Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Room temperature coherent control of defect spin qubits in silicon carbide

Abstract

Electronic spins in semiconductors have been used extensively to explore the limits of external control over quantum mechanical phenomena1. A long-standing goal of this research has been to identify or develop robust quantum systems that can be easily manipulated, for future use in advanced information and communication technologies2. Recently, a point defect in diamond known as the nitrogen–vacancy centre has attracted a great deal of interest because it possesses an atomic-scale electronic spin state that can be used as an individually addressable, solid-state quantum bit (qubit), even at room temperature3. These exceptional quantum properties have motivated efforts to identify similar defects in other semiconductors, as they may offer an expanded range of functionality not available to the diamond nitrogen–vacancy centre4. Notably, several defects in silicon carbide (SiC) have been suggested as good candidates for exploration, owing to a combination of computational predictions and magnetic resonance data4,5,6,7,8,9,10. Here we demonstrate that several defect spin states in the 4H polytype of SiC (4H-SiC) can be optically addressed and coherently controlled in the time domain at temperatures ranging from 20 to 300 kelvin. Using optical and microwave techniques similar to those used with diamond nitrogen–vacancy qubits, we study the spin-1 ground state of each of four inequivalent forms of the neutral carbon–silicon divacancy, as well as a pair of defect spin states of unidentified origin. These defects are optically active near telecommunication wavelengths11, and are found in a host material for which there already exist industrial-scale crystal growth12 and advanced microfabrication techniques13. In addition, they possess desirable spin coherence properties that are comparable to those of the diamond nitrogen–vacancy centre. This makes them promising candidates for various photonic, spintronic and quantum information applications that merge quantum degrees of freedom with classical electronic and optical technologies2,14,15,16,17.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Optical detection of defect spins in 4H-SiC.
Figure 2: Time-resolved dynamics of basal divacancy spins at 20 K.
Figure 3: Time-resolved dynamics of c -axis divacancy spins at 200 K.
Figure 4: Coherent control of defect spins in SiC at room temperature.

Similar content being viewed by others

References

  1. Hanson, R. & Awschalom, D. D. Coherent manipulation of single spins in semiconductors. Nature 453, 1043–1049 (2008)

    Article  ADS  CAS  Google Scholar 

  2. Awschalom, D. D. & Flatté, M. E. Challenges for semiconductor spintronics. Nature Phys. 3, 153–159 (2007)

    Article  ADS  CAS  Google Scholar 

  3. Jelezko, F., Gaebel, T., Popa, I., Gruber, A. & Wrachtrup, J. Observation of coherent oscillations in a single electron spin. Phys. Rev. Lett. 92, 076401 (2004)

    Article  ADS  CAS  Google Scholar 

  4. Weber, J. R. et al. Quantum computing with defects. Proc. Natl Acad. Sci. USA 107, 8513–8518 (2010)

    Article  ADS  CAS  Google Scholar 

  5. Gali, A. Time-dependent density functional study on the excitation spectrum of point defects in semiconductors. Phys. Status Solidi B 248, 1337–1346 (2011)

    Article  ADS  CAS  Google Scholar 

  6. Baranov, P. G. et al. EPR identification of the triplet ground state and photoinduced population inversion for a Si-C divacancy in silicon carbide. JETP Lett. 82, 441–443 (2005)

    Article  ADS  CAS  Google Scholar 

  7. Son, N. T. et al. Divacancy in 4H-SiC. Phys. Rev. Lett. 96, 055501 (2006)

    Article  ADS  CAS  Google Scholar 

  8. Mizuochi, N. et al. Continuous-wave and pulsed EPR study of the negatively charged silicon vacancy with S = 3/2 and C 3v symmetry in n-type 4H-SiC. Phys. Rev. B 66, 235202 (2002)

    Article  ADS  Google Scholar 

  9. Son, N. T., Zolnai, Z. & Janzén, E. Silicon vacancy related T V 2a center in 4H-SiC. Phys. Rev. B 68, 205211 (2003)

    Article  ADS  Google Scholar 

  10. Baranov, P. G., Bundakova, A. P. & Soltamov, A. A. Silicon vacancy in SiC as a promising quantum system for single-defect and single-photon spectroscopy. Phys. Rev. B 83, 125203 (2011)

    Article  ADS  Google Scholar 

  11. Saleh, B. E. A. & Teich, M. C. Fundamentals of Photonics Ch. 22 (Wiley, 1991)

    Book  Google Scholar 

  12. Powell, A. et al. Growth of SiC substrates. Int. J. High Speed Electron. Syst. 16, 751–777 (2006)

    Article  CAS  Google Scholar 

  13. Zetterling, C.-M. (ed.) Process Technology for Silicon Carbide Devices (Institution of Electrical Engineers, 2002)

    Book  Google Scholar 

  14. O'Brien, J. L., Furusawa, A. & Vučković, J. Photonic quantum technologies. Nature Photon. 3, 687–695 (2009)

    Article  ADS  CAS  Google Scholar 

  15. Maze, J. R. et al. Nanoscale magnetic sensing with an individual electronic spin in diamond. Nature 455, 644–647 (2008)

    Article  ADS  CAS  Google Scholar 

  16. Balasubramanian, G. et al. Nanoscale imaging magnetometry with diamond spins under ambient conditions. Nature 455, 648–651 (2008)

    Article  ADS  CAS  Google Scholar 

  17. Ladd, T. D. et al. Quantum computers. Nature 464, 45–53 (2010)

    Article  ADS  CAS  Google Scholar 

  18. Saddow, S. E. & Agarwal, A. (eds) Advances in Silicon Carbide Processing and Applications (Artech House, 2004)

    Google Scholar 

  19. Ryu, S.-H., Kornegay, K. T., Cooper, J. A. & Melloch, M. R. Digital CMOS IC’s in 6H-SiC operating on a 5-V power supply. IEEE Trans. Electron Dev. 45, 45–53 (1998)

    Article  ADS  CAS  Google Scholar 

  20. Cheung, R. (ed.) Silicon Carbide Microelectromechanical Systems for Harsh Environments (Imperial College Press, 2004)

    Google Scholar 

  21. Liu, L. & Edgar, J. H. Substrates for gallium nitride epitaxy. Mater. Sci. Eng. R 37, 61–127 (2002)

    Article  Google Scholar 

  22. Berger, C. et al. Electronic confinement and coherence in patterned epitaxial graphene. Science 312, 1191–1196 (2006)

    Article  ADS  CAS  Google Scholar 

  23. Magnusson, B. & Janzén, E. Optical characterization of deep level defects in SiC. Mater. Sci. Forum 483–485, 341–346 (2005)

    Article  Google Scholar 

  24. Carlos, W. E., Glaser, E. R. & Shanabrook, B. V. Optical and magnetic resonance signatures of deep levels in semi-insulating 4H SiC. Physica B 340–342, 151– 155. (2003)

    Article  ADS  Google Scholar 

  25. Carlos, W. E., Graces, N. Y., Glaser, E. R. & Fanton, M. A. Annealing of multivacancy defects in 4H-SiC. Phys. Rev. B 74, 235201 (2006)

    Article  ADS  Google Scholar 

  26. Son, N. T. et al. Identification of divacancies in 4H-SiC. Physica B 376–377, 334–337 (2006)

    Article  ADS  Google Scholar 

  27. Hanson, R., Gywat, O. & Awschalom, D. D. Room-temperature manipulation and decoherence of a single spin in diamond. Phys. Rev. B 74, 161203(R) (2006)

    Article  ADS  Google Scholar 

  28. de Lange, G., Wang, Z. H., Ristè, D., Dobrovitski, V. V. & Hanson, R. Universal dynamical decoupling of a single solid-state spin from a spin bath. Science 330, 60–63 (2010)

    Article  ADS  CAS  Google Scholar 

  29. Stanwix, P. L. et al. Coherence of nitrogen-vacancy electronic spin ensembles in diamond. Phys. Rev. B 82, 201201(R) (2010)

    Article  ADS  Google Scholar 

  30. van Oort, E. & Glasbeek, M. Optically detected low field electron spin echo envelope modulations of fluorescent N-V centers in diamond. Chem. Phys. 143, 131–140 (1990)

    Article  CAS  Google Scholar 

Download references

Acknowledgements

We are grateful to G. D. Fuchs, A. Janotti, D. M. Toyli, C. G. Van de Walle, J. B. Varley and J. R. Weber for discussions. We thank M. E. Nowakowski for help with sample preparation. This work was supported by the Air Force Office of Scientific Research (AFOSR) and the Defense Advanced Research Projects Agency (DARPA).

Author information

Authors and Affiliations

Authors

Contributions

All authors helped to design the research, perform the research and write the paper.

Corresponding author

Correspondence to David D. Awschalom.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

The file contains Supplementary Text Data and Methods, Supplementary Figures 1-11 with legends, Supplementary Table 1 and additional references. (PDF 623 kb)

PowerPoint slides

Rights and permissions

Reprints and permissions

About this article

Cite this article

Koehl, W., Buckley, B., Heremans, F. et al. Room temperature coherent control of defect spin qubits in silicon carbide. Nature 479, 84–87 (2011). https://doi.org/10.1038/nature10562

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/nature10562

This article is cited by

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing