Abstract
We synthesized orthorhombic FeB-type MnB (space group: Pnma) with high pressure and high temperature method. MnB is a promising soft magnetic material, which is ferromagnetic with Curie temperature as high as 546.3 K, and high magnetization value up to 155.5 emu/g, and comparatively low coercive field. The strong room temperature ferromagnetic properties stem from the positive exchange-correlation between manganese atoms and the large number of unpaired Mn 3d electrons. The asymptotic Vickers hardness (AVH) is 15.7 GPa which is far higher than that of traditional ferromagnetic materials. The high hardness is ascribed to the zigzag boron chains running through manganese lattice, as unraveled by X-ray photoelectron spectroscopy result and first principle calculations. This exploration opens a new class of materials with the integration of superior mechanical properties, lower cost, electrical conductivity, and fantastic soft magnetic properties which will be significant for scientific research and industrial application as advanced structural and functional materials.
Similar content being viewed by others
Introduction
Ever-growing demanded advanced magnetic materials for application in designing power electronic components, magnetic recording, magnetic refrigeration as well as spin-electronic have recently been investigated both from scientific and technological aspects1,2,3,4. Nowadays, the rapid development of micro-electromechanical systems (MEMS) devices, magnetic read, magnetic sensor, high speed motors, magnetic springs have given fresh impetus to reinforce mechanical property of ferromagnetic materials, such as high hardness, low compressible ability and ductile ability5,6,7,8,9. However, most of ferromagnetic materials (FM) are metal alloys, magnetic ion oxides, rare-earth transition metal (R-T) intermetallic compounds which are dominated by the metallic bonds or ionic bonds, a bond feature that is unfavorable to resist shear strain and compress. The relatively low hardness, typically below the value of 5 GPa, of traditional magnetic materials inevitably impede the application of traditional magnetic materials in harsh conditions9,10,11,12,13,14. To strengthen the mechanical properties of ferromagnetic materials, fabricating composite, ageing process, doping and controlling microstructure have been attempted to enhance mechanical properties7,8,9,15,16,17. However, the mechanical properties of ferromagnetic materials still fall far short the requirements of industrial applications18. Furthermore, for massive and industrial scale production, the earth abundant resources are most attractive due to high cost of rare-earth metals. Therefore, low cost mono-phase materials, combined the high temperature ferromagnetic with fantastic mechanical properties, are attractive for multifunctional application19.
Due to the strong covalent bonds between metalloid atoms and bonds between transition metal (TM) atoms and metalloid atoms, transition metal metalloid compounds typically present outstanding mechanical properties20,21,22,23. Manganese borides were one of the most promising transition metal (TM) borides because of their high hardness, low compressibility, high melting point, high electric conducting, wear resistance, thermal conduction and even room temperature magnetic properties24,25,26,27. Furthermore, from a more technological point of view, it is noteworthy that their INVAR behavior and high glass forming ability (GFA) to form bulk glass materials (BGMs) may be more useful in industrial applications6,28,29. However, lower boron contents generally contribute to relatively soft mechanical properties and the higher boron content manganese borides basically exhibit weak paramagnetic behavior. Consequently, the proper boron content and suitable crystal structure may facilitate ferromagnetic properties and outstanding mechanical property. Synthesis of orthorhombic MnB was first reported by Kiessing in 195030. Due to the proper boron contents, MnB was reported to have high Curie temperature, Tc, among transition metal borides (TMBs). Although FeB-type MnB possess outstanding ferromagnetic property, the magnetic parameters as well as the origin of strong ferromagnetic are still lacking in the literature31. This is probably because the magnetic exchange correlation between manganese atoms is complex and the intricate nature of chemical bonds. Thus, to instruct future material design, it is necessary to explore the relationship between the electron configuration and its physical property.
In this letter, to seek superior mechanical ferromagnetic materials, polycrystalline manganese mono-boride has been successfully synthesized at high pressure and high temperature (HPHT). MnB exhibits high Curie temperature, high saturated magnetization and low coercive field. Furthermore, the mechanical property, Vickers hardness (Hv), is enhanced by introducing strong covalent boron bonds. The combined mechanical, room temperature ferromagnetic, electrical conductivity and chemical inertness make this material promising candidates for engineering and technological applications.
Experiments
Pure manganese powder (99.95% in purity) and amorphous boron powder (99.5% in purity) with a ratio of 1:1 was ground together with an agate mortar and pestle until a uniform raw mixture achieved. The raw mixture was pressed into a pellet with 4 mm in diameter and 2.5 mm in height by means of hydraulic pressing. Hexagonal BN capsule was used as an insulate material to prevent the raw material reacting with carbon heater placed in the pyrophyllite cube. The synthesis experiments were carried out on SPD6 × 600 T cubic anvil apparatus with target pressure 5.0 GPa, temperature 1600 K to 2200 K and duration time of 15 min to 60 min. Finally the sample temperature was rapidly quenched to room temperature by switching off power supply and then decompressed to ambient pressure (AP). Powder X-ray diffraction (XRD) of the as-synthesized powder was performed with angle-dispersive mode at the beamline 16-BMD of the Advanced Photon Source (APS) Argone National Laboratory. GSAS program suite was used to perform Rietveld refinement32. The microstructure and the chemical compositions was observed by the scanning electron microscopy (SEM, JSM-6480LV) and the chemical composition were detected by the energy dispersive spectroscopy (EDS). The density of the specimens was measured by Archimedes methods with MDY-2 densimeter at room temperature (RT). The electrical resistivity was investigated with Van Der Pauw method. Temperature dependent dc magnetization susceptibility (χdc) curves of polycrystalline MnB from 5 K to 800 K were measured by Quantum Design MPMS 3 (superconducting quantum interference device, SQUID) with magnetic field of 500 Oe. To investigate the magnetic structure transition temperature of manganese mono-boride, differential scanning calorimetry (DSC) measurements from room temperature (RT) to 800 K were conducted utilizing a Rigaku TG-DTA 8120 system. Powder samples were heated up to 800 K at a rate of 5 K/min and soaked at the temperature of 800 K for 5 min under argon atmosphere. Then, the temperature was air cooled to the room temperature at the rate of 5 K/min. X-ray photoelectron spectrum (XPS) measurements were conducted with an X-ray source equipped with an Mg anode in an ultra-high vacuum chamber at a base pressure of 10−10 mbar.
First principles calculations were conducted with Vienna ab initio simulation package (VASP), based on density functional theory (DFT) using projector augmented waves (PAW) method33. The Perdew-Burke-Ernzerhof (PBE) version of generalized gradient approximation (GGA) was used for determining the exchange and correlation energy34. For more reliable convergent test, a cutoff energy of 500 eV and Monkhorst-Pack k mesh of 0.03 × 2 πÅ−1 were utilized to ensure that the total energies are well converged to better than 1 meV/formula units (f.u.). The Mulliken populations were obtained by density functional plane wave technique implemented in the CASTEP code and the ultrasoft Vanderbilt pseudopotentials (USPP) with PBE-GGA was chosen33,35,36.
Results and Discussions
Figure 1(a) displays the X-ray diffraction (XRD) pattern of the pure product synthesized at 5.0 GPa, 1600 K with a holding time of 60 min. X-ray diffraction pattern denotes that the as-synthesized specimen is highly crystalline and no lines of impurities were detected. Rietveld refinements discover that MnB adopts an orthorhombic Pnma (no. 62) structure, isotropic with FeB with lattice parameters a = 5.6377 Å, b = 2.9945 Å, c = 4.1795 Å. The refined crystal structure of FeB-type MnB is compiled in the Table 1. Rietveld refinements results and the later EDS measurements reveal that the obtained specimen does contain some manganese defects. Figure 1(b) shows the crystal structure of FeB-type MnB. There is one B and one Mn atom in nonequivalent atomic Wyckoff sites of Mn (4c) and B (4c). The boron atoms have the [BMn6B2] coordination polyhedral. It is worthy to be noted that the inter-atomic distances of B-B bonds in the zigzag chains is 1.7966 Å with bonds angle of 111.9° forming zigzag chains (ZC) and six manganese atoms at different distance form triangular prism. The zigzag B-B bonds length is slightly larger than the sum of covalent atomic radius, 1.68 Å, while the Mn-B bonds is 2.18 Å far shorter than the sum of atomic radius of manganese and boron (2.45 Å)37.
To investigate the morphology of synthesized specimen, the fracture surface of specimen was observed by scanning electron microscope (SEM). As can be seen in the SEM examinations, Fig. 2, that the product synthesized by HPHT is highly crystalline exhibiting an equilibrated microstructure with homogeneous grains size of about 30 μm. EDS was utilized to verify the chemical composition and the element purity of the synthesized specimen. The EDS result reveals that the synthesized specimen is chemically non-stoichiometric Mn0.95B signifying that there are some manganese defects. The density of polycrystalline pellets is 6.21 g/cm3 which are 96.2% of the theoretical density. High relative density ensures that the measurement of hardness is the intrinsic property of polycrystalline specimen38. Besides, it is worthy to note that the low density of MnB, but with high hardness, can be beneficial for the applications where light material is an asset. The electrical resistivity of MnB is measured to be 1.22 × 10−7Ω m, which is comparable to most of metal alloys39.
Successful synthesis of the well-crystalline polycrystalline MnB specimen allows us to investigate their magnetic properties. The magnetic property of the synthesized FeB-type MnB was investigated by magnetic properties measurement system (MPMS). Figure 3(a) shows the temperature dependence of magnetization in the zero field cooled (ZFC) and field cooled (FC) process with an applied magnetic field of 500 Oe from the temperature of 5 K to 800 K for polycrystalline MnB specimen. From the temperature dependent magnetization curve, it is obvious that the magnetization decreases drastically at the Curie temperature, 546.3 K. High Curie temperature manifests the presence of strong ferromagnetic (FM) interaction between manganese atoms. This Curie temperature is about 30 K lower than FeB-type MnB synthesized by arc melted method31. Futhermore, there is an abnormal transition of magnetic susceptibility at the temperature of 431 K and it is tentatively defined as the changing of easy magnetization axis. This abnormal transition has been confirmed to be its intrinsic property by different specimens and instruments measurements. Above the temperature of 500 K, the reciprocal susceptibility versus temperature is shown in the inset of Fig. 3(a). By fitting the reciprocal magnetic susceptibility (χ) plotted against temperature (T) with Curie-Weiss law, Eg. 1,
the Weiss constant, θ, can be confirmed to be 550.1 K with the Curie constant (C) of 1.15 × 10−5 emu·K·mol−1. Using equation, μeff = 2.83C1/2, and the obtained Curie constant suggests a magnetic moment near 2.71μB.
The Curie temperature measured by Zhu et al. is nearly 30 K higher than our results31. Consequently, it is more reliable to confirm the Curie temperature by another method. Ferromagnetic (FM) structure transform to paramagnetic (PM) is usually accompanied with an exothermic or endothermic peak. To confirm Tc, the differential scanning calorimetry (DSC) data of FeB-type MnB were presented in the Fig. 3(b) for 23.77 mg FeB-type MnB powder sample. There is an obvious exothermic peak at 550.9 K in the heating procedure and an endothermic peak at 552.7 K in the cooling procedure. The temperature of exothermic and endothermic peak is consistent with the Curie temperature determined by the temperature dependent magnetization curve. According to the previous reports, Curie temperature is strongly dependent on the mean diameter of grain size and the applied magnetic field40. So, the Curie temperature of MnB can be safely confirmed to be 546.3 K for the HPHT synthesized specimens when the applied magnetic field is 500 Oe.
Among the six manganese borides, Mn2B is non-magnetic, MnB2 and Mn3B4 exhibits anti-ferromagnetic behavior and MnB4 possesses paramagnetic property24,25,26,27. The absence of ferromagnetic spin order of other manganese borides is attributed to the insufficient interaction between the manganese atoms to stabilize the ferromagnetic spin order. The ferromagnetic spin order of MnB is the result of partially filled Mn valence 3d-orbital electrons, Mn-Mn exchange correlations as well as any other electronic factors41. Based on the Bethe-Slater curve, the exchange interaction is negative for the manganese metal31. In the synthesis of manganese mono-boride, boron atoms are incorporated into the matrix of manganese lattice, which expands the distances between manganese atoms. Consequently, based on the empirical Bathe-Slater curve, the negative exchange-correlation integral of antiferromagnetic α-Mn metal becomes positive. According to the Stoner model, spontaneous magnetization appears when the condition NTM × ITM > 1 is satisfied, where NTM is the non-polarized partial density of states at Fermi energy level and ITM is the exchange-correlation integral between manganese atoms41. The exchange correlation integral between manganese atoms is 0.41 eV calculated by Janak42. Besides, the density of states (DOS), shown in Fig. 4(a), is about 4.1 states/eV/f.u. which is slightly larger than the value of Park et al.43. Based on the positive exchange correlation integral and high density of states at the Fermi level, FeB-type meets the Stoner model which ensures the spontaneous magnetization.
The magnetic properties were further measured by magnetic hysteresis measurements, which were measured with the field swept from −20 KOe to 20 kOe. The hysteresis loops at 5 K and 400 K were measured and the results are shown in the Fig. 4(b). The saturated magnetization at 5 K is about 155.5 emu/g and there is hardly any hysteretic behavior. To exclude the possibility of super-paramagnetic (SPM), the hysteresis of MnB at 5 K and 400 K was fitted by Langevin equation and the results rule out the possibility of SPM44. The origin of the small coercive field may come from high relative density of the specimen and the large crystal grain size. The obtained saturation magnetization 155.5 emu/g at 5 K is higher than the value 124 emu/g obtained by Zhu et al. Because there is an obvious impurity diffraction peak at about 42 degree, higher saturated magnetization may stem from the higher sample purity than that the specimen synthesized by arc melted31. According to the saturated magnetization at 5 K, the manganese atoms in FeB-type MnB carries a magnetic moment 1.83 μB/f.u. which is consistent with our DFT calculation result of 1.87μB and 1.91μB by Kervan et al.27.
Magnetic properties of other TMBs have been investigated by previous research and the experimental results are tabulated in Table 2. Besides FeB and CoB, few TMBs are reported to be room temperature (RT) ferromagnetic45,46. The most strikingly feature of MnB is higher magnetization and lower coercive field with respect to other FM transition metal borides (TMBs). Compared with other TMBs, the saturated magnetization of MnB is nearly twice of FeB and triple of CoB. Furthermore, even compared with the widely used strong soft ferromagnetic materials, such as Fe3O4, NiMnIn, and CoFeO4, FeB-type MnB has a higher saturated magnetization, Ms, and lower coercive field, Hc. Those outstanding magnetic features may endow MnB promising soft room temperature ferromagnetic materials. It is not surprising that MnB has a higher magnetization. The electron configuration of manganese atoms is Mn-[Ar]3d54s2 which indicate that manganese atoms possess the largest number of unpaired spin electrons. Therefore, in the mono-borides, the Mn ions carries magnetic moment of 1.83 μB and Fe ions and ions Co carries smaller 1.12 μB and 0.28 μB, respectively. In addition, compared with traditional ferromagnetic materials, MnB has a comparable high Curie temperature which is suitable to use in the high temperature conditions. Owing to the high GFA of TMBs to form BMGs, BMGs MnB may exhibit more superior soft ferromagnetic materials in the future6,28,29.
Due to the exact nature of the bond in ferromagnetic crystals, a major challenge hindering the application of magnetic materials is the relatively soft mechanical properties and chemical instability9,10,11,12,13,14. Considering that the boron chains have been successfully incorporated into the lattice of manganese metals, the mechanical properties of manganese mono-boride may be higher than that of traditional ferromagnetic materials. So, after cutting and polishing, micro-indentation experiments were performed on the polished specimen surface at different applied load between 0.245 N and 4.9 N for MnB. Vickers micro-hardness (Hv) of MnB was calculated according to the following equation E.g. 2,
where P is the applied load (in N), d is the arithmetic mean of the two diagonals of the indentation (in micrometers) at a given applied load, Hv is the Vickers micro-hardness. The load dependent Vickers micro-hardness data for MnB are shown in the Fig. 5. It is clear that there is an inverse relationship between the applied load and Vickers micro-hardness. MnB has an asymptotic Vickers hardness of 15.7 GPa at 4.9 N and a maximum Vickers hardness of 29.6 GPa at 0.245 N. As shown in the Table 2, the AVH of MnB is far higher than traditional ferromagnetic materials. With those results, it denotes that the Vickers hardness of manganese metal has been drastically enhanced by incorporating zigzag boron chains into manganese atoms matrix. Other than benefits of ferromagnetic property, superior mechanical properties will bring it potential candidate to replace other conventional ferromagnetic materials in harsh application conditions.
Generally, the hardness and magnetic property are especially sensitive to the electron configuration. Hardness prefers high bond density, high electronic density as well as strong covalent bonds framework, while the metallic bonds and ionic bonds are detrimental to hardness47. For the lack of convincing experimental evidences about bonds characteristics in TMBs, many incompatible models have been proposed to illuminate the physical properties48,49,50,51,52. To further design mechanically hard ferromagnetic materials in the future, it is necessary to investigate the chemical bonds feature and electron configurations. One of the most promising methods to explore the bond characteristic of TMBs would be X-ray photoelectron spectrum (XPS) combined with first principle calculations. Figure 6(a) shows the B-1s spectrum with the binding energy from 184.0 eV to 196.0 eV and (b) shows the Mn-2p of MnB with the binding energy from 634.0 eV to 656.0 eV. B-1s core level spectrum as shown in Fig. 6(a) has a tiny component and two major distinct components. The weak peak at 191.3 eV would be assigned to the surface defects. As to the BE at 187.7 eV, it can be assigned to the B-B bonds in zigzag boron chains, while the BE at 188.1 eV may belong to Mn-B interactions which is compatible with other TMBs53. The shorter bond lengths combined with marginally binding energy (BE) shift compared with boron elementary substance manifest boron bond covalent feature. De-convolution of the two distinct unsymmetrical peaks of Mn 2p suggests the presence of three chemically distinct manganese states. There is a pair of peaks located at the binding energy of 638.6 eV, 649.8 eV and another two pairs of peaks located at the binding energy (BE) of 639.2 eV, 651.0 eV and 640.6 eV, 651.7 eV. The binding energy of Mn 2p3/2 and Mn 2p1/2 in manganese metal and manganese alloy is close to 638.6 eV and 649.8 eV, such as Al56Mn8Pd36 and Al70Mn9Pd2154,55. The compatible binding energy with manganese metal and manganese alloy suggests that the bonds between manganese atoms are metallic bonds. While the pair of peaks at 639.2 eV, 651.0 eV is higher than pure manganese metals and alloys. This higher BE suggest the hybridizations between manganese 3d orbitals and boron 2p orbitals which has been demonstrated by density of states in Fig. 4(a). Another pair of small peaks at the BE of 640.6 eV, 651.7 eV can be tentatively assigned to the manganese defects in the crystal structure or caused by HPHT.
One observes in the Fig. 4(a) that Mn-3d orbitals and B-2p orbitals form some hybridization, which contributes to the covalent component of Mn-B bonds. Futhermore, the atomic average Mulliken charge are 0.62 and −0.62 for B and Mn which is compatible with XPS results. This fact denotes that there is some ionic component between Mn-B bonds. In addition, the calculated Mulliken overlap population of Mn-B bonds is 0.24 and it also suggests that there is some ionic component in Mn-B bonds. XPS experiment results suggest that B-B bond is of strong covalent character. Compared with the Mulliken population of C-C bonds in diamond (0.75) and graphite (1.03), the B-B bonds Mulliken population, 1.52, is high which imply its strong covalent feature56.
Considering the above electron configuration of MnB, a possible model for bond feature in MnB is given as follows: there are covalent zigzag boron chains, ionic and covalent interaction between manganese and boron atoms, metallic interaction between manganese atoms in MnB crystal. Therefore, the superior mechanical properties of ferromagnetic FeB-type MnB are mainly attributed to the zigzag boron chains running through the manganese matrix. Knowledge concerning the chemical state of elements in MnB is of great value to unravel the relation between chemical bonds characteristics and its mechanical properties. Besides, the theories to design hard materials can be utilized in the synthesizing of mechanically hard ferromagnetic materials in the future.
Conclusions
We present a controlled HPHT method to synthesize polycrystalline MnB, which demonstrate its feasibility of synthesizing high density and well crystalline functional bulk materials. Due to the proper boron content, the exchange correlation between manganese atoms is positive which ensures the spontaneous magnetization. The synthesized specimen exhibits high saturated magnetization, high Curie temperature, low coercive field and outstanding mechanical properties. XPS results demonstrate that introducing the covalent zigzag boron chains brings superior mechanical properties. The integration of fantastic ferromagnetic properties with mechanical properties opens a new class of materials utilized in the areas where strong ferromagnetic and high mechanical strength is highly desired.
Additional Information
How to cite this article: Ma, S. et al. Manganese mono-boride, an inexpensive room temperature ferromagnetic hard material. Sci. Rep. 7, 43759; doi: 10.1038/srep43759 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Hosseini-Nasab, F., Tavakoli, M. M., Beitollahi, A. & Moravvej-Farshi, M. K. Kinetics of crystallization in FeB based nanocrystalline soft magnetic alloys. J. Magn. Magn. Mater. 407, 13–16 (2016).
Gschneidner, Jr K. A. & Pecharsky, V. K. Tunable magnetic regenerator alloys with a giant magnetocaloric effect for magnetic refrigeration from ~20 to ~290 K. Appl. Phys. Lett. 70, 3299–3301 (1997).
Matsumoto, Y. et al. Room-temperature ferromagnetism in transparent transition metal-doped titanium dioxide. Science 291, 854–856 (2001).
Sevel’ev, S., Rakhmanov, A. L. & Nori, F. Domain-wall step motors: Controlling the motion of magnetic domain walls using patterned magnetic films. Phys. Rev. B. 74, 204404 (2006).
Yavari, A. R. et al. FeNiB-based metallic glasses with fcc crystallisation products. J. Non-Cryst. Solids 304, 44–50 (2002).
Wang, J. et al. Ternary Fe–P–C bulk metallic glass with good soft-magnetic and mechanical properties. Scr. Mater. 65, 536–539 (2011).
Gao, Z. et al. Martensitic transformation and mechanical properties in an aged Ni–Mn–Ga–Ti ferromagnetic shape memory alloy. J. Alloys Compd. 481, 44–47 (2009).
Gao, L., Cai, W., Liu, A. & Zhao, L. Martensitic transformation and mechanical properties of polycrystalline Ni50Mn29Ga21−xGdx ferromagnetic shape memory alloys. J. Alloys Compd. 425, 314–317 (2006).
Tripathi, M. K., Singh, V. B. & Singh, H. K. Structure and properties of electrodeposited functional Ni–Fe/TiN nanocomposite coatings. Surf. Coat. Technol. 278, 146–156 (2015).
Gao, L., Cai, W., Liu, A. & Zhao, L. Martensitic transformation and mechanical properties of polycrystalline Ni50Mn29Ga21−xGdx ferromagnetic shape memory alloys. J. Alloys Compd. 425, 314–317 (2006).
Mitra, S. ; Veluri, P. S. ; Chakraborthy, A. & Petla, R. K. Electrochemical properties of spinel cobalt ferrite nanoparticles with sodium alginate as interactive binder. ChemElectroChem 1, 1068–1074 (2014).
Akkera, H. S., Singh, I. & Kaur, D. Martensitic phase transformation of magnetron sputtered nanostructured Ni-Mn-In ferromagnetic shape memory alloy thin films. J. Alloys Compd. 642, 53–62 (2015).
Kilinc, B. et al. Wear behavior of the surface alloyed AISI 1020 steel with Fe-Nb-B by TIG welding technique. AIP Conference Proceedings 1653, 020058 (2015).
Streckova, M. et al. A comparison of soft magnetic composites designed from different ferromagnetic powders and phenolic resins. Chin. J. Chem. Eng. 23, 736–743 (2015).
Dong, G. et al. The effect of ageing on the microstructure and mechanical properties of Ni53Mn23.5Ga18.5Ti5 ferromagnetic shape memory alloy. Scr. Mater. 59, 268–271 (2008).
Cai, W. et al. Martensitic transformation and mechanical properties of Ni–Mn–Ga–Y ferromagnetic shape memory alloys. Scr. Mater. 57, 659–662 (2007).
Yu, X. et al. High pressure phase-transformation induced texture evolution and strengthening in zirconium metal: experiment and modeling. Sci. Rep. 5, 12552 (2015).
Ju, J. et al. Microstructure and mechanical properties change by rare earth Dy added in as-cast Co–Ni–Al ferromagnetic shape memory alloys. Mater. Sci. Eng., A 616, 196–200 (2014).
Makino, A., Chang, C., Kubota, T. & Inoue, A. Soft magnetic Fe–Si–B–P–C bulk metallic glasses without any glass-forming metal elements. J. Alloys Compd. 483, 616–619 (2009).
Mohammadi, R. et al. Tungsten tetraboride, an inexpensive superhard material. Proc. Natl. Acad. Sci. USA. 108, 10598–10962 (2011).
Gilman, J. J., Cumberland, R. W. & Kaner, R. B. Design of hard crystals. Int. J. Refract. Met. Hard Mater 24, 1–5 (2006).
Kaner, R. B., Gillman, J. J. & Tolbert, S. H. Designing superhard materials. Science 308, 1268–1269 (2005).
Han, L. et al. Hardness, elastic, and electronic properties of chromium monoboride. Appl. Phys. Lett. 106, 221902 (2015).
Niu, H. et al. Variable-composition structural optimization and experimental verification of MnB3 and MnB4 . Phys. Chem. Chem. Phys. 16, 15866–15873 (2014).
Knappschneider, A. et al. Peierls-distorted monoclinic MnB4 with a Mn-Mn bond. Angew. Chem. Int. Ed. 53, 1684–1688 (2014).
Wang, B., Li, X., Wang, Y. & Tu, Y. Phase stability and physical properties of manganese borides: A first-principles study. J. Phys. Chem. C 115, 21429–21435 (2011).
Kervan, S. Magnetic properties of the MnB boride by density functional theory. J. Supercond. Novel Magn. 24, 815–818 (2011).
Mohn, P. & Pettifor, D. G. The calculated electronic and structural properties of the transition-metal monoborides. J. Phys. C: Solid State Phys. 21, 2829–2839 (1988).
Makino, A. et al. The effect of Cu on the plasticity of Fe–Si–B–P-based bulk metallic glass. Scr. Mater. 60, 277–280 (2009).
Kiessling, R. The borides of manganese. Acta Chem. Scand. 4, 146–159 (1950).
Zhu, H. et al. Fabrication and magnetic property of MnB alloy. J. Appl. Phys. 97, 10M512 (2005).
Larson, A. C. & Von Dreele, R. B. GSAS., LANSCE, MS-H805, Los Alamos National Laboratory, Los Alamos, NM 87545, LAUR 86-748, Vers. (2000).
Kresse, G. & Futhmüller, J. Effecient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B: Condens. Matter. 54, 11169–11186 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Segall, M. D. et al. First-principles simulation: ideas, illustrations and the CASTEP code. J. Phys.: Condens. Matter 14, 2717–2744 (2002).
Segall, M. D., Shah, R., Pickard, C. J. & Payne, M. C. Population analysis of plane-wave electronic structure calculations of bulk materials. Phys. Rev. B: Condens. Matter. 54, 16317–16320 (1996).
Gou, H. et al. Stability of MnB2 with AlB2-type structure revealed by first-principles calculations and experiments. Appl. Phys. Lett. 102, 061906 (2013).
Stevens, R. & Luo, J. Porosity-dependence of elastic moduli and hardness of 3Y-TZP ceramics. J. Ceram. Int. 25, 281–286 (1999).
Levine, J. B. et al. Preparation and properties of metallic, superhard rhenium diboride crystals. J. Am. Chem. Soc. 130, 16953–16958 (2008).
Wang, J., Wu, W., Zhao, F. & Zhao, G. Curie temperature reduction in SiO2 coated ultrafine Fe3O4 nanoparticles: Quantitative agreement with a finite-size scaling law. Appl. Phys. Lett. 98, 083107 (2011).
Bourourou, Y. et al. Structure and magnetic properties of the 3d transition-metal mono-borides TM–B (TM = Mn, Fe, Co) under pressures. J. Magn. Magn. Mater. 365, 23–30 (2014).
Janak, J. F. Uniform susceptibilities of metallic elements. Phys. Rev. B 16, 255–262 (1977).
Park, J. et al. Electronic structures of MnB soft magnet. AIP Adv. 6, 055911 (2016).
Kim, D. K. et al. Synthesis and characterization of surfactant-coated super-paramagnetic monodispersed iron oxide nanoparticles. J. Magn. Magn. Mater. 225, 30–36 (2001).
Rades, S., Kraemer, S., Seshadri, R. & Albert, B. Size and crystallinity dependence of magnetism in nanoscale iron boride, α-FeB. Chem. Mater. 26, 1549–1552 (2014).
Ge, J. et al. Superparamagnetic magnetite colloidal nanocrystal clusters. Angew. Chem. Int. Ed. 46, 4342–4345 (2007).
Gao, F. et al. Hardness of covalent crystals. Phys. Rev. Lett. 91, 015502 (2003).
Ihara, H., Hirabayashi, M. & Nakagawa, H. Band structure and x-ray photoelectron spectrum of ZrB2 . Phys. Rev. B 16, 726–730 (1997).
Silver, A. H. & Bray, P. J. NMR study of bonding in some solid boron compounds. J. Chem. Phys. 32, 288 (1960).
Dempsey, E. Bonding in the refractory hard-metals. Philos. Mag. 8, 285–299 (1963).
Tyan, Y. S., Toth, L. E. & Chang, Y. A. Low temperature specific heat study of the electron transfer theory in refractory metal borides. J. Phys. Chem. Solids. 30, 785–792 (1969).
Juretschke, H. J. & Steinitz, R. Hall effect and electrical conductivity of transition-metal diborides. J. Phys. Chem. Solids. 4, 118–127 (1958).
Shi, L. et al. Low-temperature synthesis of nanocrystalline vanadium diboride, Materials Letters. Mater. Lett. 58, 2890–2892 (2004).
Jenks, C. J. et al. Photoelectron spectra of an Al70Pd21Mn9 quasicrystal and the cubic alloy Al60Pd25Mn15 . Phys. Rev. B 54, 6301–6306 (1996).
Myers, C. E., Franzen, H. F. & Anderegg, J. W. X-ray photoelectron spectra and bonding in transition-Metal phosphides. Inorg. Chem. 24, 1822–1824 (1985).
Wang, M. et al. Origin of hardness in WB4 and its implications for ReB4, TaB4, MoB4, TcB4, and OsB4. Appl. Phys. Lett. 93, 101905 (2008).
Lundquist, N., Myers, H. P. & Westin, R. The paramagnetic properties of the monoborides of V, Cr, Mn, Fe, Co and Ni. Philos. Mag. 7, 1187–1195 (1962).
Miyamoto, T. et al. Influence of annealing conditions on magnetic properties of Ni50Mn50−xInx heusler-type alloys. Mater. Trans. 52, 1836–1839 (2011).
Kudryavtsev, Y. V., Lee, Y. P. & Rhee, J. Y. Dependence of the optical and magneto-optical properties and electronic structures on the atomic order in Ni2MnIn Heusler alloys. Phys. Rev. B 69, 195104 (2004).
Legarra, E., Apiñaniz, E., Jimenez, J. A. & Pierna, A. R. Al versus Si competition in FeSiAl alloys. J. Magn. Magn. Mater. 320, e688–e691 (2008).
Ghazali, M. J., Wahab, M. N., Daud, A. R. & Ghani, J. A. Effect of aged AlN reinforced Al-Si alloys on dry sliding wear behaviour. Advanced Materials Research, 126–128, 905–910 (2010).
Bachelet, R. et al. Flat epitaxial ferromagnetic CoFe2O4 films on buffered Si(001). Thin Solid Films, 519, 5726–5729 (2011).
Joy, P. A. & Date, S. K. Effect of sample shape on the zero-field-cooled magnetization behavior: comparative studies on NiFe2O4, CoFe2O4 and SrFe12O19 . J. Magn. Magn. Mater. 222, 33–38 (2000).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Nos 51632002, 51572108, 11634004), Program for Changjiang Scholars and Innovative Research Team in University (No. IRT_15R23), National Found for Fostering Talents of basic Science (No. J1103202). The authors would like to express their thanks to Pro. Runwei Li and Zhenxiang Cheng for discussion.
Author information
Authors and Affiliations
Contributions
T.C. initiated the project. T.C. and P.Z. designed this work. S.M., K.B., Q.T., P.Z. analyzed the data and wrote this manuscript. S.M., Q.T. conducted the high pressure synthesis, hardness measurements, and XPS measurements. Y.L. performed SEM measurements. T.M., B.L. conducted the magnetic properties measurements.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Ma, S., Bao, K., Tao, Q. et al. Manganese mono-boride, an inexpensive room temperature ferromagnetic hard material. Sci Rep 7, 43759 (2017). https://doi.org/10.1038/srep43759
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep43759
This article is cited by
-
Improving the ferromagnetic exchange coupling in hard τ-Mn53.3Al45.0C1.7 and soft Mn50B50 magnetic alloys
Applied Physics A (2020)
-
Superconductivity in two-dimensional ferromagnetic MnB
Scientific Reports (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.