Abstract
Many exotic physics anticipated in topological insulators require a gap to be opened for their topological surface states by breaking time reversal symmetry. The gap opening has been achieved by doping magnetic impurities, which however inevitably create extra carriers and disorder that undermine the electronic transport. In contrast, the proximity to a ferromagnetic/ferrimagnetic insulator may improve the device quality, thus promises a better way to open the gap while minimizing the side-effects. Here, we grow thin single-crystal Sb1.9Bi0.1Te3 micro flakes on insulating ferrimagnet BaFe12O19 by using the van der Waals epitaxy technique. The micro flakes show a negative magnetoresistance in weak perpendicular fields below 50 K, which can be quenched by increasing temperature. The signature implies the weak localization effect as its origin, which is absent in intrinsic topological insulators, unless a surface state gap is opened. The surface state gap is estimated to be 10 meV by using the theory of the gap-induced weak localization effect. These results indicate that the magnetic proximity effect may open the gap for the topological surface attached to BaM insulating ferrimagnet. This heterostructure may pave the way for the realization of new physical effects as well as the potential applications of spintronics devices.
Similar content being viewed by others
Introduction
A gap opened for the surface states by breaking time reversal symmetry in topological insulators is anticipated to host many novel physics1,2,3,4,5,6,7,8. Experimentally, the gap may be realized either by magnetic doping9,10,11,12,13,14,15, or by magnetic proximity to a ferromagnetic insulator16,17,18. One of the signatures of the gap openings is the weak localization effect19. The effect can give rise to positive low-field magnetoconductivity at low temperatures19,20,21,22. In contrast, for gapless surface states, a π Berry phase always leads to weak anti-localization and an associated negative magnetoconductivity23,24,25,26. However, in actual samples, the magnetic doping inevitably introduces magnetic scattering centers, defects, as well as magnetic clusters, which lead to mixed surface and bulk phases in magnetotransport27,28. As a result, it is hard to distinguish magnetically-doped topological insulators from diluted magnetic semiconductors20, in the latter the weak localization-like magnetoconductivity is also anticipated and not attributed to the gap of the surface states. Compared to the magnetic doping, the magnetic proximity effect may also induce a gap for the surface states of topological insulator. A higher Curie temperature magnetic order can be achieved in a heterostructure of topological insulator and ferromagnetic insulator if the Curie temperature of the ferromagnetic insulator is high enough29. Moreover, the topological insulator-ferromagnetic insulator heterostructure is expected to suppress external magnetic impurities and magnetic clusters; therefore, it may be a better experimental candidate to induce the gap for the topological surface states. A number of heterostructures have been studied29,30,31,32,33,34 with different ferromagntic insulator substrates, such as EuS30,31, yttrium iron garnet29,33, GdN32 and BaFe12O19 (BaM)34. In the experiments, only a suppressed weak antilocalization effect with a negative magnetoconductivity was achieved. The suppressed weak antilocalization cannot be unambiguously attributed to gap opening because random magnetic scattering can also induce the suppression of the weak antilocalization effect19,26. A negative magnetoresistance in low fields has been demonstrated in a Bi2Se3-EuS heterostructure with a Bi2Se3 layer thinner than 4 nm31. However, it is not sufficient to conclude that the magnetic proximity has indeed opened the gap since the finite-size effect can also open gaps in thin films35 and leads to the weak localization effect22. Very recently, a low-field positive magnetoconductivity was observed in a Bi2Se3-BaM heterostructure in parallel magnetic fields34, but the perpendicular magnetoconductivity remains negative. Domain walls may be the possible origins of the positive parallel-field magnetoconductivity in very weak parallel fields. Most heterostructures have been fabricated by the molecular beam epitaxy (MBE) method, and the size of these heterostructures is much larger than the magnetic domains of the ferrimagnetic insulator. Thus massive Dirac electrons would be expected in magnetic domain areas, but remain massless at the domain walls29. The domain walls may suppress conductivity28; then a positive magnetoconductivity arises as the magnetic field removes the domain walls.
In this work, we fabricated BaFe12O19-Sb1.9Bi0.1Te3 heterostructures by using the van der Waals epitaxial technique. The size of the topological insulator flakes can be controlled to be comparable with the magnetic domains of BaM. In perpendicular magnetic fields, a positive magnetoconductivity possibly associated with the weak localization effect is observed, indicating that the magnetic proximity has opened a gap for the surface state of topological insulator. The parallel-field magnetoconductivity shows a negative magnetoconductivity near zero field as the in-plane magnetization of BaM is not able to open the gap for the surface states. Using the magnetoconductivity formula for the competition between weak antilocalization and weak localization effects, we fitted the magnetoconductivity curves in perpendicular fields and found that the surface gap ∆ induced by the magnetic proximity is about 10 meV. Our results demonstrate that the magnetic proximity can break time-reversal symmetry and open a sizable gap for the surface states of topological insulator. This topological insulator-BaM heterostructure thus may pave the way for further experimental research on novel physics and potential applications of spintronics devices.
Results
Heterostructures of topological insulator and BaFe12O19
Hexagonal BaFe12O19 is a well-known ferrimagnetic insulator with a uniaxial anisotropy along the c crystallographic axis. The magnetic domain structure of a single-crystal BaM has been verified with positive and reversed magnetic domains along the c axis under different directions of magnetization. The size of the magnetic domains is about 5 μm. The domains exhibit labyrinth, stripe, honeycomb-type patterns as the magnetization field tilts from the c axis to the a-b plane36,37. We prepared the BaM single crystals by the floating zone method. We chose large and flat single crystals with a natural cleavage plane (0001) as the ferrimagnetic insulator substrate. Figure 1(a) shows the magnetization of the BaM substrate measured by the Magnetic Property Measurement System, where M is the magnetic moment, and MS is the saturation magnetic moment. The saturation magnetization field HS of BaM along the in-plane (perpendicular to the c axis) and out-of-plane directions are 1.5 T and 0.5 T, respectively. There is no obvious change of HS in both directions when the temperature increases from 2 K up to 50 K. Due to the free moving of domain walls in response to the variations of the external fields, no evident hysteresis is observed at low fields38.
The van der Waals epitaxy is a facile method to grow high-quality nanostructures on a clean surface of substrate irrespective of large lattice mismatch39,40. By this method, we successfully fabricated Sb1.9Bi0.1Te3-BaM heterostructures in a 1-inch horizontal tube furnace via the catalyst-free vapor-solid (v-s) growth technique similar to that in ref. 41. We choose the stoichiometric Sb1.9Bi0.1Te3, because it can effectively lift the position of the Dirac point out of the bulk valence band while tuning the Fermi level inside the bulk gap through charge compensation42. The inset of Fig. 1(b) presents the scanning electron microscope (SEM) image of the Sb1.9Bi0.1Te3 nanoplate on the BaM substrate. The warping edges of the nanoplate indicate the large lattice mismatch between Sb1.9Bi0.1Te3 and BaM. The white points on the Sb1.9Bi0.1Te3 nanoplate are redundant tellurium generated during the cooling. Figure 1(b) shows the R-T curves of both the heterostructure and BaM substrate. BaM is a ferrimagnetic insulator with high room temperature resistance. After the growth of the topological insulator on BaM, the resistance of BaM was reduced to 200 Ω at 300 K, revealing that the BaM becomes conductive after annealing for 1 hour near 300 °C. When the temperature decreased to 125 K, the resistance of BaM increased sharply. In contrast, the resistance of the heterostructure increased slowly with a decrease of temperature. For instance, at T = 100 K, the resistance of the BaM substrate reached above 2 × 106 Ω, which is 100 times larger than the resistance of the heterostructure. This high resistance indicates that when T < 100 K, the current mainly flows through the topological insulator film. Here, our temperature range of interest is below 55 K, at which the BaM substrate becomes a full insulator.
Magnetoconductivity and weak localization
We measured the magnetoconductivity of our samples by the standard four-probe transport measurement. Figure 2(a) shows the magnetoconductivity of the Sb1.9Bi0.1Te3-BaM heterostructure at different temperatures in perpendicular magnetic fields. We observed a positive magnetoconductivity (i.e., negative magnetoresistance) in the perpendicular field up to 7 T at low temperatures. The positive magnetoconductivity weakened as the temperature increased and finally the magnetoconductivity displayed mixed behavior from positive in low fields to negative in high fields when the temperature increased up to 50 K. In the perpendicular field, the classical magnetoconductivity arising from the Lorentz force always gives a negative magnetoconductivity (positive magnetoresistance). In the strong disorder regime, the transport can exhibit a negative magnetoresistance43, but it requires that the conductivity . While at 2 K, the conductivity in our heterostructures ranges between , not in the strong disorder regime. The positive magnetoconductivity here is most likely the consequence of the weak localization effect of the gapped surface states and, therefore, has a quantum interference origin19. As the temperature increased to T = 55 K, the magnetoconductivity became entirely negative. There is no obvious change in the magnetization of our BaM substrates near 50 K, so the observed sign change of the magnetoconductivity near 50 K is not due to the gap closing with vanishing magnetization, but possibly because the temperature quenched the quantum interference and then the classical magnetoconductivity became overwhelming. In order to conduct a comparative study, we also grew Sb1.9Bi0.1Te3 on a SiO2 substrate. As shown in Fig. 3(a), the perpendicular-field magnetoconductivity of Sb1.9Bi0.1Te3 on the SiO2 substrate exhibited a sharp cusp near zero field. The cusp is a typical signature of the weak antilocalization effect for the topological surface states due to their nature as massless Dirac fermions.
Magnetization induced surface state gap
Functionally, the magnetoconductivity of the weak antilocalization and weak localization effects can always be fitted by the Hikami-Larkin-Nagaoka (HLN) formula44,
where is the digamma function. The prefactor α and the phase coherence length serve as two fitting parameters. However, the information about the gap opening cannot be given by the HLN formula. To quantitatively study the gap opening in the surface states, we employed the magnetoconductivity formula derived for the weak antilocalization-localization crossover of the massive Dirac fermions19,
where the magnetic length, , and , , , are explicit functions (see Methods) of Δ/2EF, with Δ the gap of surface states and the Fermi level measured from the Dirac point. In the weak antilocalization limit, , , while in the weak localization limit, , . Equation (2) is valid when the mean free path is much shorter than the magnetic length (. We used formula (2) to fit the magnetoconductivity in perpendicular fields. The solid lines in Fig. 2(a) are the fitting curves by using equation (2). Figure 4(a) shows the fitting result of Δ/2EF as a function of temperature. At T = 2 K, Δ/2EF is about 0.329. With increasing temperature, Δ/2EF decreases. At T = 50 K, Δ/2EF = 0.304, changed by less than 10%. These values of Δ/2EF are in the regime between the unitary and orthogonal symmetry classes, where a suppressed weak localization effect can give rise to a positive magnetoconductivity19. In the earlier experiments45,46, the higher Fermi energies in topological insulators Bi2Se3 and Bi2Te3 may greatly reduce Δ/2EF, leading to only weak antilocalization-like magnetoconductivity according to the theory19.
In order to evaluate the surface gap, we used 2D carrier density derived from the Hall measurement to estimate the Fermi level. By measuring the Hall resistance of two similar devices on the SiO2 and BaM substrates, respectively, as shown in Fig.3 (b), we obtain that on SiO2 and on the BaM substrate. The values of the carrier density means that the Fermi energy is at the bottom of the bulk conduction band, which is about 0.1–0.2 eV from the Dirac point of the surface states, according to the ARPES data in ref.42. We estimate that the surface state gap induced by the magnetic proximity is of the order of
As shown in Fig. 4(b), with increasing temperature, the fitted phase coherence length is reduced by half, from 28 nm at 2 K to 14 nm at 50 K, showing a much stronger temperature dependence compared to that of Δ/2EF. Therefore, the fitting results indicate that the reduction of the phase coherence length is the main reason why the positive magnetoconductivity of weak localization is suppressed in Fig. 2.
Discussion
We also show the magnetoconductivity data in parallel fields in Fig. 2(b). The positive magnetoconductivity can still be recognized in the high-field range, but a deflection appears near 1.5 T and the magnetoconductivity becomes negative near the zero field, as shown in Fig. 2(b). The negative magnetoconductivity near the zero field indicates that there is no gap opening for the surface states in parallel magnetic fields. This absence of gap is because while applying the external magnetic field in the in-plane direction, the spin of BaM substrate will be rotated to the in-plane direction, and correspondingly, the surface state of topological insulator remains gapless. As the temperature goes up to 30 K, the deflection of the magnetoconductivity curves is weakened and disappears at 50 K. This deflection behavior has also been observed in magnetically doped topological insulators47 and undoped ultrathin topological insulator films22,48,49. In theory, if the magnetoconductivity curves exhibit a deflection, the magnetoconductivity are contributed by multiple channels and the bulk states might contribute to the transport besides the surface states50,51. In topological insulator ultrathin films, this can be well explained by the 2D modified Dirac model35, while in our heterostructure, the thickness of the topological insulator nanoflakes is about 20 nm, which is much thicker than the ultrathin limit (<5 nm). Besides, in the parallel fields, the observed deflection in magnetoconductivity happens at 1.5 T, at which the weak-field limit (usually within 0.5 T) for the weak antilocalization and weak localization effects has been violated. The observed magnetoconductivity in parallel fields cannot be explained by the competition between weak antilocalization and weak localization. The mechanism for the deflection in the parallel-field magnetoconductivity is not clear so far. One possible explanation is similar to that in ref.28, where domain walls suppress the conductivity while the magnetic field may remove the domain walls gradually, leading to the positive magnetoconductivity at high fields. The size of our heterostructure is comparable to the single magnetic domain in BaM, but the observed deflection cannot be explained by this mechanism. Another possible explanation is related to the canting of magnetization as discussed in refs.29,30. When the parallel field is larger than 1.5 T, the magnetization of BaM saturates in the in-plane direction. A canting of magnetization in the out-of-plane direction might form at the interface of our heterostructure due to strong spin-orbit coupling as well as a large anisotropy of the Lande g factor for the interface electrons29,30. The surface state gap might also be opened by the canting of magnetization in the high-field range. Also, we can see in Fig. 2, the ∆σ induced by the magnetization canting is much smaller than that in the perpendicular field direction.
The magnetic proximity effect usually is short-range, especially for a material with weak spin-orbit interaction. If the ferrimagnetic substrate cannot affect the top surface, there should be no apparent change in the resistance. However, in our Fig. 1(b), the resistance increases by one order, as the SiO2 substrate is replaced with the ferrimagnet BaFe12O19. Considering the resistance of BaFe12O19 is several orders higher, the resistance increase is not due to BaFe12O19 alone, but most likely from the topological insulator thin film under the influence of a long-range magnetic proximity effect. One of the possible reasons for the long-range proximity effect is strong spin-orbit coupling. It has been shown that the magnetic proximity effect can induce an obvious negative magnetoresistance in a Platinum film attached to a ferrimagnetic insulator YIG, up to a film thickness of 14 nm52. The topological insulator Sb1.9Bi0.1Te3 also has strong spin-orbit coupling, so the magnetic proximity between Sb1.9Bi0.1Te3 and BaFe12O19 might be also long-range. In the device for the Hall-bar meassurement in Fig. 3(b), the thickness of the topological insulator is 30 nm. In the Hall-bar device, we did not observe the negative magnetoresistance, probably because of poor interface contact or thicker topological insulator layer.
Methods
Synthesis of heterostructure
The mixed powder of Sb2Te3 and Bi2Te3 with molar ratio 19:1 was placed in the hot center of the tube furnace. Hexagonal BaM single crystals with a clean cleavage plane (0001) were put at a location about 9–12 cm away from the hot center. The tube is cleaned by ultrapure Ar gas for five times prior to the growth, and then the Ar gas flow is fixed at 50 s.c.c.m. In order to avoid the escape of tellurium, the hot centre was heated to 475° C within 5 min and kept at this temperature for one hour, followed by natural cooling. During the whole process, we maintained the pressure in the tube at 2.8 Torr. We obtained high-quality van der Waals epitaxy heterostructures of topological insulator and ferromagnetic insulator only when the substrate was placed 11.5 cm away from the hot center.
Device fabrication and characterization
To make standard four-probe devices on the topological insulator-BaM heterostructure for transport measurement, we transferred the heterostructure into a FEI SEM/FIB dual beam system for the deposition of Pt electrodes. The four Pt-stripe electrodes have a nominal width of 0.8 μm and a thickness of 200 nm deposited from a precursor gas of (methylcyclopentadienyl) trimethyl platinum (CH3)3CH3C5H4Pt. To avoid Pt contamination and Ga ion irradiation, we designed the distance between two adjacent electrodes to be larger than 2 μm. During the whole fabrication process, we only used the electron beam to guide the Pt deposition.
Magnetoconductivity fitting formula
We use equation (2) to fit the magnetoconductivity in perpendicular magnetic fields. The parameters in equation (2) are defined as19
where is the mean free path, , , and . We assume that the effects of random magnetic scattering is to reduce the phase coherence length and have been included in the definition of .
Additional Information
How to cite this article: Zheng, G. et al. Weak localization effect in topological insulator micro flakes grown on insulating ferrimagnet BaFe12O19. Sci. Rep. 6, 21334; doi: 10.1038/srep21334 (2016).
References
Chang, C. Z. et al. Experimental observation of the quantum anomalous Hall effect in a magnetic topological insulator. Science 340, 167–170 (2013).
Yu, R. et al. Quantized anomalous Hall effect in magnetic topological insulators. Science 329, 61–64 (2010).
Qi, X.-L. et al. Fractional charge and quantized current in the quantum spin Hall state. Nat. Phys. 4, 273–276 (2008).
Qi, X.-L. et al. Inducing a magnetic monopole with topological surface states. Science 323, 1184–1187 (2009).
Fu, L. & Kane, C. L. Probing Neutral Majorana Fermion Edge Modes with Charge Transport. Phys. Rev. Lett. 102, 216403 (2009).
Akhmerov, A. R. et al. Electrically Detected Interferometry of Majorana Fermions in a Topological Insulator. Phys. Rev. Lett. 102, 216404 (2009).
Law, K. T. et al. Majorana Fermion Induced Resonant Andreev Reflection. Phys. Rev. Lett. 103, 237001 (2009).
Garate, I. & Franz, M. Inverse Spin-Galvanic Effect in the Interface between a Topological Insulator and a Ferromagnet. Phys. Rev. Lett. 104, 146802 (2010).
Liu, Q. et al. Magnetic impurities on the surface of a topological insulator. Phys. Rev. Lett. 102, 156603 (2009).
Hor, Y. S. et al. Development of ferromagnetism in the doped topological insulator Bi2-xMnxTe3 . Phys. Rev. B 81, 195203 (2010).
Chen, Y. L. et al. Massive Dirac fermion on the surface of a magnetically doped topological insulator. Science 329, 659–662 (2010).
Wray, L. A. et al. A topological insulator surface under strong Coulomb, magnetic and disorder perturbations. Nat. Phys. 7, 32–36 (2010).
Abanin, D. A. & Pesin, D. A. Ordering of magnetic impurities and tunable electronic properties of topological insulators. Phys. Rev. Lett. 106, 136802 (2011).
Nomura, K. & Nagaosa, N. Surface-quantized anomalous Hall current and the magnetoelectric effect in magnetically disordered topological insulators. Phys. Rev. Lett. 106, 166802 (2011).
Xu, S.-Y. et al. Hedgehog spin texture and Berry’s phase tuning in a magnetic topological insulator. Nat. Phys. 8, 616–622 (2012).
Meng, Q. L. et al. Topological insulator magnetic tunnel junctions: Quantum Hall effect and fractional charge via folding. Phys. Rev. Lett. 109, 176803 (2012).
Habe, T. & Asano, Y. Interface metallic states between a topological insulator and a ferromagnetic insulator. Phys. Rev. B 85, 195325 (2012).
Yokoyama, T. et al. Anomalous magnetoresistance of a two-dimensional ferromagnet/ferromagnet junction on the surface of a topological insulator. Phys. Rev. B 81, 121401(R) (2010).
Lu, H.-Z. et al. Competition between weak localization and antilocalization in topological surface states. Phys. Rev. Lett. 107, 076801 (2011).
Liu, M. et al. Crossover between weak antilocalization and weak localization in a magnetically doped topological insulator. Phys. Rev. Lett. 108, 036805 (2012).
Zhang, D. et al. Interplay between ferromagnetism, surface states and quantum corrections in a magnetically doped topological insulator. Phys. Rev. B 86, 205127 (2012).
Lang, M. R. et al. Competing weak localization and weak antilocalization in ultrathin topological insulators. Nano Lett. 13, 48–53 (2013).
Checkelsky, J. G. et al. Quantum Interference in Macroscopic Crystals of Nonmetallic Bi2Se3 . Phys. Rev. Lett. 103, 246601 (2009).
Peng, H. L. et al. Aharonov–Bohm interference in topological insulator nanoribbons. Nat. Mater. 9, 225 (2010).
Chen, J. et al. Gate-voltage control of chemical potential and weak antilocalization in Bi2Se3 . Phys. Rev. Lett. 105, 176602 (2010).
He, H. T. et al. Impurity effect on weak antilocalization in the topological insulator Bi2Te3 . Phys. Rev. Lett. 106, 166805 (2011).
Haazen, P. P. J. et al. Ferromagnetism in thin-film Cr-doped topological insulator Bi2Se3 . Appl. Phys. Lett. 100, 082404 (2012).
Checkelsky, J. G. et al. Dirac-fermion- mediated ferromagnetism in a topological insulator. Nat. Phys. 8, 729–733 (2012).
Lang, M. R. et al. Proximity induced high-temperature magnetic order in topological insulator-ferrimagnetic insulator heterostructure. Nano Lett. 14, 3459–3465 (2014).
Peng, W. et al. Exchange-coupling-induced symmetry breaking in topological insulators. Phys. Rev. Lett. 110, 186807 (2013).
Yang, Q. I. et al. Emerging weak localization effects on a topological insulator–insulating ferromagnet (Bi2Se3-EuS) interface. Phys. Rev. B 88, 081407(R) (2013).
Kandala, A. et al. Growth and characterization of hybrid insulating ferromagnet-topological insulator heterostructure devices. Appl. Phys. Lett. 103, 202409 (2013).
Jiang, Z. L. et al. A comparative transport study of Bi2Se3 and Bi2Se3/yttrium iron garnet. Appl. Phys. Lett. 104, 222409 (2014).
Yang, W. M. et al. Proximity effect between a topological insulator and a magnetic insulator with large perpendicular anisotropy. Appl. Phys. Lett. 105, 092411 (2014).
Lu, H. Z. et al. Massive Dirac fermions and spin physics in an ultrathin film of topological insulator. Phys. Rev. B 81, 115407 (2010).
Kojima, H. & Goto, K. Remanent domain structures of BaFe12O19 . J. Appl. Phys. 36, 538 (1965).
Yang, Z. R. et al. Guided nucleation of superconductivity in Nb/BaFe12O19 hybrids with different domain patterns. Appl. phys. Lett. 98, 012505 (2011).
Zhang, X. X. et al. Magnetic properties and domain-wall motion in single-crystal BaFe10.2Sn0.74Co0.66O19 . Phys. Rev. B 53, 3336–3340 (1996).
