Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Arrays of single-walled carbon nanotubes with full surface coverage for high-performance electronics

Abstract

Single-walled carbon nanotubes have exceptional electronic properties and have been proposed as a replacement for silicon in applications such as low-cost thin-film transistors and high-performance logic devices1. However, practical devices will require dense, aligned arrays of electronically pure nanotubes to optimize performance, maximize device packing density and provide sufficient drive current (or power output) for each transistor2. Here, we show that aligned arrays of semiconducting carbon nanotubes can be assembled using the Langmuir–Schaefer method. The arrays have a semiconducting nanotube purity of 99% and can fully cover a surface with a nanotube density of more than 500 tubes/µm. The nanotube pitch is self-limited by the diameter of the nanotube plus the van der Waals separation, and the intrinsic mobility of the nanotubes is preserved after array assembly. Transistors fabricated using this approach exhibit significant device performance characteristics with a drive current density of more than 120 µA µm−1, transconductance greater than 40 µS µm−1 and on/off ratios of 1 × 103.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Assembly and microscopic characterizations of full-coverage aligned arrays of semiconducting single-walled carbon nanotubes.
Figure 2: Optical spectroscopic characterization of full-coverage aligned arrays of semiconducting nanotubes.
Figure 3: Electrical properties of thin-film transistors that use 99% purity full-coverage semiconducting nanotube arrays with scaled gate dielectric.
Figure 4: Electrical properties of field-effect transistors that use 99% purity full-coverage semiconducting nanotube arrays and operate in direct transport regime.

Similar content being viewed by others

References

  1. Appenzeller, J. Carbon nanotubes for high-performance electronics—progress and prospect. Proc. IEEE 96, 201–211 (2008).

    Article  CAS  Google Scholar 

  2. Pimparkar, N., Kocabas, C., Kang, S. J., Rogers, J. & Alam, M. A. Limits of performance gain of aligned CNT over randomized network: theoretical predictions and experimental validation. IEEE Electron. Dev. Lett. 28, 593–595 (2007).

    Article  CAS  Google Scholar 

  3. Kang, S. J. et al. High-performance electronics using dense, perfectly aligned arrays of single-walled carbon nanotubes. Nature Nanotech. 2, 230–236 (2007).

    Article  CAS  Google Scholar 

  4. Hersam, M. C. Progress towards monodisperse single-walled carbon nanotubes. Nature Nanotech. 3, 387–394 (2008).

    Article  CAS  Google Scholar 

  5. Sarker, B. K., Shekhar, S. & Khondaker, S. I. Semiconducting enriched carbon nanotube aligned arrays of tunable density and their electrical transport properties. ACS Nano 5, 6297–6305 (2011).

    Article  CAS  Google Scholar 

  6. Engel, M. et al. Thin film nanotube transistors based on self-assembled, aligned, semiconducting carbon nanotube arrays. ACS Nano 2, 2445–2452 (2008).

    Article  CAS  Google Scholar 

  7. LeMieux, M. C. et al. Self-sorted, aligned nanotube networks for thin-film transistors. Science 321, 101–104 (2008).

    Article  CAS  Google Scholar 

  8. Hong, S. W., Banks, T. & Rogers, J. A. Improved density in aligned arrays of single-walled carbon nanotubes by sequential chemical vapor deposition on quartz. Adv. Mater. 22, 1826–1830 (2010).

    Article  CAS  Google Scholar 

  9. Li, X. et al. Langmuir–Blodgett assembly of densely aligned single-walled carbon nanotubes from bulk materials. J. Am. Chem. Soc. 129, 4890–4891 (2007).

    Article  CAS  Google Scholar 

  10. Tao, A. R., Huang, J. & Yang, P. Langmuir–Blodgettry of nanocrystals and nanowires. Acc. Chem. Res. 41, 1662–1673 (2008).

    Article  CAS  Google Scholar 

  11. Petty, M. C. in Langmuir-Blodgett Films: An Introduction Ch. 2, 39–93 (Cambridge Univ. Press, 1996).

    Chapter  Google Scholar 

  12. Cao, Q. et al. Medium-scale carbon nanotube thin-film integrated circuits on flexible plastic substrates. Nature 454, 495–500 (2008).

    Article  CAS  Google Scholar 

  13. Sun, D. M. et al. Flexible high-performance carbon nanotube integrated circuits. Nature Nanotech. 6, 156–161 (2011).

    Article  CAS  Google Scholar 

  14. Wang, C. et al. Extremely bendable, high-performance integrated circuits using semiconducting carbon nanotube networks for digital, analog, and radio-frequency applications. Nano Lett. 12, 1527–1533 (2012).

    Article  CAS  Google Scholar 

  15. Miyata, Y. et al. Length-sorted semiconducting carbon nanotubes for high-mobility thin film transistors. Nano Res. 4, 963–970 (2011).

    Article  CAS  Google Scholar 

  16. Sangwan, V. K. et al. Fundamental performance limits of carbon nanotube thin-film transistors achieved using hybrid molecular dielectrics. ACS Nano 6, 7480–7488 (2012).

    Article  CAS  Google Scholar 

  17. Cao, Q. et al. Gate capacitance coupling of singled-walled carbon nanotube thin-film transistors. Appl. Phys. Lett. 90, 023516 (2007).

    Article  Google Scholar 

  18. Kocabas, C. et al. Experimental and theoretical studies of transport through large scale, partially aligned arrays of single-walled carbon nanotubes in thin film type transistors. Nano Lett. 7, 1195–1202 (2007).

    Article  CAS  Google Scholar 

  19. Rouhi, N., Jain, D., Zand, K. & Burke, P. J. Fundamental limits on the mobility of nanotube-based semiconducting inks. Adv. Mater. 23, 94–99 (2011).

    Article  CAS  Google Scholar 

  20. Franklin, A. D. & Chen, Z. H. Length scaling of carbon nanotube transistors. Nature Nanotech. 5, 858–862 (2010).

    Article  CAS  Google Scholar 

  21. Deng, J. & Wong, H. S. P. Modeling and analysis of planar-gate electrostatic capacitance of 1-D FET with multiple cylindrical conducting channels. IEEE Trans. Electron. Dev. 54, 2377–2385 (2007).

    Article  Google Scholar 

  22. Leonard, F. Crosstalk between nanotube devices: contact and channel effects. Nanotechnology 17, 2381–2385 (2006).

    Article  CAS  Google Scholar 

  23. Franklin, A. D., Wong, H. S. P., Lin, A. & Chen, Z. H. Current scaling in aligned carbon nanotube array transistors with local bottom gating. IEEE Electron. Dev. Lett. 31, 644–646 (2010).

    Article  CAS  Google Scholar 

  24. Ho, X. N. et al. Scaling properties in transistors that use aligned arrays of single-walled carbon nanotubes. Nano Lett. 10, 499–503 (2010).

    Article  CAS  Google Scholar 

  25. Cao, Q., Han, S. J., Tulevski, G. S., Franklin, A. D. & Haensch, W. Evaluation of field-effect mobility and contact resistance of transistors that use solution-processed single-walled carbon nanotubes. ACS Nano 6, 6471–6477 (2012).

    Article  CAS  Google Scholar 

  26. Leonard, F. & Talin, A. A. Electrical contacts to one- and two-dimensional nanomaterials. Nature Nanotech. 6, 773–783 (2011).

    Article  CAS  Google Scholar 

  27. Kocabas, C. et al. High-frequency performance of submicrometer transistors that use aligned arrays of single-walled carbon nanotubes. Nano Lett. 9, 1937–1943 (2009).

    Article  CAS  Google Scholar 

  28. Wang, C. et al. Radio frequency and linearity performance of transistors using high-purity semiconducting carbon nanotubes. ACS Nano 5, 4169–4176 (2011).

    Article  CAS  Google Scholar 

  29. Moshammer, K., Hennrich, F. & Kappes, M. M. Selective suspension in aqueous sodium dodecyl sulfate according to electronic structure type allows simple separation of metallic from semiconducting single-walled carbon nanotubes. Nano Res. 2, 599–606 (2009).

    Article  CAS  Google Scholar 

  30. Green, A. A. & Hersam, M. C. Nearly single-chirality single-walled carbon nanotubes produced via orthogonal iterative density gradient ultracentrifugation. Adv. Mater. 23, 2185–2190 (2011).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

The authors thank J. Bucchignnano for technical assistance with electron-beam lithography, D. Farmer for assistance with atomic layer deposition of dielectrics for top-gated transistors, J.D. Tersoff for helpful discussions on the electrical properties of a bilayer structure, and J.B. Hannon and S. Guha for management support.

Author information

Authors and Affiliations

Authors

Contributions

Q.C. conceived and designed the experiments. Q.C. and S.J.H. performed the experiments and analysed the data. G.S.T. purified the nanotubes. Y.Z. performed TEM imaging. D.D. Lu performed the Technology Computer-Aided Design simulation. Q.C. wrote the manuscript. All authors discussed the results and commented on the manuscript.

Corresponding author

Correspondence to Qing Cao.

Supplementary information

Supplementary information

Supplementary information (PDF 1723 kb)

Rights and permissions

Reprints and permissions

About this article

Cite this article

Cao, Q., Han, Sj., Tulevski, G. et al. Arrays of single-walled carbon nanotubes with full surface coverage for high-performance electronics. Nature Nanotech 8, 180–186 (2013). https://doi.org/10.1038/nnano.2012.257

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/nnano.2012.257

This article is cited by

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing