Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Change of carrier density at the pseudogap critical point of a cuprate superconductor

Abstract

The pseudogap is a partial gap in the electronic density of states that opens in the normal (non-superconducting) state of cuprate superconductors and whose origin is a long-standing puzzle. Its connection to the Mott insulator phase at low doping (hole concentration, p) remains ambiguous1 and its relation to the charge order2,3,4 that reconstructs the Fermi surface5,6 at intermediate doping is still unclear7,8,9,10. Here we use measurements of the Hall coefficient in magnetic fields up to 88 tesla to show that Fermi-surface reconstruction by charge order in the cuprate YBa2Cu3Oy ends sharply at a critical doping p = 0.16 that is distinctly lower than the pseudogap critical point p* = 0.19 (ref. 11). This shows that the pseudogap and charge order are separate phenomena. We find that the change in carrier density n from n = 1 + p in the conventional metal at high doping (ref. 12) to n = p at low doping (ref. 13) starts at the pseudogap critical point. This shows that the pseudogap and the antiferromagnetic Mott insulator are linked.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Temperature–doping phase diagram of YBCO.
Figure 2: Field dependence of the Hall coefficient in YBCO.
Figure 3: Temperature dependence of the normal-state Hall coefficient in YBCO at various dopings.
Figure 4: Doping evolution of the normal-state carrier density.

Similar content being viewed by others

References

  1. Norman, M. R., Pines, D. & Kallin, C. The pseudogap: friend or foe of high Tc? Adv. Phys. 54, 715–733 (2005)

    Article  CAS  ADS  Google Scholar 

  2. Wu, T. et al. Magnetic-field-induced charge-stripe order in the high-temperature superconductor YBa2Cu3Oy . Nature 477, 191–194 (2011)

    Article  CAS  ADS  Google Scholar 

  3. Ghiringhelli, G. et al. Long-range incommensurate charge fluctuations in (Y,Nd)Ba2Cu3O6+x . Science 337, 821–825 (2012)

    Article  CAS  ADS  Google Scholar 

  4. Chang, J. et al. Direct observation of competition between superconductivity and charge density wave order in YBa2Cu3O6.67 . Nature Phys . 8, 871–876 (2012)

    Article  CAS  ADS  Google Scholar 

  5. Doiron-Leyraud, N. et al. Quantum oscillations and the Fermi surface in an underdoped high-Tc superconductor. Nature 447, 565–568 (2007)

    Article  CAS  ADS  Google Scholar 

  6. LeBoeuf, D. et al. Lifshitz critical point in the cuprate superconductor YBa2Cu3Oy from high-field Hall effect measurements. Phys. Rev. B 83, 054506 (2011)

    Article  ADS  Google Scholar 

  7. He, Y. et al. Fermi surface and pseudogap evolution in a cuprate superconductor. Science 344, 608–611 (2014)

    Article  CAS  ADS  Google Scholar 

  8. Fujita, K. et al. Simultaneous transitions in cuprate momentum-space topology and electronic symmetry breaking. Science 344, 612–616 (2014)

    Article  CAS  ADS  Google Scholar 

  9. Ramshaw, B. J. et al. Quasiparticle mass enhancement approaching optimal doping in a high-Tc superconductor. Science 348, 317–320 (2015)

    Article  CAS  ADS  Google Scholar 

  10. Senthil, T. On the mass enhancement near optimal doping in high magnetic fields in the cuprates. Preprint at http://arXiv.org/abs/1410.2096 (2014)

  11. Tallon, J. L. & Loram, J. W. The doping dependence of T* — what is the real high-Tc phase diagram? Physica C 349, 53–68 (2001)

    Article  CAS  ADS  Google Scholar 

  12. Mackenzie, A. P. et al. Normal-state magnetotransport in superconducting Ta2Ba2CuO6+δ to millikelvin temperatures. Phys. Rev. B 53, 5848–5855 (1996)

    Article  CAS  ADS  Google Scholar 

  13. Ando, Y. et al. Evolution of the Hall coefficient and the peculiar electronic structure of the cuprate superconductors. Phys. Rev. Lett. 92, 197001 (2004)

    Article  ADS  Google Scholar 

  14. Vignolle, B. et al. Quantum oscillations in an overdoped high-Tc superconductor. Nature 455, 952–955 (2008)

    Article  CAS  ADS  Google Scholar 

  15. Hussey, N. E. Phenomenology of the normal state in-plane transport properties of high-Tc cuprates. J. Phys. Condens. Matter 20, 123201 (2008)

