Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Sequential deposition as a route to high-performance perovskite-sensitized solar cells

Abstract

Following pioneering work1, solution-processable organic–inorganic hybrid perovskites—such as CH3NH3PbX3 (X = Cl, Br, I)—have attracted attention as light-harvesting materials for mesoscopic solar cells2,3,4,5,6,7,8,9,10,11,12,13,14,15. So far, the perovskite pigment has been deposited in a single step onto mesoporous metal oxide films using a mixture of PbX2 and CH3NH3X in a common solvent. However, the uncontrolled precipitation of the perovskite produces large morphological variations, resulting in a wide spread of photovoltaic performance in the resulting devices, which hampers the prospects for practical applications. Here we describe a sequential deposition method for the formation of the perovskite pigment within the porous metal oxide film. PbI2 is first introduced from solution into a nanoporous titanium dioxide film and subsequently transformed into the perovskite by exposing it to a solution of CH3NH3I. We find that the conversion occurs within the nanoporous host as soon as the two components come into contact, permitting much better control over the perovskite morphology than is possible with the previously employed route. Using this technique for the fabrication of solid-state mesoscopic solar cells greatly increases the reproducibility of their performance and allows us to achieve a power conversion efficiency of approximately 15 per cent (measured under standard AM1.5G test conditions on solar zenith angle, solar light intensity and cell temperature). This two-step method should provide new opportunities for the fabrication of solution-processed photovoltaic cells with unprecedented power conversion efficiencies and high stability equal to or even greater than those of today’s best thin-film photovoltaic devices.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Transformation of PbI2 into CH3NH3PbI3 within the nanopores of a mesoscopic TiO2 film.
Figure 2: Cross-sectional SEM of a complete photovoltaic device.
Figure 3: Photovoltaic device characterization.

Similar content being viewed by others

References

  1. Kojima, A., Teshima, K., Shirai, Y. & Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050–6051 (2009)

    Article  CAS  Google Scholar 

  2. Hagfeldt, A., Boschloo, G., Sun, L., Kloo, L. & Pettersson, H. Dye-sensitized solar cells. Chem. Rev. 110, 6595–6663 (2010)

    CAS  Google Scholar 

  3. Im, J.-H. et al. 6.5% efficient perovskite quantum-dot-sensitized solar cell. Nanoscale 3, 4088–4093 (2011)

    Article  ADS  CAS  Google Scholar 

  4. Kim, H.-S. et al. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Sci. Rep. 2, 591 (2012)

    Article  Google Scholar 

  5. Lee, M. M., Teuscher, J., Miyasaka, T., Murakami, T. N. & Snaith, H. J. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643–647 (2012)

    Article  ADS  CAS  Google Scholar 

  6. Etgar, L. et al. Mesoscopic CH3NH3PbI3/TiO2 heterojunction solar cells. J. Am. Chem. Soc. 134, 17396–17399 (2012)

    Article  CAS  Google Scholar 

  7. Im, J.-H., Chung, J., Kim, S.-J. & Park, N.-G. Synthesis, structure, and photovoltaic property of a nanocrystalline 2H perovskite-type novel sensitizer (CH3CH2NH3)PbI3 . Nanoscale Res. Lett. 7, 353 (2012)

    Article  ADS  Google Scholar 

  8. Edri, E., Kirmayer, S., Cahen, D. & Hodes, G. High open-circuit voltage solar cells based on organic-inorganic lead bromide perovskite. Phys. Chem. Lett. 4, 897–902 (2013)

    Article  CAS  Google Scholar 

  9. Crossland, E. J. W. et al. Mesoporous TiO2 single crystals delivering enhanced mobility and optoelectronic device performance. Nature 495, 215–219 (2013)

    Article  ADS  CAS  Google Scholar 

  10. Noh, J. H., Im, S. H., Heo, J. H., Mandal, T. N. & Seok, S. I. Chemical management for colorful, efficient, and stable inorganic−organic hybrid nanostructured solar cells. Nano Lett. 13, 1764–1769 (2013)

    Article  ADS  CAS  Google Scholar 

  11. Cai, B., Xing, Y., Yang, Z., Zhang, W.-H. & Qiu, J. High performance hybrid solar cells sensitized by organolead halide perovskites. Energy Environ. Sci. 6, 1480–1485 (2013)

    Article  CAS  Google Scholar 

  12. Qui, J. et al. All-solid-state hybrid solar cells based on a new organometal halide perovskite sensitizer and one-dimensional TiO2 nanowire arrays. Nanoscale 5, 3245–3248 (2013)

    Article  ADS  Google Scholar 

  13. Ball, J. M., Lee, M. M., Hey, A. & Snaith, H. J. Low-temperature processed meso-superstructured to thin-film perovskite solar cells. Energy Environ. Sci. 6, 1739–1743 (2013)

    Article  CAS  Google Scholar 

  14. Bi, D., Yang, L., Boschloo, G., Hagfeldt, A. & Johansson, E. M. J. Effect of different hole transport materials on recombination in CH3NH3PbI3 perovskite-sensitized mesoscopic solar cells. J. Phys. Chem. Lett. 4, 1532–1536 (2013)

    Article  CAS  Google Scholar 

  15. Heo, J. H. et al. Efficient inorganic–organic hybrid heterojunction solar cells containing perovskite compound and polymeric hole conductors. Nature Photon. 7, 486–492 (2013)

    Article  ADS  CAS  Google Scholar 

  16. Beckmann, A. A review of polytypism in lead iodide. Cryst. Res. Technol. 45, 455–460 (2010)

    Article  CAS  Google Scholar 

  17. Baikie, T. et al. Synthesis and crystal chemistry of the hybrid perovskite (CH3NH3)PbI3 for solid-state sensitized solar cell applications. J. Mater. Chem. A 1, 5628–5641 (2013)

    Article  CAS  Google Scholar 

  18. Liang, K., Mitzi, D. B. & Prikas, M. T. Synthesis and characterization of organic-inorganic perovskite thin films prepared using a versatile two-step dipping technique. Chem. Mater. 10, 403–411 (1998)

    Article  CAS  Google Scholar 

  19. Beberwyck, B. J. & Alivisatos, A. P. Ion exchange synthesis of III–V nanocrystals. J. Am. Chem. Soc. 134, 19977–19980 (2012)

    Article  CAS  Google Scholar 

  20. Luther, J. M., Zheng, H., Sadtler, B. & Alivisatos, A. P. Synthesis of PbS nanorods and other ionic nanocrystals of complex morphology by sequential cation exchange reactions. J. Am. Chem. Soc. 131, 16851–16857 (2009)

    Article  CAS  Google Scholar 

  21. Li, H. et al. Sequential cation exchange in nanocrystals: preservation of crystal phase and formation of metastable phases. Nano Lett. 11, 4964–4970 (2011)

    Article  ADS  CAS  Google Scholar 

  22. Gurina, G. I. & Savchenko, K. V. Intercalation and formation of complexes in the system of lead(II) iodide–ammonia. J. Solid State Chem. 177, 909–915 (2004)

    Article  ADS  CAS  Google Scholar 

  23. Preda, N., Mihut, L., Baibarac, M., Baltog, I. & Lefrant, S. A distinctive signature in the Raman and photoluminescence spectra of intercalated PbI2 . J. Phys. Condens. Matter 18, 8899–8912 (2006)

    Article  ADS  CAS  Google Scholar 

  24. Warren, R. F. & Liang, W. Y. Raman spectroscopy of new lead iodide intercalation compounds. J. Phys. Condens. Matter 5, 6407–6418 (1993)

    Article  ADS  CAS  Google Scholar 

  25. Burschka, J. et al. Tris(2-(1H-pyrazol-1-yl)pyridine)cobalt(III) as p-type dopant for organic semiconductors and its application in highly efficient solid-state dye-sensitized solar cells. J. Am. Chem. Soc. 133, 18042–18045 (2011)

    Article  CAS  Google Scholar 

Download references

Acknowledgements

We thank M. Marszalek for recording SEM images, M. Tschumi for help with the stability measurements and K. Schenk for the XRD characterization. We acknowledge financial support from Aisin Cosmos R&D Co., Ltd, Japan; the European Community’s Seventh Framework Programme (FP7/2007-2013) ENERGY.2012.10.2.1; NANOMATCELL, grant agreement no. 308997; the Global Research Laboratory Program, Korea; the Center for Advanced Molecular Photovoltaics (award no. KUS-C1-015-21) of King Abdullah University of Science and Technology; and Solvay S.A. M.K.N. thanks the World Class University programmes (Photovoltaic Materials, Department of Material Chemistry, Korea University), funded by the Ministry of Education, Science and Technology through the National Research Foundation of Korea (R31-2008-000-10035-0). M.G. thanks the Max Planck Society for a Max Planck Fellowship at the MPI for Solid State Research in Stuttgart, Germany; the King Abdulaziz University, Jeddah and the Nanyang Technolocal University, Singapore for Adjunct Professor appointments; and the European Research Council for an Advanced Research Grant (ARG 247404) funded under the “Mesolight” project.

Author information

Authors and Affiliations

Authors

Contributions

J.B. developed the basic concept, carried out the spectroscopic characterization, fabricated and characterized photovoltaic devices, and coordinated the project. N.P. fabricated and characterized photovoltaic devices, optimized device performance and fabricated high-performance devices for the certification. S.-J.M. contributed to the fabrication and characterization of photovoltaic devices. R.H.-B. contributed to the spectroscopic characterization and data analysis. P.G. synthesized CH3NH3I. M.G. and J.B. analysed the data and wrote the paper. M.K.N. contributed to the supervision of the project. M.G. had the idea for, and directed, the project. All authors reviewed the paper.

Corresponding author

Correspondence to Michael Grätzel.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

This file contains Supplementary Figures 1-5 and Supplementary Table 1. (PDF 6620 kb)

PowerPoint slides

Rights and permissions

Reprints and permissions

About this article

Cite this article

Burschka, J., Pellet, N., Moon, SJ. et al. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–319 (2013). https://doi.org/10.1038/nature12340

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/nature12340

This article is cited by

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing