Abstract
The Yb62.5Zn15Mg17.5Cu5 metallic glass is investigated using synchrotron x-ray total scattering method up to 38.4 GPa. The polyamorphic transformation from low density to high density with a transition region between 14.1 and 25.2 GPa is observed, accompanying with a volume collapse reflected by a discontinuousness of isothermal bulk modulus. This collapse is caused by that distortional icosahedron short range order precedes to perfect icosahedron, which might link to Yb 4f electron delocalization upon compression, and match the result of in situ electrical resistance measurement under high pressure conditions. This discovery in Yb-based metallic glass, combined with the previous reports on other metallic glass systems, demonstrates that pressure induced polyamorphism is the general behavior for typical lanthanide based metallic glasses.
Similar content being viewed by others
Introduction
Traditional network-forming glassy state materials1, such as ice2, silica3 and silicon4 have been reported to exhibit polyamorphism induced by pressure, which tends to be ascribed to an increase in atomic coordination. Whereas, metallic glasses are distinct from the traditional glasses due to the non-directional metallic bonds. Therefore, polyamorphism induced by pressure in metallic glass was supposed to be impossible for they are spatially densely-packing and have the maximum coordination number already. However, polyamorphic transitions were discovered in Ce-based metallic glasses attributed to 4f electron delocalization in Ce under high pressure5,6. This rises a question that it is the general behavior for all lanthanide based metallic glasses, or not.
Ytterbium, as an end member of the rare-earth lanthanides, behaves irregular in comparison with other members of the lanthanide series owing to its special electronic configuration. At ambient conditions, ytterbium is considered as divalent with an electronic configuration close to 4f 14(5d6s)2, while the other lanthanides as trivalent state 4fn(5d6s)3, where n varies from 0 to 14 corresponding to lanthanum to lutetium. The special electronic configuration of ytterbium results in a special sequence of phase transitions at high temperatures as well as high pressures7,8,9,10. If Ce with electronic configuration of 4f1(5d6s)3 could be looked as “n-type one electron” like beginning member, Yb, on the other hand, could be looked as 4f 14(5d6s)3+(−1), i. e. “p-type one hole like” ending member, which indeed results in a d- rather than an f differentiating electron behavior. Therefore, searching the potential polyamorphic transformation in Yb-based metallic glasses under compression conditions will be interesting to reveal whether the generality of polyamorphism exists.
Generally, pressure-volume studies are particularly valuable in confirming whether polyamorphic transitions occur10. Such polyamorphic transformations derived from valence transitions should involve in changes of electrical transport property. In this work, to shed some light on the nature of polyamorphic transitions induced by pressure in Yb-based metallic glass systems, a study was performed by means of synchrotron x-ray total scattering and resistance measurements, focusing on another side of ending member of this lanthanide base metallic glass family, namely Yb62.5Zn15Mg17.5Cu5 metallic glass.
Results and Discussion
X-ray total scattering under pressure
The structure factor S(Q) and corresponding PDFs of the Yb62.5Zn15Mg17.5Cu5 metallic glass extracting from synchrotron x-ray scattering experiment as a function of pressure are displayed in Fig. 1. Absence of sharp peaks in S(Q) and PDFs indicates that the sample remains fully amorphous state in the entire pressure range. As expected for the compression effect, first peak position Q1 of structure factor S(Q) in reciprocal space shifts towards higher momentum transfer and the nearest-neighbor distance r1 in real space shifts to shorter distance with increasing pressure. The shifts of Q1 of structure factor S(Q) and the nearest-neighbor distance r1 reflect changes in volume or density induced by pressure, which is illustrated by a power law3,11,12,13. Using normalized first peak position Q1 with a power of 2.5 to estimate the relative volume change as a function of pressure, a fast decrease of the average atomic volume under pressure range from 14.1 to 25.2 GPa, a transition region, is observed. Two amorphous states, low density amorphous states (LDAS) and high density amorphous states (HDAS), were separated by the transition region. Fitting the pressure-volume data by the second-order Birch-Murnaghan equation of state (EoS)14, the isothermal bulk modulus are determined as B0 = 24(1) GPa and 45(7) GPa at different state region respectively, presenting a discontinuousness of isothermal bulk modulus, as shown in Fig. 2. The volume difference between the two states is as large as 15.2% at ambient pressure. Furthermore, the volume collapse taking place continuously and undergoing a broad pressure range rather than abruptly at certain pressure point shows an anomalous compressed region, which is in agreement with polyamorphic transition in Ce55Al45 metallic glass with a smooth and continuous transition region between 2 and 13.5 GPa5. This anomalous compressed curve is also observed in phase transition of ytterbium monotelluride under pressure15.
(a) Structure factor S(Q) and (b) pair distribution function G(r) of the Yb62.5Zn15Mg17.5Cu5 metallic glass at various pressure conditions.
The green and purple line show the EoS fitting results at LDAS region and HDAS region, respectively. The pink line is for transition region.
As shown in Fig. 3(a,b), both Q1 and r1 move with a relatively fast pace at transition region and the changes of both Q1 and r1as a function of pressure exhibit a trend similar to that of volume, which suggest that the polyamorphic transformation is embodied as well in medium range and short range length scale besides long range length scale. Intuitive local structure change of Yb62.5Zn15Mg17.5Cu5 within short range length scale induced by pressure was reflected by gradually disappeared the low-r shoulder of the first peak in G(r), as shown in Fig. 1(b).
Pressure dependence of (a) normalized first peak position Q1 and (b) normalized nearest-neighbor distance r1, respectively, where Q10 and r10 are initial first peak position and nearest-neighbor distance, respectively. Equation used in fitting both Q10/Q1 and r1/r10 as a function of pressure is based on second-order Birch-Murnaghan EoS.
As is displayed in Fig. 1, the second peak in S (Q) and PDFs are of splitting at each pressure point which are characteristic for conventional amorphous alloy systems16,17. In real space, the changes splitting of second peak under pressure reflect structural changes of Yb62.5Zn15Mg17.5Cu5 in medium range length scale. Such change is consistent with phase transition characterized by shifts of Q1which embody the medium range order. In reciprocal space the relationship between the first peak and splitting second peak as a function of pressure is indicative of short range order change18,19. Define position of the second peak and its shoulder as Q2 and Q2shoulder. Using two Gaussian functions to fit the second peak, the ratios of peak position show Q2shoulder/Q1 = 1.93 and Q2/Q1 varying from 1.66 to 1.72 with increased pressure, as displayed in Fig. 4. In contrast to a perfect icosahedron short range order, Q2shoulder/Q1 = 2.04 and Q2/Q1 = 1.7120, short range order changes in the Yb62.5Zn15Mg17.5Cu5 metallic glass under pressure go through from a more distortional icosahedra to a more perfect one with a different pace corresponding to different phase states. The polyamorphic transformation in the Yb62.5Zn15Mg17.5Cu5 metallic glass under pressure is thus mainly related to the reduction of icosahedra distortion with a different pace leading to volume collapse. This result is consistent with the change of PDFs whose each peak is sharper increasingly with increasing pressure, indicating the structure gradually becomes more order compared to initial structure, as presented in Fig. 1(b). At stage of LDAS, the change of distortion with pressure is slight and it contributes to a weak volume reduction. The diminution in degree of icosahedra distortion proceeds with faster pace within a transition region, then, distortional icosahedron is close to a more perfect one reaching the range of HDAS, which leads to a large volume change. Whereas, such changes of distortional icosahedra result from the decrease of average atomic distance in first neighbor shell with a different step as shown in Fig. 3(b), which should be radically associated with electronic transformation.
Q2/Q1 in the Yb62.5Zn15Mg17.5Cu5 metallic glass as a function of pressure.
The phase transition of the Yb62.5Zn15Mg17.5Cu5 metallic glass can be ascribed to the electronic transition. In the Yb62.5Zn15Mg17.5Cu5 metallic glass, the 4f shell of Yb is completely full and considered as divalent with an electronic configuration close to 4f14(5d6s)2 at ambient conditions, whereas, under high pressure conditions, it transforms to a trivalent state 4f 13(5d6s)3 when one of the localized 4f electrons is delocalized, which is deduced from mechanism lied in polymorphism in ytterbium compounds9,21 and polyamorphism in Ce-based metallic glass under pressure5,6. An Yb in the trivalent state has a smaller atomic volume compared to divalent state, and this results in a striking decrease in average bond length, which coincides with the change of icosahedral distortion and volume collapse.
The pressure dependence of electrical resistivity
Electronic transition in the Yb62.5Zn15Mg17.5Cu5 metallic glass should be reflected in changes of electronic transport property. Therefore, an in situ resistance measurement under compression conditions was carried out. Figure 5 displays the resistance of Yb62.5Zn15Mg17.5Cu5 metallic glass as a function of pressure. According to weak-scattering theory which is well suited for low-resistivity metallic glasses, the resistance of a metallic glass is considered as arising from disordered atom scattering described by structure factor22,23. The pressure dependence of electrical resistivity is effected by several factors, such as the Fermi energy, the electron-ion interaction and structure factor of the system. As a result of a rather delicate interplay of these factors, the resistivity of metallic glasses is either to increase or to decrease under compressed conditions depending on different systems24,25. In the Yb62.5Zn15Mg17.5Cu5 metallic glass system, a positive pressure coefficient of the resistivity (PCR) is observed. Additionally, both the structure and electronic transition are arising from Yb 4f electrons delocalization as well as relation between pressure and electrical resistivity is volume dependence23, therefore, resistance of the Yb62.5Zn15Mg17.5Cu5 metallic glass exhibits a similar transition region, which is from 19.3 to 30.2 GPa, to that of low density to high density transition displayed in synchrotron x-ray scattering experiment. The shift of transition region might be due to quasi-hydrostatic pressure conditions in resistance measurement experiment. The pressure effect on this metallic glass is basically reversible, but with sluggish effect when pressure released. Thus this polyamorphism could only be studied via in situ high pressure methods.
The inset shows the microphotograph of the sample with four Pt electrodes in chamber between two anvils at about 5 GPa conditions.
The positive PCR obviously reduced after transition in the Yb62.5Zn15Mg17.5Cu5 metallic glass is observed in Fig. 5. Cheung and Ashcroft26 found a positive PCR for the polyvalent metals Mg, Al, Sn and a negative PCR for the monovalent metal K in liquid metals under pressure. Particularly, the positive PCR is maximal for the divalent metals22,25. This conclusion may suit for Yb contribution to PCR of the Yb62.5Zn15Mg17.5Cu5 metallic glass as well. The conversion from divalent to trivalent Yb leads to that contribution of Yb to positive PCR in the Yb62.5Zn15Mg17.5Cu5 metallic glass decreases in case of 4f electron delocalization, which gives rise to decline of positive PCR after transition.
A polyamorphic transformation from low density to high density with a transition region between 14.1 and 25.2 GPa occurs accompanying with change of electrical transport property. The transitions could be explained by 4f electron delocalization in Yb. The 4f–5d electronic collapse is reflected in both pressure-volume and pressure-resistivity relationship. This findings, combined with the previous reports on pressure induced polyamorphism in Ce based and La based metallic glasses5,6,17, is valuable to understand the polyamorphic transformation, which could be a general behavior in lanthanide based metallic glasses.
Methods
To achieve Yb-based metallic glasses with good glass forming ability, constituent elements Zn, Mg and Cu were carefully selected and adjusted the composition. Metallic glass Yb62.5Zn15Mg17.5Cu5 ribbons were prepared using the single-roller melt-spinning technique.
High-pressure PDF
Total synchrotron x-ray scattering data of the Yb62.5Zn15Mg17.5Cu5 metallic glass were collected at the sector 11-ID-B beamline at the Advanced Photon Source, Argonne National Laboratory with the incident beam size 150 μm × 150 μm and an 86.7 keV high energy. A 2D large amorphous-silicon-based flat-panel detector was used to record the synchrotron x-ray scattering patterns. The sample with width of 150 μm, length of 150 μm and thickness of 20 μm was located in the sample chamber which is T301 stainless steel gasket with 270 μm diameter hole between two anvils of diamond anvil cell (DAC). 1:4 methanol/ethanol and ruby are as pressure medium and marker, respectively. The pressure was up to 38.4 GPa and measured by the ruby fluorescence method with error bars of 0.1~0.2 GPa.
Raw image data were processed using software Fit-2D27 with masking strategy28 to remove the diamond peaks to obtain one-dimensional scattering data. Subtracting the contributions from the sample environment and background, the reduced pair distribution function G(r) and structure factor S(Q) were extracted using the program PDFgetX229, which carries out a numerical Fourier transform of S(Q) according to
High-pressure resistivity measurements
In situ electrical resistance was measured by a four-probe resistance system in a DAC. An aluminum oxide (Al2O3)/epoxy mixture powder layer was inserted between the T301 stainless steel gasket and diamond anvil to provide electrical insulation for the electrodes and gasket. Four electrodes made of platinum foil with a thickness of 10 μm were arranged to contact the sample in the chamber. The pressure was determined by a ruby and up to 40.9 GPa. The resistance was calculated from the Van de Pauw method30.
Additional Information
How to cite this article: Li, L. et al. Polyamorphism in Yb-based metallic glass induced by pressure. Sci. Rep. 7, 46762; doi: 10.1038/srep46762 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Vink, R. L. C. & Barkema, G. T. Configurational entropy of network-forming materials. Phys. Rev. Lett. 89, 076405 (2002).
Mishima, O., Calvert, L. D. & Whalley, E. An apparently first-order transition between two amorphous phases of ice induced by pressure. Nature 314, 76–78 (1985).
Meade, C. R., Hemley, J. & Mao, H. K. High-pressure x-ray diffraction of SiO2 glass. Phys. Rev. Lett. 69, 1387–1390 (1992).
McMillan, P. F., Wilson, M., Daisenberger, D. & Machon, D. A density-driven phase transition between semiconducting and metallic polyamorphs of silicon. Nature Mater. 4, 680–684 (2005).
Sheng, H. W. et al. Polyamorphism in a metallic glass. Nature Mater. 6, 192–197 (2007).
Zeng, Q. S. et al. Origin of pressure-induced polyamorphism in Ce75Al25 metallic glass. Phys. Rev. Lett. 104, 105702 (2010).
Ramesh, T. G., Shubha, V. & Ramaseshan, S. Phase transitions in ytterbium under pressure. J. Phys. F: Metal Phys. 7, 981–990 (1977).
Zhao, Y. C., Porsch, F. & Holzapfel, W. B. Irregularities of ytterbium under high pressure. Phys. Rev. B 49, 815–817 (1994).
Chatterjee, A., Singh, A. K., Jayaraman, A. & Bucher, E. Pressure-induced 4f–5d electron collapse in ytterbium Monotelluride. Phys. Rev. Lett. 27, 1571–1573 (1971).
Jayaraman, A., Singh, A. K., Chatterjee, A. & Devi, S. U. Pressure-volume relationship and pressure-induced electronic and structural transformations in Eu and Yb monochalcogenides. Phys. Rev. B 9, 2513–2520 (1974).
Zeng, Q. et al. Universal fractional noncubic power law for density of metallic glasses. Phys. Rev. Lett. 112, 185502 (2014).
Zeng, Q. et al. General 2.5 power law of metallic glasses. Proc. Natl. Acad. Sci. 113, 1714–1718 (2016).
Chen, D. Z. et al. Fractal atomic-level percolation in metallic glasses. Science 349, 1306–1310 (2015).
Birch, F., Finite strain isotherm and velocities for single-crystal and polycrystalline NaCl at high pressures and 300 K. J. Geophys. Res. 83, 1257–1268 (1978).
Chatterjee, A., Singh, A. K. & Jayaraman, A. Pressure-induced electronic collapse and structural changes in rare-earth monochalcogenides. Phys. Rev. B 6, 2285–2291 (1972).
Wendt, H. R. & Abraham, F. F. Empirical criterion for the glass transition region based on Monte Carlo simulations. Phys. Rev. Lett. 41, 1244–1246 (1978).
Liu, R. S., Qi, D. W. & Wang, S. Subpeaks of structure factors for rapidly quenched metals. Phys. Rev. B 45, 451–453 (1992).
Sheng, H. W., Ma, E., Liu, H. Z. & Wen, J. Pressure tunes atomic packing in metallic glass. Appl. Phys. Lett. 88, 171906 (2006).
Lee, G. W. et al. Difference in icosahedral short-range order in early and late transition metal liquids. Phys. Rev. Lett. 93, 037802 (2004).
Kelton, K. F. et al. First x-ray scattering studies on electrostatically levitated metallic liquids: Demonstrated influence of local icosahedral order on the nucleation barrier. Phys. Rev. Lett. 90, 195504 (2003).
Syassen, K., Wortmann, G., Feldhaus, J., Frank, K. H. & Kaindl, G. Mean valence of Yb metal in the pressure range 0 to 340 kbar. Phys. Rev. B 26, 4745–4748 (1982).
Ziman, J. M. A theory of the electrical properties of liquid metals. I: The monovalent metals. Philos. Mag. 6, 1013–1034 (1961).
Hafner, J. Resistivity of liquid, supercooled liquid and amorphous alloys under elevated pressure. J. Non. Cryst. Solids 69, 325–345 (1985).
Fritsch, G., Dyckhoff, W., Pollich, W. & Lüscher, E. Dependence on pressure and temperature of the electrical resistivity of the amorphous alloys: Co80P20 and Pd80Si20 . J. Phys. F: Met. Phys. 15, 1537–1545 (1985).
Fritsch, G., Willer, J., Wildermuth, A. & Lüscher, E. Pressure dependence of the electrical resistivity of some metallic glasses. J. Phys. F: Met. Phys. 12, 2965–2974 (1982).
Cheung, J. & Ashcroft, N. W. Resistivity of liquid metals under elevated pressure. Phys. Rev. B 18, 559–568 (1978).
Hammersley, A. P. FIT2D: a multi-purpose data reduction, analysis and visualization program. J. Appl. Cryst. 49, 646–652 (2016).
Chapman, K. W. et al. Optimizing high-pressure pair distribution function measurements in diamond anvil cells. J. Appl. Cryst. 43, 297–307 (2010).
Qiu, X. J., Thompson, W. & Billinge, S. J. L. PDFgetX2: a GUI-driven program to obtain the pair distribution function from X-ray powder diffraction data. J. Appl. Cryst. 37, 678 (2004).
van der Pauw, L. J. A method of measuring specific resistivity and Hall Effect of discs of arbitrary shape. Philips Res. Rep. 13, 1–9 (1958).
Acknowledgements
This work was performed at Argonne National Laboratory and use of the Advanced Photon Source were supported by the US Department of Energy, Office of Science, Office of Basic Energy Sciences, under contract No. DE-AC02-06CH11357. This work was partially supported by Natural Science Foundation of China (U1530402, 11374075, 51371127), Heilongjiang Province Science Fund for Distinguished Young Scholars (JC201005), Heilongjiang Natural Science Foundation (E200948), Longjiang Scholar, the Fundamental Research Funds for the Central Universities (HIT. BRET1.2010002, HIT. IBRSEM.A.201403), HIT-Argonne Overseas Collaborative Base Project, and Chinese Scholarship Council.
Author information
Authors and Affiliations
Contributions
H.L., L.L. and R.L. designed all research work; K.C. and P.C. designed PDF work; L.L. and R.L. performed experiments and analyzed data; Q.L. prepared the sample; L.L., Q.L., R.L., H.Z., K.C., P.C., L.W. and H.L. drafted and revised the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, L., Luo, Q., Li, R. et al. Polyamorphism in Yb-based metallic glass induced by pressure. Sci Rep 7, 46762 (2017). https://doi.org/10.1038/srep46762
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep46762
This article is cited by
-
Breakdown of One-to-One Correspondence in Energy and Volume in a High-Pressure Heat-Treated Zr-Based Metallic Glass During Annealing
Scientific Reports (2020)
-
Unveiling a new type of ultradense anomalous metallic glass with improved strength and ductility through a high-pressure heat treatment
NPG Asia Materials (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.