    Article  ADS  Google Scholar 

  16. Segawa, K. & Ando, Y. Intrinsic Hall response of the CuO2 planes in a chain-plane composite system of YBa2Cu3Oy . Phys. Rev. B 69, 104521 (2004)

    Article  ADS  Google Scholar 

  17. Balakirev, F. F. et al. Quantum phase transition in the magnetic-field-induced normal state of optimum-doped high-Tc cuprate superconductors at low temperatures. Phys. Rev. Lett. 102, 017004 (2009)

    Article  CAS  ADS  Google Scholar 

  18. Yoshida, T. et al. Systematic doping evolution of the underlying Fermi surface of La2-xSrxCuO4 . Phys. Rev. B 74, 224510 (2006)

    Article  ADS  Google Scholar 

  19. Croft, T. P., Lester, C., Senn, M. S., Bombardi, A. & Hayden, S. M. Charge density wave fluctuations in La2-xSrxCuO4 and their competition with superconductivity. Phys. Rev. B 89, 224513 (2014)

    Article  ADS  Google Scholar 

  20. Balakirev, F. F. et al. Signature of optimal doping in Hall-effect measurements on a high-temperature superconductor. Nature 424, 912–915 (2003)

    Article  CAS  ADS  Google Scholar 

  21. Fournier, D. et al. Loss of nodal quasiparticle integrity in underdoped YBa2Cu3O6+x . Nature Phys . 6, 905–911 (2010)

    Article  CAS  ADS  Google Scholar 

  22. Hücker, M. et al. Competing charge, spin and superconducting orders in underdoped YBa2Cu3Oy . Phys. Rev. B 90, 054514 (2014)

    Article  ADS  Google Scholar 

  23. Blanco-Canosa, S. et al. Resonant X-ray scattering study of charge-density wave correlations in YBa2Cu3O6+x . Phys. Rev. B 90, 054513 (2014)

    Article  ADS  Google Scholar 

  24. Wu, T. et al. Emergence of charge order from the vortex state of a high-temperature superconductor. Nature Commun . 4, 2113 (2013)

    Article  ADS  Google Scholar 

  25. Tallon, J. L. et al. Zn-induced Tc reduction in high-Tc superconductors: scattering in the presence of a pseudogap. Phys. Rev. Lett. 79, 5294–5297 (1997)

    Article  CAS  ADS  Google Scholar 

  26. Blanco-Canosa, S. et al. Momentum-dependent charge correlations in YBa2Cu3O6+δ superconductors probed by resonant X-ray scattering: evidence for three competing phases. Phys. Rev. Lett. 110, 187001 (2013)

    Article  CAS  ADS  Google Scholar 

  27. Dagan, Y. et al. Evidence for a quantum phase transition in Pr2-xCexCuO4-δ from transport measurements. Phys. Rev. Lett. 92, 167001 (2004)

    Article  CAS  ADS  Google Scholar 

  28. Haug, D. et al. Neutron scattering study of the magnetic phase diagram of underdoped YBa2Cu3O6+x . New J. Phys. 12, 105006 (2010)

    Article  ADS  Google Scholar 

  29. Taillefer, L. Scattering and pairing in cuprate superconductors. Annu. Rev. Condens. Matter Phys. 1, 51–70 (2010)

    Article  CAS  ADS  Google Scholar 

  30. Sénéchal, D. & Tremblay, A.-M. S. Hot spots and pseudogaps for hole- and electron-doped high-temperature superconductors. Phys. Rev. Lett. 92, 126401 (2004)

    Article  ADS  Google Scholar 

  31. Ferrero, M. et al. Pseudogap opening and formation of Fermi arcs as an orbital-selective Mott transition in momentum space. Phys. Rev. B 80, 064501 (2009)

    Article  ADS  Google Scholar 

  32. Rice, T. M. et al. A phenomenological theory of the anomalous pseudogap phase in underdoped cuprates. Rep. Prog. Phys. 75, 016502 (2012)

    Article  CAS  ADS  Google Scholar 

  33. Chowdhury, D. & Sachdev, S. Density-wave instabilities of fractionalized Fermi liquids. Phys. Rev. B 90, 245136 (2014)