Koma, A. Van der Waals epitaxy for highly lattice-mismatched systems. J. Cryst. Growth 201, 236–241 (1999).
Li, H. et al. Controlled synthesis of topological insulator nanoplate arrays on mica. J. Am. Chem. Soc. 134, 6132−6135 (2012).
Kong, D. S. et al. Few-Layer nanoplates of Bi2Se3 and Bi2Te3 with highly tunable chemical potential. Nano Lett. 10, 2245–2250 (2010).
Zhang, J. S. et al. Band structure engineering in (Bi1-xSbx)2Te3 ternary topological insulators. Nat. Commun. 2, 574 (2011).
Liao, J. et al. Observation of Anderson localization in ultrathin films of three-dimensional topological insulators. Phys. Rev. Lett. 114, 216601 (2015).
Hikami, S. et al. Spin-orbit interaction and magnetoresistance in the two dimensional random system. Prog. Theor. Phys. 63, 707–710 (1980).
Analytis, J. G. et al. Bulk Fermi surface coexistence with Dirac surface state in Bi2Se3: A comparison of photoemission and Shubnikov–de Haas measurements. Phys. Rev. B 81, 205407 (2010).
Chen, X. et al. Molecular beam epitaxial growth of topological insulators. Adv. Mater. 23, 1162–1165 (2011).
Cha, J. J. et al. Effects of magnetic doping on weak antilocalization in narrow Bi2Se3 nanoribbons. Nano Lett. 12, 4355–4359 (2012).
Zhang, L. et al. Weak localization effects as evidence for bulk quantization in Bi2Se3 thin films. Phys. Rev. B 88, 121103(R) (2013).
Wang, H. C. et al. Crossover between weak antilocalization and weak localization of bulk states in ultrathin Bi2Se3 films. Sci. Rep. 4, 5817 (2014).
Lu, H.-Z. & Shen, S.-Q. Weak localization of bulk channels in topological insulator thin films. Phys. Rev. B 84, 125138 (2011).
Garate, I. & Glazman, L. Weak localization and antilocalization in topological insulator thin films with coherent bulk-surface coupling. Phys. Rev. B 86, 035422 (2012).
Huang, S. Y. et al. Transport Magnetic Proximity Effects in Platinum. Phys. Rev. Lett. 109, 107204 (2012).
Acknowledgements
We thank Murong Lang for fruitful discussion. This work was supported by the Natural Science Foundation of China (Grant No. 11174294, 11374302, 11574127, U1432251 and U1332209), and the program of Users with Excellence, the Hefei Science Center of CAS and the CAS/SAFEA international partnership program for creative research teams of China.
Author information
Authors and Affiliations
Contributions
G.Z., N.W., H.Z.L. and M.T. conceived and designed the experiment. G.Z. and N.W., synthesized the samples and fabicated the devices. W.N., H.D., J.Y., W.W. and Z.Y. carried out the transport measurement. H.Z.L., G.Z., M.T. and Y. Z. provided the analysis and the theoretical interpretation. G.Z., H.Z.L. and M.T., wrote the paper, with assistance from all the co-authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zheng, G., Wang, N., Yang, J. et al. Weak localization effect in topological insulator micro flakes grown on insulating ferrimagnet BaFe12O19. Sci Rep 6, 21334 (2016). https://doi.org/10.1038/srep21334
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep21334
This article is cited by
-
Proximity induced band gap opening in topological-magnetic heterostructure (Ni80Fe20/p-TlBiSe2/p-Si) under ambient condition
Scientific Reports (2023)
-
Engineering the breaking of time-reversal symmetry in gate-tunable hybrid ferromagnet/topological insulator heterostructures
npj Quantum Materials (2018)
-
Reversible and nonvolatile manipulation of the electronic transport properties of topological insulators by ferroelectric polarization switching
npj Quantum Materials (2018)
-
Proximity Effect induced transport Properties between MBE grown (Bi1−xSbx)2Se3 Topological Insulators and Magnetic Insulator CoFe2O4
Scientific Reports (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.