMO (Fig. 3b) exhibits metallic characteristics, as indicated by the absence of an energy gap near the Fermi energy, and is symmetric with respect to zero bias, consistent with a previous study of LCMO in the metallic phase32. The spectrum of YBCO, on the other hand, exhibits an asymmetric shape with the minimum located at ~30 meV, in agreement with the background shape observed previously33. Spectroscopic features connected to the superconducting state34 are, however, not resolved because the room-temperature tip used in this study smears out these features. Despite this kBT smearing, the LDOS probed by XSTS can provide the spatial evolution of the conduction and valence bands across the interface. Here, we use the locations of the spectra minima (indicated as red marks in Fig. 3a) to visualize the spatial evolution of the spectra. It is also important to note that, as we are mapping surface bands, they might be altered with respect to the bulk, but, as shown below, the good correspondence between the structural and electronic interfaces, by STM and STEM, is consistent with these being closely correlated with the behaviour of the bulk bands.
A closer inspection of Fig. 3a reveals that the spectrum transition is unexpectedly asymmetric for the two types of interfaces, namely, YBCO/LCMO (Y/L) and LCMO/YBCO (L/Y). The Y/L interfaces appear to be abrupt, whereas the transitions at the L/Y interfaces are more gradual. The rough nature of the fractured surface tends to reduce the signal-to-noise ratio in the spectra. In order to gain better statistics, we perform averaging over the repeated SL cells using LCMO/YBCO half layers as the averaging block. For alignment, each interface location was determined by monitoring the dI/dV signal at zero bias, where a drastic change could be seen in the two different materials (YBCO or LCMO). The spatial evolution of the averaged dI/dV spectra across the two types of interfaces is given in Fig. 4a. In this dI/dV mapping, we confirm that the evolution of the electronic properties is asymmetric across the top (L/Y) and bottom (Y/L) YBCO interfaces. The transition from LCMO to YBCO in the growth direction is abrupt, whereas the YBCO to LCMO interface is much more gradual. To quantitatively determine the electronic transition length scale, the minimum of each averaged dI/dV spectra is determined by fitting each spectrum with parabolic function and is shown as a red dot in Fig. 4a. We can further quantify this by defining a spatial decay function:
where ɛmin(x) is the energy of the minimum conductance in each spectrum; ɛ0 is the ɛmin value in YBCO at the interface, while ɛ∞ is the value in LCMO, far from the interface; x is the distance from the interface into LCMO, while ξ is the spectrum decay length. By fitting the red dots in Fig. 4a with equation (1), ξ for both interfaces could be determined. When moving along the growth direction, the transition from LCMO into YBCO (YBCO/LCMO) is abrupt, with ξY/L=0.26±0.02 nm, while the transition from YBCO into LCMO (LCMO/YBCO) is by a factor of ~3 broader: ξL/Y=0.96±0.13 nm. Though interface roughness or intermixing might also contribute to the observed spectrum evolution, these values place the upper limit for the charge transfer length scale at the YBCO/LCMO interface to, on average, less than a single YBCO unit cell along the c-axis (~1.2 nm).
This length scale is remarkably similar to the order of the length scale of the suppressed magnetization (1.2±0.1 nm), but different from the transition length scale of the charge profile (~4–8 nm) observed previously16. Note that the surface roughness increased from less than one unit cell, for the layer close to the substrate, to ~3.5 nm, for the topmost layers, in Hoffmann et al.16 This indicates that the interface roughness might be one origin of the discrepancy between the length scales of the charge transfer found here and in the previous report16. This picture is consistent with the explanation that the observed asymmetric spectra transition is due to the asymmetric chemical roughness, as will be discussed below.
