Abstract
While the precise design of catalysts is one of ultimate goals in catalysis, practical strategies often fall short, especially for complicated photocatalytic processes. Here, taking the hydrogen evolution reaction (HER) as an example, we introduce a theoretical approach for designing robust metal cocatalysts supported on TiO2 using density functional theory calculations adopting on-site Coulomb correction and/or hybrid functionals. The approach starts with clarifying the individual function of each metal layer of metal/TiO2 composites in photocatalytic HER, covering both the electron transfer and surface catalysis aspects, followed by conducting a function-oriented optimization via exploring competent candidates. With this approach, we successfully determine and verify bimetallic Pt/Rh/TiO2 and Pt/Cu/TiO2 catalysts to be robust substitutes for conventional Pt/TiO2. The right metal type as well as the proper stacking sequence are demonstrated to be key to boosting performance. Moreover, we tentatively identify the tunneling barrier height as an effective descriptor for the important electron transfer process in photocatalysis on metal/oxide catalysts. We believe that this study pushes forward the frontier of photocatalyst design towards higher water splitting efficiency.
Similar content being viewed by others
Introduction
Titanium dioxide (TiO2) is an important material for photocatalytic water splitting1,2,3, on which loading of proper cocatalysts (usually metals) is routinely used to enhance the hydrogen evolution reaction (HER) performance4,5. As photoelectrons are first generated in the bulk region of TiO2 after photon excitation6,7,8, good metal/titania catalysts should qualify at least two aspects of (i) efficient electron transfer across the interface (from TiO2 to the metal) and (ii) rapid H2 production on metal surface9,10. Noble metals such as Pt, Pd, and Rh are able to meet both requirements, as benefited from their large work functions (or low Fermi levels)4,11 and suitable Gibbs adsorption energies of H atom (ΔGH)12,13, and thus they were frequently used in photocatalytic HER5,11. In particular, Pt is known as the optimal material for catalyzing HER4,5,11, but how to reduce the catalyst cost and/or increase the activity has aroused significant interests in both academia and industry.
One potential solution is to properly regulate the interface structure. Since the interface bridges the oxide and metals, its structure as well as the metal-support interaction (MSI)14, on one hand controls the adhesive contact strength and the electron transfer process, and on the other hand affects the surface reaction activity owing to the induced charge redistributions15,16,17,18. Many modification techniques, such as morphology engineering19,20, particle size control21,22, alloying23,24 etc., are all able to alter the interface properties and furthermore the photocatalytic performance (albeit uncertainty in promotion or not). Nevertheless, in addition to trial-and-error experiments, strategic knowledges about how to conduct rational design of metal/oxide catalysts and where to start are still open questions. Besides, given that the ΔGH is generally regarded as an effective descriptor signifying surface HER activity12,13, whether there also exists some physicochemical properties that could directly scale the electron transfer efficiency remains elusive yet.
Intriguingly, Umezawa and colleagues25 investigated electronic structures of metal/TiO2 composites (metal = Pt, Pd, Au) and found that the MSI-induced charge redistribution is largely confined within the first contact metal layer and drops quickly to the second and the third layer. Similar phenomena have also been observed at other metal/oxide interfaces26,27. These findings imply that each metal layer at the interface is unique and may exhibit distinct catalytic behaviors compared with other layers or bulk metals (i.e., layer-dependent catalytic function). Moreover, our previous study on the size effect of supported Pt cocatalysts demonstrated that smaller one-Pt-layer clusters have good electron transfer character but low surface H–H coupling activity, whereas larger multilayer particles show an opposite trend with limited electron transfer efficiency28. It was thus anticipated that (i) the interface first metal layer might be related to the electron transfer process, while the exterior layer to surface catalytic reactions; (ii) further, by optimizing the individual function of each layer, the overall performance could be improved.
Herein, we report a function-oriented design of efficient metal/TiO2 catalysts for photocatalytic HER. Differing from the precise size control of Pt nanoparticles to reach a balance between the electron transfer and surface catalysis28, we achieved in theory excellent performance in both aspects (rather than making compromises), by means of alloying robust electron transfer and surface reaction components in a right combination sequence. Furthermore, once the optimal alloying patterns were determined, it is technically feasible to fabricate them in experiments perhaps via the atomic layer deposition (ALD)29,30 or underpotential deposition31,32 techniques. For example, Moffat and colleagues23 reported the precise control of the structure and quantity of deposited metals even in the range of monolayer level, whereas Chen and Bent33 realized the area-selective ALD by selectively pre-adsorbing a proper molecule (e.g., 1-octadecene, octadecyltrichlorosilane), which resists the attachment of deposition precursors on the substrate.
Results
Exploring robust electron transfer materials
As Pt is highly effective for surface HER and thus the best candidate for constructing the exterior metal layer12,13, the first priority is to find excellent materials for the interface electron transfer layer. Herein, we adopted our previous approach of calculating the intrinsic electron transfer (IET) energy28, defined by the energy change of moving an excess electron from TiO2 bulk to supported metal particles in the absence of surface adsorbates, to compare the electron transferring ability among candidate metals. The initial state of a localized electron at a Ti site (Ti3+) in the bulk region of TiO2 and the final state of delocalized electron densities on supported metal particles were confirmed by calculating the site-projected magnetic moments and Bader charges (see details in “IET energy calculation” in Methods)15,28. It should be mentioned that, since there are many possible electron trapping sites in bulk TiO2, we have calculated at least three different Ti sites for each metal/TiO2 composite and the reported energies were the averaged value. Eventually, the IET results can be obtained by comparing the total energy along the electron transfer pathway, as summarized in Supplementary Table 1.
In Fig. 1, we assessed the electron transferring ability of 10 candidate metals (Supplementary Fig. 1) by calculating the IET energies. It is noteworthy that other transition metals (first ~ third periods) are generally too active with electron affinity < 1 eV34 and can readily cause interface distortion (e.g., Hf and Ta) and/or oxide reduction (e.g., Ti, Mn, Co, Nb, Mo, and W) upon deposition (Supplementary Fig. 2)35, and thus were not considered in the screening scope. It was found that noble metals in the VIII group (except Ru) are able to promote the directional electron transfer (namely, from bulk TiO2 to the metal) with exothermic IET energies, but Ag and Au turn to be bad choices, consistent with experimental observations5,11. In particular, the screening results (using the M8/TiO2 model) suggest that Rh, with strong IET energy of −0.27 eV, might be more efficient than Pt (−0.17 eV) in facilitating the directional electron transfer, but the main drawback is again its high price. Encouragingly, cheap metal Cu also shows an impressive IET energy of −0.15 eV close to Pt, serving as a promising electron transfer material. Moreover, the excellent electron transferring ability of Rh and Cu was further confirmed by using relatively larger M19/TiO2 models, obtained via ab initio molecular dynamics simulations (AIMD; Supplementary Fig. 3). Therefore, we theoretically proposed two bimetallic models, constructed by one layer of noble Rh or cheap Cu directly adhering to TiO2 and a second layer of Pt capping on the top, to be competitive substitutes (either in benefits or costs) of the conventional Pt for photocatalytic H2 production.
Verifying the effectiveness of proposed catalysts
By utilizing geometry features of the stable Pt13/TiO2 composite (obtained via AIMD simulations; Supplementary Fig. 4) and replacing the first interface layer of six Pt atoms with Rh or Cu, we determined the bimetallic structure of Pt7Rh6/TiO2(101) and Pt7Cu6/TiO2(101) via unconstrained relaxations. No obvious structure changes were observed for the Pt7Rh6/TiO2 (Fig. 2a) relative to that of Pt13/TiO2, indicating a lattice-matched alloying between Pt and Rh, whereas noticeable distortions for the Pt7Cu6/TiO2 (Fig. 2c) can be attributed to the distinct atomic radius difference (~7%)36. Further, IET energy calculations showed that the directional electron transfer (confirmed by charge density plots in Supplementary Fig. 5) indeed gets promoted for both the Pt7Rh6/TiO2 and Pt7Cu6/TiO2 composites, being −0.04 and −0.08 eV, respectively, as compared with the endothermic 0.05 eV for Pt13/TiO215,28. Such promotion is consistent with the downward shift of the Fermi level (Ef), from 0.45 eV below TiO2 conduction band minimum (CBM) for Pt13/TiO228 to ~0.65 eV (see Fig. 2b, d), considering that a relatively lower energy level is beneficial to accept electrons. It is also necessary to address that the geometry of deposited metals has significant impacts on their physicochemical properties (Supplementary Fig. 6), signifying the importance of determining stable metal/oxide interfaces on reliable calculation results.
In addition, we also picked a less effective electron transfer metal of Ir for fair comparison, using similar approaches above. Consistently, the Pt7Ir6/TiO2 composite (Fig. 2e) was found to be no better than Pt13/TiO2 with an endothermic IET energy of 0.09 eV, verifying the effectiveness of our screening approach. Furthermore, we investigated the electron transfer for models with inverted metal stacking sequence, namely the Rh7Pt6/TiO2 and Cu7Pt6/TiO2 composites (Fig. 2g, i). As expected, the electron transfer process turns to be retarded with endothermic IET energies and up-shifted Ef (Fig. 2g–j). Despite minor oscillations induced by the upper Rh or Cu layers, the electron transfer ability of the two inverted models generally resembles that of Pt13/TiO2. These results revealed evidently the electron transfer function of the first interface metal layer, and demonstrated that not only the right metal type (Rh or Cu) but also proper stacking sequence (Pt/Rh/TiO2, Pt/Cu/TiO2) are essential to achieve improved electron transfer efficiency.
Next, it is necessary to verify whether the catalytically efficient HER continues to proceed on the exterior Pt layer of the bimetallic composites. Considering the diverse ΔGH results on different surface sites (Supplementary Table 2) and also the volcano-shaped ΔGH ~ activity relationship9,10, we uniformly selected two of the most active sites with ΔGH approaches zero for computing the H–H coupling barrier (Eacoup) and determining the HER activity of the alloy models. In Fig. 3a, b, one can see that both Pt7Rh6/TiO2 and Pt7Cu6/TiO2 give moderate hydrogen adsorption strength close to the volcano peak of ΔGH = 0 eV9,10. Moreover, we determined the coupling barrier Eacoup to be 0.71 and 0.69 eV for Pt7Rh6/TiO2 and Pt7Cu6/TiO2 (Fig. 3d, e), respectively, being even slightly lower than the value of 0.75 eV on Pt13/TiO228. It is noteworthy that the coupling state on Pt7Rh6/TiO2 shows quite late transition structure resembling the H2 adsorption configuration, which was further confirmed by using the climbing image nudged elastic band method (CI-NEB; Supplementary Fig. 7)37. Apparently, the HER activity on these alloy cocatalysts could be higher than extended Pt surfaces, owing to large Eacoup of 0.88 and 1.07 eV on Pt(111) and Pt(100), respectively38.
Hence, by integrating good surface catalytic activity of Pt and robust electron transfer ability of Rh or Cu, the alloyed Pt/Rh or Pt/Cu cocatalyst breaks the intrinsic constraints between the two key photocatalytic factors for mono-type materials (e.g., Pt), and could in principle achieve superior performance than conventional Pt/TiO2. It is worth noting that this strategy resembles the concept of using multiphase materials to break the scaling constraint between chemisorption energies of key intermediates (e.g., C and O in CO oxidation) in heterogenous catalysis39 and also offers probabilities to approach the global activity maximum in photocatalysis. In particular, we underline the striking results of Pt/Cu/TiO2 with enhanced photocatalytic performance but reduced catalyst cost as compared to pure Pt cocatalysts. This is further validated by using a trilayer Pt6Cu13/TiO2 model with much lower Pt content, where suitable ΔGH and Eacoup are still well conserved (Fig. 3c, f). Furthermore, the Pt/Cu/TiO2 composite was validated to be fairly stable via long-time AIMD simulations (>20 ps; Supplementary Fig. 8). Overall, TiO2 supported Cu nanoparticles coated with a thin film of Pt skin are theoretically predicted to be efficient yet inexpensive catalysts for photocatalytic HER.
Generalized correlations
Finally, given the crucial role of electron transfer in photocatalysis, one may ask what physical properties might be related with the electron transfer efficiency across the interface. Here we calculated the effective potential, which represents the carrier interaction with other electrons in the system and the external electrostatic field40,41, of relevant metal/TiO2 composites using the HSE06 functional (Supplementary Table 1). In particular, the tunneling barrier height (ΦTB), defined as the potential difference between the peak at the interface and TiO2 slab (Fig. 4a), indicates the minimum energy cost of directional electronic injection via quantum tunneling40,41. Intriguingly, the IET energies was found to correlate well with the ΦTB, which although is typically mentioned in van der Waals junctions (e.g., metal/MoS2 interfaces)42, among a wide range of metal/TiO2 composites (Fig. 4b) holding short interface distances (Supplementary Table 1). Furthermore, despite the significant impact of particle size on IET energies as previously discovered28, the linear relationship between the IET energy and the ΦTB was found irrelevant to either the metal type (indicated by different colors) or particle size (different shapes in Fig. 4b). We notice that the number of sampling points might still be limited, but the good correlation coefficient in a wide sampling range encourages to regard such correlation as a general trend (at least for supported metals on TiO2), which is beyond the considered metal/TiO2 models in this work. As far as we know, this is the first piece of report on the electron transfer descriptor for photocatalytic reactions on metal/oxide catalysts. Considering the significance of electron transfer efficiency in photocatalysis, this finding could possibly promote future photocatalysts design via coordinating conventional catalytic descriptors (e.g., ΔGH for HER) and the electron transfer properties ΦTB.
Discussion
In summary, we decomposed the complicated photocatalytic HER (after photoexcitation) into elementary processes of interface electron transfer and surface catalytic reactions in this work. For metal/TiO2 composites, the interfacial first metal layer was evidenced to be responsible for collecting photoelectrons from TiO2, while the exterior layer is largely related to catalysing surface HER. Regarding particularly the former, we theoretically identified Rh and Cu to be robust electron transfer materials, which, after alloying with the optimal HER catalyst of Pt, give rise to bimetallic Pt/Rh/TiO2 and Pt/Cu/TiO2 as excellent substitutes for the conventional Pt/TiO2. Our results demonstrated clearly the importance of both the right metal type and the proper stacking sequence in improving the performance of alloyed materials. We furthermore generalized a linear correlation between IET energies and the tunneling barrier height ΦTB of metal/TiO2 composites, paving the way to the rational design of highly-efficient and cost-effective photocatalysts, for instance, the proposed Pt/Cu/TiO2 for photocatalytic hydrogen production.
Methods
DFT calculations
All density functional theory (DFT) calculations were performed using the Vienna Ab-initio Simulation Package (VASP) with the spin-polarization being considered. The DFT functional was utilized at the Perdew–Burke–Ernzerhof level. The project-augmented wave method was used to represent the core-valence electron interaction. The valence electronic states were expanded in plane wave basis sets with energy cutoff at 450 eV. The transition states were searched using a constrained optimization scheme and were verified when (i) all forces on atoms vanish and (ii) the total energy is a maximum along the reaction coordination but a minimum with respect to the rest of the degrees of freedom. The force threshold for the transition state search and structural optimization was 0.05 eV/Å. The dipole correction was applied throughout the calculations to take the polarization effect into account.
For the TiO2 system, we have demonstrated previously43,44 that the DFT + U method can yield similar structures and energies as those from the hybrid HSE06 functional. Here we mainly applied the DFT + U method in computing the thermodynamic properties (e.g., adsorption energy and energy barriers), where the on-site Coulomb correction was set on Ti 3d orbitals with an effective U value of 4.2 eV as suggested in literature works45,46. To produce electronic structure properties more accurately (e.g., band gap, band edge position, and effective potential), we further performed hybrid HSE06 calculations utilizing the DFT + U geometry, in which the electronic minimization algorithm was set as ALGO = All with a very soft augmentation charge (PRECFOCK = Fast). The lattice parameters and band gap of bulk anatase TiO2 determined via the HSE06 functional (a = b = 3.766, c = 9.448 Å; Eg = 3.31 eV) agree well with the experimental values (a = b = 3.776, c = 9.486 Å; Eg = ~3.2 eV).
The effective potential was calculated by including (i) the Hartree potential caused by the mean-field electrostatic interaction, (ii) the exchange-correlation potential due to the quantum mechanical nature of the electrons, and (iii) other external electrostatic interactions in the system. Technically, this can be done by invoking the LVTOT parameter in the input file using the VASP program (version 5.4 or later).
The adsorption energy of hydrogen atom (EadH) is defined as the energy difference after and before the adsorption with respect to the gas phase H2 molecule according to EadH = E(total) − E(surface) − 1/2E(H2), where E(surface), E(H2), and E(total) are the energies for the clean surface, H2 molecule in the gas phase, and hydrogen atom adsorbed on the surface, respectively. It is noteworthy that ΔGH is obtained by adopting the entropy correction proposed by Norskov et al.12,13 according to ΔGH = EadH + 0.24. The more negative the EadH (or ΔGH) is, the more strongly the H atom binds on surface.
Model construction for metal/TiO2 composites
To properly accommodate the metal cluster, we utilized a relative large supercell of anatase (101) surface, that is a p(2 × 3) three-Ti-layer slab (72 Ti and 36 O atoms) with a vacuum thickness of 16 Å. We have checked the electron transfer energetics by enlarging the slab thickness to four-Ti-layer models, which produce similar results as that from three-layer calculations (Tables S1 and S2 in ref. 15). It is noteworthy that all the metal/TiO2 composites containing non-Pt metals were constructed by utilizing geometry features of the optimal Pt13/TiO2 or Pt8/TiO2, or Pt7/TiO2 composites, determined via extensive AIMD simulations as shown in Supplementary Fig. 4, and replacing Pt with other metals by needs. Both the conjugate gradient and Quasi-Newton optimization methods were used to determine the stable structures.
Regarding the optimal structure of Rh19/TiO2, Cu19/TiO2 and bimetallic Pt7Cu6/TiO2 composites, AIMD simulation was performed to investigate their structural evolutions. The simulation was carried out in the canonical NVT ensemble employing Nosé–Hoover thermostats. The temperature was set at 450 K that is taken from the temperature of hydrothermal treatment commonly used in experiments21,47 and the time step was 1 fs. More than 20 ps AIMD simulations were performed (Supplementary Figs. 3 and 8) and from the equilibrated trajectory we selected structural snapshots in every 2 ps interval and fully optimized them until all forces diminish. The optimal composite structure can be determined as the lowest-energy configuration.
IET energy calculation
The extra photoelectron in the system was simulated by adding an excess electron into the supercell as common practice8,46,48. We have also previously validated the approach by comparing the electron transfer results with those obtained by introducing an additional H atom on the opposite layer of TiO2 slab in charge-neutral systems (Table S1 in ref. 28.). The localization of the electron on a particular Ti site of TiO2 can be initially configured and followed by DFT + U electronic structure optimizations. Initial magnetic moments on each atom are usually necessary in the input settings, although they will be optimized during the calculation. None of any constraints on the distribution/population of spin-polarized charges were imposed during the optimization.
To calculate the IET energy, the initial state is set as a localized electron at a Ti site in the bulk region of TiO2. The as-formed Ti3+ cation shows distinctive features relative to the regular lattice Ti4+ and one can distinguish them easily as follows. (i) Geometry structures: the electron localization (generation of Ti3+ cation) is accompanied with the distinct elongations of Ti-O bonds by the outward movement of surrounding lattice O, consistent with literation reports8,48. (ii) Electronic structure analysis: the position of electron localization can be further confirmed by calculating the site-projected magnetic moments (~0.8 µe) and Bader charges (negatively charged with ~0.4 | e| relative to lattice Ti4+ in bulk TiO2), as visualized by the spin density plots in Supplementary Fig. 5. Whereas for the final state, the electron delocalization on metal particles can also be confirmed by (i) the absence of Ti3+ cation in TiO2 but (ii) the increased electron quantities of ~0.4 |e| on metals (relative to the charge-neutral metal/TiO2 model) via Bader charge analysis. It should also be noted that, our research focused on the post-photoexcitation electron migration process, which can be approximately regarded as a ground-state event, and therefore no excited states were simulated in calculating the IET energies.
Data availability
The data that support the results of this study are available from the corresponding author upon reasonable request.
Code availability
The commercialized VASP code was used only and no custom codes were involved in this work.
References
Chen, X. & Mao, S. S. Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications. Chem. Rev. 107, 2891–2959 (2007).
De Angelis, F., Di Valentin, C., Fantacci, S., Vittadini, A. & Selloni, A. Theoretical studies on anatase and less common TiO2 phases: bulk, surfaces, and nanomaterials. Chem. Rev. 114, 9708–9753 (2014).
Thompson, T. L. & Yates, J. T. Jr. Surface science studies of the photoactivation of TiO2-new photochemical processes. Chem. Rev. 106, 4428–4453 (2006).
Yang, J., Wang, D., Han, H. & Li, C. Roles of cocatalysts in photocatalysis and photoelectrocatalysis. Acc. Chem. Res. 46, 1900–1909 (2013).
Ran, J., Zhang, J., Yu, J., Jaroniec, M. & Qiao, S. Z. Earth-abundant cocatalysts for semiconductor-based photocatalytic water splitting. Chem. Soc. Rev. 43, 7787–7812 (2014).
Zhang, Z. & Yates, J. T. Direct observation of surface-mediated electron-hole pair recombination in TiO2(110). J. Phys. Chem. C. 114, 3098–3101 (2010).
Thompson, T. L. & Yates, J. T. Monitoring hole trapping in photoexcited TiO2(110) using a surface photoreaction. J. Phys. Chem. B 109, 18230–18236 (2005).
Di Valentin, C. & Selloni, A. Bulk and surface polarons in photoexcited anatase TiO2. J. Phys. Chem. Lett. 2, 2223–2228 (2011).
Patrocinio, A. O. T. et al. Charge carrier dynamics and photocatalytic behavior of TiO2 nanopowders submitted to hydrothermal or conventional heat treatment. RSC Adv. 5, 70536–70545 (2015).
Cowan, A. J., Tang, J. W., Leng, W. H., Durrant, J. R. & Klug, D. R. Water splitting by nanocrystalline TiO2 in a complete photoelectrochemical cell exhibits efficiencies limited by charge recombination. J. Phys. Chem. C 114, 4208–4214 (2010).
Ni, M., Leung, M. K. H., Leung, D. Y. C. & Sumathy, K. A review and recent developments in photocatalytic water-splitting using TiO2 for hydrogen production. Renew. Sust. Energ. Rev. 11, 401–425 (2007).
Nørskov, J. K. et al. Trends in the exchange current for hydrogen evolution. J. Electrochem. Soc. 152, J23 (2005).
Greeley, J., Jaramillo, T. F., Bonde, J., Chorkendorff, I. B. & Norskov, J. K. Computational high-throughput screening of electrocatalytic materials for hydrogen evolution. Nat. Mater. 5, 909–913 (2006).
Tauster, S. Strong metal-support interactions. Acc. Chem. Res. 20, 389 (1987).
Wang, D., Liu, Z. P. & Yang, W. M. Proton-promoted electron transfer in photocatalysis: key step for photocatalytic hydrogen evolution on metal/titania composites. ACS Catal. 7, 2744–2752 (2017).
Klyushin, A. Y. et al. Is nanostructuring sufficient to get catalytically active Au? ACS Catal. 6, 3372–3380 (2016).
Wang, Y. G., Yoon, Y., Glezakou, V. A., Li, J. & Rousseau, R. The role of reducible oxide-metal cluster charge transfer in catalytic processes: new insights on the catalytic mechanism of CO oxidation on Au/TiO2 from ab initio molecular dynamics. J. Am. Chem. Soc. 135, 10673–10683 (2013).
Muhich, C. L., Zhou, Y., Holder, A. M., Weimer, A. W. & Musgrave, C. B. Effect of surface deposited Pt on the photoactivity of TiO2. J. Phys. Chem. C 116, 10138–10149 (2012).
Karan, H. I. et al. Catalytic activity of platinum monolayer on iridium and rhenium alloy manoparticles for the oxygen reduction reaction. ACS Catal. 2, 817–824 (2012).
Lee, K. S. et al. Surface structures and electrochemical activities of Pt overlayers on Ir nanoparticles. Langmuir 27, 3128–3137 (2011).
Yu, J., Qi, L. & Jaroniec, M. Hydrogen production by photocatalytic water splitting over Pt/TiO2 nanosheets with exposed (001) facets. J. Phys. Chem. C 114, 13118–13125 (2010).
Xing, J. et al. Active sites on hydrogen evolution photocatalyst. J. Mater. Chem. A 1, 15258 (2013).
Liu, Y., Gokcen, D., Bertocci, U. & Moffat, T. P. Self-terminating growth of platinum films by electrochemical deposition. Science 338, 1327–13301228925 (2012).
Li, M. et al. Pt monolayer coating on complex network substrate with high catalytic activity for the hydrogen evolution reaction. Sci. Adv. 1, e1400268 (2015).
Chen, H. et al. Bonding and electron energy-level alignment at metal/TiO2 interfaces: a density functional theory study. J. Phys. Chem. C 120, 5549–5556 (2016).
Goniakowski, J. Electronic structure of MgO-supported palladium films: influence of the adsorption site. Phys. Rev. B 57, 1935–1941 (1998).
Bogicevic, A. & Jennison, D. R. Variations in the nature of metal adsorption on ultrathin Al2O3 films. Phys. Rev. Lett. 82, 4050–4053 (1999).
Wang, D., Liu, Z. P. & Yang, W. M. Revealing the size effect of platinum cocatalyst for photocatalytic hydrogen evolution on TiO2 support: a DFT study. ACS Catal. 8, 7270–7278 (2018).
George, S. M. Atomic layer deposition: an overview. Chem. Rev. 110, 111–131 (2010).
Johnson, R. W., Hultqvist, A. & Bent, S. F. A brief review of atomic layer deposition: from fundamentals to applications. Mater. Today 17, 236–246 (2014).
Yu, Y., Hu, Y., Liu, X., Deng, W. & Wang, X. The study of Pt@Au electrocatalyst based on Cu underpotential deposition and Pt redox replacement. Electrochim. Acta 54, 3092–3097 (2009).
Asano, M., Kawamura, R., Sasakawa, R., Todoroki, N. & Wadayama, T. Oxygen reduction reaction activity for strain-controlled Pt-based model alloy catalysts: surface strains and direct electronic effects induced by alloying elements. ACS Catal. 6, 5285–5289 (2016).
Chen, R. & Bent, S. F. Chemistry for positive pattern transfer using area-selective atomic layer deposition. Adv. Mater. 18, 1086–1090 (2006).
Wang, D., Wang, C. M. & Yang, W. M. Three-dimensional kinetic trends in zeolites catalyzed benzene ethylation reaction: a descriptor-based DFT study coupled with microkinetic modeling. ACS Catal. 10, 1652–1662 (2020).
Chen, X., Shen, S., Guo, L. & Mao, S. S. Semiconductor-based photocatalytic hydrogen generation. Chem. Rev. 110, 6503–6570 (2010).
Ruban, A. V., Skriver, H. L. & Nørskov, J. K. Surface segregation energies in transition-metal alloys. Phys. Rev. B 59, 15990–16000 (1999).
Henkelman, G., Uberuaga, B. P. & Jónsson, H. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).
Wei, G.-F. & Liu, Z.-P. Restructuring and hydrogen evolution on Pt nanoparticle. Chem. Sci. 6, 1485–1490 (2015).
Cheng, J. & Hu, P. Utilization of the three-dimensional volcano surface to understand the chemistry of multiphase systems in heterogeneous catalysis. J. Am. Chem. Soc. 130, 10868–10869 (2008).
Shen, T., Ren, J. C., Liu, X., Li, S. & Liu, W. van der Waals stacking induced transition from Schottky to ohmic contacts: 2D metals on multilayer InSe. J. Am. Chem. Soc. 141, 3110–3115 (2019).
Kang, J., Liu, W., Sarkar, D., Jena, D. & Banerjee, K. Computational study of metal contacts to monolayer transition-metal dichalcogenide semiconductors. Phys. Rev. X 4, 0031005 (2014).
Gong, C., Colombo, L., Wallace, R. M. & Cho, K. The unusual mechanism of partial Fermi level pinning at metal-MoS2 interfaces. Nano Lett. 14, 1714–1720 (2014).
Wang, D., Wang, H. & Hu, P. Identifying the distinct features of geometric structures for hole trapping to generate radicals on rutile TiO2(110) in photooxidation using density functional theory calculations with hybrid functional. Phys. Chem. Chem. Phys. 17, 1549–1555 (2015).
Wang, D., Sheng, T., Chen, J., Wang, H.-F. & Hu, P. Identifying the key obstacle in photocatalytic oxygen evolution on rutile TiO2. Nat. Catal. 1, 291–299 (2018).
Morgan, B. J. & Watson, G. W. A DFT+U description of oxygen vacancies at the TiO2 rutile (110) surface. Surf. Sci. 601, 5034–5041 (2007).
Yan, L. K. & Chen, H. N. Migration of Holstein polarons in anatase TiO2. J. Chem. Theory Comput. 10, 4995–5001 (2014).
Ide, Y. et al. Remarkable charge separation and photocatalytic efficiency enhancement through interconnection of TiO2 nanoparticles by hydrothermal treatment. Angew. Chem. Int. Ed. 55, 3600–3605 (2016).
Ma, X., Dai, Y., Guo, M. & Huang, B. Relative photooxidation and photoreduction activities of the {100}, {101}, and {001} surfaces of anatase TiO2. Langmuir 29, 13647–13654 (2013).
Acknowledgements
We acknowledge the financial support from the National Key Research and Development Program of China (2018YFA0208602) and National Natural Science Foundation of China (21903025 and 21825301).
Author information
Authors and Affiliations
Contributions
D.W. conceived and conducted the research and wrote the paper. X.Q.G. participated in results discussion and manuscript modification. All authors commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewers for their contributions to the peer review of this work. Peer review reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, D., Gong, XQ. Function-oriented design of robust metal cocatalyst for photocatalytic hydrogen evolution on metal/titania composites. Nat Commun 12, 158 (2021). https://doi.org/10.1038/s41467-020-20464-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-20464-x
This article is cited by
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.