Abstract
Metal halide perovskite materials are an emerging class of solution-processable semiconductors with considerable potential for use in optoelectronic devices1,2,3. For example, light-emitting diodes (LEDs) based on these materials could see application in flat-panel displays and solid-state lighting, owing to their potential to be made at low cost via facile solution processing, and could provide tunable colours and narrow emission line widths at high photoluminescence quantum yields4,5,6,7,8. However, the highest reported external quantum efficiencies of green- and red-light-emitting perovskite LEDs are around 14 per cent7,9 and 12 per cent8, respectively—still well behind the performance of organic LEDs10,11,12 and inorganic quantum dot LEDs13. Here we describe visible-light-emitting perovskite LEDs that surpass the quantum efficiency milestone of 20 per cent. This achievement stems from a new strategy for managing the compositional distribution in the device—an approach that simultaneously provides high luminescence and balanced charge injection. Specifically, we mixed a presynthesized CsPbBr3 perovskite with a MABr additive (where MA is CH3NH3), the differing solubilities of which yield sequential crystallization into a CsPbBr3/MABr quasi-core/shell structure. The MABr shell passivates the nonradiative defects that would otherwise be present in CsPbBr3 crystals, boosting the photoluminescence quantum efficiency, while the MABr capping layer enables balanced charge injection. The resulting 20.3 per cent external quantum efficiency represents a substantial step towards the practical application of perovskite LEDs in lighting and display.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Yang, W. S. et al. Iodide management in formamidinium-lead-halide-based perovskite layers for efficient solar cells. Science 356, 1376–1379 (2017).
Ha, S.-T., Shen, C., Zhang, J. & Xiong, Q. Laser cooling of organic–inorganic lead halide perovskites. Nat. Photon. 10, 115–121 (2016).
Ning, Z. et al. Quantum-dot-in-perovskite solids. Nature 523, 324–328 (2015).
Yuan, M. et al. Perovskite energy funnels for efficient light-emitting diodes. Nat. Nanotechnol. 11, 872–877 (2016).
Xiao, Z. G. et al. Efficient perovskite light-emitting diodes featuring nanometre-sized crystallites. Nat. Photon. 11, 108–115 (2017).
Cho, H. et al. Overcoming the electroluminescence efficiency limitations of perovskite light-emitting diodes. Science 350, 1222–1225 (2015).
Zhang, L. et al. Ultra-bright and highly efficient inorganic based perovskite light-emitting diodes. Nat. Commun. 8, 15640 (2017).
Wang, N. N. et al. Perovskite light-emitting diodes based on solution-processed self-organized multiple quantum wells. Nat. Photon. 10, 699–704 (2016).
Yang, X. et al. Efficient green light-emitting diodes based on quasi-two-dimensional composition and phase engineered perovskite with surface passivation. Nat. Commun. 9, 570 (2018); correction 9, 1169 (2018).
Seino, Y., Inomata, S., Sasabe, H., Pu, Y. J. & Kido, J. High-performance green OLEDs using thermally activated delayed fluorescence with a power efficiency of over 100 lm W(-1). Adv. Mater. 28, 2638–2643 (2016).
Di, D. et al. High-performance light-emitting diodes based on carbene-metal-amides. Science 356, 159–163 (2017).
Aizawa, N. et al. Solution-processed multilayer small-molecule light-emitting devices with high-efficiency white-light emission. Nat. Commun. 5, 5756 (2014).
Dai, X. et al. Solution-processed, high-performance light-emitting diodes based on quantum dots. Nature 515, 96–99 (2014).
Tan, Z. K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nanotechnol. 9, 687–692 (2014).
Wei, Z. et al. Solution-processed highly bright and durable cesium lead halide perovskite light-emitting diodes. Nanoscale 8, 18021–18026 (2016).
Li, X. et al. CsPbX3 quantum dots for lighting and displays: room-temperature synthesis, photoluminescence superiorities, underlying origins and white light-emitting diodes. Adv. Funct. Mater. 26, 2435–2445 (2016).
Kim, Y. H. et al. Highly efficient light-emitting diodes of colloidal metal-halide perovskite nanocrystals beyond quantum size. ACS Nano 11, 6586–6593 (2017).
Protesescu, L. et al. Nanocrystals of cesium lead halide perovskites (CsPbX(3), X = Cl, Br, and I): novel optoelectronic materials showing bright emission with wide color gamut. Nano Lett. 15, 3692–3696 (2015).
Xing, J. et al. High-efficiency light-emitting diodes of organometal halide perovskite amorphous nanoparticles. ACS Nano 10, 6623–6630 (2016).
de Mello, J. C., Wittmann, H. F. & Friend, R. H. An improved experimental determination of external photoluminescence quantum efficiency. Adv. Mater. 9, 230–232 (1997).
Yang, Y. et al. High-efficiency light-emitting devices based on quantum dots with tailored nanostructures. Nat. Photon. 9, 259 (2015).
Lee, S. et al. Growth of nanosized single crystals for efficient perovskite light-emitting diodes. ACS Nano 12, 3417–3423 (2018).
Yan, F. et al. Highly efficient visible colloidal lead-halide perovskite nanocrystal light-emitting diodes. Nano Lett. 18, 3157–3164 (2018).
Chin, X. Y. et al. Self-assembled hierarchical nanostructured perovskites enable highly efficient LEDs via an energy cascade. Energy Environ. Sci. http://dx.doi.org/10.1039/c8ee00293b (2018).
Song, J. et al. Room-temperature triple-ligand surface engineering synergistically boosts ink stability, recombination dynamics, and charge injection toward EQE-11.6% perovskite QLEDs. Adv. Mater. 30, e1800764 (2018).
Saliba, M. et al. Incorporation of rubidium cations into perovskite solar cells improves photovoltaic performance. Science 354, 206–209 (2016).
Chen, W. et al. Efficient and stable large-area perovskite solar cells with inorganic charge extraction layers. Science 350, 944–948 (2015).
Zhao, L. et al. Electrical stress influences the efficiency of CH3 NH3 PbI3 perovskite light emitting devices. Adv. Mater. 29, 1605317 (2017).
Acknowledgements
This work was supported by the Scientific Research Funds of Huaqiao University (600005-Z16J0038) and the National Natural Science Foundation of China (U1705256). Z.W. thanks Y. Wang (Technical Institute of Physics and Chemistry, Chinese Academy of Sciences) and J. Wang (Institute of Advanced Materials, Nanjing Tech University) for helpful discussions on how to accurately measure the performance of perovskite LED devices. Z.W. also thanks S. Yang (Hong Kong University of Science and Technology) for carrying out time-of-flight/secondary ion mass spectrometry (TOF-SIMS) analysis. Q.X. acknowledges support from the Singapore National Research Foundation through an NRF Investigatorship award (NRF-NRFI2015-03); and from the Ministry of Education via an AcRF Tier2 grant (MOE-2015-T2-1-047) and Tier1 grants (RG 113/16 and RG 194/17). This publication is based in part on work supported by the Canada Research Chairs program, the Natural Sciences and Engineering Research Council of Canada, and the US Department of the Navy, Office of Naval Research (grant N00014-17-1-2524).
Author information
Authors and Affiliations
Contributions
Z.W., Q.X. and E.H.S. conceived the idea. K.L., J.X. and W.Z. prepared the samples and carried out optical spectroscopy characterizations. L.X. and Y.L. carried out XPS, AFM and some other materials characterizations. K.L., J.L., D.Z., C.Y., W.L. and X.L. fabricated and characterized perovskite LED devices. Z.W. supervised the fabrication and characterization of perovskite LEDs. L.N.Q., X.G., J.K. and F.P.G.A. assisted with device fabrication, measurements and manuscript writing. K.L., Z.W., Q.X. and E.H.S. carried out data analysis and wrote the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
Extended Data Fig. 1 Emission properties and formation mechanism of mixture perovskites.
a, Photoluminescence spectra of single-layered CsPbBr3, bilayered CsPbBr3/MABr, and quasi-core/shell-structured mixture-1.0 films. b, Photoluminescence spectra of various mixture perovskite films with different amounts of MABr. The numbers in the key indicate the molar ratio of MABr to CsPbBr3. c, Photograph of mixture perovskite films under ultraviolet light. d, The formation process of the CsPbBr3/MABr quasi-core/shell structure. The yellow areas in the left panel denote the precursor solution.
Extended Data Fig. 2 SEM and TEM images of the mixture-1.0 films.
a, Cross-sectional SEM images of the as-prepared mixture-1.0 film at different magnifications. b, Cross-sectional TEM images (greyscale) and elemental mapping images (in colour) of the mixture-1.0 film. The sample was prepared using a focused ion beam, and the top C and Pt layers were predeposited to protect the perovskite film.
Extended Data Fig. 3 Comparison of CsPbBr3, MAPbBr3 and mixture-1.0 perovskite films.
a, Estimation of trap-state density using the space-charge-limited current method, obtained using dark I–V curves of perovskite devices with the structure ITO/perovskite/Au. VTFL, trap-filled limiting voltage. b, Photographs of a pristine mixture-1.0 perovskite film (left) and a film treated by washing with IPA (right; to remove the MABr capping layer) under ultraviolet light. c, Photograph of the three perovskite films under ultraviolet light. d, Ultraviolet–visible absorbance spectra of the CsPbBr3 film and different mixture films. The black arrows indicate the disappearance of the exciton peak from the CsPbBr3 sample to the mixture-1.0 sample. e, f, Photoluminescence spectra (e) and time-resolved photoluminescence decay curves (f; excitation source: 400 nm, 4 μW) of the CsPbBr3, MAPbBr3 and mixture-1.0 films. τ is the lifetime.
Extended Data Fig. 4 XRD and XPS characteristics of the perovskite films.
a, Original and magnified XRD patterns from CsPbBr3, MAPbBr3, mixture-1.0, and MABr + PbBr2 + CsBr mixture perovskite films. 2-theta is the diffraction angle multiplied by 2. b, c, XPS results from CsPbBr3, MAPbBr3 and mixture-1.0 perovskite films, indicating that there are CsPbBr3 and MABr phases in the mixture-1.0 film, but not in MAPbBr3.
Extended Data Fig. 5 Comparison of the morphology of the three perovskite films.
Left, top-view SEM image; centre, AFM topography; and right, root-mean-square roughness (R) of the a, CsPbBr3, b, MAPbBr3 and c, mixture-1.0 perovskite films.
Extended Data Fig. 6 Fabrication and evaluation of a perovskite LED device.
a, Energy-level diagram of the as-fabricated perovskite LED. b, Photograph of a large-area perovskite LED device (6 mm × 20 mm). c, Device performance of the bilayered CsPbBr3/MABr perovskite LEDs. S1 and S2 are step 1 and step 2. d, e, Electroluminescence spectra (d) and CIE chromatic diagram (e) of the three as-fabricated perovskite LEDs. f, g, J–V (f) and L–V (g) curves of the three as-fabricated three perovskite LEDs. h, L–V and J–V curves of the best-performing mixture-1.0 perovskite LED without a PMMA layer.
Extended Data Fig. 7 Performance optimization of the mixture-1.0 perovskite LED.
a, Cross-sectional SEM image of a perovskite LED device with a PMMA blocking layer. b, c, AFM topography image (b) and thickness measurement (c) of the optimized PMMA layer. The differently coloured lines show multiple test results from the same sample. d, e, Optimizing device performance by tuning the thickness of the PMMA layer (d) and the amount of MABr additives in the perovskite precursor (e).
Extended Data Fig. 8 Electroluminescence spectra and power efficiency of the best-performing mixture-1.0 perovskite LED device.
a, Electroluminescence spectra at various applied voltages. b, Power efficiency curve.
Extended Data Fig. 9 Measurement of operational lifetime of typical mixture-1.0 devices.
a, Extrapolation of lifetime from accelerated ageing tests, from which one can see that the acceleration factor, n, is about 1.5 in the devices investigated herein. b, Measurement of the operational lifetime of a perovskite LED working in continuous luminance mode; by carefully tuning the applied current, we could maintain a luminance output of around 100 cd m−2.
Supplementary information
Video 1
Preparing a highly luminous film using the mixture-1.0 precursor.
Video 2
Real-time measurement of a perovskite LED device.
Video 3
Measurement of a high-performance perovskite LED device with a current efficiency of 74.2 cd A−1.
Video 4
Operational lifetime measurement of a perovskite LED device working in continuous mode with luminance of around 100 cd m−2.
Rights and permissions
About this article
Cite this article
Lin, K., Xing, J., Quan, L.N. et al. Perovskite light-emitting diodes with external quantum efficiency exceeding 20 per cent. Nature 562, 245–248 (2018). https://doi.org/10.1038/s41586-018-0575-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41586-018-0575-3
Keywords
This article is cited by
-
Inorganic perovskite-based active multifunctional integrated photonic devices
Nature Communications (2024)
-
Solution-processable mixed-anion cluster chalcohalide Rb6Re6S8I8 in a light-emitting diode
Nature Materials (2024)
-
Chiral materials and mechanisms for circularly polarized light-emitting diodes
Nature Photonics (2024)
-
High brightness and low operating voltage CsPbBr3 perovskite LEDs by single-source vapor deposition
Scientific Reports (2024)
-
Vapour-deposited perovskite light-emitting diodes
Nature Reviews Materials (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.