Two possible reasons for the observed asymmetric electronic ‘roughness’ at the interfaces are (1) an asymmetric interface stacking sequence or (2) an asymmetric interface roughness. As has been previously reported in the literature, the interfacial stacking sequences may depend on the mode of synthesis. The top/bottom interfaces of pulsed laser deposition-fabricated YBCO/LCMO SLs have asymmetric atomic plane sequences: …–BaO–CuO2–(La,Ca)O–MnO–… at the top and …–(La,Ca)O–MnO–BaO–CuO–BaO–CuO2–Y–CuO2–… at the bottom YBCO interface taken with respect to the growth direction35. In sharp contrast to this, regions of the top and bottom interfaces of sputtered LCMO/YBCO/LCMO tri-layers were reported to exhibit symmetric stacking sequences (YBCO–BaO–CuO2–Y–CuO2–BaO–MnO2–(La,CaO)–LCMO) by electron microscopy, even though X-ray and neutron depth profiles demonstrate that the average roughness at the LCMO/YBCO interface is larger than that of the YBCO/LCMO interface14,36.
Atomic and chemical interface mapping
To investigate the possible asymmetry in atomic layer stacking sequence, we have performed extensive EELS measurements in an aberration-corrected STEM at the top/bottom interfaces. With aberration-corrected STEM/EELS, atomic-resolution spectroscopic imaging of interfaces is now possible and allows an atom-column by atom-column analysis of composition and local chemical environment37. Using spectroscopic imaging (Fig. 4b), the electronically abrupt YBCO/LCMO interface is found to also be chemically abrupt with a …–BaO–CuO2–Y-CuO2–BaO–MnO2–(La,CaO)–… atomic layer sequence. This sequence is similar to the termination observed in sputtered YBCO/LCMO interfaces14. On the other hand, instead of resolving a different atomic stacking sequence, the electronically broader interface (that is, LCMO/YBCO) almost always exhibits a more disordered crystal structure. These results strongly suggest that the broader electronic interface correlates with the structurally rougher interface, while the effects from different stacking sequences are still unclear.
Variations in the local chemical environment can be extracted by analysing the EELS edge fine structures. La–M, Mn–L, Ba–M, Cu–L, and O–K edge EELS spectra across the top and bottom interfaces are shown in Fig. 5a. Among them, the evolution of O–K edge spectra is of particular interest. As shown in Fig. 5c, three types of O–K edge spectra can be readily distinguished. Although there are states due to hybridization with all atoms in the system, we want to focus on the low-energy pre-peak due to hybridization with 3d states. In Fig. 5b, we can see oxygen states due to hybridization with Mn 3d states in LCMO as well as the apical and in-plane oxygen in YBCO (Cu–Oa and Cu–Ob). The oxygen environment can be obtained by least-squares fitting to the O–K edge spectra (Fig. 5b). The asymmetric interface profiles can be observed in the LCMO component (the top curve in Fig. 5b). The transition from LCMO to YBCO at the bottom interface, that is, Y/L, occurs over ~0.6 nm, which is more abrupt than the transition at the top interface (~1.2 nm). It is important to point out that the remarkably similar length scales found in EELS and STS strongly imply that the asymmetric electronic transition at both interfaces is directly coupled to the atomic roughness and that the characteristic length scale of charge transfer between YBCO and LCMO is limited to the subnanometre range. This length scale is consistent with a theoretical calculation that shows that the charge transfer in FM is roughly one to two ‘sites’ in a cubic lattice, which is ~0.4–0.8 nm (ref. 38). It has also been shown within the Fulde, Ferrell, Larkin and Ovchinnikov framework that the coherence length of the Cooper pairs in FM could be described by ξF=ħνF/2Eex, where vF is the Fermi velocity and Eex is the exchange energy in FM1. For LCMO, the νF and Eex are 7.4 × 107 cm s−1 and 3 eV, respectively39; hence, ξF is expected to be ~0.2 nm and thus strongly supports the notion that the physics is likely confined to a subnanometre region at the interface.
Discussion
From the combined results we conclude that for both interfaces any charge-transfer-induced band bending occurs in a subnanometre region. In other words, this result places a fundamental upper limit on the length scale for charge transfer between YBCO and LCMO. Our findings are at strong variance with the previously reported large charge-transfer length scale (~4 nm) between YBCO and LCMO by EELS16 and theoretical SC/FM proximity effect models relying on long-range charge transfer16. Possible explanations for such discrepancy are as follows: (1) different sample preparation methods (high-pressure sputtering versus pulsed laser deposition (PLD)), which could result in very different stacking configurations; and (2) as described in Hoffmann et al.16, the interface roughness increases from submonolayer roughness close to the substrate to ~3.5 nm roughness at the topmost layers, which is similar to the charge-transfer length scale reported in the same study. Interestingly, a similar gradually increasing interfacial roughness was also observed in (LaNiO3)n/(SrMnO3)2 SLs40. Nonetheless, the short-range charge transfer found here decisively rules out the mechanisms based on intrinsic long-range charge transfer as opposed to something structural or chemical in nature. Although proximity effects based solely on charge transfer can be excluded, it is possible that mechanisms involving coupling between charge and other degrees of freedom with longer length scale could have an important role in explaining the long-range proximity effect in YBCO/LCMO systems. Candidate mechanisms are, for examples, strain fields41 or long-range electron–phonon coupling (consequence of long-range Coulomb forces in conjunction with a short-range orbital reconstruction at the interface)9.
In summary, a new methodology based on the powerful combination of XSTM/S and EELS+STEM techniques has successfully been developed to directly probe the electronic and structural properties of interfaces of high-Tc SC/FM SLs. The spatially resolved dI/dV spectra provide direct evidence that the length scale for charge transfer between YBCO and LCMO has an upper limit of ~1 nm and that the spatial broadening of the electronic transition originates from rougher interfaces. In short, this result sets a fundamental upper limit on the charge-transfer length scale in the YBCO/LCMO system, ruling out a popular class of theories based on the long-range proximity effect based on charge transfer at the interfaces of YBCO and LCMO.
Methods
Sample fabrication
YBCO/LCMO SLs were deposited on Nb-doped SrTiO3 (Nb:STO) (5 mm × 5 mm × 0.5 mm) by interval PLD in a layer-by-layer fashion. Fabrication of the SLs was carried out in a newly developed PLD system featuring infrared laser substrate heating and in situ monitoring via high-pressure reflection high-energy electron diffraction (HP RHEED). Stoichiometric targets of YBCO and LCMO were sequentially ablated by a KrF laser (λ=248 nm). In the case of YBCO, the optimal conditions for 2-D growth are found to be a low laser frequency of 6–8 Hz with a dwell between the epitaxial depositions of each individual unit cell, which allowed for thermal smoothening processes. For LCMO, interval deposition with a laser frequency of 15–25 Hz proved to be the most favourable condition for a layer-by-layer growth. RHEED specular intensity oscillations are observed for both YBCO and LCMO layers, allowing for unit cell control during the construction of these SLs. The substrate temperature is continuously monitored and held at 740 °C, and an oxygen partial pressure P(O2)=150–200 mTorr is maintained inside the chamber throughout the deposition. Immediately after the deposition the sample is annealed at 550 °C, and the chamber is back-filled with oxygen to 500 Torr. These annealing conditions are maintained for 1 h.
Scanning tunnelling microscopy
The cross-sectional scanning tunnelling microscopy and spectroscopy (XSTM/S) were performed under in situ UHV fracturing with base pressure at 1.0 × 10−10 Torr. Sample temperature could be controlled by maintaining an equilibrium of the heating/cooling power using a heater and using liquid He in the cryogenic sample stage. The cross-sectional view of the interfaces was achieved by following a controlled fracturing procedure18,23,24,25,26. First, the as-grown samples were diced into 1 mm × 5 mm × 0.5 mm size. A 0.5-mm notch was created by scribing from the side and the fracturing process was finished in a UHV chamber by moving the vertically mounted sample against a rigid cleaver prior to the XSTM/S measurement. The set point of the STM constant current images was set to 3.0 V and 20 pA unless specified.
Electron microscopy
The microstructure of the YBCO/LCMO multilayers was studied by high-angle annular dark field imaging in a FEI Tecnai F20-ST STEM. More detailed chemical composition and bonding was probed on an atomic scale using spatially resolved EELS performed on an aberration-corrected NION UltraSTEM 100, which enables two-dimensional element and valence-sensitive imaging at atomic resolution37.
Additional information
Accession Codes: The new Psychotrieae gene sequence data have been deposited in the GenBank nucleotide database under accession numbers KC480521-KC480546.
How to cite this article: Chien, T. Y. et al. Visualizing short-range charge transfer at the interfaces between ferromagnetic and superconducting oxides. Nat. Commun. 4:2336 doi: 10.1038/ncomms3336 (2013).
References
Buzdin, A. I. Proximity effects in superconductor-ferromagnet heterostructures. Rev. Mod. Phys. 77, 935–976 (2005).
Dagotto, E. Complexity in strongly correlated electronic systems. Science 309, 257–262 (2005).
Bibes, M., Villegas, J. E. & Barthélémy, A. Ultrathin oxide films and interfaces for electronics and spintronics. Adv. Phys. 60, 5–84 (2011).
Peña, V. et al. Coupling of superconductors through a half-metallic ferromagnet: evidence for a long-range proximity effect. Phys. Rev. B 69, 224502 (2004).
Visani, C. et al. Equal-spin Andreev reflection and long-range coherent transport in high-temperature superconductor/half-metallic ferromagnet junctions. Nature Phys. 8, 539–543 (2012).
Przyslupski, P. et al. Magnetic properties of La0.67Sr0.33MnO3/YBa2Cu3O7 superlattices. Phys. Rev. B 69, 134428 (2004).
Hoppler, J. et al. Giant superconductivity-induced modulation of the ferromagnetic magnetization in a cuprate-manganite superlattice. Nature Mater. 8, 315–319 (2009).
Giblin, S. R. et al. Measurement of magnetic exchange in ferromagnet-superconductor La2/3Ca1/3MnO3/YBa2Cu3O7 bilayers. Phys. Rev. Lett. 109, 137005 (2012).
Driza, N. et al. Long-range transfer of electron-phonon coupling in oxide superlattices. Nature Mater. 11, 675–681 (2012).
Satapathy, D. K. et al. Magnetic proximity effect in YBa2Cu3O7/La2/3Ca1/3MnO3 and YBa2Cu3O7/LaMnO3+δ superlattices. Phys. Rev. Lett. 108, 197201 (2012).
Freeland, J. W., Chakhalian, J., Habermeier, H.-U., Cristiani, G. & Keimer, B. On magnetic interlayer coupling and proximity effect in a La0.67Ca0.33MnO3(10 nm)/YBa2Cu3O7(10 nm) superlattice. Appl. Phys. Lett. 90, 242502 (2007).
Fridman, I., Gunawan, L., Botton, G. A. & Wei, J. Y. T. Scanning tunneling spectroscopy study of c-axis proximity effect in epitaxial bilayer manganite/cuprate thin films. Phys. Rev. B 84, 104522 (2011).
Kalcheim, Y., Kirzhner, T., Koren, G. & Millo, O. Long-range proximity effect in La2/3Ca1/3MnO3/(100)YBa2Cu3O7−δ ferromagnet/superconductor bilayers: evidence for induced triplet superconductivity in the ferromagnet. Phys. Rev. B 83, 064510 (2011).
Visani, C. et al. Symmetrical interfacial reconstruction and magnetism in La0.7Ca0.3MnO3/YBa2Cu3O7/La0.7Ca0.3MnO3 heterostructures. Phys. Rev. B 84, 060405(R) (2011).
Chakhalian, J. et al. Orbital reconstruction and covalent bonding at an oxide interface. Science 318, 1114–1117 (2007).
Hoffmann, A. et al. Suppressed magnetization in La0.7Ca0.3MnO3/YBa2Cu3O7−δ superlattices. Phys. Rev. B 72, 140407(R) (2005).
Gwo, S., Chao, K.-J., Shih, C. K., Sadra, K. & Streetman, B. G. Direct mapping of electronic structure across Al0.3Ga0.7As/GaAs heterojunctions: band offsets, asymmetrical transition widths, and multiple-valley band structures. Phys. Rev. Lett. 71, 1883–1886 (1993).
Chien, T. Y., Liu, J., Chakhalian, J., Guisinger, N. P. & Freeland, J. W. Visualizing nanoscale electronic band alignment at the La2/3Ca1/3MnO3/Nb:SrTiO3 interface. Phys. Rev. B 82, 041101(R) (2010).
Liu, J. et al. Interfacial electronic and magnetic properties of a Y0.6Pr0.4Ba2Cu3O7/La2/3Ca1/3MnO3 superlattice. Phys. Rev. B 84, 092506 (2011).
Habermeier, H.-U., Cristiani, G., Kremer, R. K., Lebedev, O. & van Tendeloo, G. Cuprate/manganite superlattices A model system for a bulk ferromagnetic superconductor. Physica C 364-365, 298–304 (2001).
Sefrioui, Z. et al. Ferromagnetic/superconducting proximity effect in La0.7Ca0.3MnO3/YBa2Cu3O7-δ superlattices. Phys. Rev. B 67, 214511 (2003).
Holden, T. et al. Proximity induced metal-insulator transition in YBa2Cu3O7/La2/3Ca1/3MnO3 superlattices. Phys. Rev. B 69, 064505 (2004).
Guisinger, N. P. et al. Nanometer-scale striped surface terminations on fractured SrTiO3 surfaces. ACS Nano 3, 4132–4136 (2009).
Chien, T. Y., Santos, T. S., Bode, M., Guisinger, N. P. & Freeland, J. W. Controllable local modification of fractured Nb-doped SrTiO3 surfaces. Appl. Phys. Lett. 95, 163107 (2009).
Chien, T. Y., Guisinger, N. P. & Freeland, J. W. Survey of fractured SrTiO3 surfaces: from the micrometer to nanometer scale. J. Vac. Sci. Technol. B 28, C5A11–C5A13 (2010).
Chien, T. Y., Guisinger, N. P. & Freeland, J. W. Cross-sectional scanning tunneling microscopy for complex oxide interfaces. Proc. SPIE 7940, 79400T (2011).
Chiu, Y.-P. et al. Atomic-scale evolution of local electronic structure across multiferroic domain walls. Adv. Mater. 23, 1530–1534 (2011).
Huang, B.-C. et al. Direct observation of ferroelectric polarization-modulated band bending at oxide interfaces. Appl. Phys. Lett. 100, 122903 (2012).
Huang, B.-C. et al. Mapping band alignment across complex oxide heterointerfaces. Phys. Rev. Lett. 109, 246807 (2012).
Chu, C. W. High temperature superconducting materials: present status, future challenges, and one recent example—the superconducting ferromagnet. Physica C 341-348, 25–30 (2000).
Schiffer, P., Ramirez, A. P., Bao, W. & Cheong, S.-W. Low temperature magnetoresistance and the magnetic phase diagram of La1-xCaxMnO3 . Phys. Rev. Lett. 75, 3336–3339 (1995).
Mitra, J., Paranjape, M., Raychaudhuri, A. K., Mathur, N. D. & Blamire, M. G. Temperature dependence of density of states near the Fermi level in a strain-free epitaxial film of the hole-doped manganite La0.7Ca0.3MnO3 . Phys. Rev. B 71, 094426 (2005).
Krupke, R. & Deutscher, G. Anisotropic magnetic field dependence of the zero-bias anomaly on in-plane oriented [100] Y1Ba2Cu3O7-x/In tunnel junctions. Phys. Rev. Lett. 83, 4634–4637 (1999).
Wei, J. Y. T., Yeh, N.-C., Garrigus, D. F. & Strasik, M. Directional tunneling and Andreev reflection on YBa2Cu3O7-δ single crystals: predominance of d-wave pairing symmetry verified with the generalized Blonder, Tinkham, and Klapwijk Theory. Phys. Rev. Lett. 81, 2542–2545 (1998).
Zhang, Z. L., Kaiser, U., Soltan, S., Habermeier, H.-U. & Keimer, B. Magnetic properties and atomic structure of La2/3Ca1/3MnO3–YBa2Cu3O7 heterointerfaces. Appl. Phys. Lett. 95, 242505 (2009).
Varela, M., Lupini, A. R., Pennycook, S. J., Sefrioui, Z. & Santamaria, J. Nanoscale analysis of YBa2Cu3O7/La0.67Ca0.33MnO3 interfaces. Solid State Electron. 47, 2245–2248 (2003).
Muller, D. A. et al. Atomic-scale chemical imaging of composition and bonding by aberration-corrected microscopy. Science 319, 1073–1076 (2008).
Yunoki, S. et al. Electron doping of cuprates via interfaces with manganites. Phys. Rev. B 76, 064532 (2007).
Soltan, S., Albrecht, J. & Habermeier, H.-U. Ferromagnetic/superconducting bilayer structure: a model system for spin diffusion length estimation. Phys. Rev. B 70, 144517 (2004).
May, S. J., Santos, T. S. & Bhattacharya, A. Onset of metallic behavior in strained (LaNiO3)n/(SrMnO3)2 superlattices. Phys. Rev. B 79, 115127 (2009).
Goldman, A. M., Vas’ko, V., Kraus, P., Nikolaev, K. & Larkin, V. A. Cuprate/manganite heterostructures. J. Magn. Magn. Mater. 200, 69–82 (1999).
Acknowledgements
Work at Argonne, including the Center for Nanoscale Materials, is supported by the US Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract No. DE-AC02-06CH11357. The majority of the research at the University of Arkansas was supported by the grant from the NSF (DMR-0747808) and partially by DOD-ARO (W911NF-11-1-0200). Work at Cornell is supported by the Army Research Office under award W911NF0910415, and made use of the Cornell Center for Materials Research (CCMR) electron microscopy facility supported by the National Science Foundation Materials Research Science and Engineering Centers (MRSEC) program (DMR 1120296).
Author information
Authors and Affiliations
Contributions
T.Y.C., N.P.G. and J.W.F. measured and analysed XSTM/S, transport and X-ray rocking curve data. L.F.K. and D.A.M. performed EELS/STEM measurements and analysis. J.C., B.G. and M.K. prepare the samples. Data interpretations were achieved by discussion among all authors. T.Y.C., J.W.F., J.C., L.F.K. and D.A.M. wrote the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
About this article
Cite this article
Chien, T., Kourkoutis, L., Chakhalian, J. et al. Visualizing short-range charge transfer at the interfaces between ferromagnetic and superconducting oxides. Nat Commun 4, 2336 (2013). https://doi.org/10.1038/ncomms3336
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms3336
This article is cited by
-
Charge transfer driving interfacial reconstructions in perovskite oxide heterostructures
Communications Physics (2023)
-
Modulation of metal-insulator transitions of NdNiO3/LaNiO3/NdNiO3 trilayers via thickness control of the LaNiO3 layer
Scientific Reports (2019)
-
Low-temperature photovoltaic effect and current transport characteristics of YBa2Cu3O7−x/Nb:SrTiO3 heterojunction
Journal of Materials Science (2019)
-
Abnormal Transport and Magnetic Properties Induced by Change of the Phase Volume Ratio for YBa2Cu3O7-δ /La0.67Sr0.33MnO3 Hybrids
Journal of Superconductivity and Novel Magnetism (2018)
-
Long-range charge-density-wave proximity effect at cuprate/manganate interfaces
Nature Materials (2016)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.