Abstract
We report organocuprates initiated anionic polymerizations of various α,β-unsaturated ester monomers in tetrahydrofuran (THF) under various conditions. It was found that catalysts prepared by reaction of CuI with methyllithium (MeLi) very effectively cause the polymerization of meth(acrylate) monomers. At molar ratio of [MeLi] to [CuI] higher than 2 the polymerization of t-butyl methacrylate (TBMA) proceeded quantitatively in THF at O–45°C to afford high molecular weight poly(t-butyl methacrylate) (PTBMA) with extremely narrow molecular weight distribution (MWD) (Mw/Mn=1.05–1.17). Initiator efficiency was less than 10% and highest at about [MeLi]/[CuI]=4.0. The post-polymerization proved the livingness of the polymerization of TBMA caused by lithium methylcuprate in THF at 0°C. The active species for the polymerization of TBMA was thought to be higher cuprate, such as Li2Cu(CH3)3. For the polymerizations of other methacrylates and t-butyl acrylate lithium methylcuprate initiators effectively afforded the polymers but with very broad MWD.
Similar content being viewed by others
Article PDF
References
G. H. Posner, “An Introduction to Synthesis Using Organocopper Reagents,” John Wiley & Sons, Inc., New York, N.Y., 1980.
C. E. Bawn and F. J. Whitby, J. Chem. Soc., 3926 (1960).
T. Ikariya and A. Yamamoto, J. Organomet. Chem., 72, 145 (1974).
H. O. House and W. F. Fisher, J. Org. Chem., 33, 949 (1968).
H. O. House and M. J. Umen, J. Am. Chem. Soc., 94, 5495 (1972).
T. Saegusa, S. Horiguchi, and T. Tsuda, Macromolecules, 8, 112 (1975).
T. Saegusa and S. Horiguchi, Polym. J., 6, 419 (1974).
D. E. Gregonis, G. A. Russell, J. D. Andrade, and A. C. deVisser, Polymer, 19, 1279 (1978).
Y. K. Han, J. M. Park, and S. K. Choi, J. Polym. Sci., Polym. Chem. Ed., 20, 1549 (1982).
P. Day, G. C. Eastmond, T. L. Gilchrist, and P. C. Bulmanpage, Pure Appl. Chem., A29, 545 (1992).
M. Dimonie, D. Mardare, S. Coca, T. E. Hogen-Esch, and J. Zoller, Makromol. Chem., Macromol. Symp., 67, 175 (1993).
T. Ibuka, T. Aoyagi, K. Kitada, F. Yoneda, and Y. Yamamoto, J. Organomet. Chem., 287, C18 (1985).
T. Kitano, A. Ishigaki, G. Uematsu, S. Kawaguchi, and K. Ito, J. Polym. Sci., Polym. Chew. Ed., 25, 979 (1987).
E. Nomura, S. Kawaguchi, and K. Ito, Polym. Prepr., Jpn., 42, 339 (1993).
S. Kawaguchi, T. Takahashi, H. Tajima, Y. Hirose, and K. Ito, Polym. J., 28, 735 (1996).
It has been reported that the anionic polymerization of TBMA in THF proceed in a living manner at 17°C when using lithium as a countercation and at 37°C when using sodium.17
T. E. Long, R. D. Allen, and J. E. McGrath, “Recent Advances in Mechanistic and Synthetic Aspects of Polymerization,” M. Fontanille and A. Guyot, Ed., NATO ASI Series 215, 1987, p 79.
A. H. E. Müller, Makromol. Chem., 482, 2863 (1981).
E. C. Ashby and J. J. Watkins, J. Am. Chem. Soc., 99, 5312 (1977).
E. C. Ashby and J. J. Lin, J. Org. Chem., 42, 2805 (1977).
H. Gilman and F. Schulze, J. Am. Chem. Soc., 47, 2002 (1925).
Y. Yamamoto and K. Maruyama, J. Am. Chem. Soc., 100, 3240 (1978).
Y. Yamamoto, S. Yamamoto, H. Yatagai, Y. Ishihara, and K. Maruyama, J. Org. Chem., 47, 119 (1982).
The refractive index increment of PTBMA and PMMA in THF at 25°C was determined to be 0.0728 and 0.0900 mL g−1, respectively.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kawaguchi, S., Nomura, E. & Ito, K. Organocuprates Initiated Anionic Living Polymerization of tert-Butyl Methacrylate. Polym J 30, 546–551 (1998). https://doi.org/10.1295/polymj.30.546
Issue Date:
DOI: https://doi.org/10.1295/polymj.30.546