Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Roll-to-roll production of 30-inch graphene films for transparent electrodes

This article has been updated

Abstract

The outstanding electrical1, mechanical2,3 and chemical4,5 properties of graphene make it attractive for applications in flexible electronics6,7,8. However, efforts to make transparent conducting films from graphene have been hampered by the lack of efficient methods for the synthesis, transfer and doping of graphene at the scale and quality required for applications. Here, we report the roll-to-roll production and wet-chemical doping of predominantly monolayer 30-inch graphene films grown by chemical vapour deposition onto flexible copper substrates. The films have sheet resistances as low as 125 Ω □−1 with 97.4% optical transmittance, and exhibit the half-integer quantum Hall effect, indicating their high quality. We further use layer-by-layer stacking to fabricate a doped four-layer film and measure its sheet resistance at values as low as 30 Ω □−1 at 90% transparency, which is superior to commercial transparent electrodes such as indium tin oxides. Graphene electrodes were incorporated into a fully functional touch-screen panel device capable of withstanding high strain.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Schematic of the roll-based production of graphene films grown on a copper foil.
Figure 2: Photographs of the roll-based production of graphene films.
Figure 3: Optical characterizations of the graphene films prepared using layer-by-layer transfer on SiO2/silicon and PET substrates.
Figure 4: Electrical characterizations of layer-by-layer transferred and HNO3-doped graphene films.

Similar content being viewed by others

Change history

  • 25 June 2010

    In the PDF version of this Letter originally published online, the authors were listed incorrectly. This error has now been corrected.

References

  1. Geim, A. K. & Novoselov, K. S. The rise of graphene. Nature Mater. 6, 183–191 (2007).

    Article  CAS  Google Scholar 

  2. Lee, C., Wei, X., Kysar, J. W. & Hone, J. Measurement of the elastic properties and intrinsic strength of monolayer graphene. Science 321, 385–388 (2008).

    Article  CAS  Google Scholar 

  3. Bunch, J. S. et al. Impermeable atomic membranes from graphene sheets. Nano Lett. 8, 2458–2462 (2008).

    Article  CAS  Google Scholar 

  4. Elias, D. C. et al. Control of graphene's properties by reversible hydrogenation: evidence for graphene. Science 323, 610–613 (2009).

    Article  CAS  Google Scholar 

  5. Wang, X. et al. N-doping of graphene through electrothermal reactions with ammonia. Science 324, 768–771 (2009).

    Article  CAS  Google Scholar 

  6. Kim, K. S. et al. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457, 706–710 (2009).

    Article  CAS  Google Scholar 

  7. Kim, D.-H. et al. Stretchable and foldable silicon integrated circuits. Science 320, 507–511 (2008).

    Article  CAS  Google Scholar 

  8. Sekitani, T. et al. A rubberlike stretchable active matrix using elastic conductors. Science 321, 1468–1472 (2008).

    Article  CAS  Google Scholar 

  9. Reina, A. et al. Large area, few-layer graphene films on arbitrary substrates by chemical vapor deposition. Nano Lett. 9, 30–35 (2009).

    Article  CAS  Google Scholar 

  10. Cai, W. W. et al. Large area few-layer graphene/graphite films as transparent thin conducting electrodes. Appl. Phys. Lett. 95, 123115 (2009).

    Article  Google Scholar 

  11. Lee, Y. et al. Wafer-scale synthesis and transfer of graphene films. Nano Lett. 10, 490–493 (2010).

    Article  CAS  Google Scholar 

  12. Caldwell, J. D. et al. Technique for the dry transfer of epitaxial graphene onto arbitrary substrates. ACS Nano 4, 1108–1114 (2010).

    Article  CAS  Google Scholar 

  13. Li, X. et al. Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324, 1312–1314 (2009).

    Article  CAS  Google Scholar 

  14. Ahn, S. H. & Guo, L. J. High-speed roll-to-roll nanoimprint lithography on flexible plastic substrates. Adv. Mater. 20, 2044–2049 (2008).

    Article  CAS  Google Scholar 

  15. Yerushalmi, R., Jacobson, Z. A., Ho, J. C., Fan, Z. & Javey, A. Large scale, highly ordered assembly of nanowire parallel arrays by differential roll printing. Appl. Phys. Lett. 91, 203104 (2007).

    Article  Google Scholar 

  16. Chang, Y. K. & Hong, F. C. The fabrication of ZnO nanowire field-effect transistors by roll-transfer printing. Nanotechnology 20, 195302 (2009).

    Article  Google Scholar 

  17. Jo, G. et al. Etching solution for etching Cu and Cu/Ti metal layer of liquid crystal display device and method of fabricating the same. US patent, 6,881,679 (2005).

  18. Hecht, D. S. et al. Carbon nanotube film on plastic as transparent electrode for resistive touch screens. J. Soc. Inf. Display 17, 941–946 (2009).

    Article  CAS  Google Scholar 

  19. Li, X. et al. Transfer of large-area graphene films for high-performance transparent conductive electrodes. Nano Lett. 9, 4359–4363 (2009).

    Article  CAS  Google Scholar 

  20. Hass, J. et al. Why multilayer graphene on 4H-SiC(000–1) behaves like a single sheet of graphene. Phys. Rev. Lett. 100, 125504 (2008).

    Article  CAS  Google Scholar 

  21. Sprinkle, M. et al. First direct observation of a nearly ideal graphene band structure. Phys. Rev. Lett. 103, 226803 (2009).

    Article  CAS  Google Scholar 

  22. Ferrari, A. C. et al. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 97, 187401 (2006).

    Article  CAS  Google Scholar 

  23. Nair, R. R. et al. Fine structure constant defines visual transparency of graphene. Science 320, 1308 (2008).

    Article  CAS  Google Scholar 

  24. Das, A. et al. Monitoring dopants by Raman scattering in an electrochemically top-gated graphene transistor. Nature Nanotech. 3, 210–215 (2008).

    Article  CAS  Google Scholar 

  25. Geng, H.-Z. et al. Effect of acid treatment on carbon nanotube-based flexible transparent conducting films. J. Am. Chem. Soc. 129, 7758–7759 (2007).

    Article  CAS  Google Scholar 

  26. Schrivera, M., Reganb, W., Losterb, M. & Zettl, A. Carbon nanostructure–aSi:H photovoltaic cells with high open-circuit voltage fabricated without dopants. Solid State Commun. 150, 561–563 (2010).

    Article  Google Scholar 

  27. Wu, J. et al. Organic light-emitting diodes on solution-processed graphene transparent electrodes. ACS Nano 4, 43–48 (2010).

    Article  CAS  Google Scholar 

  28. Lee, J.-Y., Connor, S. T., Cui, Y. & Peumans, P. Solution-processed metal nanowire mesh transparent electrodes. Nano Lett. 8, 689–692 (2008).

    Article  CAS  Google Scholar 

  29. Cao, H. L. et al. Electronic transport in chemical vapor deposited graphene synthesized on Cu: Quantum Hall effect and weak localization. Appl. Phys. Lett. 96, 122106 (2010).

    Article  Google Scholar 

  30. Cairns, D. R. et al. Strain-dependent electrical resistance of tin-doped indium oxide on polymer substrates. Appl. Phys. Lett. 76, 1425–1427 (2000).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by the National Research Foundation of Korea (NRF), funded by the Ministry of Education, Science and Technology (2009-0081966, 2009-0082608, 2009-0083540, 2009-0090017, World Class University R33-2008-000-10138-0, National Honor Scientist Program), the Research Centre of Breakthrough Technology Program through the Korea Institute of Energy Technology Evaluation and Planning (KETEP), funded by the Ministry of Knowledge Economy (2009-3021010030-11-1), Singapore National Research Foundation (NRF-RF2008-07) & NUS NanoCore, and T.J. Park Junior Faculty Fellowship. The authors thank R. Ruoff (University of Texas at Austin) and P. Kim (Columbia University) for helpful comments, W.S. Lim, K.D. Kim and Y.D. Kim (SKKU) for assistance in XPS analysis, and Samkwang Well Tech Co. for assistance with the touch-panel fabrication.

Author information

Authors and Affiliations

Authors

Contributions

B.H.H. planned and supervised the project, with assistance in supervision from J.H.A. Y.-J.K., B.O., K.S.K. and S.I. provided advice for the project. B.H.H., S.B. and H.K. conceived and carried out the experiment. B.H.H., J.H.A. and B.O. analysed the data and wrote the manuscript. X.X., J.B., Y.Z. and B.O. fabricated the QHE devices, and carried out the measurements. Y.L. and Y.I.S. helped with the fabrication of touch-screen panels and electromechanical analysis. J.S.P., H.R.K. and T.L. helped with the doping experiment.

Corresponding authors

Correspondence to Jong-Hyun Ahn or Byung Hee Hong.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary information

Supplementary information (PDF 1412 kb)

Supplementary information

Supplementary movie (MOV 12086 kb)

Rights and permissions

Reprints and permissions

About this article

Cite this article

Bae, S., Kim, H., Lee, Y. et al. Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nature Nanotech 5, 574–578 (2010). https://doi.org/10.1038/nnano.2010.132

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/nnano.2010.132

This article is cited by

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing