Abstract
The structural, electronic, and optical properties of β-Ga2O3 with oxygen vacancies are studied by employing first-principles calculations based on density function theory. Based on the defects formation energies, we conclude the oxygen vacancies are most stable in their fully charge states. The electronic structures and optical properties of β-Ga2O3 are calculated by Generalized Gradient Approximation + U formalisms with the Hubbard U parameters set 7.0 eV and 8.5 eV for Ga and O ions, respectively. The calculated bandgap is 4.92 eV, which is consistent with the experimental value. The static real dielectric constants of the defective structures are increased compared with the intrinsic one, which is attributed to the level caused by the Ga-4s states in the bandgap. Extra peaks are introduced in the absorption spectra, which are related to Ga-4s and O-2p states. Experimentally, β-Ga2O3 films are deposited under different O2 volume percentage with ratio-frequency magnetron sputtering method. The measured results indicate that oxygen vacancies can induce extra emission peaks in the photoluminescence spectrum, the location of these peaks are close to the calculated results. Extra O2 can increase the formation energies of oxygen vacancies and thus reduce oxygen vacancies in β-Ga2O3.
Similar content being viewed by others
Introduction
Among the transparent conducting oxides (TCOs), monoclinic β-Ga2O3 is a promising semiconductor with bandgap of 4.9 eV, excellent chemical and thermal stability has gained considerable attention for many applications1,2. It has been widely used as photocatalyst, solar-blind UV detectors, gas sensors, and short wavelength light emitting diodes3,4,5,6,7. Besides, it is a promising candidate for power devices as higher Baliga’s figures of merit (over 3000) and higher breakdown field (8 MV/cm), a lower cost and more easily accessible properties compared with the conventional power semiconductors such as SiC and GaN8,9,10,11. However, like the traditional TCOs such as ZnO, pure β-Ga2O3 usually presents an n-type characteristic, and a p-type doped β-Ga2O3 is hard to get, which hampers its further applications. As an intrinsic defect, oxygen vacancy are usually supposed to be the reason of the n-type property of the intrinsic TCOs. While some theoretical calculation results suggest that the oxygen vacancies act as deep donors in β-Ga2O3, which make this issue controversial12,13,14. In various manufacture procedures of β-Ga2O3, oxygen vacancies can be widely introduced. The ambient conditions, especially the oxygen pressure and post-annealed atmosphere are directly related with the concentration of oxygen vacancies. Oxygen vacancies can introduce extra peaks in the bandgap of β-Ga2O3, which can affect the efficiency and accuracy of the optical devices such as solar-blind UV detectors. However, taking advantage of the oxygen vacancies, amorphous Ga2O3 has been used as a resistance random access memory (RRAM)15,16,17. Thus, the oxygen vacancies have a significant impact on the application of β-Ga2O3.
Recently, first-principles calculations based on density functional theory (DFT) have been used for many studies of the material properties such as optics, magnetism and electronic structures18,19,20,21. The theoretical calculation can give a deep insight of the material, which can help us get further acquainted with the material itself. The formation energy of the oxygen vacancies of β-Ga2O3 has been investigated in the past years, and the results can vary with different functionals and approximation methods12,13,14. Up to now, few studies of the effects on the structural and optical properties caused by oxygen vacancies have been discussed systematically. Moreover, the electronic structures of β-Ga2O3 with oxygen vacancies have not been reported. While in the application of β-Ga2O3, the oxygen vacancies can have a great influence on the performance of the devices. Thus, it is necessary to detailedly discuss the oxygen vacancies of β-Ga2O3.
It is well known that the electronic structures of semiconductors are not well described by generalized gradient approximation (GGA) and local-density approximation (LDA) functionals, which will lead to an underestimation of bandgap in semiconductors22,23,24,25. As a result, the defects states caused by the defects are not correctly treated. The accurate electronic structures can be described by more elaborate approaches, such as hybrid Hartree-Fock (HF) density functionals, Heyd-Scuseria-Ernzerhof (HSE) and the screened exchange (sX)14,26. However, these accurate methods are limited to the computational resources.
In this paper, first-principles based on all-electron DFT is used to study the atomic structures, formation energies, electronic structures and optical properties of the intrinsic β-Ga2O3 with different oxygen vacancies. In order to get a reasonable result, the GGA+U approach is used, which is computational frugally compared with other hybrid density functionals and also can give an accurate description by controlling the Hubbard U parameter27,28.
Results and Discussion
Structural properties
Monoclinic structural β-Ga2O3 with C2/m symmetry can be described with four lattice parameters, i.e, a, b, c and β. Figure 1(a) shows the optimized conventional cell of β-Ga2O3. The structural parameters of β-Ga2O3 based on our calculation results and other previous theoretical with experimental results are listed in Table 1. The calculation results are in good agreement with other results derived from different functionals, which indicate our optimization method is reasonable.
There are three types of O sites in β-Ga2O3 cell as shown in Fig. 1(a). As a result, three O vacancies exist, which are denoted as VOI, VOII (both are 3-fold) and VOIII (4-fold), respectively. For VOI, there are two 6-fold Ga ions and one 4-fold Ga ion surrounded, while two 4-fold Ga ions and one 6-fold Ga ion are adjacent to VOII. For Ga ions, there are two nonequivalent sites, the 4-fold one and 6-fold one, respectively. The crystalline structures are described in terms of GaO6 octahedron and GaO4 tetrahedron chains. Based on the former optimized cell, we calculate the defective structures with the 1 × 2 × 2 supercell shown in Fig. 1(b).
Defects formation energies
The formation energy of an oxygen vacancy D in β-Ga2O3 with charge state q is given by30:
Where is the total energy of the supercell with an oxygen vacancy D in charge state q, is the total energy of the β-Ga2O3 perfect supercell structure. μO is the chemical potential of O which we use the potential of O2 molecule as a reference, nO denotes the numbers of the vacancies in the supercell. εF is the Fermi level measured from the top of the valence band EVBM and ΔV is the average potential difference between the defective supercell and the perfect one.
From Eq. (1), the formation energy of an oxygen vacancy in charge state q can be determined. In this method, the chemical environment difference between the different finite defective supercells, which leads to the errors in the formation energy, are taken into account. Besides, EVBM varies with the different O vacancies and charge states, which can lead to unreasonable formation energies results. Therefore, it is necessary to align the band structures of the different supercells31. EVBM of the defective supercells is defined by30:
Where is the total energy of neutral perfect supercell and is the total energy of the perfect supercell in charge state q.
The O defects formation energy is associated with oxygen condition in the synthesis process of β-Ga2O3, and the oxygen chemical potential varies with the different ambient atmospheres. Both μO and are confined by the phase equilibrium condition of β-Ga2O3. The range of μO is between the oxygen poor (, where is the total energies per atom of molecular O2) and oxygen rich (, where denotes the formation energy of β-Ga2O3. is derived from , where is the total energy per atom of metallic Ga).
and are obtained by separate calculations of total energies of metallic Ga with orthorhombic structure and molecular O2, respectively. For O2, an isolated O2 molecule is placed in a cubic cell with the dimension of 15 × 15 × 15 Å. In this case, only the Γ-point is used. The O-O bond length is 1.24 Å, which is in good agreement with experiment value32. For the potential of Ga, an orthorhombic structure is used. The formation energy of β-Ga2O3 in our calculation results is 3.19 eV per O atom.
The formation energies for different O vacancies with different charge states as a function of the Fermi energy are obtained by the GGA+U method, and the results are shown in Fig. 2. Both oxygen-rich and oxygen-poor cases are calculated. For each defect, only the charge state in the most energetically favorable at a given Fermi energy is shown. The defects formation energies vary with the Fermi level εF. When εF is close to valence band, the stable charge states correspond to , and , respectively. With the εF moving up, the neutral defects are dominant. There are no +1 charge state of oxygen vacancies, which indicates that +1 charge state is not stable for all three type vacancies. The followed discussion we will focus only on these stable structures, namely, neutral and +2 charge states.
Thermodynamic transitions between the different charge states of the same defect are denoted by the kinks as shown in Fig. 2, which are derived from the formation energies. Measured from the valence band maximum (VBM), the ε(+2/0) transition level of , and are 3.2 eV, 3.7 eV and 3.9 eV, respectively. The deep transition levels mean all the oxygen vacancies act as deep donors. When Fermi level εF locates at the mid-gap around, the charged vacancies are more stable than the neutral ones. Under oxygen-poor atmosphere, the negative oxygen vacancies formation energy make the vacancies easy to form. While in the case of oxygen-rich, the positive formation energy of neutral oxygen vacancies is higher than the ones under oxygen-poor atmosphere. As a result, it is hard to generate a high concentration of oxygen vacancies under this atmosphere. These results indicate the oxygen vacancies are hard to be effective n-type donors, and under oxygen-poor atmosphere, the high compensation effects between oxygen vacancies and p-type acceptor impurity may be the reason of the difficulty to get a well performance p-type β-Ga2O3. Our conclusions are consistent with other previous theoretical studies13,14.
