Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Printing ferromagnetic domains for untethered fast-transforming soft materials

Abstract

Soft materials capable of transforming between three-dimensional (3D) shapes in response to stimuli such as light, heat, solvent, electric and magnetic fields have applications in diverse areas such as flexible electronics1,2, soft robotics3,4 and biomedicine5,6,7. In particular, magnetic fields offer a safe and effective manipulation method for biomedical applications, which typically require remote actuation in enclosed and confined spaces8,9,10. With advances in magnetic field control11, magnetically responsive soft materials have also evolved from embedding discrete magnets12 or incorporating magnetic particles13 into soft compounds to generating nonuniform magnetization profiles in polymeric sheets14,15. Here we report 3D printing of programmed ferromagnetic domains in soft materials that enable fast transformations between complex 3D shapes via magnetic actuation. Our approach is based on direct ink writing16 of an elastomer composite containing ferromagnetic microparticles. By applying a magnetic field to the dispensing nozzle while printing17, we reorient particles along the applied field to impart patterned magnetic polarity to printed filaments. This method allows us to program ferromagnetic domains in complex 3D-printed soft materials, enabling a set of previously inaccessible modes of transformation, such as remotely controlled auxetic behaviours of mechanical metamaterials with negative Poisson’s ratios. The actuation speed and power density of our printed soft materials with programmed ferromagnetic domains are orders of magnitude greater than existing 3D-printed active materials. We further demonstrate diverse functions derived from complex shape changes, including reconfigurable soft electronics, a mechanical metamaterial that can jump and a soft robot that crawls, rolls, catches fast-moving objects and transports a pharmaceutical dose.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Purchase on Springer Link

Instant access to full article PDF

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Design of ferromagnetic domains in 3D-printed soft materials.
Fig. 2: Various two-dimensional planar structures with programmed ferromagnetic domains demonstrating complex shape changes under applied magnetic fields.
Fig. 3: Various 3D structures with programmed ferromagnetic domains demonstrating complex shape changes under applied magnetic fields.
Fig. 4: Functional demonstrations of 3D-printed soft materials with programmed ferromagnetic domains.

Similar content being viewed by others

References

  1. Ma, M., Guo, L., Anderson, D. G. & Langer, R. Bio-inspired polymer composite actuator and generator driven by water Gradients. Science 339, 186–189 (2013).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  2. Zarek, M. et al. 3D printing of shape memory polymers for flexible electronic devices. Adv. Mater. 28, 4449–4454 (2016).

    Article  PubMed  CAS  Google Scholar 

  3. Wehner, M. et al. An integrated design and fabrication strategy for entirely soft, autonomous robots. Nature 536, 451–455 (2016).

    Article  ADS  PubMed  CAS  Google Scholar 

  4. Park, S. J. et al. Phototactic guidance of a tissue-engineered soft-robotic ray. Science 353, 158–162 (2016).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  5. Zhao, X. H. et al. Active scaffolds for on-demand drug and cell delivery. Proc. Natl Acad. Sci. USA 108, 67–72 (2011).

    Article  ADS  PubMed  Google Scholar 

  6. Fusco, S. et al. An integrated microrobotic platform for on-demand, targeted therapeutic interventions. Adv. Mater. 26, 952–957 (2014).

    Article  PubMed  CAS  Google Scholar 

  7. Davis, K. A., Burke, K. A., Mather, P. T. & Henderson, J. H. Dynamic cell behavior on shape memory polymer substrates. Biomaterials 32, 2285–2293 (2011).

    Article  PubMed  CAS  Google Scholar 

  8. Erb, R. M., Martin, J. J., Soheilian, R., Pan, C. & Barber, J. R. Actuating soft matter with magnetic torque. Adv. Funct. Mater. 26, 3859–3880 (2016).

    Article  CAS  Google Scholar 

  9. Hines, L., Petersen, K., Lum, G. Z. & Sitti, M. Soft actuators for small-scale robotics. Adv. Mater. 29, 1603483 (2017).

    Article  CAS  Google Scholar 

  10. Martel, S. Beyond imaging: macro-and microscale medical robots actuated by clinical MRI scanners. Science Robotics 2, eaam8119 (2017).

    Article  Google Scholar 

  11. Rahmer, J., Stehning, C. & Gleich, B. Spatially selective remote magnetic actuation of identical helical micromachines. Science Robotics 2, eaal2845 (2017).

    Article  Google Scholar 

  12. Boncheva, M. et al. Magnetic self-assembly of three-dimensional surfaces from planar sheets. Proc. Natl Acad. Sci. USA 102, 3924–3929 (2005).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  13. Kim, J., Chung, S., Choi, S., Lee, H. & Kwon, S. Programming magnetic anisotropy in polymeric microactuators. Nat. Mater. 10, 747–752 (2011).

    Article  ADS  PubMed  CAS  Google Scholar 

  14. Lum, G. Z. et al. Shape-programmable magnetic soft matter. Proc. Natl Acad. Sci. USA 113, E6007–E6015 (2016).

    Article  PubMed  PubMed Central  CAS  Google Scholar 

  15. Hu, W., Lum, G. Z., Mastrangeli, M. & Sitti, M. Small-scale soft-bodied robot with multimodal locomotion. Nature 554, 81–85 (2018).

    Article  PubMed  CAS  Google Scholar 

  16. Lewis, J. A. Direct ink writing of 3D functional materials. Adv. Funct. Mater. 16, 2193–2204 (2006).

    Article  CAS  Google Scholar 

  17. Kokkinis, D., Schaffner, M. & Studart, A. R. Multimaterial magnetically assisted 3D printing of composite materials. Nat. Commun. 6, 8643 (2015).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  18. Silverberg, J. L. et al. Using origami design principles to fold reprogrammable mechanical metamaterials. Science 345, 647–650 (2014).

    Article  ADS  PubMed  CAS  Google Scholar 

  19. Yuan, C. et al. 3D printed reversible shape changing soft actuators assisted by liquid crystal elastomers. Soft Matter 13, 5558–5568 (2017).

    Article  ADS  PubMed  CAS  Google Scholar 

  20. Ware, T. H., McConney, M. E., Wie, J. J., Tondiglia, V. P. & White, T. J. Voxelated liquid crystal elastomers. Science 347, 982–984 (2015).

    Article  ADS  PubMed  CAS  Google Scholar 

  21. Oyefusi, A. & Chen, J. Reprogrammable chemical 3D shaping for origami, kirigami, and reconfigurable molding. Angew. Chem. 129, 8362–8365 (2017).

    Article  Google Scholar 

  22. Zhao, Z. et al. Origami by frontal photopolymerization. Sci. Adv. 3, e1602326 (2017).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  23. Na, J. H. et al. Programming reversibly self-folding origami with micropatterned photo-crosslinkable polymer trilayers. Adv. Mater. 27, 79–85 (2015).

    Article  PubMed  CAS  Google Scholar 

  24. Xu, S. et al. Assembly of micro/nanomaterials into complex, three-dimensional architectures by compressive buckling. Science 347, 154–159 (2015).

    Article  ADS  PubMed  CAS  Google Scholar 

  25. Zhang, Y. H. et al. A mechanically driven form of kirigami as a route to 3D mesostructures in micro/nanomembranes. Proc. Natl Acad. Sci. USA 112, 11757–11764 (2015).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  26. Babaee, S. et al. 3D soft metamaterials with negative Poisson’s ratio. Adv. Mater. 25, 5044–5049 (2013).

    Article  PubMed  CAS  Google Scholar 

  27. Ding, Z. et al. Direct 4D printing via active composite materials. Sci. Adv. 3, e1602890 (2017).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  28. Kim, J., Hanna, J. A., Byun, M., Santangelo, C. D. & Hayward, R. C. Designing responsive buckled surfaces by halftone gel lithography. Science 335, 1201–1205 (2012).

    Article  ADS  MathSciNet  PubMed  MATH  CAS  Google Scholar 

  29. Ge, Q. et al. Multimaterial 4D printing with tailorable shape memory polymers. Sci. Rep. 6, 31110 (2016).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  30. Gladman, A. S., Matsumoto, E. A., Nuzzo, R. G., Mahadevan, L. & Lewis, J. A. Biomimetic 4D printing. Nat. Mater. 15, 413–418 (2016).

    Article  ADS  PubMed  CAS  Google Scholar 

  31. Fu, H. et al. Morphable 3D mesostructures and microelectronic devices by multistable buckling mechanics. Nat. Mater. 17, 268–276 (2018).

    Article  ADS  PubMed  CAS  PubMed Central  Google Scholar 

  32. Zhang, Q., Zhang, K. & Hu, G. Smart three-dimensional lightweight structure triggered from a thin composite sheet via 3D printing technique. Sci. Rep. 6, 22431 (2016).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  33. Mirfakhrai, T., Madden, J. D. & Baughman, R. H. Polymer artificial muscles. Mater. Today 10, 30–38 (2007).

    Article  CAS  Google Scholar 

  34. Illeperuma, W. R., Sun, J.-Y., Suo, Z. & Vlassak, J. J. Force and stroke of a hydrogel actuator. Soft Matter 9, 8504–8511 (2013).

    Article  ADS  CAS  Google Scholar 

  35. Huang, L. M. et al. Ultrafast digital printing toward 4D shape changing materials. Adv. Mater. 29, 1605390 (2017).

    Article  CAS  Google Scholar 

  36. Bakarich, S. E., Gorkin, R., Panhuis, M. h. & Spinks, G. M. 4D printing with mechanically robust, thermally actuating hydrogels. Macromol. Rapid Commun. 36, 1211–1217 (2015).

    Article  PubMed  CAS  Google Scholar 

  37. Wu, J. et al. Multi-shape active composites by 3D printing of digital shape memory polymers. Sci. Rep. 6, 24224 (2016).

    Article  ADS  PubMed  PubMed Central  CAS  Google Scholar 

  38. Ambulo, C. P. et al. Four-dimensional printing of liquid crystal elastomers. ACS Appl. Mater. Interfaces 9, 37332–37339 (2017).

    Article  PubMed  CAS  Google Scholar 

  39. Kotikian, A., Truby, R. L., Boley, J. W., White, T. J. & Lewis, J. A. 3D printing of liquid crystal elastomeric actuators with spatially programed nematic order. Adv. Mater. 30, 1706164 (2018).

    Article  CAS  Google Scholar 

  40. Li, W. et al. Flexible circuits and soft actuators by printing assembly of graphene. ACS Appl. Mater. Interfaces 8, 12369–12376 (2016).

    Article  ADS  PubMed  CAS  Google Scholar 

Download references

Acknowledgements

We thank D. Bono for help in magnetic characterizations. This work is supported by the National Science Foundation (CMMI-1661627) and the Office of Naval Research (N00014-17-1-2920) and the MIT Institute for Soldier Nanotechnologies. Y.K. acknowledges financial support from Harvard-MIT Division of Health Sciences and Technology. H.Y. acknowledges financial support from a Samsung Scholarship.

Author information

Authors and Affiliations

Authors

Contributions

Y.K., H.Y., R.Z. and X.Z. designed the study and interpreted the results. H.Y., Y.K. and X.Z. conceived the idea of printing ferromagnetic domains. H.Y. and X.Z. developed the 3D printing platform. Y.K. and H.Y. developed materials and methods of printing and performed material characterizations. Y.K. designed and fabricated the printed structures and demonstrated their functions. X.Z., R.Z. and Y.K. developed the theory for soft materials with ferromagnetic domains, R.Z. and S.A.C. implemented the numerical models, and R.Z. performed the simulations. Y.K., H.Y. and R.Z. produced the figures and videos. Y.K. and X.Z. wrote the manuscript with input from all authors. X.Z. supervised the study.

Corresponding author

Correspondence to Xuanhe Zhao.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Scanning electron microscope images of NdFeB and fumed silica particles and printed fibres.

a, Magnetizable microparticles of NdFeB alloy in flake-like shapes with an average size of 5 µm. b, Fumed silica nanoparticles with an average size of 30 nm. cf, Fibres printed using nozzles with diameters of 50 µm (c), 100 µm (d), 200 µm (e), and 410 µm (f). g, The ratio between the printed fibre and the nozzle diameter, which is called the die-swelling ratio, plotted against the nozzle diameter.

Extended Data Fig. 2 Mechanical characterizations of the ink and the printed materials.

a, b, Apparent viscosity as a function of applied shear rate (a) and storage modulus as a function of applied shear stress (b) for 20 vol% magnetized ink (red), 20 vol% nonmagnetized ink (black) and support ink (grey). c, Nominal tensile stress–stretch curves (solid lines) for specimens printed with the magnetic ink in the absence of external fields (black), with applied magnetic fields of 50 mT (red) at the nozzle tip generated by a permanent magnet, and the elastomer matrix with no magnetic particles (blue). The shear modulus µ of each material was obtained by fitting the experimental curves to a neo-Hookean model (dashed lines).

Extended Data Fig. 3 Micro-computed tomography images of printed fibres.

a, A fibre printed with a nozzle of diameter 410 µm in the absence of applied magnetic field. b, A fibre printed with a nozzle of diameter 410 µm in the presence of an applied magnetic field of 50 mT at the nozzle tip. No obvious aggregation of ferromagnetic particles in the printed fibres can be observed.

Extended Data Fig. 4 Experimental validation of the magnetization induced during printing under the applied magnetic field.

a, Experimental setup with a vibrating sample magnetometer for measuring the magnetization of a sample printed with a nozzle of diameter 410 µm under the presence of magnetic field of 50 mT at the nozzle tip. b, Magnetization values measured at various angular positions of the printed fibres with respect to the external magnetic field applied by the vibrating sample magnetometer.

Extended Data Fig. 5 Magnetic moment densities of printed samples with different NdFeB particle volume fractions.

For printed specimens at each volume fraction, a permanent magnet is used to generate external fields (50 mT at the nozzle tip). The magnetization values of printed samples (red) are compared with the maximum achievable magnetization values (black) measured from uniformly magnetized samples. The uniformly magnetized samples are printed in the absence of external fields, cured, and then magnetized under impulsive fields (about 2.7 T). Printing under the applied field of 50 mT yields a magnetic moment density that corresponds to 63%–64% of the maximum achievable magnetization at each volume fraction of NdFeB particles.

Extended Data Fig. 6 Schematic designs and dimensions of the two-dimensional and 3D structures in Figs. 2 and 3.

a, An annulus encoded with alternating domains that are equidistant. b, An annulus encoded with alternating domains that vary in size. c, A Miura-ori fold encoded with alternating oblique patterns of ferromagnetic domains. d, A hollow cross encoded with alternating ferromagnetic domains along the perimeter. e, f, Quadrupedal (e) and hexapedal (f) structures enabled by folding of the magnetically active segments surrounding the magnetically inactive segments. g, Two adjoining hexagonal tubes programmed to form undulating surfaces under applied magnetic fields. h, A pyramid-shaped thin-walled structure programmed to elongate in its diagonal direction along applied magnetic fields. ik, A set of auxetic structures (with negative Poisson’s ratios) programmed to shrink in both length and width under applied magnetic fields. The dimensions in this figure are given in millimetres.

Extended Data Fig. 7 Overall fabrication process of printing multilayered structures assisted by the use of support inks.

a, Printing multilayered hexagonal arrays using magnetic and support inks. The use of support inks as fugitive buttresses enables stacking the deposited magnetic inks stably up to tens or even hundreds of layers. b, Chemical composition of magnetic and support inks. The higher concentration of catalyst in the support ink prevents diffusion of catalyst molecules through the interface and thus prevents imperfect curing of the adjacent magnetic inks. Δc denotes the difference in catalyst concentration between the support and magnetic inks. c, The printed magnetic inks are cured by heating at 120 °C for 1 h. The support ink is then removed by solvent rinses.

Extended Data Fig. 8 Actuation performance of 3D-printed shape-programmable soft materials.

a, Energy density and actuation rate of our magnetically responsive structures presented in Figs. 13 are plotted and compared with those of existing 3D-printed shape-programmable soft materials in the literature27,28,29,30,32,35,36,37,38,39,40. b, Power density is calculated as energy density multiplied by the actuation rate of each material and plotted for comparison; the materials are listed in order of increasing power densities. PNIPAAm = poly(N-isopropylacrylamide); PMBA = poly(benzyl methacrylate); PHEMA = poly(hydroxyl ethyl methacrylate); PLA = poly(lactic acid); RM82 = 1,4-bis-[4-(6-acryloyloxhexyloxy)benzoyloxy]-2-methylbenzene. TangoBlack and VeroClear are commercially available acrylic photocurable polymers from Stratasys Ltd.

Extended Data Fig. 9 Schematic designs and working principles of the reconfigurable soft electronic device demonstrated in Fig. 4a.

a, Exploded and bottom views of the printed device, in which soft electronic circuitry and components are embedded by means of a hybrid fabrication process based on multimaterial 3D printing. b, Two different shapes depending on the direction of applied magnetic fields of 30 mT, which yield different electronic functions (red micro-LEDs lit up in Mode 1 and green micro-LEDs lit up in Mode 2). c, Schematic diagram of the embedded soft electronic circuits, which are designed to turn active only in the designated mode of transformation owing to the selective contact with the gold electrode on the substrate.

Extended Data Fig. 10 Schematic illustrations of the methods for applying magnetic fields to actuate the printed structures.

a, b, The magnetic fields for actuating the printed structures can be applied in two ways. A pair of electromagnetic coils are used to generate a uniform magnetic field (a). A NdFeB magnet (width 2 in, length 3 in, thickness 0.5 in, surface flux density 300 mT) is used to create spatially varying magnetic fields for dynamic actuation by combining vertical, horizontal and rotational movements of the magnet (b).

Supplementary information

Supplementary Information

This file contains Supplementary Text and Data, and Supplementary Figure 1.

Video 1 Fast transformation of a straight line with an alternating magnetization pattern.

A straight line printed with an alternating magnetization pattern rapidly transforms into an ‘m’ shape under the applied magnetic field and quickly reverts to its original shape upon removal of the applied field.

Video 2 Complex shape changes of various two-dimensional planar structures with programmed ferromagnetic domains under applied magnetic fields.

Various two-dimensional planar structures, including two annular rings with equidistant and varying -magnitude alternating magnetization patterns, a Miura-ori pattern, a hollow cross and quadrupedal and hexapedal structures, exhibit fast and reversible transformations via magnetic actuations.

Video 3 Overall process of printing a multi-layered, 3D elastomeric structure with programmed ferromagnetic domains.

This video shows the overall process of (i) printing a 3D construct with programmed magnetic domains, assisted by the use of support ink and (ii) actuating the printed structure by magnetic fields.

Video 4 Complex shape changes of various 3D structures with programmed ferromagnetic domains under applied magnetic fields.

Various 3D structures, including two adjoining hexagonal tubes with high aspect ratios and a pyramid-shaped thin-walled construct, exhibit fast and reversible transformations via magnetic actuations.

Video 5 Various 3D auxetic structures with programmed ferromagnetic domains, showing negative Poisson’s ratios.

Various 3D auxetic structures, or mechanical metamaterials, exhibit fast shrinkage and recovery in both length and width via magnetic actuation.

Video 6 Demonstration of a reconfigurable soft electronic device based on the annular ring structure with alternating ferromagnetic domains.

The reconfigurable electronic device exhibits different electronic functions depending on the direction of applied magnetic fields.

Video 7 Demonstration of interactions with an object using the programmed shape changes.

The hexapedal structure exhibits a diverse set of interactions, including stopping, catching, holding and releasing of a glass ball, under applied magnetic fields.

Video 8 Rolling-based locomotion of the hexapedal structure and delivery of a drug pill under a rotating magnetic field.

The hexapedal structure wraps its body and rotates along a horizontal axis under a rotating magnetic field to create rolling-based locomotion, which allows the hexapedal structure to move forwards and backwards depending on the rolling direction.

Video 9 Horizontal leap of a 3D auxetic structure based on drastic release of the elastic and magnetic potential energies.

Sudden reversal of the applied field direction while attenuating the strength triggers drastic release of the combined elastic and magnetic potential energies that are converted to kinetic energy, creating a horizontal leap of the demonstrated 3D auxetic structure.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Kim, Y., Yuk, H., Zhao, R. et al. Printing ferromagnetic domains for untethered fast-transforming soft materials. Nature 558, 274–279 (2018). https://doi.org/10.1038/s41586-018-0185-0

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41586-018-0185-0

This article is cited by

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing