Abstract
We present theoretical results on the high-temperature phase stability and phonon spectra of paramagnetic bcc iron which explicitly take into account many-body effects. Several peculiarities, including a pronounced softening of the [110] transverse (T1) mode and a dynamical instability of the bcc lattice in harmonic approximation are identified. We relate these features to the α-to-γ and γ-to-δ phase transformations in iron. The high-temperature bcc phase is found to be highly anharmonic and appears to be stabilized by the lattice entropy.
Similar content being viewed by others
Introduction
The extraordinary magnetic and metallurgical properties of elemental iron (Fe) have attracted the attention of mankind for several thousand years already. In particular, iron is the main ingredient of steel which is one of the most important construction materials of modern civilization1. In this respect we still live in the “iron age”. Iron is also of primary interest for geophysics as the main constituent of the Earth's core2,3,4,5,6,7. Furthermore, iron is perhaps the most famous example of allotropy in metals. Indeed, iron is a very complicated material where magnetic order8,9,10,11,12,13,14,15,16 and correlation effects17,18,19,20,21,22 play an important role. For these reasons the electronic and lattice properties of iron are still far from understood.
Iron has at least four allotropes: the α, γ and δ phases at low and the ε phase at high pressure, respectively. It is particularly remarkable that the low-temperature structure of iron, the ferromagnetic α phase, is not close-packed but body-centered cubic (bcc). This already indicates that iron has highly unusual features. In fact, among the elements iron is characterized by the unique property of having two stable bcc phases: the aforementioned α phase, which is stable below 1185 K and the δ phase which is stable above 1670 K up to the melting curve. Sandwiched in between those two phases is the γ phase (“austenite”) which has a closed-packed face-centered cubic (fcc) structure. It is understood that magnetism (iron is ferromagnetic below the Curie temperature TC ~ 1043 K) stabilizes the low-temperature α phase by compensating for the too low cohesive energy. Indeed, the low-temperature bcc phase does not exist for nonmagnetic Ru and Os, which lie below Fe in the periodic table. Moreover, iron makes a transition to a hexagonal closed-packed (hcp) structure (ε phase) once ferromagnetism is suppressed by pressure. Clearly it is the interplay between magnetism of the electrons and the lattice degrees of freedom which determines the complexity of the low-temperature phase diagram of iron.
At high temperatures, in the absence of ferromagnetic long-range order, the situation is even less clear. In general, polymorphic metals which have both bcc and closed-packed structures (e.g., Fe, Ca, Sr, Ti, Zr, Ce, Pu) are known to melt from the bcc phase. As argued by Zener23, this can be caused by a somewhat lower Debye temperature in a bcc lattice. Namely, the bcc phase has a low-energy T1 phonon [transverse (110)] branch, whose frequencies vanish in the case of pair-wise, nearest-neighbor interatomic interactions. Such a soft-mode behavior is associated with a large amplitude of vibrations. It leads to a high lattice entropy, which lowers the free energy and thereby stabilizes the bcc lattice. This behavior is clearly revealed in prototypical systems with metallic chemical bonds, such as alkali and alkaline-earth metals24, as well as in the high temperature bcc phase of the group 3 (Sc, Y, La) and 4 (Ti, Zr, Hf) metals25. By contrast, the phonon modes in bcc transition metals like Cr, Mo and W, where the valence d-band is almost half-filled and the chemical bond is covalent, are hard. Moreover, these metals are not polymorphic. For a general discussion of the effects of electronic structure on lattice properties of metals and alloys see Ref.26.
It is quite surprising to note that in the case of iron the experimental information about electronic and dynamical lattice properties at high temperatures is still very limited. In fact, to the best of our knowledge results on the lattice dynamical properties of δ iron are presently not available. In particular, soft-mode behavior of the phonon spectra has neither been reported at the α-to-ε phase transition, nor in the γ phase27,28,29. Thus the lattice dynamics, in particular its evolution at high temperatures and near the α-to-γ and γ-to-δ phase transitions in iron, remain unexplored.
An overall explanation of the electronic and lattice properties of iron at high temperatures requires a formalism which can treat both paramagnetic and magnetically ordered states on equal footing and can describe local moments above TC. Therefore conventional band-structure techniques cannot be used to describe the α-to-γ phase transition in paramagnetic iron, although they provide a good quantitative description of the properties of ferromagnetic α iron9,10,11,12,13. By contrast, the structural transition actually occurs at a temperature Tstruc which lies about 150 K above TC. Moreover, these techniques find the bcc phase to be elastically unstable in the absence of magnetization. Today we know20,21 that an improved description of these transitions can only by obtained when the existence of local moments above TC is taken into account.
To clarify these fundamental questions we performed microscopic calculations of the structural phase stability and the phonon spectra of iron within the so-called LDA + DMFT approach30,31,32. It merges ab initio techniques for the calculation of band structures, such as the local density approximation (LDA) or the generalized gradient approximation (GGA), with dynamical mean-field theory (DMFT)33,34,35 – a state-of-the-art computational scheme for the calculation of the electronic structure of strongly correlated materials. This combined approach allows one to compute the properties of correlated materials in both their paramagnetic or magnetically ordered states. Several applications of this scheme have provided very good quantitative descriptions of the electronic, magnetic and structural properties of iron17,18,19,20,21,22. In particular, the LDA + DMFT method implemented with plane-wave pseudopotentials36 has recently been employed to compute the equilibrium crystal structure and phase stability of iron near the α-to-γ phase transition20,21. Electronic correlations were found to be essential for the explanation of the electronic and structural properties of paramagnetic iron. For example, the α-to-γ phase transition was found to occur at ~1.3 TC, i.e., well above the magnetic transition, in agreement with experiment. Moreover, the calculated phonon spectra of iron near the α-to-γ phase transition were also shown to be in good agreement with experiment.
Results
We computed the temperature evolution of the lattice dynamical properties of iron near the α-to-γ and γ-to-δ phase transformations within LDA + DMFT for Coulomb interaction parameters U = 1.8 eV and J = 0.9 eV as obtained by earlier theoretical and experimental estimations37,38. Our calculations of the Curie temperature in bcc Fe yield TC = 1650 K, which is in reasonable agreement with the experimental value 1043 K given the local nature of the DMFT approach32,33,34,35 and the approximate density-density form of the Coulomb interaction22. To extract the phonon frequencies, the dynamical matrix was evaluated using the method of frozen phonons39 implemented within LDA + DMFT. By introducing small displacements of atoms from their equilibrium positions, we determined the phonon frequencies at given q-points. The phonon dispersion curves were obtained by using a standard Born–von Kármán (BvK) force constant model with interactions expanded up to the fifth-nearest neighbor. In the following all results will be presented as a function of the reduced temperature T/TC, where TC is the calculated Curie temperature (1650 K).
Our results for the phonon dispersion curves of iron near the magnetic phase transition temperature TC are shown in Fig. 1. The calculated phonon dispersions exhibit the typical behavior of a bcc metal. The phonon frequencies are overall positive, both in the ferromagnetic and paramagnetic phase. This implies the stability of the bcc lattice structure of iron in accordance with experiment. We also note the remarkably good quantitative agreement between the calculated phonon dispersions of bcc iron and the experimental data28 taken at T ~ TC (a detailed comparison at 1.2 TC was reported earlier21). In the given temperature range the calculated phonon dispersions show only a rather weak temperature-dependence. However, there is an anomaly in the transverse (110) acoustic mode (T1 mode) along the Γ-N branch near the bcc-fcc phase transition temperature at T ~ 1.2 TC. This can be ascribed to a dynamical precursor effect of the bcc-to-fcc phase transition which occurs at Tstruct ~ 1.3 TC in our calculations20.