Electronic structures
The calculated band structure and densities of states (DOS) of the intrinsic β-Ga2O3 under GGA+U approximation are shown in Fig. 3(a,b). The bandgap of β-Ga2O3 in our calculation result is about 4.92 eV and both the VBM and the conduction band minimum (CBM) are situated at the G point, which means the material belongs to the direct bandgap semiconductor. These calculated results are nearly consistent with the results in previous experiment2. To illustrate the effects of the Hubbard U, the band structure of β-Ga2O3 under GGA approximation is also shown in Fig. 3(c). The bandgap of β-Ga2O3 under GGA approximation is only 1.98 eV, which is far deviated from the value of experimental result. The band structure of β-Ga2O3 shows a much flat valence band, indicating a large hole effective mass and leading to the low mobility of hole, which hamper the fabrication of p-type β-Ga2O3. From the DOS results, the valence band of the intrinsic β-Ga2O3 is composed of three subbands. The upper subband consists mainly of O 2p states with a width of about 7.8 eV. The middle subband is formed mainly by Ga 3d states at about 10.5 eV below the VBM. The lowest one consists mainly of O 2 s along with Ga 3d states and locates at 14.8 eV below the VBM. These bandgap, VB and CB features of β-Ga2O3 are consistent with previous theoretical results, which indicate our GGA+U method is valid18.
When an oxygen ion is removed, a defective β-Ga2O3 model with oxygen vacancy is created. For the neutral oxygen vacancies (, and ), a defective level occupied by two electrons appears, which are shown in Fig. 4. The total energy of the defective β-Ga2O3 is lowered by the attraction of the surrounded Ga ions, and these ions sites distortion leave the defects level set at the middle of the bandgap. When the vacancies carry with two positive charges (, and ), the results are very different from the neutral ones. The defects levels are unoccupied, the outward of surrounded Ga ions make the Ga-O bond strengthen, leading to the decrease of the formation energy. As a result, the defective level moves to the conduction band. These results are similar with the band structures of other defective oxides such as ZnO and Al2O330,33.
Figure 5 presents the total density of states (TDOS) of β-Ga2O3 with various oxygen vacancies, and detailed partial density of states (PDOS) results induced by the defects are shown inset. Compared with the TDOS of the intrinsic β-Ga2O3, new peaks arise in the bandgap. For , with the VBM chosen as the reference, the DOS peak of is 2.77 eV away from the VBM. Based on the PDOS of the Ga ions and O ions shown in Fig. 5(a,b), the unpaired hanging bond of Ga ions around the vacancies make the most contributions to these defective peaks. The DOS of defects almost come from Ga-4s and Ga-4p states along with a few O-2p states. In the presence of shown in Fig. 2(a), it is found that Ga1 and Ga3 ions move 0.21 Å toward the vacancy, while Ga2 slightly move about 0.16 Å away from the oxygen vacancy, which is shown in Fig. 6(a). The movement of the Ga ions can be attributed to the ionic size and crystalline structure. When two electrons move away, the defects level caused by the charged oxygen vacancies move toward the conduction band, the interaction caused by the overlap between the defects level and the conduction bottom level make the conduction band bottom shift down, as shown in Fig. 4(d). The attractive interactions between Ga ions and O vacancy disappear. There will be considerate space left in the vacancy site, which will give the adjacent Ga ions more freedom to disperse. For both equivalent tetrahedral structure Ga1 and Ga3 ions, the space makes them move toward to vacancy after the relaxation. While for Ga2 ion, Ga2 ion is not electrostatically attracted by the vacancy anymore, the closer Ga1 and Ga3 ions product more electrostatically repulsion to Ga2 ion, these effects leave Ga3 ions move away. However, compared with Ga1 and Ga3 ions, Ga2 ion with an octahedral structure has seven bonds connected to neighboring oxygen ions, which make Ga2 ion more geometrically stable.
Similar to , the band structures and DOS of and shown in Figs 4 and 5, respectively. Extra levels emerge in the band structures, with the VBM chosen as the reference, the DOS peak of and is 3.10 eV and 3.40 eV away from the VBM, respectively. The structural relaxations of the supercell models with and are also calculated, and the variation between the defect and surrounding ions after relaxation are listed in Table 2. Detailed atomic structures relaxations shown in Fig. 6(b,c). It is noted that the 4-fold connected there octahedron and one tetrahedron, which makes the more geometrically stable. As a result, when induced, the variation of adjacent Ga ions are less, the three equivalent 6-fold Ga ions move less away from the , more relaxation is applied to 4-fold Ga1 ion, the result is Ga1 ion is attracted to the vacancy 0.33 Å closer.
Optical properties
As a promising material for optoelectronic devices, a deep understanding of optical properties of β-Ga2O3 is very necessary. To investigate the optical properties of β-Ga2O3 with oxygen vacancies, the complex dielectric function is calculated. The imaginary part of complex dielectric function ε2(ω) is calculated by summing the transitions between occupied and unoccupied electronic states, which is relevant to the electronic band structure that can determine other optical properties of the material. The imaginary part is given by the following equation34:
Where e is the electron charge, m is the mass of free electrons, ω is the frequency of incident photons, M is the dipole matrix, i and j are the initial and final states, respectively. fi is the fermi distribution function for i-th state with wave function vector k. According to the Kramers-Kronig transformation, the real part ε1 can derived from the imaginary ε2, which is given as follows:
Where P denotes the principal value of the integral. The other optical properties such as absorption coefficient α(ω), reflectivity R(ω), refractive index n(ω), extinction coefficient k(ω), and energy-loss L(ω) can be derived from the dielectric function and defined by35:
Figure 7(a,b) display the real and imaginary parts of the dielectric function ε(ω) of β-Ga2O3 with different oxygen vacancies, respectively. For the pure β-Ga2O3, from a general view, our calculation dielectric function ε(ω) are consistent with previous studies in tendency. It is noted that the peak for the imaginary part dielectric function at 8.7 eV is much stronger than other peaks, which is related to the interband transition between O 2p and Ga 4 s states. Taking the oxygen vacancies into consideration, new peaks (3.17eV, 3.37eV and 3.69 eV for , and , respectively) arise in the low energy region, while the effect is barely noticeable in ultraviolet region. From the electronic structures and DOS results, we concluded that these peaks are caused by the transition from Ga-4s states in the defective level induced by oxygen vacancies to the Ga-4s states in the conduction band. The difference locations among these peaks are consistent with the defective levels in the band structures from our previous calculated results.
The static dielectric constant ε1(0) is given by the low energy limit of ε1(∞). The calculated ε1(0) of pure β-Ga2O3 is 1.36, which is smaller than the experiment results. The underestimation of ε1(0) is due to the low number of conduction bands and overlook of phonon contribution. When oxygen vacancies induced in the β-Ga2O3, all the values of ε1(0) increase, the ε1(0) for β-Ga2O3 with , and are 1.52, 1.46 and 1.64, respectively, which are attributed to the extra levels in the bandgap of β-Ga2O3 caused by oxygen vacancies.
The absorption spectra of all the β-Ga2O3 systems are illustrated in Fig. 7(c). The incident radiation has linear polarization along the (100) direction. The intrinsic absorption edge of β-Ga2O3 is consistent with the bandgap (4.9 eV) with the urgently decreases absorption edge, which means β-Ga2O3 is a promising optical material at DUV region. The intrinsic absorption is related with the interband electron transition between O-2p states in the VBM and Ga-4s states in the CBM. Compared with pure β-Ga2O3, the absorption coefficient of the structures with oxygen vacancies increase in visible and infrared region while decrease in the deep violet region. New absorption peaks appear at 3.80 eV, 3.52 eV and 3.37 eV for, and, respectively. According our first-principles calculation results, a schematic diagram of the possible absorption processes of oxygen vacancies in β-Ga2O3 is illustrated in Fig. 8. The intrinsic absorption process is the electron transition from O-2p states in the VBM and Ga-4s states in the CBM. The additional absorption parts are deduced from the electron transition between the defective level caused by oxygen vacancies and the valence band.
The reflectivity, and refractive index are depicted in Fig. 7(d,e). For β-Ga2O3 with oxygen vacancies, the reflectivity and refractive index enhance in the low energy region, which is contributed to the defective levels in the bandgap induced by the oxygen vacancies. The location of reflectivity and refractive index peaks are consistent with the dielectric function. The energy loss function describes the energy lost by an electron passing from a homogeneous dielectric material. It has the advantage of covering the complete energy range, including non-scattered and elastically scattered electrons (zero loss), which excite the electrons of atom’s outer shell (valence loss) or valence inter-band transitions. In Fig. 7(f), the energy loss peaks caused by oxygen vacancies locates at 3.96eV, 3.45eV and 3.58 eV for, and, respectively. These peaks are corresponding to where the reflectivity decrease rapidly.
XRD and photoluminescence spectra results
To explore the effects of oxygen vacancies on the structural and optical properties of β-Ga2O3, β-Ga2O3 films were deposited under different O2 volume percentage. Figure 9 presents the XRD results of the films deposited under 0% and 1% O2 volume percentage, respectively. Through XRD patterns, both films exhibit β-Ga2O3 structure. The average crystalline sizes in β-Ga2O3 films were estimated from the (400) peak by using the Scherrer’s equation, D = kλ/(B × cosθ), where k is Scherrer’s constant with a value of 0.89, λ is the wavelength of the X-ray radiation, B is the FWHM of (400) peak, and θ is the angle of the diffraction peak. The calculated crystalline sizes for the films deposited under 0% and 1% O2 volume percentage are 20.15 nm and 22.45 nm, respectively. Room-temperature photoluminescence (PL) spectra of the β-Ga2O3 films excited with 325 nm laser are shown in Fig. 10. The fitting curve of the film deposited under 1% O2 volume percentage is shown in the inset figure. The emission band can be divided into four Gaussian bands centered at about 380 nm, 416 nm, 442 nm and 464 nm, respectively. The emission peak centers at 380 is in the UV region, this peak is concerned with the transition levels between the oxygen vacancy and unintended N impurities introduced in the N2 annealed36. While for the peaks center at 416 nm, 442 nm (both in the violet region) and 464 nm (blue region), these three emission peaks are originated from the electron-hole recombination formed by oxygen vacancies, or to the recombination of Ga-O vacancy pair37,38.
From our previous calculated results, extra oxygen gas induced in the procedure of deposition can increase the formation energy of oxygen vacancies. The higher formation energy can reduce the concentration of oxygen vacancies. From the PL results, the emission peaks related to oxygen vacancies of the film deposited under 1% O2 volume percentage is higher than that deposited under 0%. According to our first-principles calculation results, the peaks center at 416 nm and 442 nm are most related with , and , while the peak at 464 nm is most attributed to . When irradiated with high energy photon, the electron at defective levels caused by oxygen vacancies can absorb the photon and then jump to the levels in the valance band consists of O-2p states or the defective level caused by Ga vacancies, with more photons release in this procedure.
In summary, we have investigated the structural, electronic and optical properties of defected β-Ga2O3 with oxygen vacancies by employing first-principles calculations based on density function theory. The relaxed lattice parameters are in consistent with the experiment and previous theoretical results. The variation in defective structures caused by the O vacancies is discussed systematically. To revise the error calculated under the Generalized Gradient Approximation, the electronic structures, and optical properties of β-Ga2O3 are calculated by GGA+U method. Our calculated bandgap result (4.92 eV) is in good agreement with the previous experiment results. The formation energies of the oxygen vacancies and transition levels between different charge states are calculated, the results indicate that +2 charge states are most stable state while +1 charge states are not stable for all three type O vacancies, the +2/0 transition level location implying O vacancy is a deep donor. When the ambient atmosphere becomes oxygen poor, the oxygen vacancies are easier to form. The electronic structures show the oxygen vacancies can introduce deep levels around the Fermi level, detailed PDOS of the defects level are described. The static real dielectric constants of the defective structures increase compared with the intrinsic one, which is attributed to the level caused by the Ga-4s states in the bandgap. New absorption peaks appear at 3.80 eV, 3.52 eV and 3.37 eV for, and, respectively. The additional absorption parts are deduced from the electron transition between the defective level caused by oxygen vacancies and the valence band. The absorption intensity is increasing in visible and infrared region but decreasing in the deep violet region. Besides, β-Ga2O3 films are deposited under different O2 volume percentage with ratio frequency magnetron sputtering method. The measured results indicate that oxygen vacancies can induce extra emission peaks in the photoluminescence spectrum of β-Ga2O3, the location of these peaks is close to our calculated results. Extra O2 can increase the formation energies of oxygen vacancies and reduce oxygen vacancies in β-Ga2O3. These results are consistent with first-principles calculations results.
Methods
All calculations were based on the density functional theory with Cambridge Serial Total Energy Package (CASTEP) code39. The exchange-correlation potential was described with the Perdew-Burke-Ernzerhof (PBE) functional under the Generalized Gradient Approximation (GGA) exchange-correlation functional40. The ultrasoft pseudopotential method was used for the interactions between the electrons and ions. The atomic configuration of Ga was [Ar] 3d10, and the 3d10 electrons were considered as valence electrons, while the atomic configuration of O is [He] 2s22p4, the 2s2 and 2p4 electrons were treated as valence electrons. Before the electronic and optical calculations, structural relaxation was employed. The lattice parameters and internal coordinates were relaxed with Broyden-Fletcher-Goldfarb-Shanno (BFGS) optimization method41. The energy tolerance, the tolerance of the force, maximum stress and maximum displacement were 5 × 10−6 eV/atom, 0.01 eV/Å, 0.02 Gpa and 5 × 10−4 Å, respectively. The cutoff energy for the plane wave basis set was 450 eV, and a Monkhorst-Pack 2 × 8 × 4 k-points was used for integrations of the Reduced Brillouin zone42. For the defective crystal, a 1 × 2 × 2 supercell of β-Ga2O3 based on the optimized cell with 80 atoms was created to act as the computational model, which is presented in Fig.1 (b). The lattice constants of the defective supercell were fixed, only the internal coordinates can be relaxed.
For the calculations of formation energies, electronic structures and optical properties, the GGA+U method was adopted. After series tests, the Ud value for Ga-3d and Up value for O-2p were set at 7.0 eV and 8.5 eV, respectively. Under this correction, the reasonable results can be obtained. All of our calculations are carried out at the theoretical equilibrium lattice constants, which is essential in order to avoid the spurious effects in the process of relaxation.
β-Ga2O3 films were prepared on sapphire substrates (0001) by the radio-frequency magnetron sputtering method with a high-purity Ga2O3 target (99.995% purity, 50.8 mm diameter). The distance between the target and substrate was about 150 mm, and the output of the ratio source was 60 W. To explore the oxygen vacancies on the properties of β-Ga2O3 films, several experiments were conducted by varying the oxygen concentration in the growth chamber. Before the deposition, the chamber was pumped down to 5 × 10−6 mTorr as the base pressure. The films were deposited under 5 mTorr atmosphere pressure at room temperature. To exclude any interference caused by the variation of film thickness, the thickness of both films were kept between 220 to 250 nm. To improve the crystalline properties, the as-deposited Ga2O3 sample was subsequently annealed at 1000 °C for 60 min. Pure N2 was chosen as the annealing atmosphere to avoid any effects of caused by extra oxygen. The oxygen volume percentage was varied by changing the gas volume percentage of oxygen to argon gas introduced into the growth chamber. To investigate the crystalline structures of the films, 2θ scan were conducted using an X-ray diffractometer (SHIMADZU XRD-7000), with Cu Kα radiation (λ = 0.154056 nm). The Photoluminescence (PL) spectra were measured under the excitation by a He-Cd UV laser (325 nm and 20 mW).
Additional Information
How to cite this article: Dong, L. et al. Effects of oxygen vacancies on the structural and optical properties of β-Ga2O3. Sci. Rep. 7, 40160; doi: 10.1038/srep40160 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
M. Orita, H. Ohta, M. Hirano & H. Hosono Deep-ultraviolet transparent conductive beta-Ga2O3 thin films. Appl Phys Lett 77, 4166 (2000).
S. Kumar, C. Tessarek, G. Sarau, S. Christiansen & R. Singh Self‐Catalytic Growth of β‐Ga2O3 Nanostructures by Chemical Vapor Deposition. Adv Eng Mater 17, 709–715 (2015).
E. G. Víllora, S. Arjoca, K. Shimamura, D. Inomata & K. Aoki In SPIE OPTO. (International Society for Optics and Photonics), pp. 89871U-89871U–89812 (2014).
S. Q. Jin et al. Effect of Phase Junction Structure on the Photocatalytic Performance in Overall Water Splitting: Ga2O3 Photocatalyst as an Example. J Phys Chem C 119, 18221–18228 (2015).
R. Suzuki, S. Nakagomi, Y. Kokubun, N. Arai & S. Ohira Enhancement of responsivity in solar-blind β-Ga2O3 photodiodes with a Au Schottky contact fabricated on single crystal substrates by annealing. Appl. Phys. Lett 94, 222102–222101 (2009).
X. Chen et al. Self-Powered Solar-Blind Photodetector with Fast Response Based on Au/beta-Ga2O3 Nanowires Array Film Schottky Junction. ACS Appl Mater Interfaces 8, 4185–4191 (2016).
M. Ogita, K. Higo, Y. Nakanishi & Y. Hatanaka Ga2O3 thin film for oxygen sensor at high temperature. Appl Surf Sci 175, 721–725 (2001).
K. Matsuzaki et al. Field-induced current modulation in epitaxial film of deep-ultraviolet transparent oxide semiconductor Ga2O3 . Appl Phys Lett 88 (2006).
M. Higashiwaki et al. Depletion-mode Ga2O3 metal-oxide-semiconductor field-effect transistors on β-Ga2O3 (010) substrates and temperature dependence of their device characteristics. Appl Phys Lett 103, 123511 (2013).
M. Higashiwaki, K. Sasaki, A. Kuramata, T. Masui & S. Yamakoshi, Development of gallium oxide power devices. physica status solidi (a) 211, 21–26 (2014).
M. Higashiwaki, K. Sasaki, A. Kuramata, T. Masui & S. Yamakoshi, Gallium oxide (Ga2O3) metal-semiconductor field-effect transistors on single-crystal beta-Ga2O3 (010) substrates. Appl Phys Lett 100 (2012).
Z. Hajnal et al. Role of oxygen vacancy defect states in the n-type conduction of beta-Ga2O3 . J Appl Phys 86, 3792–3796 (1999).
T. Zacherle, P. C. Schmidt & M. Martin Ab initio calculations on the defect structure of beta-Ga2O3 . Phys Rev B 87 (2013).
J. B. Varley, J. R. Weber, A. Janotti & C. G. Van de Walle Oxygen vacancies and donor impurities in beta-Ga2O3 . Appl Phys Lett 97 (2010).
D. Y. Guo et al. Abnormal bipolar resistive switching behavior in a Pt/GaO1.3/Pt structure. Appl Phys Lett 107, 032104 (2015).
C. W. Hsu & L. J. Chou Bipolar resistive switching of single gold-in-Ga2O3 nanowire. Nano Lett 12, 4247–4253 (2012).
D. Y. Lee & T. Y. Tseng Forming-free resistive switching behaviors in Cr-embedded Ga2O3 thin film memories. J Appl Phys 110 (2011).
H. Y. He et al. First-principles study of the structural, electronic, and optical properties of Ga2O3 in its monoclinic and hexagonal phases. Phys Rev B 74 (2006).
A. Di Trolio et al. The effect of Co doping on the conductive properties of ferromagnetic ZnxCo1−xO films. J. Mater. Chem. C 3, 10188–10194 (2015).
R. Zhou, B. Qu, B. Zhang, P. Li & X. C. Zeng Role of vacancies to p-type semiconducting properties of SiGe nanowires. J Mater Chem C 2, 6536 (2014).
Y. Wang et al. Zn vacancy induced ferromagnetism in K doped ZnO. J. Mater. Chem. C 3, 11953–11958 (2015).
J. P. Perdew & A. Zunger Self-interaction correction to density-functional approximations for many-electron systems. Phys Rev B 23, 5048 (1981).
D. M. Ceperley & B. Alder Ground state of the electron gas by a stochastic method. Phys Rev Lett 45, 566 (1980).
J. P. Perdew, S. Kurth, A. Zupan & P. Blaha Accurate density functional with correct formal properties: A step beyond the generalized gradient approximation. Phys Rev Lett 82, 2544 (1999).
P. Rinke, A. Janotti, M. Scheffler & C. G. Van de Walle Defect formation energies without the band-gap problem: combining density-functional theory and the GW approach for the silicon self-interstitial. Phys Rev Lett 102, 026402 (2009).
D. Liu, Y. Guo, L. Lin & J. Robertson First-principles calculations of the electronic structure and defects of Al2O3 . J Appl Phys 114, 083704 (2013).
A. Liechtenstein, V. Anisimov & J. Zaanen Density-functional theory and strong interactions: Orbital ordering in Mott-Hubbard insulators. Phys Rev B 52, R5467 (1995).
S. Dudarev, G. Botton, S. Savrasov, C. Humphreys & A. Sutton Electron-energy-loss spectra and the structural stability of nickel oxide: An LSDA+ U study. Phys Rev B 57, 1505 (1998).
S. Geller Crystal Structure of β‐Ga2O3 . The Journal of Chemical Physics 33, 676–684 (1960).
K. Matsunaga, T. Tanaka, T. Yamamoto & Y. Ikuhara First-principles calculations of intrinsic defects inAl2O3 . Phys Rev B 68 (2003).
T. Mattila & A. Zunger Deep electronic gap levels induced by isovalent P and As impurities in GaN. Phys Rev B 58, 1367 (1998).
G. Herzberg Forbidden Transitions in Diatomic Molecules: I. The Quadrupole Rotation-Vibration Spectrum of H2. Canadian Journal of Research 28, 144–152 (1950).
F. Oba, A. Togo, I. Tanaka, J. Paier & G. Kresse, Defect energetics in ZnO: A hybrid Hartree-Fock density functional study. Phys Rev B 77, 245202 (2008).
C. Chen et al. Nonlinear Optical Borate Crystals: Principals and Applications. (John Wiley & Sons, 2012).
L. Li et al. First principles calculations of electronic band structure and optical properties of Cr-doped ZnO. The Journal of Physical Chemistry C 113, 8460–8464 (2009).
L. Liu et al. Fabrication and characteristics of N-doped β-Ga2O3 nanowires. Applied Physics A 98, 831–835 (2010).
L. Binet & D. Gourier Origin of the blue luminescence of β-Ga2O3 . J Phys Chem Solids 59, 1241–1249 (1998).
K. W. Chang & J. J. Wu Low‐Temperature Growth of Well‐Aligned β‐Ga2O3 Nanowires from a Single‐Source Organometallic Precursor. Adv Mater 16, 545–549 (2004).
S. J. Clark et al. First principles methods using CASTEP. Zeitschrift für Kristallographie-Crystalline Materials 220, 567–570 (2005).
J. P. Perdew, K. Burke & M. Ernzerhof Generalized gradient approximation made simple. Phys Rev Lett 77, 3865 (1996).
B. G. Pfrommer, M. Côté, S. G. Louie & M. L. Cohen Relaxation of crystals with the quasi-Newton method. Journal of Computational Physics 131, 233–240 (1997).
H. J. Monkhorst & J. D. Pack Special points for Brillouin-zone integrations. Phys Rev B 13, 5188 (1976).
Acknowledgements
Authors would like to acknowledge that this work is supported by the National Natural Science Foundation of China (Grant No. 51272202 and No. 61234006).
Author information
Authors and Affiliations
Contributions
Y.Z. and R.J. designed this project. L.D. performed the thin film growths, the measurements, analysed the results, and wrote the original manuscript. L.D. and B.X performed the first-principles calculations, and analysed the calculated results. B.X. and B.P modified the manuscript. All authors discussed the results and worked on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Dong, L., Jia, R., Xin, B. et al. Effects of oxygen vacancies on the structural and optical properties of β-Ga2O3. Sci Rep 7, 40160 (2017). https://doi.org/10.1038/srep40160
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep40160
This article is cited by
-
State-of-art review on smart perovskites materials: properties and applications
Emergent Materials (2024)
-
Influence of Sm3+ doped β-Ga2O3 thin films on structural, optical, and photoluminescence properties
Journal of Materials Science: Materials in Electronics (2023)
-
Dielectric and structural properties of pure and Sn-mixed Ga2O3 compounds
Journal of Materials Science: Materials in Electronics (2023)
-
In-sensor reservoir computing system for latent fingerprint recognition with deep ultraviolet photo-synapses and memristor array
Nature Communications (2022)
-
Origin of the Band Gap Reduction of In-Doped β-Ga2O3
Journal of Electronic Materials (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.