    Article  ADS  Google Scholar 

  34. Liang, R., Bonn, D. A. & Hardy, W. N. Growth of YBCO single crystals by the self-flux technique. Phil. Mag. 92, 2563–2581 (2012)

    Article  CAS  ADS  Google Scholar 

  35. Liang, R., Bonn, D. A. & Hardy, W. N. Evaluation of CuO2 plane hole doping in YBa2Cu3O6+x single crystals. Phys. Rev. B 73, 180505 (2006)

    Article  ADS  Google Scholar 

  36. Gagnon, R., Lupien, C. & Taillefer, L. T2 dependence of the resistivity in the CuO chains of YBa2Cu3O6.9 . Phys. Rev. B 50, 3458–3461 (1994)

    Article  CAS  ADS  Google Scholar 

  37. Hussey, N. The normal state scattering rate in high-Tc cuprates. Eur. Phys. J. B 31, 495–507 (2003)

    Article  CAS  ADS  Google Scholar 

  38. Manako, T. et al. Transport and structural study of Tl2Ba2CuO6+δ single crystals prepared by the KCl flux method. Phys. Rev. B 46, 11019–11024 (1992)

    Article  CAS  ADS  Google Scholar 

  39. Hussey, N. E. et al. Angular dependence of the c-axis normal-state magnetoresistance in single crystal Tl2Ba2CuO6 . Phys. Rev. Lett. 76, 122–125 (1996)

    Article  CAS  ADS  Google Scholar 

Download references

Acknowledgements

We thank the following for discussions: Y. Ando, D. Basov, G. Boebinger, C. Bourbonnais, J. P. Carbotte, A. Carrington, J. Chang, A. V. Chubukov, J. C. Davis, A. Georges, N. E. Hussey, M.-H. Julien, H.-Y. Kee, S. A. Kivelson, P. A. Lee, T. Loew, G. G. Lonzarich, W. Metzner, A. J. Millis, M. R. Norman, C. Pépin, J. Porras, B. J. Ramshaw, T. M. Rice, G. Rikken, S. Sachdev, D. J. Scalapino, C. B. Taillefer, J. L. Tallon, S. Todadri, and A.-M. S. Tremblay. We also thank P. Frings and J.P. Nicolin for help during the measurements in Toulouse. L.T. thanks the Laboratoire National des Champs Magnétiques Intenses (LNCMI) in Toulouse for their hospitality and LABEX NEXT for their support while this work was being performed. A portion of this work was performed at the LNCMI, which is supported by the French ANR SUPERFIELD, the EMFL, and the LABEX NEXT. R.L., D.A.B. and W.N.H. acknowledge funding from the Natural Sciences and Engineering Research Council of Canada (NSERC). L.T. acknowledges support from the Canadian Institute for Advanced Research (CIFAR) and funding from NSERC, the Fonds de recherche du Québec – Nature et Technologies (FRQNT), the Canada Foundation for Innovation (CFI) and a Canada Research Chair.

Author information

Authors and Affiliations

Authors

Contributions

S.B., W.T., F.L., B.V., D.V., J.B. and C.P. performed the transport measurements at the LNCMI. S.B. and N.D.-L. performed the transport measurements at Sherbrooke. G.G. performed the calculations of the transport coefficients. D.A.B., W.N.H. and R.L. prepared the YBCO single crystals at UBC. S.B., L.T. and C.P. wrote the manuscript, in consultation with all authors. L.T. and C.P. co-supervised the project.

Corresponding authors

Correspondence to Louis Taillefer or Cyril Proust.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Extended data figures and tables

Extended Data Figure 1 Temperature dependence of resistivity of CuO chains in YBCO at p = 0.177.

Shown is the chain resistivity in YBCO at p = 0.177 (red), defined as ρchain = 1/[(1/ρb) − (1/ρa)], where ρa and ρb are the in-plane resistivities along the a and b directions of the orthorhombic structure, respectively, plotted versus T2. The black line is a linear fit that extrapolates to ρchain = 50 μΩ cm at T = 50 K.

Extended Data Figure 2 Isotherms of RH versus H in YBCO at p = 0.16.

Shown is the magnetic field dependence of the Hall coefficient RH in our YBCO sample with y = 6.92 (Tc = 93.5 K; p = = 0.161) at various temperatures, as indicated (key at right).

Extended Data Figure 3 Isotherms of RH versus H in YBCO at p = 0.177.

As for Extended Data Fig. 2 but for our YBCO sample with y = 6.97 (Tc = 91 K; p = 0.177).

