Abstract
Tailoring the spin orientation at the atomic scale has been a key task in spintronics technology. While controlling the out-of-plane to in-plane spin orientation has been achieved by a precise control of the perpendicular magnetic anisotropy at atomic layer thickness level, a design and control of the in-plane magnetic anisotropy has not yet been well developed. On well aligned atomic steps of a 6° vicinal Cu(001) surface with steps parallel to the [110] axis, we grow Py/Ni overlayer films epitaxially to permit a systematic exploration of the step-induced in-plane magnetic anisotropy as a function of both the Py and the Ni film thicknesses. We found that the atomic steps from the vicinal Cu(001) induce an in-plane uniaxial magnetic anisotropy that favors both Py and Ni magnetizations perpendicular to the steps, opposite to the behavior of Co on vicinal Cu(001). In addition, thickness-dependent study shows that the Ni films exhibit different magnetic anisotropy below and above ~6 ML Ni thickness.
Similar content being viewed by others
Introduction
Engineering the spin orientation at the atomic scale in a magnetic nanostructure has been one of the most important issues in spintronics development. Since the spin orientation in a ferromagnetic crystal is determined by the so-called magnetic anisotropy1,2,3, a design and control of the magnetic anisotropy by atomic engineering has been one of the most challenging topics in nanomagnetism research4,5,6,7.
For out-of-plane to in-plane spin orientation of a magnetic thin film, great success has been achieved by tailoring the perpendicular magnetic anisotropy by controlling the film thickness at atomic layer level8,9. Moreover, many important and interesting phenomena have been discovered such as the stripe10,11,12 and bubble phases in continuous films13 and the topological magnetic skyrmions in patterned films14. In comparison, limited success has been achieved in understanding and tailoring the in-plane spin orientation of a ferromagnetic thin film. In an attempt to engineer the in-plane magnetic anisotropy, atomic steps on vicinal films have been employed to induce in-plane uniaxial magnetic anisotropy15,16,17,18,19,20,21. The general approach to the control of the in-plane magnetic anisotropy has been more or less limited to the modulation of the vicinal surface by various methods. For example, it was shown recently that a direct heating of a vicinal Si(111) can effectively modulate the magnetic anisotropy of an Fe overlayer6 and that microstep- and macrostep-bunched vicinal Si(111) substrates could modulate the Co overlayer magnetic anisotropy very differently22. However, it is unclear on how the vicinal surface exactly modulates the magnetic anisotropy at different film thicknesses7,22.
Noticing that the d electrons in transition metals are very sensitive to their local environment and sometimes even exhibit exotic anisotropy behaviors such as the quantum size effect23,24,25, it is very important and constructive to design a well defined system whose anisotropy can be modulated continually in both the out-of-plane and the in-plane directions as a function of the ferromagnetic film thickness. For this purpose, we fabricated Py/Ni bilayer films on vicinal Cu(001) surface. Ni on Cu(001) has a tetragonal distorted fct structure which carries a volume-type out-of-plane uniaxial anisotropy to result in an in-plane to out-of-plane spin reorientation transition (SRT) with increasing the Ni film thickness26. However, the step-induced in-plane magnetic anisotropy cannot be fully studied because of the limited thickness range below the Ni SRT thickness. For example, Dhesi et al. investigated the SRT of Ni film on vicinal Cu(1 1 32) and found a very peculiar behavior that below the SRT thickness, the Ni magnetization is titled from the surface normal direction with the in-plane component perpendicular to the steps above 5.5 ML and then switches to in-plane direction and parallel to the steps below 5.5 ML27. Thus it has remained as a mystery on the sign of the step-induced magnetic anisotropy in vicinal Ni/Cu(001): is the easy axis parallel to the steps as in the Co/vicinal Cu(001) or perpendicular to the steps?
