Figure 3.

Unfortunately we are unable to provide accessible alternative text for this. If you require assistance to access this image, please contact help@nature.com or the author

The normalized M(T) data of the La2CoMnO6 films on (a) the (111)-oriented substrates and (b) the (001)-oriented substrates. The arrow in a marks the TC of La2CoMnO6 on LSAT (111) at 211K. The inset of a shows normalized M(T) and χ(T) of La2CoMnO6 on LSAT (111) near TC as well as its corresponding Curie–Weiss fit. The in-plane M(H) hysteresis curves of the corresponding films at 5K are shown in c and d. A linear paramagnetic background of the SrTiO3 substrate was subtracted.