Nitrogen fixation is essential for the synthesis of many important chemicals (e.g., fertilizers, explosives) and basic building blocks for all forms of life (e.g., nucleotides for DNA and RNA, amino acids for proteins). However, direct nitrogen fixation is challenging as nitrogen (N2) does not easily react with other chemicals. By dry ball-milling graphite with N2, we have discovered a simple, but versatile, scalable and eco-friendly, approach to direct fixation of N2 at the edges of graphene nanoplatelets (GnPs). The mechanochemical cracking of graphitic C−C bonds generated active carbon species that react directly with N2 to form five- and six-membered aromatic rings at the broken edges, leading to solution-processable edge-nitrogenated graphene nanoplatelets (NGnPs) with superb catalytic performance in both dye-sensitized solar cells and fuel cells to replace conventional Pt-based catalysts for energy conversion.
Nitrogen (N2) fixation is essential for the manufacture of fertilizer and explosives (e.g., gunpowder, TNT) as well as the biosynthesis of basic building blocks for all forms of life (e.g., nucleotides for DNA and RNA, amino acids for proteins)1. However, N2, the most abundant constituent in air, is normally considered to be inert diatomic gas due to the extremely strong triple bond. As a result, there are only a few of chemical/biological processes to convert the nitrogen gas into other compounds. While nitrogen is reduced into ammonia in the root nodules of plants2, the Haber process to convert nitrogen into ammonia involves the use of an iron oxide (Fe3O4) catalyst in the presence of hydrogen under extremely harsh conditions of about 500°C and 200 atm3. Likewise, graphite with the planar layered structure is the most thermodynamically stable form of carbon allotropes. Hence, it is an extreme challenge for the C−N bond formation directly from graphite and N2. Based on our recent work on the direct C−C bond formation between graphite and carbon dioxide (CO2) by dry ball-milling in a sealed crusher4, we demonstrated in the present study the direct N2 fixation at the broken edges of graphitic frameworks by dry ball-milling graphite in the presence of N2 gas. The nature of the edge-functionalization by the dry ball-milling has been amply established in our previous study4,5.
On the other hand, the search for economically viable alternatives to fossil fuels has attracted even increased attention among energy communities due to the continuously increasing energy price and global warming. Solar cells (SCs) and fuel cells (FCs) are considered to be promising alternatives. Although platinum (Pt)-based electrodes have been known to be the most efficient catalysts for dye-sensitized solar cells (DSSCs)6 and proton exchange membrane fuel cells (PEMFCs)7, they are too expensive and too susceptible to aggregation8 and poisoning impurities9 for practical applications. Recently, much effort has been devoted to reduce or replace Pt-based electrodes. In particular, heteroatom-doped carbon-based materials, such as carbon black10, carbon nanoparticles11, carbon nanotubes12,13 and graphene nanoplatelets14,15,16,17, have been intensively studied as metal-free catalysts. However, the commonly used chemical vapor deposition (CVD)18 and/or Hummers' methods19 for the production of carbon nanotubes and graphene are either too expensive for practical applications or involving environmentally hazardous reagents. Therefore, the full potential of these carbon-based metal-free catalysts is hard to achieve without scalable production at low cost, though the basic catalytic mechanism has been established20. The large quantity of the edge-nitrogenated graphene nanoplatelets (NGnPs) produced through such a simple, low-cost, and eco-friendly ball-milling process were further demonstrated to be effective metal-free catalysts for the replacement of precious Pt-based catalysts in DSSCs and PEMFCs for energy conversion. Therefore, the approach developed in this study can be regarded as a versatile technique toward multifunctional carbon nanomaterials of practical significance.
As schematically shown in Fig. 1a, the ball-milling-induced direct nitrogen fixation at the broken edges of graphitic frameworks involves the breakage of large grain size of graphite (Fig. 1b) into small ones (Fig. 1c). The cleavage of graphitic C−C bonds by ball-milling created active carbon species to react with nitrogen, as shown in Fig. S1 (Electronic Supplementary Information, ESI). Thermodynamically, the most preferred edge formation of NGnPs is to maintain the aromaticity. The calculated binding energies (δE) of nitrogen onto the zigzag-shaped and armchair-shaped broken edges were −2.50 eV/N2 (−57.65 kcal/N2 mol) (Fig. 1d) and −1.96 eV/N2 (−45.20 kcal/N2 mol) (Fig. 1e), respectively, indicating an exothermic (spontaneous) reaction to form nitrogenated aromatic rings at the broken edges. Both aromatic 5-membered pyrazole and 6-membered pyridazine rings could form at the edges of NGnPs via the zigzag and armchair cracking, respectively (Fig. S1). The unreacted residual active carbon species could be terminated by air moisture upon opening the lid as judged by violent sparkling (Supplementary Video), leading to the formation of some oxygenated groups at the edges (Figs. 1a and S1). The available number of active carbon atoms at the broken edges was calculated to exponentially increase as an average grain size reduces (Fig. S2, ESI for detailed calculation). This leads to high nitrogen content at the edges, though not all active carbon atoms could react with nitrogen.
The corresponding TEM images given in Figs. S3a–S3c clearly show relatively small and uniform NGnPs with a round shape compared with starting large graphite flake (Fig. 1b). Fig. S3b reveals the edge-stripes associated with a few graphitic layers of a high crystallinity. These results, together with a dramatic increase (39 times) in the Brunauer-Emmett-Teller (BET) surface area of NGnPs (Table S1), indicate an effective and spontaneous delamination of the starting graphite into small GnPs even in the solid state by dry ball-milling. Dark field TEM image also shows similar morphology (Fig. S3c) with carbon- (Fig. S3d), nitrogen- (Fig. S3e) and oxygen-mappings (Fig. S3f) clearly showing the effective incorporation of nitrogen into the resultant NGnPs.
Elemental analyses (EA) indicate that the starting graphite has a carbon content of 99.64 wt% and oxygen content of 0.13 wt% from physisorption (Table S2)21. The resultant NGnPs have a decreased carbon content of 70.67 wt% and a high nitrogen content of 14.84 wt% (equivalent to a carbon/nitrogen atomic ratio of 5.6, see Table S2), assuring that significant amount of nitrogen has been fixed at the edges of NGnPs via the mechanochemical reaction of graphite with the inert nitrogen (Figs. 1a and S1). In addition, hydrogen and oxygen contents as much as 0.79 and 7.43 wt%, respectively, were also observed arising from the remnant active carbon species, which reacted with air moisture to introduce oxygenated groups.
Fourier transform infrared spectrum of NGnPs evidently shows strong aromatic C−N stretching peak at 1400 cm−1 and C = O stretching peak at 1624 cm−1 (Fig. S4a), implying the presence of nitrogen-containing aromatic rings and carboxylic acid groups, respectively. In addition, the strong peak at 3400 cm−1 is attributable to the hygroscopic nature of NGnPs and crystal water associated with KBr used for the specimen preparation. NGnPs also display sp2 and sp3 C−H peaks at around 2927 cm−1 associated with defects created during ball-milling4. However, the corresponding spectrum for the starting graphite shows only a weak band at 1632 cm−1 characteristic of the vibration mode of adsorbed water molecules22.
The NGnP powder was further characterized by Raman spectroscopy. As expected, the starting graphite showed the G and 2D bands at 1585 and 2722 cm−1, respectively (Fig. S4b), with undetectable edge distortion and structural defects, and hence the ratio of the D- to G-band intensity equals zero (ID/IG = 0.0). In contrast, NGnPs exhibited a broad and strong D band over 1364 cm−1 with the ID/IG ratio of 1.0 (Fig. S4b), indicating the grain size reduction by mechanochemical cracking (see Fig. 1c) and significant edge distortion by edge-nitrogenation (see Figs. 1a and S1).
TGA thermogram of the pristine graphite displays negligible weight loss up to 900 °C in nitrogen (Fig. S4c and Table S3). However, the NGnPs showed gradual weight loss up to 600 °C, followed by a dramatic weight loss at around 723 °C. Due to the hygroscopic and polar natures of pyrazole and pyridazine rings at the NGnP edges, the initial weight loss could be originated from bound moisture (H2O), hydrochloric acid (HCl, see Experimental Section) and oxygenated groups23. The weight loss at 723 °C could be attributed to the loss of relatively much stable edge-heterocyclic rings (see Figs. 1a and S1). The observed gradual weight loss for NGnPs, unlike the stepwise weight loss for GO24, suggests the presence of strong inter-sheet interactions (e.g., polar interaction and H-bonding) between some of the edge-oxygenated groups to alter their decomposition temperature depending on their specific location along the edges of NGnPs. The much higher stepwise decomposition temperature (~723 °C) for NGnPs than that (~165 °C) for GO indicates a significantly improved overall thermal stability for the NGnPs due, most probably, to the edge-selective functionalization in NGnPs without basal plane distortion.
XRD diffraction pattern for the starting graphite shows a strong  peak at 26.5° corresponding to a layer-to-layer d-spacing of 0.34 nm (Fig. S4d)25. Compared with the starting graphite, the NGnPs displayed only a very weak  peak (less than 0.1% intensity) centered at 25.6° (Fig. S4d, inset), indicating the occurrence of delamination of the highly edge-functionalized graphite into a few layer graphene nanoplatelets (GnPs) even in the solid state during the ball-milling and workup processes.
Further evidence for the presence of nitrogen at the edges of NGnPs comes from the XPS spectroscopic measurements. As expected, the starting graphite showed only a pronounced C 1s peak at 284.3 eV (Fig. 2a) with a very weak, but noticeable, O 1s band at ~532 eV attributable to the presence of a trace amount of physically adsorbed oxygen21. In addition to the C 1s and O 1s peaks, NGnPs showed the characteristic N 1s peak at 399 eV. High-resolution XPS spectra with curve fittings for the C 1s (Fig. 2b), O 1s (Fig. 2c), and N 1s (Fig. 2d) peaks showed that the aromatic C−N in pyrazole (pyrrolic−N) and pyridazine (pyridinic−N) rings are the dominant N components in NGnPs. It is noteworthy that the ratio of pyrazole (5N)/pyridazine (6N) nitrogen is 2.9 (Fig. 2d and Table S3), implying that zigzag unzipping is major process (cf. Fig. S1). Furthermore, XPS measurements were performed on the NGnPs having thermally annealed at 400 (below 723 °C) and 1000 °C (above 723 °C) for 30 min under argon atmosphere to assure the origins of the weight losses observed in TGA (see Fig. S4c). The XPS survey of the heat-treated NGnPs at 400 °C shows no obvious change in the intensities of both O 1s and N 1s peaks (Fig. S5 and Table S3), implying that nitrogen atoms were covalently incorporated into aromatic rings. For the NGnPs heat-treated at 1000 °C, the intensities of both the O 1s and N 1s peaks were dramatically decreased (Fig. S6 and Table S3). Therefore, the early gradual weight loss observed in the TGA measurements should be related to the unbound volatile substances, due to hygroscopic and polar natures of NGnPs, whereas the corresponding weight loss at 723 °C is due to the loss of relatively stable edge-heterocyclic rings. Interestingly, the ratios of 5N/6N nitrogen were gradually reduced from 2.9 to 2 and 1.5 for the NGnPs heat-treated at 400 and 1000 °C, respectively, suggesting that the 5-membered pyrazole ring is less stable than the 6-membered pyridazine ring (Figs. 2d, S5d, S6d and Table S3). Overall, the XPS results are in accordance with the FT-IR (see Fig. S4a) and TGA results (see Fig. S4c), supporting the mechanism shown in Figs. 1a and S1.
The grain size reduction for an entropic gain (see Figs. 1b and 1c) and the edge-selective functionalization (nitrogenation and subsequent oxygenation) for an enthalpic enhancement could greatly improve solubility of the NGnPs. Indeed, NGnPs were found to be readily dispersible not only in polar protic solvents, such as neutral water, basic water (containing ammonium hydroxide), methanol and isopropyl alcohol, but also polar aprotic solvents, including acetone, N,N-dimethylacetamide (DMAc), N,N-dimethylformamide (DMF) and N-methyl-2-pyrrolidone (NMP) (Fig. S7). Among all the solvents tested, DMAc was found to be the best for dispersing NGnPs into a stable dispersion with similar Zeta-potential values of −42.4 and −31.9 mV at the concentrations of 0.02 and 0.10 mg/mL (Figs. S7c, S7d and Table S4), respectively. It is well known that a Zeta-potential value either more negative or positive than ±30 mV is sufficient to ensure good dispersion stability via charge repulsion26.
Having assured the structure and solubility of NGnPs, we further investigated their applications as electrode materials for energy conversion in dye-sensitized solar cells (DSSCs) and fuel cells (FCs). To start with, we performed density functional calculations, using the Vienna Ab initio Simulation Package (VASP)27,28, to analyze the stability and electronic structure of the nitrogenated edges. The plane-wave basis set with an energy cut-off of 400 eV, and the PBE-type gradient-corrected exchange-correlation potential were employed29. The passivation of the active carboradicals with the uncleaved N2 resulted in 5-membered pyrazole (Fig. 3a) and 6-membered pyridazine (Fig. 3c) rings at the zigzag- and armchair-shaped broken edges, respectively. As shown in Figs. 3b and 3d, the lone-pair states of nitrogen in-plane orbitals constituted the distinctive edge-localized bands just below the Fermi level. More remarkably, however, the π states of graphene are well preserved including the nitrogen pz-orbitals in the conjugated networks. These unique edge-localized band structures, in conjunction with the undamaged basal plane of NGnPs, can lead to advantageous catalysts that surpass the performance of Pt for DSSC and FC applications described below.
For construction of DSSCs, a uniform NGnP film on fluorine (F)-doped tin oxide (SnO2, FTO)/glass was deposited by an electrostatic spray (e-spray) deposition technique from an NGnPs dispersion in 2-propanol (Fig. S8a). SEM images of the bare FTO (Fig. S8b) and NGnP deposited FTO (NGnP-FTO) (Fig. S8c) exhibit different surface morphologies. DSSC with O-alkylated-JK-225-sensitizer30 and HC-A as a coadsorbent31 was fabricated using the resultant NGnP-FTO as a counter electrode (CE). For comparison purpose, DSSC with Pt-FTO CE was also fabricated. As judged by the peak-to-peak separations (EPP) and current densities, the cyclic voltammograms (CV) of NGnP-FTO electrode for the Co(bpy)33+/2+ redox couple showed very similar curve shape with apparently much higher electrocatalytic activity than that of the Pt-FTO electrode (Fig. S9a). In addition, the oxidation peak of NGnP-FTO CE located at less positive potential than that of the Pt-FTO CE electrode, implying better electrocatalytic performance for the former. The higher current density observed for the NGnP-FTO CE with respect to the Pt-FTO CE could be attributed to an efficient charge transfer resulted from the sufficient nitrogen doping (~15% by EA, see Table S2).
On the basis of promising CV results (Fig. S9a), the electrocatalytic activities of the sample electrodes were further examined by electrochemical impedance spectroscopy (EIS) using symmetrical dummy cells (Fig. S9b)32. The EIS results could be fitted by using a Randles-type circuit (Fig. 4a), where RS is the Ohmic serial resistance, RCT is the charge transfer resistance at the interface between the electrode surface and the electrolyte, ZW is the Nernst diffusion impedance in the bulk electrolyte solution between the two identical electrodes, and CPE is a constant phase element describing the deviation from the ideal capacitance due to the surface roughness of the electrodes33. As seen in Fig. 4b, both impedance spectra of NGnP and Pt exhibited two distinct semicircles, while semicircles in between them at low frequency regions are no significant difference, e.g., diffusion coefficients of Co(bpy)33+ in the NGnP- and Pt-FTO dummy cells were almost similar values, which were found to be 4.5 × 10−6 and 3.2 × 10−6 cm2/s, respectively, and other EIS parameters were summarized in Table S5. The result implies that ionic diffusion in the bulk electrolyte solution is independent of the electrodes (i.e., this parameter is invariant with the electrocatalytic activities of the electrodes). However, the RCT of the NGnP-FTO is lower than that of the Pt-FTO. The result provides strong evidence that the intrinsic catalytic activity of the NGnP-FTO is much higher than that of the Pt-FTO.
On the basis of the in-depth evaluation of the NGnP CE described in Fig. S9 and corresponding explanation, we further investigated the photocatalytic activities of the NGnP electrodes as the CE in actual devices in Co(bpy)3-mediated solar cells. The NGnP-based DSSC outperformed its Pt counterpart (Fig. 4c and Table S6). The Pt-based DSSC exhibited a short circuit current (Jsc) of 14.113 mA/cm2, open circuit voltage (Voc) of 886 mV, fill factor (FF) of 70.8%, and an overall power conversion efficiency (PCE) of 8.85%. The DSSC with the NGnP-based DSSC showed an even higher Voc of 890 mV, FF of 74.1% and PCE of 9.34%, but a similar Jsc of 14.162 mA/cm2. On the basis of the EIS measurements (Fig. S10a) and curve fittings with an equivalent circuit (Fig. S10b), the RCT value of the DSSC with the NGnP-FTO CE is much lower than that of Pt-FTO CE (Table S7), and it might allow for an increase in FF of DSSC. Clearly, therefore, the NGnP CE with a higher electrocatalytic activity, less RCT and better stability outperformed the Pt CE in DSSCs.
To investigate the electrocatalytic activity of NGnPs for oxygen reduction in fuel cells (FCs), we further measured the reduction capability of the NGnPs on glassy carbon (GC) in N2- and O2-saturated alkaline electrolytes (0.1 M aq. KOH solution). The pristine graphite and commercially available Pt/C (Vulcan XC-72R) with the same mass loadings on GC were also measured as references. While the NGnP/GC electrode showed featureless CV in the N2-saturated 0.1 M aq. KOH solution (Fig. 4d), it exhibited an obvious oxygen reduction peak in the corresponding O2-saturated electrolyte (Fig. 4e). The pristine graphite showed a single cathodic reduction peak at −0.43 V with a current density of −0.19 mA cm−2 in the O2-saturated 0.1 M aq. KOH solution. The corresponding cathodic reduction peak for the NGnPs was positively shifted to −0.28 V with a current density of −0.54 mA cm−2. The Pt/C exhibited a single cathodic reduction peak at −0.10 V with a current density of −0.52 mA cm−2. The current density from NGnP is over 2.8 times that of the pristine graphite and comparable to that of Pt/C. Furthermore, the NGnP electrode has high capacitances of 126.6 and 161.3 F g−1 with superb cycle stabilities in both N2− and O2−saturated electrolytes, respectively (Figs. S11–S14 and Table S8), which can be attributed to the relatively high BET surface area (Table S1) and structural stability of NGnPs (see Fig. S4c).
To gain further study the kinetics of the NGnP-catalyzed ORR process, the rotating disk electrode (RDE) measurements were performed in an O2-saturated, 0.1 M aq. KOH solution at various rotating speeds and a constant scan rate of 0.1 V s−1. As shown in Figs. S14a–14c, the diffusion current densities increased with increasing the rotating rates, while the onset potentials remained almost constant. The number of electron transfers (n) per O2 molecule involved in the ORR process can be calculated from the slope of the Koutecky-Levich equation (see Experimental section in ESI) (Figs. S14d–14f). As summarized in Fig. S15 and Table S9, while the number of transferred electrons for the pristine graphite is close to the classical two-electron process (n ~ 2.0), the ORR processes at the NGnP and Pt electrodes are an ideal four-electron process (n ~ 4.0). Evidently, therefore, the edge-nitrogenation played an important role to significantly improve the ORR performance of NGnPs (Table S10).
In summary, we have developed a simple and eco-friendly ball-milling process to efficiently exfoliate the pristine graphite directly into edge-nitrogenated graphene nanoplatelets (NGnPs). A plausible reaction mechanism for the direct nitrogen fixation (C-N bond formation) by ball-milling process in the presence of nitrogen was proposed and confirmed by various microscopic and spectroscopic measurements. The resultant NGnPs were demonstrated to be highly dispersible in various polar solvents suitable for solution processes. The solution-cast NGnP electrodes exhibited superior catalytic properties in DSSCs and FCs with respect to the precious Pt counterparts. Hence, direct nitrogen fixation developed in this study using ball-milling technique could be regarded as a general approach toward low-cost, mass production of NGnPs for multifunctional materials and devices applications.
Preparation of NGnPs
NGnPs were prepared by ball-milling the pristine graphite flake in a planetary ball-mill machine (Pulverisette 6, Fritsch) in the presence of nitrogen (N2). The pristine graphite (5.0 g, Alfa Aesar, natural graphite, 100 mesh (< 150 μm), 99.9995% metals basis, Lot#14735) was placed into a stainless steel ball-mill capsule (500 mL) containing stainless steel balls (500.0 g, diameter 5 mm). The capsule was sealed and charged with N2 (8 bar of cylinder pressure) after five charging-discharging cycles and then it was fixed in the planetary ball-mill machine and agitated at 500 rpm for 48 h. The resultant product was Soxhlet extracted with methanol and 1 M aq. HCl solution to get rid of metallic impurities, if any. Further repeated treatments with ethylenediaminetetraacetic acid (EDTA), concentrated ammonium hydroxide (NH4OH) and 1 M aq. HCl solution were carried until there is no metallic residue detected by XPS. Final product was freeze-dried at −120°C under a reduced pressure (0.05 mmHg) for 48 h to yield 5.67 g (at least 0.67 g N2 uptake) of dark black powder, implying the occurrence of nitrogen-fixation to the ball milled graphite.
This research was supported by World Class University (WCU), US-Korea NBIT, Mid-Career Researcher (MCR), Converging Research Center (CRC) and Basic Research Laboratory (BRL) programs through the National Research Foundation (NRF) of Korea funded by the Ministry of Education, Science and Technology (MEST), US Air Force Office of Scientific Research through Asian Office of Aerospace R&D (AFOSR-AOARD), and AFOSR (FA9550-12-1-0037, FA-9550-12-1-0069).
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 3.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/3.0/