In this work, we studied Py/Ni bilayer films on vicinal Cu(001) to permit a modulation of the magnetic anisotropy in both the out-of-plane and the in-plane directions. We found that both Py and Ni films on vicinal Cu(001) have a step-induced in-plane magnetic anisotropy that favors the magnetization perpendicular to the steps, which is opposite to the result in vicinal Co/Cu(001) system. Moreover, the step-induced anisotropy has different values below and above ~5–6 ML Ni thickness. Finally, systematic thickness-dependent study allows us to separate the volume and surface contributions to the step-induced magnetic anisotropy. Our result provides a new method for the modulation of the magnetic anisotropy in both the out-of-plane and the in-plane directions which is important to the prospective application in future spintronics devices.
Results
Spin reorientation transition (SRT)
To obtain the Ni SRT thickness as a function of Py thickness, both polar and longitudinal (field perpendicular to the steps) hysteresis loops were measured on Cu/Py/Ni/Cu(001) by scanning the MOKE laser along the Ni wedge at a fixed Py thickness. After finishing a one line scan, the laser beam position was moved to a new position along the Py wedge to change the Py thickness. Then polar and longitudinal MOKE loops were taken again by scanning the MOKE laser beam along the Ni wedge.
Figure 1(a) shows typical polar and longitudinal hysteresis loops of a line scan along the Ni wedge at 6 ML Py thickness (dPy = 6 ML). Below 11 ML Ni thickness (dNi < 11 ML), no polar hysteresis loops were observed. In contrast, the longitudinal MOKE exhibits a square shape hysteresis loop, showing that the Cu/Py(6 ML)/Ni/Cu(001) film has an in-plane magnetization for dNi < 11 ML. Above 11 ML Ni thickness, the polar hysteresis loop develops into a square shape with increasing Ni thickness. Meanwhile, the longitudinal hysteresis loop reverses direction with a much greater magnitude. This behavior indicates a SRT of the Py/Ni magnetization from in-plane to out-of-plane direction as Ni film thickness increases above 11 ML. The reversed longitudinal MOKE loop with a much greater magnitude is due to a polar MOKE signal in the vicinity of the SRT, which was already reported previously in an Fe/Ag(001) system9. The result of Fig. 1(a) shows that Cu/Py(6 ML)/Ni/Cu(001) undergoes a SRT at dNi ≈ 11 ML, which is thicker than the Cu/Ni/Cu(001) SRT thickness of dNi ≈ 10 ML. This is because Py/Cu(001) has an in-plane magnetization so that once the Py and Ni are coupled together the Ni perpendicular magnetic anisotropy in Py/Ni/Cu(001) has to overcome an extra Py in-plane shape anisotropy in order to give a perpendicular magnetization.
To have a systematic thickness-dependent study of the SRT, we plotted the polar remanence of the Py/Ni films in the dPy-dNi thickness plane [Fig. 1(b)]. The SRT character shown in Fig. 1(b) exists for all Py thicknesses studied: the polar MOKE signal develops above a critical Ni thickness as a result of in-plane to out-of-plane SRT. We define a ~5% polar MOKE signal as the practical definition of the SRT point [dashed line in Fig. 1(b)]. Then it is clearly seen that the Ni SRT thickness increases with increasing Py thickness. Similar behavior was also observed in a Co/Ni/Cu(001) system28.
Step-induced in-plane uniaxial magnetic anisotropy in vicinal Cu/Py/Cu(001)
To study the step-induced magnetic anisotropy, we first performed longitudinal MOKE measurements on vicinal Cu/Py(10 ML)/Cu(001) film. For magnetic field perpendicular to the atomic steps, a square shape hysteresis loop was observed with a full remanence. For the field parallel to the atomic steps, the film exhibited a hard axis hysteresis loop with zero remanence [Fig. 2(a)]. The above observation shows that the atomic steps on the vicinal Cu(001) substrate induce a uniaxial magnetic anisotropy in the Py overlayer with the easy magnetization axis perpendicular to the atomic steps. This result is opposite to the vicinal Co/Cu(001) system where the step-induced uniaxial magnetic anisotropy favors the easy magnetization axis parallel to the atomic steps. We then measured the longitudinal MOKE at different Py thicknesses by applying the magnetic field parallel to the step direction. The vicinal Cu/Py/Cu(001) always exhibited the hard axis loops [Fig. 2(b)]. Moreover, we found that the saturation field increases with increasing Py thickness. Note that the saturation field is a measure of the strength of the step-induced magnetic anisotropy, so the increase of the hard axis loop saturation field shows that the step-induced magnetic anisotropy increases with increasing Py film thickness. To understand this behavior, we need to determine quantitatively the surface and volume contribution of the step-induced anisotropies.
To obtain the magnetic anisotropy quantitatively, we performed ROTMOKE measurements on the sample. The in-plane projection of the incident laser beam was set to be parallel to the in-plane hard magnetization axis (parallel to the steps). As the magnetic field H = 200 Oe rotated in the film plane, the ROTMOKE signal picked up the projection of the magnetization along the hard axis [inset of Fig. 3(a)]. Then the angular difference between the magnetic field and the magnetization contains the information of the magnetic anisotropy. Since the Py 4-fold anisotropy is negligibly small, the magnetic anisotropy energy per unit area can be written as
Here H = 200 Oe is the strength of the rotating magnetic field, ϕH and ϕM are the angles of the magnetic field and magnetization with respect to the atomic steps [inset of Fig. 3(a)], and are the surface (including both Py/Cu interfaces) and volume parts of the step-induced uniaxial magnetic anisotropy, respectively. Minimizing eqn. (1) yields the magnetic torque equilibrium equation.
ROTMOKE measures cosϕM as a function of ϕH (5o per step) from which we determine ϕM. Then the torque of H sin(ϕH − ϕM) can be determined in the experiment as a function of ϕM [Fig. 3(a)]. Fitting the experimental data using eqn. (2) yields the red line in Fig. 3(a), which fits the data very well. We repeated the ROTMOKE measurement as a function of Py thickness and plotted the corresponding H2MPydPy in Fig. 3(b), where MPy = 800 Oe and 1.8 Å/ML have been taken for Py. The result shows a pretty good linear dependence as given by eqn. (3). Then fitting the data in Fig. 3(b) yields = −(1.8 ± 0.1) × 10−3 erg/cm2 and = (3.1 ± 0.1) × 104 erg/cm3 for the surface and volume parts of the step-induced magnetic anisotropy.
Step-induced in-plane uniaxial magnetic anisotropy in vicinal Cu/Py/Ni/Cu(001)
After studying the step-induced anisotropy in vicinal Cu/Py/Cu(001) films, we studied the step-induced anisotropy in vicinal Cu/Py/Ni/Cu(001) films. We first measured the longitudinal MOKE hysteresis loops of vicinal Cu/Py(10 ML)/Ni/Cu(001) for the field along the hard axis (parallel to the steps). The saturation field increases with increasing Ni thickness, showing that the Ni film enhances the step-induced uniaxial magnetic anisotropy [Fig. 4(a)]. In other words, there should exist a step-induced uniaxial anisotropy in the Ni film which also favors the easy magnetization axis perpendicular to the atomic steps, the same as in the vicinal Py/Cu(001) film but opposite to the vicinal Co/Cu(001) film. In addition, we notice that the shape of the hysteresis loop in vicinal Cu/Py/Ni/Cu(001) is different from that of vicinal Cu/Py/Cu(001) but similar to the hard axis loop of vicinal Cu/Co/Cu(001)19, showing that the 4-fold anisotropy can no longer be ignored in the vicinal Cu/Py/Ni/Cu(001) system. Then the magnetic anisotropy energy per unit area for the Py/Ni bilayer film will be
Here KS and KV denote surface (including all interfaces) and volume anisotropies and the subscriptions of “2” and “4” denote the uniaxial and 4-fold anisotropies, respectively. The 4-fold anisotropy of Py film is ignored because it is too small. Minimizing eqn. (4) leads to the following equation.
with
From eqn. (6), it is easy to see that at a fixed Ni thickness, H2(MPydPy+MNidNi) should depend on dPy linearly with the linear slope being the Py volume uniaxial anisotropy and vice versa. ROTMOKE measurement was performed on vicinal Cu/Py/Ni/Cu(001) as a function of Py thickness at dNi = 4.8 ML and dNi = 9.0 ML. Figure 4(b) shows the result of the anisotropy field versus Py thickness. The same slope of the two straight lines in Fig. 4(b) shows that remains the same in vicinal Cu/Py/Ni/Cu(001) for Ni between 4.8 ML and 9 ML. Then we conclude that the Ni film consists a step-induced uniaxial anisotropy which favors the magnetization perpendicular to the steps, confirming the hysteresis loop measurement in Fig. 4(a). A linear fitting using eqn. (6) yields = (4.5 ± 0.2) × 104 erg/cm3, where MNi = 490 Oe has been used. This value is greater than the value of = 3.1 × 104 erg/cm3 in vicinal Cu/Py/Cu(001), showing that the Ni underlayer in vicinal Cu/Py/Ni/Cu(001) changes the Py step-induced anisotropy. This is not surprising because Py grown on top of Ni/Cu(001) should be slightly different than Py grown on top of Cu(001) (e.g, strain due to lattice mismatch). The interesting observation is that changes from the value in vicinal Cu/Py/Cu(001) to the value in vicinal Cu/Py/Ni/Cu(001) within 4.8 ML Ni film, suggesting that any structural changes in the Py film due to the Ni underlayer should have occurred within 5 ML Ni thickness. Alternatively, the Ni magnetic anisotropy could/should also undergo a change below and above ~5 ML thickness.
To retrieve the Ni anisotropy in Py/Ni bilayers, we performed ROTMOKE measurement as a function of Ni thickness at different Py thicknesses in the range of 5 ML < dPy < 9 ML where the has a constant value of = 4.5 × 104 erg/cm3. We fit the ROTMOKE data using eqn. (5) by considering both the uniaxial and 4-fold magnetic anisotropies in vicinal Cu/Py/Ni/Cu(001) films. Figure 5(a) shows the results of H2 and H4 from the ROTMOKE data fitting using eqn. (5). Both H2 and H4 increase with increasing Ni thickness. To single out the anisotropy constants of the Ni film from the data, we plot H2(MPydPy + MNidNi)− dPy and H4(MPydPy + MNidNi) as a function of Ni thickness at different Py thicknesses [Fig. 5(b)]. According to eqn. (6) and (7), all curves should collapse into a single straight line with the slope being the volume anisotropy of the Ni film and the intersection of the straight line at dNi = 0 being the surface anisotropy of the Ni film. While Fig. 5(b) indeed shows a universal behavior for all curves, it also shows that the Ni magnetic anisotropies have different values for dNi < ~5 ML and dNi > ~6 ML.
From a linear fitting using eqn. (6) and (7) [red lines in Fig. 5(b)], we obtained the Ni anisotropy constants for dNi < 5 ML and dNi > 6 ML. The result is summarized in Table 1. We do not know the exact reason which causes the different Ni anisotropy constants below and above ~5–6 ML thickness. But this behavior is consistent with our observation that changes from 3.1 × 104 erg/cm3 in vicinal Cu/Py/Cu(001) to 4.5 × 104 erg/cm3 in vicinal Cu/Py/Ni/Cu(001) in the range of 0 < dNi < 4.8 ML. This behavior is also consistent with the result of Ref. 27 which shows that the Ni in-plane component behaves differently below and above ~5.5 ML thickness.
We would like to point out that the Ni magnetic anisotropy is very sensitive to volume strain and temperature29,30,31 as compared to Fe and Co. The different behaviors of the Ni anisotropy below and above ~5–6 ML thickness may be due to its structural strain variation as a function of its film thickness. Obviously, more experimental and theoretical works are needed to fully understand this behavior.
Discussion
Table 1 shows the fitted anisotropy constants (including interface and volume contributions). In Cu/Py/Cu(001) system, the opposite sign of and show that the interface and volume uniaxial anisotropies of the Py film prefer the easy magnetization axis being perpendicular and parallel to the steps, respectively. According to the general Néel’s expression for the effective anisotropy Keff = KV + 2 KS/d Ref. [32], the competition between the interface and the volume anisotropy energies is responsible for the overall effective uniaxial anisotropy induced by the steps and the interfacial contribution should gradually decrease with increasing the Py thickness.
Comparing the volume part of the step-induced uniaxial anisotropy, KV2,Ni has a lower value than for Ni film thinner than 5 ML but a greater value than for Ni film thicker than 6 ML. For Ni film on vicinal Cu (001), it was reported that the Ni in-plane easy axis behave differently, resulting in a peculiar canted spin structure in the 5.5–7 ML thickness range27. Our result is consistent with the above behavior as the Ni step-induced magnetic anisotropy exhibits distinct different values below and above ~6 ML. This behavior is also evident in our and which also exhibit different values below and above ~6 ML Ni thickness. This phenomenon is different from the FeMn/Co/Cu(001) system although the antiferromagnetic FeMn layer induces a change of the Co four fold anisotropy33. It is should be mentioned that Ni film has a fct pseudomorphic growth on Cu(001) with an in-plane tensile strain because of the ~2.5% smaller lattice constant of bulk Ni than bulk Cu. A Ni film on Cu(001) will enlarge its in-plane lattice to that of Cu, leading to an out-of-plane contraction. Because of the special Ni electronic structure34, it is generally believed that a Ni lattice distortion in the out-of-plane direction should modify greatly the Ni magnetic anisotropy. LEED I-V study on Ni/Cu(001) has confirmed that the Ni film indeed contracts in the out-of-plane direction35 However, the experimental result could not further resolve a detailed thickness-dependent Ni lattice spacing at the instrumental limit of ~0.01-0.02 Å. If we trust the theoretical calculation36,37 a 0.01 Å change in the out-of-plane lattice spacing would result in a magnetic anisotropy change of ~20 μeV/atom which corresponds to a change of 6 × 10−2 erg/cm2 for surface anisotropy or a change of 3 × 106 erg/cm3 for volume anisotropy. Both values are 10-100 times greater than the anisotropy change in Table 1. In another word, to account for the surface and volume anisotropy changes in Table 1 below and above 6 ML Ni, the out-of-plane lattice spacing has to be determined at the 0.001–0.0001 Å accuracy which is far beyond current experimental capability.
In summary, we investigated vicinal Cu/Py/Ni/Cu(001) with the atomic steps parallel to the [110] crystal axis. We found that atomic steps of the vicinal surface induce an in-plane uniaxial anisotropy in both Py and Ni films with the easy magnetization axis perpendicular to the steps. ROTMOKE was used to determine the step-induced magnetic anisotropy. By a systematic thickness-dependent study as a function of both Py and Ni thicknesses, we retrieved the anisotropy constants for Py and Ni films in vicinal Cu/Py/Ni/Cu(001). We show that Ni anisotropy behaves differently below and above ~5–6 ML thickness. Our result will provide valuable information for the control of in-plane step-induced magnetic anisotropy in bilayer systems grown on vicinal surfaces.
Method
A 10 mm × 10 mm Cu(001) single crystal disk was polished into a 6° vicinal surface with the steps parallel to the [110] crystalline axis. After cycles of cleaning in an ultrahigh vacuum (UHV) system by Ar ion sputtering at 2 keV and annealing at 600°C, sharp split low energy electron diffraction (LEED) spots were observed indicating the formation of a high quality vicinal Cu(001) surface (Fig. 6). Double wedges of Py and Ni films (Fig. 6) were grown epitaxially at room temperature in vacuum with a pressure below 3 × 10−9 torr. A 3 nm Cu layer was grown on top of the vicinal Py/Co/Cu(001) film to protect the sample from oxidation. The epitaxial growth nature of the Py/Ni films on top of the vicinal Cu(001) was confirmed by the LEED patterns (Fig. 6). Magneto-optical Kerr effect (MOKE) was used to measure the magnetic hysteresis loops of the sample with the magnetic field applied either perpendicular (polar MOKE) or parallel (longitudinal MOKE) to the sample surface. After the MOKE hysteresis loop measurement, the sample was taken out of the UHV chamber and measured using a table top rotation MOKE (ROTMOKE) setup. A detailed description of our ROTMOKE setup was reported previously38. All MOKE and ROTMOKE measurements were performed at room temperature.
Additional Information
How to cite this article: Ma, S. et al. Tailoring the magnetic anisotropy of Py/Ni bilayer films using well aligned atomic steps on Cu(001). Sci. Rep. 5, 11055; doi: 10.1038/srep11055 (2015).
References
Gradmann, U. et al. In-plane magnetic surface anisotropies in Fe(110). Appl. Phys. A 39, 101 (1986).
Wang, D. et al. State-Tracking first-principles determination of magnetocrystalline anisotropy. Phys. Rev. Lett. 70, 869 (1993).
Vaz, C. A. F. Magnetism in ultrathin film structures. Rep. Prog. Phys. 71, 056501 (2008).
Gambardella, P. et al. Ferromagnetism in one-dimensional monatomicmetal chains. Nature 416, 301 (2002).
Bander, M. et al. Ferromagnetism of ultrathin films. Phys. Rev. B 38, 12015 (1988).
Wu, Q. et al. Tuning magnetic anisotropies of Fe films on Si(111) substrate via direction variation of heating current. Sci. Rep. 3, 1547 (2013).
Ye, J. et al. Dertermination of magnetic anisotropy constants in Fe ultrathin film on vicinal Si(111) by anisotropic magnetoresistance. Sci. Rep. 3, 2148 (2013).
Pappas, D. P. et al. Reversible Transition between Perpendicular and In-Plane Magnetization in Ultrathin Films. Phys. Rev. Lett. 64, 3179 (1990).
Qiu, Z. Q. et al. Asymmetry of the Spin Reorientation Transition in Ultrathin Fe Films and Wedges Grown on Ag(100). Phys. Rev. Lett. 70, 1006 (1993).
Allenspach, R. et al. Magnetization Direction Switching in Fe/Cu(100) Epitaxial Films: Temperature and Thickness Dependence. Phys. Rev. Lett. 69, 3385 (1992).
Portmann, O. et al. An inverse transition of magnetic domain patterns in ultrathin films. Nature 422, 701 (2003).
Wu, Y. Z. et al. Magnetic Stripe Domains in Coupled Magnetic Sandwiches. Phys. Rev. Lett. 93, 117205 (2004).
J. Choi, J. et al. DomainWall Formation in NixFe1-x . Phys. Rev. Lett. 98, 207205 (2007).
Li, J. et al. Tailoring the topology of an artificial magnetic skyrmion. Nat. Commun. 5, 4704 (2014).
Berger, A. et al. Symmetry-Induced Uniaxial Anisotropy in Ultrathin Epitaxial Cobalt Films Grown on Cu(1113). Phys. Rev. Lett. 68, 839 (1992).
Chen, J. et al. Surface-Step-Induced Magnetic Anisotropy in Thin Epitaxial Fe Films on W(001). Phys. Rev. Lett. 68, 1212 (1992).
Kawakami, R. K. et al. Symmetry-Induced Magnetic Anisotropy in Fe Films Grown on Stepped Ag(001). Phys. Rev. Lett. 77, 2570 (1996).
Weber, W. et al. Morphology-Induced Oscillations of the Magnetic Anisotropy in Ultrathin Co Films. Phys. Rev. Lett. 76, 1940 (1996).
Kawakami, R. K. et al. Effect of atomic steps on the magnetic anisotropy in vicinal Co/Cu(001). Phys. Rev. B 58, R5924 (1998).
Qiu, Z. Q., Bader, S. D. Symmetry at magnetic surfaces and interfaces. Surf. Sci. 438, 319 (1999).
Bovensiepen, U. et al. Step-induced magnetic anisotropy in vicinal Ni/Cu(001) and its effect on the spin-reorientation transition. Phys. Rev. B 61, 3235 (2000).
Davydenko, A. V. et al. Spatial modulation of in-plane magnetic anisotropy in epitaxial Co(111) films grown on macrostep-bunched Si(111). J. Appl. Phys. 116, 143901 (2014).
Bauer, U. et al. Experimental confirmation of quantum oscillations of magnetic anisotropy in Co/Cu(001). Phys. Rev. B 84, 144433 (2011).
Li, J. et al. Oscillatory Magnetic Anisotropy Originating from QuantumWell States in Fe Films. Phys. Rev. Lett. 102, 207206 (2009).
Dąbrowski, M. et al. Oscillations of the Orbital Magnetic Moment due to d-Band Quantum Well States. Phys. Rev. Lett. 113, 067203 (2014).
Farle, M. et al. Anomalous reorientation phase transition of the magnetization in fct Ni/Cu(001). Phys. Rev. B 56, 5100 (1997).
Dhesi, S. S. et al. Canted spin structures in Ni films on stepped Cu(001). Phys. Rev. B 59, 8408 (1999).
Won, C. et al. Evidence of the oscillatory magnetic anisotropy in Ni/Co/Ni/Cu(100). Phys. Rev. B 67, 174425 (2003).
Schulz, B. et al. Crossover from in-plane to perpendicular magnetization in ultrathin Ni/Cu(001) films. Phys. Rev. B 50, 13467 (1994).
Farle, M. et al. Higher-order magnetic anisotropies and the nature of the spin-reorientation transition in face-centered-tetragonal Ni(001)/Cu(001). Phys. Rev. B 55, 3708 (1997).
Platow, W. et al. Structure of ultrathin Ni/Cu(001) films as a function of film thickness, temperature and magnetic order. Phys. Rev. B 59, 12641 (1999).
Sander, D. The magnetic anisotropy and spin reorientation of nanostructures and nanoscale films. J. Phys.: Condens. Matter. 16, R603 (2004).
Chen, G. et al. Four-fold magnetic anisotropy induced by the antiferromagnetic order in FeMn/Co/Cu(001) system. J. Appl.Phys. 108, 073905 (2010).
Srivastava, P. et al. Modifications of the electronic structure of Ni/Cu(001) as a function of the film thickness. Phys. Rev. B 56, R4398 (1997).
Platow,W et al. Structure of ultrathin Ni/Cu(001) films as a function of film thickness, temperature and magnetic order. Phys. Rev. B 59, 12641 (1999).
Hjortstam, O. et al. Magnetic anisotropy and magnetostriction in tetragonal and cubic Ni. Phys. Rev. B 55, 15026 (1997).
Uiberacker, C. et al. Lattice Relaxation Driven Reorientation Transition in Nin/Cu(100). Phys. Rev. Lett. 82, 1289 (1999).
Li, J. et al. Design of a vector magnet for the measurements of anisotropic magnetoresistance and rotational magneto-optic Kerr effect. Rev. Sci. Instrum. 83, 033906 (2012).
Acknowledgements
Financial support through National Science Foundation DMR-1210167 NRF through the Global Research Laboratory project of Korea is gratefully acknowledged. S. M. and J.D. acknowledge fellowship support from the China Scholarship Council and National Science Foundation of China under Grant Nos. 51271178 and 51331006.
Author information
Authors and Affiliations
Contributions
S.M. and J.D. did the ROTMOKE measurement. A.T. and J.L. built the ROTMOKE setup. C.H., Z.Z. and Z.Q. analyzed the data. S.M. and Z.Q. wrote the paper. All authors participated the result discussion and reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Ma, S., Tan, A., Deng, J. et al. Tailoring the magnetic anisotropy of Py/Ni bilayer films using well aligned atomic steps on Cu(001). Sci Rep 5, 11055 (2015). https://doi.org/10.1038/srep11055
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep11055
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.