Remarkable magnetic and spin-dependent transport properties arise from well-designed spintronic materials and heterostructures. Half-metallic Heusler alloys with high spin polarization exhibit properties that are particularly advantageous for the development of high-performance spintronic devices. Here, we report fully (001)-epitaxial growth of a high-quality half-metallic NiMnSb half-Heusler alloy films, and their application to current-perpendicular-to-plane giant magnetoresistance (CPP-GMR) devices with Ag spacer layers. Fully (001)-oriented NiMnSb epitaxial films with very flat surface and high magnetization were prepared on Cr/Ag-buffered MgO(001) single crystalline substrates by changing the substrate temperature. Epitaxial CPP-GMR devices using the NiMnSb films and a Ag spacer were fabricated, and room-temperature (RT) CPP-GMR ratios for the C1b-type half-Heusler alloy were determined for the first time. A CPP-GMR ratio of 8% (21%) at RT (4.2 K) was achieved in the fully epitaxial NiMnSb/Ag/NiMnSb structures. Furthermore, negative anisotropic magnetoresistance (AMR) ratio and small discrepancy of the AMR amplitudes between RT and 10 K were observed in a single epitaxial NiMnSb film, indicating robust bulk half metallicity against thermal fluctuation in the half-Heusler compound. The modest CPP-GMR ratios could be attributed to interface effects between NiMnSb and Ag. This work provides a pathway for engineering a new class of ordered alloy materials with particular emphasis on spintronics.
Engineering of advanced half-metallic materials is of particular importance for achieving ideal magnetic and spin-dependent transport properties for a variety of significant spintronic applications, because 100% spin polarization of the conductive electrons at the Fermi level is theoretically predicted for these series of materials1,2,3,4. Heusler alloys, a type of half-metallic materials, have properties that are particularly advantageous to achieving half-metallicity at room temperature (RT)3,5,6, and have been attracting extensive interest for the development of next-generation spintronic devices, such as magnetoresistive random access memories (MRAMs)7,8,9, current-perpendicular-to-plane giant magnetoresistance (CPP-GMR) read heads for hard disk drives (HDDs)10,11,12,13, spin torque oscillators (STO)14,15,16, and spin transistors17,18. Half-metallic Heusler alloys are classified into full- and half-Heusler compounds with the chemical formula of X2YZ in the L21 structure and XYZ in the C1b structure (X and Y: transition metals; Z: non-magnetic element)6, as shown in Fig. 1. Recently, cobalt-based full-Heusler alloys were proposed as a candidate material for high-output CPP-GMR effect, which is a key technology for next-generation HDDs with an areal density of more than 2 Tb/inch2,7,19,20. CPP-GMR junctions have been fabricated using several full-Heusler compounds, such as Co2Fe(Al-Si)10, Co2MnSi11, Co2(Fe-Mn)Si12, and Co2Fe(Ge-Ga)13, and these studies promoted the further development of Heusler alloys for practical applications. However, despite these developments, it remains difficult to overcome the spin-transfer torque and Joule heating problems associated with realizing ultra-high density HDDs. Therefore, advanced materials with high-performance half-metallicity are desired for further improvement of CPP-GMR junctions.
The bandgap in half-metallic Heusler alloys originates from the strong d-band hybridization of the two transition metals21. For full-Heusler alloys, the bandgap is dominated by the d-band hybridization between elements X (X-X hybridization). The antibonding states formed by X–X hybridization cannot couple with the Y degenerates, resulting in a small gap across the Fermi level (EF). For half-Heusler alloys, however, the origin of the bandgap is the hybridized states of elements X and Y, which can form a very large bandgap between the bonding (t2g) and antibonding (eg) degenerates. Figure 1 illustrates a comparison of crystalline cell structures and the electronic band structure near the Fermi level between L21-type full-Heusler and C1b-type half-Heusler alloys. Based on the origin of their bandgaps, half-Heusler alloys with a large bandgap (e.g. 0.5 eV for NiMnSb and 1 eV for CoMnSb)21 are promising for the development of high-performance magnetoresistive devices owing to the suppression of thermal activations of the electrons above the bandgap. Nevertheless, previous studies have demonstrated that the half-metallic properties of half-Heusler alloys can be very easily degraded by disordering and the presence of defects and/or surface segregation and termination atoms22,23,24, and a few percent CPP-GMR ratio was only observed at low temperature (4.2 K) in a polycrystalline NiMnSb/Cu/NiFe system25. This indicates that a precise control over the ordering and structure of half-Heusler alloys is highly desired.
In this work, we open a new field in Heusler spintronics, i.e. half-Heusler compounds for CPP-GMR devices, and room-temperature CPP-GMR ratios are achieved in fully epitaxial NiMnSb/Ag/NiMnSb structures for the first time. High-quality half-Heusler NiMnSb films with an almost perfectly stoichiometric composition were fabricated using a co-sputtering method. Fully (001)-orientation epitaxy NiMnSb alloy films with high magnetization and a very flat surface were achieved on Cr/Ag-buffered MgO(001) single crystalline substrates by optimizing the substrate temperature (Tsubstrate). CPP-GMR effect in the NiMnSb/Ag/NiMnSb structures was investigated. Anisotropic magnetoresistance (AMR) measurement in a single epitaxial NiMnSb film indicates robust half metallicity against thermal fluctuation in the half-Heusler compound.
Structural and magnetic properties
Half-Heusler NiMnSb films were formed by a co-sputtering method using Ni and MnSb targets. After optimizing the sputtering rate of both the targets, the composition of the deposited NiMnSb films was confirmed to be Ni1.01 ± 0.02Mn0.98 ± 0.02Sb1.01 ± 0.02 by inductively coupled plasma (ICP) analysis, which is an almost ideal stoichiometric composition for the half-Heusler compound. We deposited the films on Cr(20 nm)/Ag(40 nm)-buffered MgO(001) single crystalline substrates at varied Tsubstrate ranging from RT to 773 K. The structural properties were characterized by two dimensional (2D) out-of-plane (2θ-scan) X-ray diffraction (XRD) patterns, as shown in Fig. 2a–f. For the as-deposited NiMnSb film at RT, the out-of-plane diffraction peaks from the NiMnSb(002) and (004) super lattices are clearly observed in addition to the Cr(002) and Ag(002) peaks from the buffer layers, while peaks corresponding to other phases and/or orientations of the NiMnSb layer also appear, as pointed out by the arrows in Fig. 2a. When the Tsubstrate increases to 473−673 K, the single phase and (001)-orientated peaks of NiMnSb can be seen in the deposited films. At Tsubstrate = 773 K, however, multi-phases and other orientations appear again, i.e. NiMnSb(111), NiSb(101) and NiSb(002), as shown in Fig. 2e. We extracted the 2D out-of-plane XRD data in a zero-dimensional diffraction region in Fig. 2f, where the phases of NiSb and NiMnSb(111) orientation are indicated. In order to confirm the C1b structure and epitaxial growth of NiMnSb films, out-of-plane and in-plane (ϕ-scan) XRD patterns of the NiMnSb(202) and NiMnSb(111) planes were investigated by tilting the sample plane to χ = 45° and 54.7°, respectively. For the NiMnSb sample deposited at 573 K, the (202) and (111) peaks are clearly observed in Figure S1 (Supplementary Information), consistent with the C1b structure. Figures 2g,h show typical in-plane (ϕ-scan) XRD patterns for the sample in which the 4-fold peaks are observed for both planes. This indicates that the NiMnSb film has a 4-fold symmetry and was epitaxially grown in the engineered structure of MgO(001)-substrate//Cr(20)/Ag(40)/NiMnSb(50) (unit: nm).
Figure 3a shows the integrated intensity and the full width at half maximum (FWHM) of the NiMnSb(002) peaks as a function of Tsubstrate for the samples with the structure of MgO(001)-substrate//Cr(20)/Ag(40)/NiMnSb(50) (unit: nm). With increasing Tsubstrate, the intensity of the peaks initially increases for the samples owing to the improved ordering and the (001)-epitaxy of the NiMnSb layers, and it reaches a maximum at Tsubstrate = 573 K. Furthermore, in accordance with the maximum in the peak intensity, a minimum in the FWHM was observed at Tsubstrate = 573 K, indicating that optimum crystalline quality was achieved at Tsubstrate = 573 K. The reduction in the peak intensity at a higher Tsubstrate may be caused by the generation of other phases. Figure 3b shows the Tsubstrate dependence of the in-plane and out-of-plane lattice constants of the NiMnSb films, derived from the 2θ positions of the NiMnSb(002), (202), and (111) peaks in the XRD patterns. With increasing Tsubstrate, all the experimental lattice constants of aexp., aexp., and aexp. monotonically decrease. The decrease in lattice constants may be explained by the increase of C1b ordering of NiMnSb films as indicated in XRD results when the substrate temperature increases to the optimized value. With the C1b structure enhancing, unoccupied Ni sites (vacancy sites) increase in the NiMnSb films, which results in the reduction in the lattice constants. However, when the substrate temperature further increases to a higher value than the optimized one, the other phases (such as NiSb) appear as observed in XRD results, which causes the Mn substitution for Sb or/and Ni sites in the NiMnSb films. Especially, the radius of Mn ion is much smaller than that of Sb, resulting in a further reduction in the lattice constants with increasing substrate temperature. Although the out-of-plane lattice aexp. shows a slightly higher value than the others, the deviation between the observed lattice constants and the theoretical ones (acal.) is smaller than 0.4% at Tsubstrate = 573 K. This result suggests that an excellent (001)-epitaxy of NiMnSb films was successfully achieved on the Cr(20 nm)/Ag(40 nm)-buffered MgO(001) substrates without losing the half-metallicity26.
The magnetic properties of NiMnSb epitaxial films deposited at different Tsubstrate were investigated. Figure 4a shows the magnetic hysteresis (M-H) loops for 50-nm-thick NiMnSb films on the Cr/Ag-buffered MgO(001) substrates, which were measured along the NiMnSb crystalline orientation. The saturation magnetization (Ms) increases with increasing Tsubstrate to 673 K, and then decreases at 773 K, as shown in Fig. 4b. The increase in Ms is attributed to the increased order in the structure at a high temperature, while the reduction at 773 K could be due to the appearance of other phases and orientations in the NiMnSb films, as demonstrated in the XRD patterns. An optimum Ms value of ~3.7 μB/f.u. was achieved at Tsubstrate = 573−673 K, which is comparable to the saturation magnetization (Mbulk) of bulk NiMnSb at RT27,28. Figure 4c shows the easy-axis coercivity (Hc) and hard-axis saturation field (Hs) as a function of Tsubstrate for the NiMnSb films along the NiMnSb (easy axis) and NiMnSb (hard axis) crystalline orientations, respectively. Both Hc and Hs increase with increasing Tsubstrate for temperatures ranging between 200 and 673 K, indicating an improvement in magnetic anisotropy. The trend deviation of Hs for the as-deposited sample and for that deposited at Tsubstrate = 773 K could be due to the multi phases and/or the poor epitaxy of the NiMnSb film as observed in XRD patterns. Further investigation on the mechanism of magnetic anisotropy is required.
For stacking GMR multilayers using the fully (001)-epitaxial NiMnSb films, the Tsubstrate dependence of the surface morphology of NiMnSb films was investigated by atomic force microscopy (AFM). Figure 5 shows the average surface roughness (Ra) and peak-to-valley (P-V) value as a function of Tsubstrate for 50-nm-thick NiMnSb films capped by 2-nm-thick Ag layers on Cr(20 nm)/Ag(40 nm)-buffered MgO(001) single crystalline substrates. On increasing the Tsubstrate to 573 K, the surface of the deposited NiMnSb film becomes slightly flatter than that of the sample deposited at RT. An optimally flat surface with Ra ∼ 0.35 nm and P-V ∼ 3.9 nm was obtained at Tsubstrate = 573 K, and the high-quality surface without segregation is shown in the inset of Fig. 5. However, when the Tsubstrate is higher than 673 K, an abrupt increase in the surface roughness is observed. As shown in the inset of Fig. 5, for the sample deposited at 773 K, we can see the three-dimensional growth of square islands, which could be attributed to the nucleation and growth thermodynamics at a high temperature24. These results indicate that Tsubstrate ranging from 473 to 673 K is feasible for stacking whole CPP-GMR multilayers.
Magneto-electrical transport properties
Based on the above structural and magnetic investigations, whole CPP-GMR stacks with the structure of MgO(001)-substrate/Cr(20)/Ag(40)/NiMnSb(20)/Ag(5)/NiMnSb(7)/Ag(2)/Au(7) (unit: nm) were deposited by varying Tsubstrate (=473, 573, or 673 K), for the growth of NiMnSb layers. Figure 6a shows a schematic of the fully epitaxial CPP-GMR multilayers. For the whole stack, the XRD patterns show only single phase and (001)-orientation peaks, as shown in Figure S2 (Supplementary Information), indicating a uniform structure between the bottom and top NiMnSb layers because both of them were deposited upon the Ag(001) layer under the same conditions. The multilayer films were then nano-patterned into rectangular pillars with designed sizes ranging from 50 × 100 nm2 to 400 × 800 nm2 for the measurement of magneto-electrical transport properties. Figure 6b shows the scanning electron microscopy (SEM) image of a typical CPP-GMR nanopillar with a minimum dimension of 100 × 140 nm2.
The dependence of the junction resistance on the pillar size was investigated for determining the RA values as well as the parasitic resistance (Rpara) in the devices. Figure 7a shows the junction resistance (Rp) at the parallel magnetization state between the bottom and top NiMnSb layers as a function of the inverse of the junction area (1/A) for the patterned CPP-GMR devices with NiMnSb layers deposited at Tsubstrate = 573 K. The dependence of Rp on 1/A is well reproduced by a linear relationship, indicating an excellent electron beam lithography process for controlling the nanopillar sizes. From the linear fitting, RA and Rpara were estimated to be 26 ± 1 mΩ·μm2 and 0.42 ± 0.05 Ω, respectively for the CPP-GMR junctions. Thus, the CPP-GMR ratio can be deduced using the formula (Rap-Rp)/(Rp-Rpara) where Rap represents the junction resistance in an antiparallel magnetization configuration. A CPP-GMR ratio of 8% at RT was achieved in the fully epitaxial NiMnSb/Ag/NiMnSb CPP-GMR junction, as shown in Fig. 7b. A typical pseudo spin-valve MR curve was observed with separated switching fields between the top and bottom NiMnSb layers. Figure 7c shows the Tsubstrate dependence of the CPP-GMR ratio and RA value for the CPP-GMR junctions. For the samples with NiMnSb layers deposited at 473 K, only a small CPP-GMR ratio was observed because of the low ordering of the NiMnSb layers, as investigated by XRD analysis; on the other hand, the reduction in the CPP-GMR ratio, associated with an increment in the RA value to 45 mΩ·μm2 for the sample at Tsubstrate = 673 K, could be attributed to the increased surface roughness.
Figure 8 shows the dependence of the CPP-GMR ratio on measuring temperature and the RA values for a NiMnSb/Ag/NiMnSb CPP-GMR device in which the NiMnSb layers were deposited at Tsubstrate = 573 K. A CPP-GMR ratio of 21% was achieved at 4.2 K, as shown in Fig. 8a. The CPP-GMR ratio is enhanced to more than double, which could be attributed to the excellent ordering structure of NiMnSb and the Ag spacer achieved in this study. Moreover, at 4.2 K, an imperfect antiparallel state and antisymmetric feature were observed in the MR loops, indicating an enhanced magnetic coupling between the bottom and the top NiMnSb layers at low temperature29. As seen in Fig. 8b, the CPP-GMR ratio monotonically increases with decrease in the measuring temperature, which is different from the anomalous temperature dependence of the CPP-GMR ratio at low temperatures (<80 K) observed in the Co2MnSi/Ag/Co2MnSi system due to Mn inter-diffusion30. This could be indicative that our NiMnSb/Ag/NiMnSb structure is free from Mn inter-diffusion. In contrast to the CPP-GMR ratio, the RA values at both the parallel (RAp) and antiparallel (RAap) magnetic states decrease with decreasing temperature.
Well-grown NiMnSb films are of particular significance for maintaining the half metallic property as well as reducing the spin-flip scattering at the NiMnSb/Ag interface for successful demonstration of CPP-GMR devices. Fully (001)-oriented epitaxial NiMnSb films were achieved on Cr/Ag-buffered MgO (001) substrates by optimizing the Tsubstrate. The optimum condition for the preparation of an epitaxial NiMnSb alloy film with a high magnetization and a very flat surface was achieved by investigating the magnetic properties and the surface morphology. We also deposited NiMnSb films on MgO(001) substrates directly by varying the Tsubstrate; in this case, only polycrystalline films with multi-phases were observed. These indicate that not only deposition conditions but also well-designed buffer layers are indispensable for the engineering of half-Heusler NiMnSb alloy films with an ideal ordered structure and epitaxial growth.
Epitaxial CPP-GMR devices with NiMnSb/Ag/NiMnSb multilayers were fabricated and a RT CPP-GMR ratio of 8% was successfully achieved. Study of the spin-dependent transport properties as a function of the measuring temperature revealed a monotonic increase in the CPP-GMR ratio with decreasing temperature. A significant improvement in the CPP-GMR ratio (21%) at low temperatures was achieved. The first observation of RT CPP-GMR in the C1b-type half-Heusler alloy-based CPP-GMR devices indicates that the composition, structure, and magnetic properties of the NiMnSb alloys and the CPP-GMR stacks are well optimized. According to the Valet–Fert model31, the CPP-GMR ratio is proportional to in the limit where spin-diffusion lengths of electrons are much longer than the layer thicknesses. Here, β and γ are the coefficients of bulk and interfacial spin asymmetry, respectively; tF is the thickness of the ferromagnetic layer; and represent the resistivity of the ferromagnetic layer () and the resistance at the ferromagnetic/nonmagnetic interface () including spin asymmetries, respectively. The increase in the CPP-GMR ratio with decreasing temperature could result from the increase in β and γ because of high spin polarization at low temperatures owing to the suppression of the thermal excitation of electrons to the bandgap. Furthermore, we measured AMR effect in a typical epitaxial NiMnSb single film utilized in the CPP-GMR devices since AMR ratio was known to be a fingerprint of half-metallicity32. Figure 9 shows the dependence of AMR ratio on the in-plane relative angle ϕ in the typical NiMnSb single film where ϕ = 0° (90°) represents that magnetization is normal (parallel) to the measuring current. The negative AMR ratio was observed which indicates the half metallicity of the film. Especially, the discrepancy of AMR amplitudes between 300 K and 10 K is much smaller than that of Co2MnSi full-Heusler alloy films33, indicating robust bulk half metallicity against thermal fluctuation in the half-Heusler NiMnSb films. The modest CPP-GMR ratios with relatively large measuring temperature dependence could be attributed to interface effects between NiMnSb and Ag. Additional investigations to improve the interface properties would be required to further increase the CPP-GMR ratio.
Although the modest MR values were shown at present, this pioneering work will stimulate future studies for achieving a higher MR value. This work indicates that the NiMnSb half-Heusler alloy could be a potentially promising material for spintronic applications because of the physical advantages of the half-Heulser compound material, and provides a pathway for engineering a new class of ordered alloy materials with particular emphasis on spintronics.
All multilayer stacks were deposited by an ultrahigh vacuum magnetron sputtering system, with a base pressure lower than 1 × 10−7 Pa. Prior to depositing NiMnSb films, the bilayers of Cr(20 nm)/Ag(40 nm) were deposited at RT on MgO(001) single-crystalline substrates, where the 20-nm-thick Cr layer was in-situ post-annealed at 973 K for 1 h. NiMnSb layers were deposited at varied Tsubstrate from RT to 773 K by a co-sputtering method using Ni and MnSb targets, and the composition of the deposited NiMnSb films was confirmed by ICP analysis. The structural properties of NiMnSb films on Cr/Ag buffers were characterized by out-of-plane (2θ-scan) XRD with Cu Kα radiation (λ = 0.15418 nm) and a two-dimensional detector. Surface morphology of NiMnSb half-Heusler alloy films as a function of Tsubstrate was investigated by AFM with a scan area of 1 × 1 μm2. Magnetization hysteresis loops were measured at RT using a vibrating sample magnetometer. The CPP-GMR multilayer films were nano-fabricated into rectangular pillars with junction sizes ranging from 50 × 100 nm2 to 400 × 800 nm2 by electron beam lithography and a lift-off technique, while the top and bottom electrical pads were patterned by conventional UV lithography. Magneto-electrical transport properties were measured at RT and low temperatures using a four-probe method in a physical property measurement system.
How to cite this article: Wen, Z. et al. Fully epitaxial C1b-type NiMnSb half-Heusler alloy films for current-perpendicular-to-plane giant magnetoresistance devices with a Ag spacer. Sci. Rep. 5, 18387; doi: 10.1038/srep18387 (2015).
This work was partially supported by the KAKENHI (S) (No. 25220910) from the Japan Society for the Promotion of Science (JSPS); the ImPACT program of the Council for Science, Technology and Innovation (Cabinet Office, Government of Japan).
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/