Extended Data Figure 4 Isotherms of RH versus H in YBCO at p = 0.19.

As for Extended Data Fig. 2 but for our YBCO sample with y = 6.99 and 1.4% Ca doping (Tc = 87 K; p = 0.19).

Extended Data Figure 5 Isotherms of RH versus H in YBCO at p = 0.205.

As for Extended Data Fig. 2 but for our YBCO sample with y = 6.99 and 5% Ca doping (Tc = 77 K; p = 0.205).

Extended Data Figure 6 Doping dependence of Tmax.

Shown is the temperature Tmax at which RH versus T peaks in YBCO (Fig. 3a), plotted versus doping p. At p = 0.16, there is no downturn in the normal-state RH(T) down to 40 K. The p = 0.16 data are consistent with Tmax = 0 (lower bound), with an upper bound at Tmax = 40 K (shown as black vertical segment). The width of the grey band marks the upper and lower limits for Tmax versus p. The green diamond defines the critical doping above which FSR is no longer present, at pFSR = 0.16 ± 0.005, with an error bar defined from the minimal and maximal possible values of Tmax. Error bars on the three data points (black dots) represent the uncertainty in defining the peak position of the RH(T) curves in Fig. 3a.

Extended Data Figure 7 Zoom on RH versus T in Tl-2201 and YBCO at high doping.

a, Temperature dependence of RH in Tl-2201 (squares) at p = 0.3 (blue, Tc = 10 K; ref. 38) and p = 0.27 (green, Tc = 25 K; ref. 39). b, RH versus T in YBCO (circles, from Extended Data Figs 4, 5 and 8) at p = 0.205 (yellow) and p = 0.19 (blue). The dashed lines are an extrapolation of the low-T data to T = 0. The YBCO curve at p = 0.205 is qualitatively similar to the two Tl-2201 curves, all exhibiting an initial rise with increasing temperature from T = 0, and a characteristic peak at T ≈ 100 K—two features attributed to inelastic scattering on a large hole-like Fermi surface15. The YBCO curve at p = 0.19 is qualitatively different, showing no sign of a drop at low T (see Extended Data Fig. 8). We attribute the twofold increase in the magnitude of RH at T → 0 to a decrease in carrier density as the pseudogap opens at p*, with p* located between p = 0.205 and p = 0.19. The error bars are defined in the legend of Fig. 3.

Extended Data Figure 8 Comparison between p = 0.205 and p = 0.19.

a, b, The field dependence of the Hall coefficient RH in YBCO at p = 0.205 (a) and p = 0.19 (b), for different temperatures as indicated. The colour-coded lines are parallel linear fits to the high-field data. They show that at low temperature RH decreases upon cooling at p = 0.205, while it saturates at p = 0.19. The value of RH given by the fit line, at H = 80 T, is plotted in Fig. 3 and in Extended Data Fig. 7b. Similar fits are used to extract RH(80 T) for p = 0.16 and p = 0.177 (from data in Extended Data Figs 2 and 3).

Extended Data Figure 9 Scenario of inelastic scattering.

a, RH versus T in YBCO at four dopings p, as indicated (Fig. 3b). b, Electrical resistivity ρa versus T in YBCO at four dopings, as indicated. Lines are at H = 0; dots are in the normal state at high field. c, RH versus T calculated for five values of inelastic scattering, with Γ1 = 0, 1, 5, 15 and 25 THz K−1, showing that RH(T) grows with increasing Γ1 (see Methods). Dots are from a. d, Corresponding calculated values of the electrical resistivity ρa, plotted versus T, using the same parameters and values of Γ1 as for the colour-coded curves of c. The vertical grey lines mark T = 50 K, the temperature at which we see a sixfold increase in RH (a), yet no increase in ρa (b). The calculation can reproduce the large increase in RH (c), but it is accompanied by a tenfold increase in ρa (d).

Extended Data Figure 10 Magnetic field profile.

Time dependence of the magnetic field pulse in the 90 T dual-coil magnet at the LNCMI in Toulouse. Inset, zoom around maximum field.

PowerPoint slides

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Badoux, S., Tabis, W., Laliberté, F. et al. Change of carrier density at the pseudogap critical point of a cuprate superconductor. Nature 531, 210–214 (2016). https://doi.org/10.1038/nature16983

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/nature16983

This article is cited by

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing