Introduction

In 1961, Shockley and Queisser developed a theoretical framework for determining the limiting efficiency of a single junction solar cell based on the principle of detailed balance equating the incoming and outgoing fluxes of photons for a device at open-circuit conditions1. This model incorporates various light management and trapping techniques including photon recycling, optical concentration and emission angle restriction1,2,3. It was recently suggested that a nanowire solar cell could exceed the Shockley-Queisser (SQ) limit based on its geometry4; however, without exploiting 3rd generation photovoltaic (PV) concepts that break the assumptions of Shockley and Queisser (e.g. multi-exciton generation, hot carrier collection, etc)5,6,7, even nanowire solar cells should be bounded by the SQ limit. Here we show that for any nanostructured solar cell (e.g. composed from wires, cones, pyramids, etc.), the limiting efficiency is identical to that of a planar solar cell with concentrating optics and that the improvement results strictly from an increase in the open-circuit voltage. This formalism leads to a maximum efficiency of 42% for a nanostructured semiconductor with a bandgap energy of 1.43 eV (e.g. GaAs) under AM 1.5G illumination8.

The SQ limit is reached by applying the principle of detailed balance to the particle flux into and out of the semiconductor1. For every above bandgap photon that is absorbed by the semiconductor, one electron-hole pair is generated. The maximum possible efficiency is achieved when non-radiative recombination is absent and all generated carriers are either collected as current in the leads or recombine, emitting a single photon per electron-hole pair. The total generated current is:

where q is the charge of an electron and Nabs and Nemit are the numbers of photons per unit time that are absorbed or emitted by the photovoltaic device, respectively. These rates can be calculated as2:

where σabs(θ, ϕ, E) is the absorption cross-section, F(E, T, V) is the spectral photon flux and θmax is the maximum angle for absorption (for Nabs) or emission (for Nemit). For a bulk planar cell, the absorption cross-section is given by σabs(θ, ϕ, E) = Acell × a(θ, ϕ, E), where Acell is the top illuminated surface area of the cell and a(θ, ϕ, E) is the angle dependent probability of photon absorption for incident photons of energy E. In the simplest case, a(θ, ϕ, E) is a step-function going from 0 (for E < Eg) to 1 (for E ≥ Eg). The spectral photon flux can be obtained from the generalized Planck blackbody law9:

where h is Planck’s constant, kb is Boltzmann’s constant, c is the speed of light, n is the refractive index of the surroundings, which is usually taken to be vacuum (n = 1) and qV characterizes the quasi-Fermi level splitting when describing emission from the cell. The incoming flux from the sun can be obtained from experimental data (e.g. AM 1.5 solar spectrum) or from the blackbody expression above with V = 0 and where θmax = θs = 0.267° is the acceptance half-angle for incident light from the sun at temperature T = Ts = 5760 K. The outgoing flux from the cell is given by Eq. (2) for a cell temperature Tc = 300 K, operating voltage V and emission half-angle θmax = θc = 90°. At open-circuit conditions, there is no current extracted and the current balance equation becomes

where the middle term corresponds to absorption due to emission from the ambient surroundings, also at T = 300 K; however, this term is much smaller than the flux from the sun. Thus, the light generated current is given by IL = qNs, Ts, V = 0) and the dark current, in the radiative limit, is given by , where IR is the reverse saturation current. Solving Eq. (4) for the voltage yields the common expression for the open-circuit voltage1,8:

which is valid for both bulk planar solar cells and nanostructured solar cells with the appropriate absorption cross-sections as described in the next section.

Results

Nanostructured solar cells with built-in optical concentration

To achieve the maximum efficiency, we need to increase the light generated current compared to its bulk form or reduce the reverse saturation current to increase Voc. For any absorbing structure, Eqs (2, 3, 4, 5) can be used to determine the resulting Voc numerically; however, for the limiting case, we will consider a simple analytical expression. For maximum Voc, we want the absorption cross-section to be maximized for angles near normal incidence up to an angle θm (where θs ≤ θm) and minimized for all other angles θm ≤ θ ≤ θc, where θm is some angle defined by the structure. We can define this piece-wise function for the absorption cross-section as: σabs(θ : 0 →θm) = σmax and σabs(θ : θm →θc) = σmin, which allows us to perform the solid angle integration to determine the light and dark currents:

where σabs = 0 for E < Eg, IL,0 is the light generated current for an ideal bulk cell of area Acell, and

where IR,0 is the reverse saturation current for a bulk cell. Substituting these expressions into Eq. (5), we have

where

Thus, the open-circuit voltage for a nanostructured device takes on the same form as the open-circuit voltage for a macroscopic concentrating system, where X is the concentration factor8. For maximum concentration, we consider the limit as θm →θs and σmin  → 0, yielding

which is the same as the maximum concentration factor that is obtained for a macroscale concentrator and results in a maximum solar energy conversion efficiency of 42%. For practical devices it is reasonable to assume a minimum value of σmin corresponding to the geometric cross-section of the device, σmin →σgeo. For this case and with cos(2θm) = cos(2θs) ≈ 1, we get X = σmaxgeo and the open-circuit voltage reduces to:

Finally, the power conversion efficiency is given by η = ILVocFF/Pin, where FF is the fill-factor, which can be obtained from the IV characteristic defined by Eq. 1 and Pin is the incident power from the sun. We note that the area used to calculate Pin is determined by the illumination area and not the geometric cross-section, which would lead to undercounting the number of incident photons. In general, optical concentration can be achieved using lenses, mirrors, or unique optical nanostructures (see Fig. 1(a)). A nanostructured solar cell can result in optical concentration that is similar to the concentration obtained using lens or parabolic mirrors but relies on the wave nature of light. Fig. 1 (b) shows the power conversion efficiency of recently reported vertically aligned nanowire-based PV cells4,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24. The optical and geometrical cross-sections are extracted from the current density data and from the geometrical information provided within the references. The vast majority of the experiments are focused on Si, GaAs and InP radial or axial junction nanowire arrays fabricated with various techniques, such as MBE, MOVCD, reactive-ion etching, etc. Generally, is found to fall in the range of 1–10 for these structures; however, the actual concentration factor is likely significantly smaller if σmin > σgeo. Additionally, the reduced efficiency in these nanowire structures compared to the theoretical limit is due to significant surface recombination and device and material constraints that could be improved with further experimental development.

Figure 1
figure 1

The Shockley-Queisser limit for nanostructures.

(a) Schematic of the optical concentration implemented by a concentrating lens, parabolic mirror and using a nanostructure itself (self-concentration). (b) The efficiencies of cells with optical concentration. The solid line is the theoretical limit of nanostructured PV devices based on detailed balance, whereas individual dots represents experimental data reported in the literature4,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24.

The effect of entropic losses on Voc

Next we consider an alternative, but equivalent, approach to understanding the maximum efficiency of a nanostructured PV device by considering the energetic and entropic loss mechanisms25,26,27. The generalized Planck equation can be used to determine the open-circuit voltage of a solar cell operating at the maximum efficiency limit25,28,29:

where γs and γc are blackbody radiation flux terms that depend on Eg, Ts and Tc. The first term represents a voltage drop related to the conversion of thermal energy into work (sometimes called the Carnot factor). The second term occurs from the mismatch between Boltzmann distributions at Tc and Ts30. The third term is the voltage loss due to entropy generation as a result of a mismatch between the absorption solid angle and the emission solid angle of the cell. This third term represents a voltage drop of 0.28 V, which can be recovered if Ωemit = Ωabs. Modification of the directionality of absorption and emission to improve the open-circuit voltage of a solar cell is well-known31,32,33 and has recently been shown in experiments34,35.

The most common way to recover the entropy loss due to the mismatch between the absorption and emission solid angles is through optical concentration (Fig. 2(a)). For a planar solar cell without optical concentration, the absorption solid angle corresponds to the sun’s angular extent, i.e. Ωabs = 2π(1 − cos(θs)) = 6.82 × 10−5 sr. However, emission from the cell occurs over Ωemit = 4π. The addition of a back reflector reduces the emission solid angle to Ωemit = 2π, resulting in a slight voltage improvement2. For more substantial voltage improvements, optical concentration is necessary. Optical concentration enables the absorption solid angle to exceed the sun’s solid angle and approach the cell’s emission solid angle (Fig. 2(a)), which could largely increase the Voc.

Figure 2
figure 2

Nanostructures can reduce the mismatch between absorption and emission angles.

(a) A traditional planar solar cell with concentrator increases Ωabs to approach Ωemit, thus reducing the entropy generation caused by their mismatch. (b) Similarly, a nanostructured solar cell can reduce the difference between Ωabs and Ωemit.

Properly designed photovoltaic nanostructures can have the same effect, reducing the entropy generation by either increasing Ωabs or by reducing Ωemit in an attempt to achieve Ωemit = Ωabs (Fig. 2(b)). From a device point-of-view, Ωabs is related to the light generated current density, JL = IL/A and Ωemit is related to the reverse saturation current density, JR = IR/A. Because the Voc depends on their ratio (see Eq. 5), increasing Ωabs will have the same affect as decreasing Ωemit. Thus, the voltage improvement can equivalently be seen from the thermodynamics of reduced entropy generation or from the device aspects of the p-n junction.

According to Kirchhoff’s law, the emissivity and absorptivity of a solar cell are equal in thermal equilibrium2,36. For a standard cell without back reflector, the device can absorb the incident power from all directions and hence will emit in all directions (Fig. 3(a)). The addition of a back reflector reduces both absorption and emission from the back surface (Fig. 3(b)); however, this has no effect on the absorption of the incident solar power because no illumination is coming from the back. Thus, IL is unaffected by the addition of the back reflector but IR is reduced (note: technically IL could be slightly increased due to an increased path length in thin or low absorption materials, resulting in a small increase in Voc). An ideal nanostructure would allow for absorption only over the range of angles corresponding to the incident illumination of the source, i.e. the sun (Fig. 3(c)). The current-voltage characteristics for these devices show that a back reflector yields a 2% increase in efficiency over the traditional planar device and an ideal nanostructure yields a 11% improvement, resulting in a 42% efficient device.

Figure 3
figure 3

Modification of absorption and emission results in an ideal PV nanostructure achieving >40% power conversion efficiency.

Emission and absorption for (a) slab without back reflector (i.e. light can escape through the back surface without reflection), (b) slab with back reflector and (c) ideal nanostructured cell. The emission and absorption are represented in terms of their half-angle, θ. Absorption/emission over all angles (standard cell) corresponds to θ = 180°; however, the illumination from the sun is only over a subset of half-angles from 0 to θs. Thus, the mismatch between θs and θemit results in a decreased voltage. (d) I-V curves corresponding to the three structures (ac). All structures are illuminated with the AM 1.5G spectrum and show increased Voc as θemit→θs.

Effect of diffuse illumination

While the maximum power conversion efficiency is achieved with 100% direct illumination (i.e. the incident light is completely within the solid angle defined by θs), an efficiency of 38% can be achieved when 25% of the incident illumination is diffuse (Fig. 4), which is typical of many geographic regions. Incident illumination on earth contains both direct and diffuse components (due to scattering of the incident light). Using traditional macroscopic concentrating optics, light is concentrated for all wavelengths and only the direct components can be used. Alternatively, nanostructures typically have a wavelength-dependent response and may only be able to concentrate light over a particular bandwidth, e.g. from the semiconductor bandgap energy (Esc) to some cut-off energy (Ecut-off). This limited bandwidth for concentration is beneficial when the illumination is not 100% direct, because the diffuse components that lie outside this range can still be collected.

Figure 4
figure 4

Effect of diffuse illumination.

(a) Contour plot showing the influence of diffuse illumination on nanostructured PV as the cut-off energy for nanoscale concentration (Ecut-off) is varied, assuming maximum concentration (X = 46,050). Esc corresponds to the semiconductor bandgap of the device. (b) 3 slices of the contour plot in (a) corresponding to Ecut-off = 1.43 eV (traditional PV), Ecut-off = 1.74 eV (concentration for photons from Esc to Ecut-off) and Ecut-off  →∞ (concentration for all incident photons); similar calculations performed for X = 1,000 are also shown. The nanostructured device with complete concentration (i.e. concentration for all energies of incident photons) outperforms traditional PV when diffuse illumination accounts for <20% of the incident light. The nanostructured device with partial concentration (corresponding to concentrating only light with energies 1.43–1.74 eV) outperforms the traditional device when the incident light is <60% diffuse. With only modest concentration (X = 1,000), the device has an efficiency of 35.5% under 25% diffuse illumination. (c) Absorption contour plot and schematic depicting a nanoscale device that is able to concentrate light with energies Esc to Ecut-off but unable to concentrate light with energy greater than Ecut-off.

Figure 4 shows that efficiencies >35% can be achieved even when the illumination contains a significant fraction of diffuse light. The nanostructures depicted in Fig. 4 are able to concentrate the incident light from Esc to Ecut-off and are unable to concentrate light with energies >Ecut-off, which corresponds to absorption of diffuse light in that bandwidth. For Ecut-off = 1.74 eV, X = 1,000 and 25% diffuse illumination, the nanostructured devices reach an efficiency of 35.5%.

Numerical simulation of nanowire PV

While the above discussion is general and provides the limiting efficiency of any nanostructured solar cell (e.g. wires, cones, pyramids, etc.), explicate cell architectures can be studied via numerical simulation. There are no implicit assumption about the directionality of the absorption or emission; these quantities are numerically calculated directly for each structure. We have simulated a bulk (80 μm thick) GaAs solar cell and a nanowire solar cell with the same thickness (with periodicity of 300 nm and radius of 75 nm) using the S4 simulation package37 to obtain the absorption profiles. We then solved the detailed balance expression numerically38,39. A similar method was recently used to calculate the detailed balance efficiency for an InP nanowire array and an efficiency improvement of 1.5% was reported compared to a bulk device40. For simplicity, we used the blackbody spectrum in the following calculations. The nanowires are embedded within a material with an index of refraction of n = 2.66 and both the nanowire and planar structures are coated with a double-layer antireflection coating (a 52 nm layer with n = 2.66 and a 98 nm layer with n = 1.46). The antireflection coating is designed to maximize the efficiency of the bulk GaAs cell. The integrated short circuit current density is almost identical for both cases (<1% difference); however, the emitted power density is significantly different. Because a large amount of the radiated power is near the bandgap, the lower absorption rate near the bandgap that occurs with the nanowire structure leads to a decrease in emission. This effect is demonstrated in Fig. 5(d), where the bulk cell has a higher reverse saturation current density compared to the nanowire cell with same thickness. The reverse saturation current of the nanowire cell decreases by 3.46% and the absorption increases by 0.38%. As a result, the Voc increases by 1 mV due to these combined effects in the nanowire device and thus, the nanowire solar cell has a slightly higher efficiency than the bulk device (28.22% vs. 28.09%).

Figure 5
figure 5

Reduced dark current in nanowire structures.

Angular dependence of the absorption spectrum for (a) a bulk (80 μm thick) GaAs solar cell, (b) a GaAs nanowire solar cell (embedded in a dielectric) with a period of 300 nm, a radius of 75 nm and length of 80 μm and (c) a GaAs nanowire solar cell with a period of 200 nm, a radius of 40 nm and a length of 2 μm. The devices in (a,b) have a double-layer ARC on top and all cells have a perfect back reflector. The nanowire solar cells have decreased absorption (and hence emission) near the bandedge for angles >θs. (d) The current density corresponding to the three structures (ac) decreases, showing an improved Voc for the nanowire devices.

Ideally, an optical structure should be designed to minimize absorption for angles greater than θs, particularly near the semiconductor bandgap, which is where the emission is peaked. To emphasize this effect, we consider a smaller radius nanowire (40 nm), which will have increased optical concentration. In order to minimize the loss in photogenerated current, the periodicity is decreased to 200 nm and the nanowire length is set to 2 μm, which is a reasonable thickness for a GaAs cell. Figure 5(c) shows this device whose absorption near the bandgap is limited so that the reverse saturation current density is one order of magnitude smaller than that of the bulk cell (Fig. 5(d)). This nanostructuring leads to the reverse saturation current decreasing from 8.751 × 10−18 to 9.946 × 10−19 A/m2. Although the absorption is also decreased (JL decreased from 362.68 to 237.55 A/m2), the Voc is increased from 1.169 V to 1.214 V, showing an improvement of 45 mV in Voc. This result suggests that nanostructures that incorporate more complexity may yield higher Voc’s without loss in IL.

Discussion

While the overall performance of nanostructured solar cells is still bounded by the SQ limit, one must consider the built-in optical concentration when applying this theory. Recently an InP nanowire solar cell was found to have a Voc in excess of the record InP planar device21,41. This improvement is likely the result of the built-in optical concentration, which leads to higher carrier densities and hence a higher Voc. Although the best devices to date are <14% efficient4,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24, there is great potential for improvement, which could allow nanowire solar cells to exceed 40% solar power efficiency. Here we have shown that besides the possibility of improved carrier collection that has been previously reported42,43,44, another key advantage of nanostructured solar cells over planar ones is that the optical concentration is already built-in, yielding the possibility of higher efficiencies than planar devices.

The main limitations for exploiting these concepts in practical devices lie in minimization of non-radiative recombination and achieving appropriate optical design. Minimizing both surface and bulk non-radiative recombination is important for all PV technologies and great strides have been achieved recently. GaAs has been shown to have an internal luminescence efficiency of >99%, leading to solar cells that operate in the radiative limit45,46, a key requirement for exploiting the concepts discussed in this manuscript. For nanostructured PV, non-radiative recombination is likely dominated by surface recombination. InP has shown excellent promise for nanostructured PV with unpassivated nanowire structures yielding surface recombination velocities as low as 170 cm/s47,48. Finally, implementation of high quality optical structures with the appropriate angular and frequency dependence may be further guided by concepts from metamaterials, metasurfaces and transformation optics, which have previously yielded broadband angular selectivity49,50.

In conclusion, we have used the principle of detailed balance to determine the maximum efficiency for nanostructured photovoltaic devices. Because the principle of detailed balance requires knowledge of the absorption within the structure rather than the detailed geometry or arrangement, any specific nanostructure (regardless of configuration) will be bounded by this limit. The role of the geometry, period, disorder, etc. are all included by considering the absorption spectrum. The ideal nanostructured devices result in an efficiency of 42%, which is equivalent to the result of Shockley and Queisser when considering full optical concentration. This improvement comes strictly from an improvement of the open-circuit voltage and not from an improvement in the current. We have assumed that the cell is limited by radiative emission and is under direct illumination in order to achieve the maximum efficiency limit. As with other forms of optical concentration, the efficiency is reduced if part of the incident illumination is diffuse (e.g. if 25% of the incident light is diffuse, the maximum efficiency is reduced to 38%). For future nanostructured devices to take advantage of these benefits, high quality surface passivation and reduced non-radiative recombination are needed. From an optical design point-of-view, nanostructures should be created that have limited absorption for angles and wavelengths that do not match the incident illumination. When this condition is achieved, new high efficiency nanostructured PV devices will be possible.

Additional Information

How to cite this article: Xu, Y. et al. The generalized Shockley-Queisser limit for nanostructured solar cells. Sci. Rep. 5, 13536; doi: 10.1038/srep13536 (2015).