Next we discuss the lattice dynamics of paramagnetic bcc iron in more detail. Our results (Fig. 2), obtained in the harmonic approximation, clearly indicate that at T ~ 1.4 TC, i.e., above the α-to-γ phase transition temperature, the bcc phase is dynamically unstable. The origin of the instability lies in the T1 mode in the Γ-N direction whose frequency becomes imaginary near the N-point. At the same time other phonon branches remain stable and are weakly temperature dependent near the transition point. At even higher temperatures, T ~ 1.8 TC, in the δ phase, the bcc lattice structure is dynamically unstable in the whole Γ-N branch, again due to the T1 mode, with an additional anomaly near the (2/3,2/3,2/3) point. The latter anomaly may be interpreted as a precursor effect similar to the one occurring at the β-ω transition in Ti and Zr25,40. Therefore our calculations reveal the crucial importance of the T1 phonon mode for the explanation of the structural phase stability of paramagnetic bcc iron, in agreement with the Zener's hypothesis23. Anharmonic lattice effects must be included to obtain a complete description of the lattice dynamics of δ iron. This situation is quite similar to that in the ε phase of Pu, which has a bcc structure and which is dynamically unstable in the harmonic approximation41. It also seems to be the case in other bcc transition metals, such as Sc, Y, La, Ti, Zr, Hf and Th25,42. However, in the δ phase of Fe and the ε phase of Pu the situation is very special since, both, anharmonic lattice and electron-electron correlation effects are highly relevant, making the problem particularly difficult to investigate.
To illustrate the importance of anharmonic effects in bcc iron, we calculated the total energy profiles for the longitudinal (L) and the two transverse (T1 and T2) modes at the N-point. The results are shown in Fig. 3, as a function of the corresponding atomic displacement for three different temperatures. We compare our results with those obtained for the lowest phonon, the transverse (111) mode, of the fcc phase. It is seen that the two bcc phonon modes L and T2 are rigid and do not change across the α-to-γ phase transition. Similarly, the fcc (111) phonon mode is stable and is almost temperature independent. By contrast, the T1 mode is strongly affected by temperature: while it is stable at T ~ 1.2 TC < Tstruc, i.e., below the calculated α-to-γ phase transition temperature, a shallow double-well potential develops at T ~ 1.4 TC > Tstruc, which is responsible for the lattice instability. Our estimate of the phonon free energy, which is based on the method described in Ref. 43, shows that the bcc lattice is favored over the fcc lattice since the corresponding phonon free energy is lower by ~0.007 eV/atom. This, however, is not sufficient to stabilize the bcc phase, since the electronic energy of the fcc phase is substantially (by ~0.03 eV/atom) lower than that of the bcc phase (see Fig. 3b). Therefore the fcc lattice structure is the stable one. At even higher temperatures, T ~ 1.8 TC, the T1 mode becomes strongly anharmonic, with a pronounced double-well structure. It results in a high lattice entropy which lowers the phonon free energy and hence favors the bcc lattice structure over the fcc lattice by ~0.055 eV/atom. This is sufficient to overcome the electronic energy loss of ~0.04 eV/atom (see Fig. 3c) and to stabilize the bcc phase at high temperatures. On the basis of our results we therefore conclude that the high-temperature bcc (δ) phase of iron is stabilized by the lattice entropy, which gradually increases upon heating due to the increasingly anharmonic behavior of the T1 phonon mode.
Our results for the temperature evolution of the lattice dynamics offer a new perspective on the microscopic origin of polymorphism of iron. We find that the T1 transverse (110) phonon mode is responsible for the α-to-γ and γ-to-δ allotropic transformations in iron. Furthermore we predict that this mode continuously softens upon temperature increase – a feature which is typical for simple nonmagnetic metals25,42. For T > Tstruc ~ 1.3 TC the bcc lattice becomes dynamically unstable near the N-point and collapses at ~1.8 TC, at least in the harmonic approximation. By contrast, at temperatures T < Tstruct the phonon modes of bcc iron are relatively rigid and resemble those of non-polymorphic bcc metals such as Cr, Mo, W. The phonon spectra of the fcc (γ) iron show only a rather weak temperature dependence21. For the bcc phase the phonon spectra are strongly affected by temperature, i.e., the phonon frequencies decrease as the temperature is raised. We found that the T1 phonon mode softens at the fcc-to-bcc phase transition, which indicates the importance of anharmonic effects for a correct description of the high-temperature δ phase of iron. Obviously, lattice anharmonicity and electron-electron correlations have to be taken into account simultaneously. This is a great challenge for future research.
During the review process, a detailed experimental study of the lattice dynamical properties of iron was reported by J. Neuhaus et al.45. The authors found a pronounced softening of the [110] transverse (T1) mode and conclude that the high-temperature bcc phase is essentially stabilized by the vibrational entropy. These new experimental findings are completely in line with our theoretical prediction.
Methods
We employed the LDA + DMFT scheme30,31,32 to compute lattice dynamical properties of iron in the temperature range covering the α-to-γ and γ-to-δ phase transitions. This state-of-the-art method combines ab initio density-functional-based techniques, e.g., the local density approximation (LDA) or general gradient approximation (GGA), with dynamical-mean field theory (DMFT) for correlated electrons systems, which describes the quantum dynamics of the many-electron problem exactly but neglects non-local effects. The LDA + DMFT approach allows one to include the effect of electronic correlations on the electronic band structure and phonon properties of correlated materials. To include the electronic correlations we derived an effective low-energy Hamiltonian for the valence Fe sd orbitals. We employed the non-magnetic GGA together with plane-wave pseudo-potentials to construct a basis of atomic centered symmetry constrained Wannier functions for the Fe sd orbitals36. The multi-orbital Hubbard Hamiltonian obtained thereby, which includes the Coulomb repulsion U and Hund's exchange interaction J for the 3 d Fe orbitals, is solved by DMFT using quantum Monte Carlo (QMC) simulations44. To determine the phase stability and lattice dynamics, we calculated the total energy and evaluated the corresponding phonon frequencies using the frozen-phonons method39. The interaction parameters U = 1.8 eV and J = 0.9 eV are assumed to remain constant during the structural transformations. Further technical details about the method used can be found in Ref. 36.
References
Honeycombe, R. W. K. & Bhadeshia, H. K. D. H. Steels: Microstructure and Properties (Butterworth-Heinemann, Oxford, 1995).
Alfè, D., Gillan, M. J. & Price, G. D. The melting curve of iron at the pressures of the Earth's core from ab initio calculations. Nature 401, 462 (1999).
Steinle-Neumann, G., Stixrude, L., Cohen, R. E. & Gülseren, O. Elasticity of iron at the temperature of the Earth's inner core. Nature 413, 57 (2001).
Vočadlo, L. et al. Possible thermal and chemical stabilization of body-centred-cubic iron in the Earth's core. Nature 424, 536 (2003).
Belonoshko, A. B., Ahuja, R. & Johansson, B. Stability of the body-centred-cubic phase of iron in the Earth's inner core. Nature 424, 1032 (2003).
Dubrovinsky, L. et al. Body-Centered Cubic Iron-Nickel Alloy in Earth's Core. Science 316, 1880 (2007).
Tateno, S., Hirose, K., Ohishi, Y. & Tatsumi, Y. The Structure of Iron in Earth's Inner Core. Science 330, 359 (2013).
Hasegawa, H. & Pettifor, D. G. Microscopic Theory of the Temperature-Pressure Phase Diagram of Iron. Phys. Rev. Lett. 50, 130 (1983).
Söderlind, P., Moriarty, J. A. & Wills, J. M. First-principles theory of iron up to earth-core pressures: Structural, vibrational and elastic properties. Phys. Rev. B 53, 14063 (1996).
Dal Corso, A. & de Gironcoli, S. Ab initio phonon dispersions of Fe and Ni. Phys. Rev. B 62, 273 (2000).
Sha, X. & Cohen, R. E. Lattice dynamics and thermodynamics of bcc iron under pressure: First-principles linear response study. Phys. Rev. B 73, 104303 (2006).
Körmann, F. et al. Free energy of bcc iron: Integrated ab initio derivation of vibrational, electronic and magnetic contributions. Phys. Rev. B 78, 033102 (2008).
Stixrude, L. Structure of Iron to 1 Gbar and 40 000 K. Phys. Rev. Lett. 108, 055505 (2012).
Zhang, H., Johansson, B. & Vitos, L. Density-functional study of paramagnetic iron. Phys. Rev. B 84, 140411 (2011).
Körmann, F., Dick, A., Grabowski, B., Hickel, T. & Neugebauer, J. Atomic forces at finite magnetic temperatures: Phonons in paramagnetic iron. Phys. Rev. B 85, 125104 (2012).
Ruban, A. V. & Razumovskiy, V. I. Spin-wave method for the total energy of paramagnetic state. Phys. Rev. B 85, 174407 (2012).
Lichtenstein, A. I., Katsnelson, M. I. & Kotliar, G. Finite-Temperature Magnetism of Transition Metals: An ab initio Dynamical Mean-Field Theory. Phys. Rev. Lett. 87, 067205 (2001).
Katanin, A. A. et al. Orbital-selective formation of local moments in α-iron: First-principles route to an effective model. Phys. Rev. B 81, 045117 (2010).
Glazyrin, K. et al. Importance of Correlation Effects in hcp Iron Revealed by a Pressure-Induced Electronic Topological Transition. Phys. Rev. Lett. 110, 117206 (2013).
Leonov, I., Poteryaev, A. I., Anisimov, V. I. & Vollhardt, D. Electronic Correlations at the α-γ Structural Phase Transition in Paramagnetic Iron. Phys. Rev. Lett. 106, 106405 (2011).
Leonov, I., Poteryaev, A. I., Anisimov, V. I. & Vollhardt, D. Calculated phonon spectra of paramagnetic iron at the α-γ phase transition. Phys. Rev. B 85, 020401 (2012).
Belozerov, A. S., Leonov, I. & Anisimov, V. I. Magnetism of iron and nickel from rotationally invariant Hirsch-Fye quantum Monte Carlo calculations. Phys. Rev. B 87, 125138 (2013).
Zener, C. Elasticity and Anelasticity (University of Chicago Press, Chicago, 1952).
Vaks, V. G., Kravchuk, S. P. & Trefilov, A. V. Anharmonic lattice dynamics of alkali metals. J. Phys. F 10, 2105 (1980).
Petry, W. Dynamical precursors of martensitic transitions. J Phys IV 5, C2–15 (1995).
Katsnelson, M. I., Naumov, I. I. & Trefilov, A. V. Singularities of the electronic structure and pre-martensitic anomalies of lattice properties in β-phases of metals and alloys. Phase Trans. 49, 143 (1994).
Zarestky, J. & Stassis, C. Lattice dynamics of γ-Fe. Phys. Rev. B 35, 4500 (1987).
Neuhaus, J., Petry, W. & Krimmel, A. Phonon softening and martensitic transformation in α-Fe. Physica B 234–236, 897 (1997).
Klotz, S. & Braden, M. Phonon Dispersion of bcc Iron to 10 GPa. Phys. Rev. Lett. 85, 3209 (2000).
Anisimov, V. I., Poteryaev, A. I., Korotin, M. A., Anokhin, A. O. & Kotliar, G. First-principles calculations of the electronic structure and spectra of strongly correlated systems: dynamical mean-field theory. J. Phys. Condens. Matter 9, 7359 (1997).
Lichtenstein, A. I. & Katsnelson, M. I. Ab initio calculations of quasiparticle band structure in correlated systems: LDA++ approach. Phys. Rev. B 57, 6884 (1998).
Kotliar, G. et al. Electronic structure calculations with dynamical mean-field theory. Rev. Mod. Phys. 78, 865 (2006).
Metzner, W. & Vollhardt, D. Correlated Lattice Fermions in d = ∞ Dimensions. Phys. Rev. Lett. 62, 324 (1989).
Georges, A., Kotliar, G., Krauth, W. & Rozenberg, M. J. Dynamical mean-field theory of strongly correlated fermion systems and the limit of infinite dimensions. Rev. Mod. Phys. 68, 13 (1996).
Kotliar, G. & Vollhardt, D. Strongly correlated materials: Insights from dynamical mean-field theory. Phys. Today 57, 53 (2004).
Leonov, I., Korotin, Dm., Binggeli, N., Anisimov, V. I. & Vollhardt, D. Computation of correlation-induced atomic displacements and structural transformations in paramagnetic KCuF3 and LaMnO3 . Phys. Rev. B 81, 075109 (2010).
Steiner, M. M., Albers, R. C. & Sham, L. J. Quasiparticle properties of Fe, Co and Ni. Phys. Rev. B 45, 13272 (1992).
Cococcioni, M. & de Gironcoli, S. Linear response approach to the calculation of the effective interaction parameters in the LDA + U method. Phys. Rev. B. 71, 035105 (2005).
Stokes, H. T., Hatch, D. M. & Campbell, B. J. ISOTROPY (2007), [stokes.byu.edu/isotropy.html], (Date of access:27/02/2014).
Chen, Y., Fu, C.-L., Ho, K.-M. & Harmon, B. N. Calculations for the transverse N-point phonons in bcc Zr, Nb and Mo. Phys. Rev. B 31, 6775 (1985).
Dai, X. et al. Calculated Phonon Spectra of Plutonium at High Temperatures. Science 300, 953 (2003).
Souvatzis, P., Eriksson, O., Katsnelson, M. I. & Rudin, S. P. Entropy Driven Stabilization of Energetically Unstable Crystal Structures Explained from First Principles Theory. Phys. Rev. Lett. 100, 095901 (2008).
Drummond, N. D. & Ackland, G. J. Ab initio quasiharmonic equations of state for dynamically stabilized soft-mode materials. Phys. Rev. B 65, 184104 (2002).
Hirsch, J. E. & Fye, R. M. Monte Carlo Method for Magnetic Impurities in Metals. Phys. Rev. Lett. 56, 2521 (1986).
Neuhaus, J. et al. Role of vibrational entropy in the stabilization of the high-temperature phases of iron. Phys. Rev. B 89, 184302 (2014).
Acknowledgements
We thank Igor Abrikosov, Michael Leitner and Winfried Petry for helpful discussions. This work was partially supported by the Deutsche Forschungsgemeinschaft through TRR 80 (I.L.) and FOR 1346 (A.I.L., D.V.), by the Russian Foundation for Basic Research through Project Nos. 13-02-00050 (V.I.A.) and 13-03-00641 (A.I.P.). M.I.K. acknowledges a support by the Nederlandse Organisatie voor Wetenschappelijk Onderzoek (NWO) via Spinoza Prize.
Author information
Authors and Affiliations
Contributions
I.L., V.I.A. and D.V. conceived and supervised the project. I.L. performed the computations. All authors contributed to the interpretation of the data and to the writing of the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/4.0/
About this article
Cite this article
Leonov, I., Poteryaev, A., Gornostyrev, Y. et al. Electronic correlations determine the phase stability of iron up to the melting temperature. Sci Rep 4, 5585 (2014). https://doi.org/10.1038/srep05585
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep05585
This article is cited by
-
Prediction of the Curie temperature considering the dependence of the phonon free energy on magnetic states
npj Computational Materials (2020)
-
Hydrogen in α-iron: role of phonons in the diffusion of interstitials at high temperature
Scientific Reports (2019)
-
Temperature-dependent phonon spectra of magnetic random solid solutions
npj Computational Materials (2018)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.